CN106182280A - A kind of yellowing-resistant UV resistance straw treatment fluid and preparation method thereof - Google Patents
A kind of yellowing-resistant UV resistance straw treatment fluid and preparation method thereof Download PDFInfo
- Publication number
- CN106182280A CN106182280A CN201610723733.7A CN201610723733A CN106182280A CN 106182280 A CN106182280 A CN 106182280A CN 201610723733 A CN201610723733 A CN 201610723733A CN 106182280 A CN106182280 A CN 106182280A
- Authority
- CN
- China
- Prior art keywords
- treatment fluid
- water
- yellowing
- resistant
- polyvinyl chloride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of yellowing-resistant UV resistance straw treatment fluid, it is to be prepared by the raw material of following weight parts: Tissuemat E 35, Benzoinum 0.3 0.5, white mineral oil 12, peregal o 10 0.4 0.6, UV absorbent UV 327 0.1 0.2, Tween 80 0.1 0.2, modified polyvinyl chloride emulsion 10 15, hydroxyethyl cellulose 0.3 0.5, sodium citrate 0.3 0.5, water 40 50.The straw treatment fluid of the present invention can form the coating of clear homogeneous on straw surface, and it is water-fast, water vapour permeability is excellent, and stalk material plays good protective action, is difficult to make moist, go mouldy.There is good UV resistance performance simultaneously, be effective against aging, xanthochromia, attractive and durable.
Description
Technical field
The present invention relates to straw technical field of surface, particularly relate to a kind of yellowing-resistant UV resistance straw treatment fluid and
Preparation method.
Background technology
China is large agricultural country, and stalk resource is the abundantest, and distribution is wide, and kind is many and yield is huge.At present, crops straw
The processing mode of the stalk overwhelming majority is to process at direct open incineration, and this not only causes the great wasting of resources, and causes big
Gas pollutes, and affects atmosphere quality.Straw has the advantages that quality is pliable and tough, cheap, is suitable for weaving industry, makes grass
Kinds of processes product and the article of everyday use such as cap, straw mat, hand basket, extension picture, can make full use of existing resource, alleviates ambient pressure, again can
Develop the value of straw substantially, meet consumer's market demand to baskets craft.But straw is as one
Vegetable material, its resistance to water is poor, is susceptible to go rotten, deliquescence, it is difficult to long-term preserve and uses, and UV resistance poor performance,
It is susceptible to xanthochromia, affects outward appearance and serviceability, and then have impact on the using value of straw baskets craft.
Summary of the invention
The object of the invention is contemplated to make up the defect of prior art, it is provided that a kind of yellowing-resistant UV resistance straw treatment fluid and
Its preparation method.
The present invention is achieved by the following technical solutions:
A kind of yellowing-resistant UV resistance straw treatment fluid, it is to be prepared by the raw material of following weight parts:
Tissuemat E 3-5, Benzoinum 0.3-0.5, white mineral oil 1-2, peregal o-10 0.4-0.6, UV absorbent UV-327
0.1-0.2, tween 80 0.1-0.2, modified polyvinyl chloride emulsion 10-15, hydroxyethyl cellulose 0.3-0.5, sodium citrate
0.3-0.5, water 40-50;
Wherein modified polyvinyl chloride emulsion is prepared by the raw materials in: vinyl chloride 10-15, acrylic acid 3-5, and carboxymethyl is fine
Dimension element 0.5-1, trifluoro propyl methyl cyclotrisiloxane 0.3-0.5, potassium peroxydisulfate 0.01-0.02, nano titanium oxide 1-2, ten
Sodium dialkyl sulfate 0.05-0.1, water 20-30;The preparation method of modified polyvinyl chloride emulsion be first by sodium lauryl sulphate and
Carboxymethyl cellulose be added to the water stirring until being completely dissolved, be subsequently adding vinyl chloride, acrylic acid, nano titanium oxide and trifluoro
Hydroxypropyl methyl cyclotrisiloxane 800-1000r/min stirs 0.5-1h, is eventually adding remaining raw material 70-80 DEG C reaction 2-4h, cold
The most afterwards and get final product.
The preparation method of a kind of yellowing-resistant UV resistance straw treatment fluid, comprises the following steps:
(1) Tissuemat E, Benzoinum, white mineral oil and peregal o-10 are added jointly in container after 110-120 DEG C of melting mixing
Add 1/2-2/3 amount water in 90-95 DEG C, 800-1000r/min stir 0.5-1h, after cooling addition modified polyvinyl chloride emulsion
Stir, obtain complex emulsions;
(2) 400-600r/min, 60-80 DEG C of stirring 0.5-1h after being mixed by remaining raw material, adds the Composite Milk in (1) after cooling
Liquid 1000-1500r/min stirs 5-10min, obtains yellowing-resistant UV resistance straw treatment fluid.
