CN106284015B - 高使用寿命压花地坪及其制备方法 - Google Patents
高使用寿命压花地坪及其制备方法 Download PDFInfo
- Publication number
- CN106284015B CN106284015B CN201610743892.3A CN201610743892A CN106284015B CN 106284015 B CN106284015 B CN 106284015B CN 201610743892 A CN201610743892 A CN 201610743892A CN 106284015 B CN106284015 B CN 106284015B
- Authority
- CN
- China
- Prior art keywords
- cement
- parts
- service life
- iron oxide
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种高使用寿命压花地坪及其制备方法，所述制备方法包括以下步骤：(1)混凝土面找平：将混凝土铺设在地面上，震捣、找平；(2)彩色强化剂处理；(3)脱模粉处理；(4)压模；(5)水洗；(6)保护剂处理。本发明具有整体施工，一次成型、快速固化、维修简便的优点，采用本发明生产的压花地坪具有耐磨、耐腐、致密、抗压、抗折、不起尘，地坪颜色多样，款式多样，色彩鲜艳持久，性价比高、选择面广，使用寿命长达8年以上。
Description
技术领域
本发明涉及地坪技术领域，尤其涉及一种高使用寿命压花地坪及其制备方法。
背景技术
传统的压模地坪也叫艺术地坪、压花地坪，是采用特殊耐磨矿物骨料、高标号水泥、无机颜料及聚合物添加剂合成的彩色地坪硬化剂，通过压模、整理、密封处理等施工工艺使混凝土表面产生不同凡响的石质纹理和丰富的色彩效果，属于无机地坪。
普通硅酸盐水泥呈灰色粉末状，而其他硅酸盐水泥的颜色会根据水泥熟料的化学成分和矿物组成、矿物混合材的品种和惨量不同而有所不同。在装饰混凝土中，可以利用普通硅酸盐水泥的特征灰色，造就混凝土的本色美。如果想要改变装饰混凝土的颜色，可以在本色混凝土的基础上，再通过颜料、染色剂等对其进行着色，也可以选择使用白色或彩色硅酸盐水泥。
白色硅酸盐水泥简称白水泥，是以氧化铁含量低的石灰石、白泥、硅石为主要原料，经烧结得到以硅酸钙为主要矿物组成的熟料，再经淬冷处理，加入适量石膏磨细而成。白水泥的一般物理性能和普通硅酸盐水泥相似。
彩色硅酸盐水泥简称彩色水泥，一般用白色硅酸盐水泥熟料、优质白色石膏及矿物颜料共同磨细而制得：深色的彩色水泥可用普通硅酸盐水泥加深色颜料调制。所用颜料需要满足耐碱要求，且颜料的化学成分组成应当既不会被水泥影响，也不会对水泥的组成和性能起破坏作用；同时，颜料要满足耐太阳辐射的要求，在阳光和大气中能耐久不褪色；颜料的细度要求很高，与水泥混合时要能均匀分散，避免形成色差，并且不含可溶性盐，以免在干湿循环中析出结晶，造成混凝土表面褪色。常用的无机颜料有氧化铁(可制红、黄、褐、黑色)，氧化铬(绿色)，钴蓝(蓝色)，群青蓝(蓝色)等；有机颜料有孔雀蓝(蓝色)，天津绿(绿色)等。彩色水泥的另一种生产方法是在生料中加入少量着色剂，直接煅烧成彩色熟料后再磨成水泥。由于需求量不够和储存时间的限制，这种水泥难以在现代规模化的水泥厂中组织批量生产。
