CN106313236A - Straw processing solution resistant to abrasion and scrubbing and preparation method thereof - Google Patents
Straw processing solution resistant to abrasion and scrubbing and preparation method thereof Download PDFInfo
- Publication number
- CN106313236A CN106313236A CN201610718251.2A CN201610718251A CN106313236A CN 106313236 A CN106313236 A CN 106313236A CN 201610718251 A CN201610718251 A CN 201610718251A CN 106313236 A CN106313236 A CN 106313236A
- Authority
- CN
- China
- Prior art keywords
- parts
- straw
- water
- processing solution
- polyvinyl chloride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a straw processing solution resistant to abrasion and scrubbing. The straw processing solution resistant to abrasion and scrubbing is prepared from, by weight, 3-5 parts of waterborne amino resin, 3-5 parts of nano-scale silicon carbide, 0.1-0.2 part of pentaerythritol oleate, 1-2 parts of zinc stearate, 3-5 parts of polyethylene wax, 0.4-0.6 part of peregal o-10, 10-15 parts of modified polyvinyl chloride latex, 0.01-0.02 part of oxypropylene ethylene oxide glyceryl ether, 2-4 parts of styrene-acrylic emulsions and 40-50 parts of water. Through the straw processing solution, a transparent uniform coating can be formed on the surface of straw, the waterproof performance and water vapor permeability are excellent, and the straw material is well protected and is not prone to being affected with damp or mildew. Meanwhile, the straw processing solution has the characteristics of good abrasion and scrubbing resistance and is convenient to clean in daily life, and the service life of the straw product can be effectively prolonged.
Description
Technical field
The present invention relates to straw technical field of surface, particularly relate to a kind of wear-resisting scrubbing resistance straw treatment fluid and system thereof
Preparation Method.
Background technology
China is large agricultural country, and stalk resource is the abundantest, and distribution is wide, and kind is many and yield is huge.At present, crops straw
The processing mode of the stalk overwhelming majority is to process at direct open incineration, and this not only causes the great wasting of resources, and causes big
Gas pollutes, and affects atmosphere quality.Straw has the advantages that quality is pliable and tough, cheap, is suitable for weaving industry, makes grass
Kinds of processes product and the article of everyday use such as cap, straw mat, hand basket, extension picture, can make full use of existing resource, alleviates ambient pressure, again can
Develop the value of straw substantially, meet consumer's market demand to baskets craft.But straw is as one
Vegetable material, its resistance to water is poor, is susceptible to go rotten, deliquescence, and surface abrasion resistance damages, scrub performance is poor, it is difficult to for a long time
Preserve and use, have impact on the using value of straw baskets craft.
Summary of the invention
The object of the invention is contemplated to make up the defect of prior art, it is provided that a kind of wear-resisting scrubbing resistance straw treatment fluid and
Preparation method.
The present invention is achieved by the following technical solutions:
A kind of wear-resisting scrubbing resistance straw treatment fluid, it is to be prepared by the raw material of following weight parts:
Water-compatible amino resin 3-5, nanometer silicon carbide 3-5, PETO 0.1-0.2, zinc stearate 1-2, Tissuemat E
3-5, peregal o-10 0.4-0.6, modified polyvinyl chloride emulsion 10-15, polyoxypropylene ethylene oxide glycerin ether 0.01-0.02,
Styrene-acrylic emulsion 2-4, water 40-50；
Wherein modified polyvinyl chloride emulsion is prepared by the raw materials in: vinyl chloride 10-15, acrylic acid 3-5, and carboxymethyl is fine
Dimension element 0.5-1, trifluoro propyl methyl cyclotrisiloxane 0.3-0.5, potassium peroxydisulfate 0.01-0.02, nano titanium oxide 1-2, ten
Sodium dialkyl sulfate 0.05-0.1, water 20-30；The preparation method of modified polyvinyl chloride emulsion be first by sodium lauryl sulphate and
Carboxymethyl cellulose be added to the water stirring until being completely dissolved, be subsequently adding vinyl chloride, acrylic acid, nano titanium oxide and trifluoro
Hydroxypropyl methyl cyclotrisiloxane 800-1000r/min stirs 0.5-1h, is eventually adding remaining raw material 70-80 DEG C reaction 2-4h, cold
The most afterwards and get final product.
The preparation method of a kind of wear-resisting scrubbing resistance straw treatment fluid, comprises the following steps:
(1) nanometer silicon carbide, Tissuemat E, zinc stearate, peregal o-10 and PETO are added container jointly
After middle 110-120 DEG C of melting mixing add 1/2-2/3 amount water in 90-95 DEG C, 800-1000r/min stir 0.5-1h, cool down
Rear addition modified polyvinyl chloride emulsion and styrene-acrylic emulsion stir, and obtain complex emulsions；
(2) 400-600r/min, 60-80 DEG C of stirring 0.5-1h after being mixed by remaining raw material, adds the Composite Milk in (1) after cooling
Liquid 1000-1500r/min stirs 5-10min, obtains wear-resisting scrubbing resistance straw treatment fluid.