The invention have the advantage that
The present invention improves poisture-penetrability by acrylic acid and Modified by Carboxymethyl Cellulose, is changed by trifluoro propyl methyl cyclotrisiloxane
Property improve resistance to water, by compound ageing resistance and the mechanical property of improving of nano titanium oxide, prepared modified polyvinyl chloride breast
Obtaining straw treatment fluid after liquid is compounding with remaining raw material, can form the coating of clear homogeneous on straw surface, it is water-fast, poisture-penetrability
Can be excellent, stalk material is played good protective action, is difficult to make moist, go mouldy.There is good UV resistance performance simultaneously, have
Effect resists aging, xanthochromia, attractive and durable.
Detailed description of the invention
A kind of yellowing-resistant UV resistance straw treatment fluid, it is to be prepared by the raw material of following weight parts:
Tissuemat E 3, Benzoinum 0.3, white mineral oil 1, peregal o-10 0.4, UV absorbent UV-327 0.1, tween 80
0.1, modified polyvinyl chloride emulsion 10, hydroxyethyl cellulose 0.3, sodium citrate 0.3, water 40;
Wherein modified polyvinyl chloride emulsion is prepared by the raw materials in: vinyl chloride 10, acrylic acid 3, carboxymethyl cellulose
0.5, trifluoro propyl methyl cyclotrisiloxane 0.3, potassium peroxydisulfate 0.01, nano titanium oxide 1, sodium lauryl sulphate 0.05,
Water 20;The preparation method of modified polyvinyl chloride emulsion is first sodium lauryl sulphate and carboxymethyl cellulose to be added to the water stirring
Until being completely dissolved, it is subsequently adding vinyl chloride, acrylic acid, nano titanium oxide and trifluoro propyl methyl cyclotrisiloxane 800r/
Min stirs 0.5h, is eventually adding remaining raw material 70 DEG C reaction 2h, after cooling and get final product.
The preparation method of a kind of yellowing-resistant UV resistance straw treatment fluid, comprises the following steps:
(1) Tissuemat E, Benzoinum, white mineral oil and peregal o-10 are added jointly in container and add after 110 DEG C of melting mixing
In the water of 1/2 amount 90 DEG C, 800r/min stir 0.5h, after cooling add modified polyvinyl chloride emulsion stir, obtain Composite Milk
Liquid;
(2) after being mixed by remaining raw material, 400r/min, 60 DEG C of stirring 0.5h, add the complex emulsions 1000r/ in (1) after cooling
Min stirs 5min, obtains yellowing-resistant UV resistance straw treatment fluid.
Above-mentioned prepared straw treatment fluid is carried out performance test, and result is as follows:
Project | Testing result |
Appearance of film | Normally |
Transparency | Excellent |
Fineness (μm) | ≤10 |
Bin stability (50 DEG C) | Without exception |
Resistance to water (24h) | Without exception |
Claims (2)
1. a yellowing-resistant UV resistance straw treatment fluid, it is characterised in that it is to be prepared by the raw material of following weight parts:
Tissuemat E 3-5, Benzoinum 0.3-0.5, white mineral oil 1-2, peregal o-10 0.4-0.6, UV absorbent UV-327
0.1-0.2, tween 80 0.1-0.2, modified polyvinyl chloride emulsion 10-15, hydroxyethyl cellulose 0.3-0.5, sodium citrate 0.3-
0.5, water 40-50;
Described modified polyvinyl chloride emulsion is prepared by the raw materials in: vinyl chloride 10-15, acrylic acid 3-5, and carboxymethyl is fine
Dimension element 0.5-1, trifluoro propyl methyl cyclotrisiloxane 0.3-0.5, potassium peroxydisulfate 0.01-0.02, nano titanium oxide 1-2, ten
Sodium dialkyl sulfate 0.05-0.1, water 20-30;The preparation method of modified polyvinyl chloride emulsion be first by sodium lauryl sulphate and
Carboxymethyl cellulose be added to the water stirring until being completely dissolved, be subsequently adding vinyl chloride, acrylic acid, nano titanium oxide and trifluoro
Hydroxypropyl methyl cyclotrisiloxane 800-1000r/min stirs 0.5-1h, is eventually adding remaining raw material 70-80 DEG C reaction 2-4h, cold
The most afterwards and get final product.
The preparation method of a kind of yellowing-resistant UV resistance straw treatment fluid the most according to claim 1, it is characterised in that include
Following steps:
(1) Tissuemat E, Benzoinum, white mineral oil and peregal o-10 are added jointly in container after 110-120 DEG C of melting mixing
Add 1/2-2/3 amount water in 90-95 DEG C, 800-1000r/min stir 0.5-1h, after cooling addition modified polyvinyl chloride emulsion
Stir, obtain complex emulsions;
(2) 400-600r/min, 60-80 DEG C of stirring 0.5-1h after being mixed by remaining raw material, adds the Composite Milk in (1) after cooling
Liquid 1000-1500r/min stirs 5-10min, obtains yellowing-resistant UV resistance straw treatment fluid.