The invention have the advantage that
The present invention improves poisture-penetrability by acrylic acid and Modified by Carboxymethyl Cellulose, is changed by trifluoro propyl methyl cyclotrisiloxane
Property improve resistance to water, by compound ageing resistance and the mechanical property of improving of nano titanium oxide, prepared modified polyvinyl chloride breast
Obtaining straw treatment fluid after liquid is compounding with remaining raw material, can form the coating of clear homogeneous on straw surface, it is water-fast, poisture-penetrability
Can be excellent, stalk material is played good protective action, is difficult to make moist, go mouldy.Have simultaneously wear-resistant, scrub performance good
Feature, it is simple to daily cleaning, can effectively extend the service life of stalk product.
Detailed description of the invention
A kind of wear-resisting scrubbing resistance straw treatment fluid, it is to be prepared by the raw material of following weight parts:
Water-compatible amino resin 3, nanometer silicon carbide 3, PETO 0.1, zinc stearate 1, Tissuemat E 3, peregal o-
10 0.4, modified polyvinyl chloride emulsion 10, polyoxypropylene ethylene oxide glycerin ether 0.01, styrene-acrylic emulsion 2, water 40；
Wherein modified polyvinyl chloride emulsion is prepared by the raw materials in: vinyl chloride 10, acrylic acid 3, carboxymethyl cellulose
0.5, trifluoro propyl methyl cyclotrisiloxane 0.3, potassium peroxydisulfate 0.01, nano titanium oxide 1, sodium lauryl sulphate 0.05,
Water 20；The preparation method of modified polyvinyl chloride emulsion is first sodium lauryl sulphate and carboxymethyl cellulose to be added to the water stirring
Until being completely dissolved, it is subsequently adding vinyl chloride, acrylic acid, nano titanium oxide and trifluoro propyl methyl cyclotrisiloxane 800r/
Min stirs 0.5h, is eventually adding remaining raw material 70 DEG C reaction 2h, after cooling and get final product.
The preparation method of a kind of wear-resisting scrubbing resistance straw treatment fluid, comprises the following steps:
(1) nanometer silicon carbide, Tissuemat E, zinc stearate, peregal o-10 and PETO are added container jointly
In add after 110 DEG C of melting mixing in the water of 1/2 amount 90 DEG C, 800r/min stir 0.5h, addition modified polyvinyl chloride after cooling
Emulsion and styrene-acrylic emulsion stir, and obtain complex emulsions；
(2) after being mixed by remaining raw material, 400r/min, 60 DEG C of stirring 0.5h, add the complex emulsions 1000r/ in (1) after cooling
Min stirs 5min, obtains wear-resisting scrubbing resistance straw treatment fluid.
Above-mentioned prepared straw treatment fluid is carried out performance test, and result is as follows:
| Project | Testing result |
| Appearance of film | Normally |
| Transparency | Excellent |
| Fineness (μm) | ≤10 |
| Bin stability (50 DEG C) | Without exception |
| Resistance to water (24h) | Without exception |
Claims (2)
1. a wear-resisting scrubbing resistance straw treatment fluid, it is characterised in that it is to be prepared by the raw material of following weight parts:
Water-compatible amino resin 3-5, nanometer silicon carbide 3-5, PETO 0.1-0.2, zinc stearate 1-2, Tissuemat E
3-5, peregal o-10 0.4-0.6, modified polyvinyl chloride emulsion 10-15, polyoxypropylene ethylene oxide glycerin ether 0.01-0.02,
Styrene-acrylic emulsion 2-4, water 40-50；
Described modified polyvinyl chloride emulsion is prepared by the raw materials in: vinyl chloride 10-15, acrylic acid 3-5, and carboxymethyl is fine
Dimension element 0.5-1, trifluoro propyl methyl cyclotrisiloxane 0.3-0.5, potassium peroxydisulfate 0.01-0.02, nano titanium oxide 1-2, ten
Sodium dialkyl sulfate 0.05-0.1, water 20-30；The preparation method of modified polyvinyl chloride emulsion be first by sodium lauryl sulphate and
Carboxymethyl cellulose be added to the water stirring until being completely dissolved, be subsequently adding vinyl chloride, acrylic acid, nano titanium oxide and trifluoro
Hydroxypropyl methyl cyclotrisiloxane 800-1000r/min stirs 0.5-1h, is eventually adding remaining raw material 70-80 DEG C reaction 2-4h, cold
The most afterwards and get final product.
The preparation method of a kind of wear-resisting scrubbing resistance straw treatment fluid the most according to claim 1, it is characterised in that include with
Lower step:
(1) nanometer silicon carbide, Tissuemat E, zinc stearate, peregal o-10 and PETO are added container jointly
After middle 110-120 DEG C of melting mixing add 1/2-2/3 amount water in 90-95 DEG C, 800-1000r/min stir 0.5-1h, cool down
Rear addition modified polyvinyl chloride emulsion and styrene-acrylic emulsion stir, and obtain complex emulsions；
(2) 400-600r/min, 60-80 DEG C of stirring 0.5-1h after being mixed by remaining raw material, adds the Composite Milk in (1) after cooling
Liquid 1000-1500r/min stirs 5-10min, obtains wear-resisting scrubbing resistance straw treatment fluid.