利用彩色水泥、彩色骨料、以及着色添加剂等方法，混凝土的色彩可以随意变化，除了人们印象中的灰色特征，混凝土可以呈现绚丽色彩。装饰混凝土中常用的着色方法有添加颜料的整体着色、干撒彩色硬化剂表层着色，还有通过化学反应染色等方法。
彩色水泥在涂抹之后，经过一段时间的曝晒和雨水冲刷，其表面会蒙上一层白霜，从而失去光彩，色泽暗淡，图案受损，影响装饰效果，此现象称为水泥的盐析或泛白。国外对泛白问题早已提出并进行了大量的研究，而我国的装饰混凝土刚刚起步，对泛白问题的研究还在探索之中。
随着人们生活水平的提高，对生活环境的要求也越来越高，地面整洁、平坦、美观也是人们对生活环境追求的一部分，但目前市场上销售的地坪或色彩不均、观赏度不足，或地坪不够坚固、使用寿命短，不能满足人们对地坪美观实用的要求，因此，生产出一种既能够保持色彩均匀鲜艳，又有良好实用性能的地坪产品是目前地坪生产的研究重点。
发明内容
针对现有技术中存在的上述不足，本发明所要解决的技术问题是提供一种压花地坪的生产方法。
本发明目的是通过如下技术方案实现的：
一种高使用寿命压花地坪的制备方法，包括下述步骤：
(1)混凝土面找平：将混凝土铺设在地面上，震捣、找平；
(2)彩色强化剂处理；
(3)脱模粉处理；
(4)压模；
(5)水洗；
(6)保护剂处理。
所述步骤(2)中的彩色强化剂由下述重量份原料组成：黄沙2-4份、水泥1-3份、颜料0.03-0.07份。
优选地，
所述彩色强化剂中的水泥为P.C 32.5水泥、P.O 42.5水泥、P.O 42.5R水泥、P.O52.5水泥、P.O 52.5R水泥中一种或多种的混合物；
所述彩色强化剂中的颜料为氧化铁黄、氧化铁红、氧化铁棕、氧化铁黑、复合颜料蓝、复合颜料绿中一种或多种的混合物。
所述步骤(3)中的脱模粉由下述重量份原料组成：碳酸钙1-3份、滑石粉3-5份、脂肪酸盐0.2-1.8份、颜料0.002-0.007份。
优选地，
所述脱模粉中颜料为氧化铁黄、氧化铁红、氧化铁棕、氧化铁黑、复合颜料蓝、复合颜料绿中一种或多种的混合物。
所述的脂肪酸盐为硬脂酸锌、十六烷酸钙、硬脂酸钙中一种或多种的混合物。
更优选地，
所述的脂肪酸盐由硬脂酸锌、十六烷酸钙、硬脂酸钙混合而成，所述硬脂酸锌、十六烷酸钙、硬脂酸钙的质量比为(1-3)：(1-3)：(1-3)。
所述步骤(6)中保护剂由下述重量份原料组成：有机溶剂1-3份、丙烯酸树脂1-3份。
优选地，
所述的有机溶剂为乙酸正丁酯、乙酸叔丁酯、乙酸异丙酯、二甲苯中一种或多种的混合物。
所述的丙烯酸树脂为丙烯酸树脂BS1206、丙烯酸树脂BS108、丙烯酸树脂BS2050、丙烯酸树脂BS2350、丙烯酸树脂BS1880、丙烯酸树脂BS1863中一种或多种的混合物。
更优选地，
所述的有机溶剂由乙酸正丁酯、乙酸叔丁酯、乙酸异丙酯混合而成，所述乙酸正丁酯、乙酸叔丁酯、乙酸异丙酯的质量比为(1-3)：(1-3)：(1-3)。
优选地，
所述的高使用寿命压花地坪的制备方法，包括下述步骤：
(1)混凝土面找平：将混凝土铺设在地面上，震捣、找平；
(2)彩色强化剂处理：将彩色强化剂均匀撒在混凝土表面，整平、拉光，所述彩色强化剂的用量为1-4千克/平方米；
(3)脱模粉处理：将脱模粉均匀撒在混凝土表面，所述脱模粉的用量为0.1-0.4千克/平方米；
(4)压模：用压花模板覆盖在混凝土表面，压模；
(5)水洗：静置2-3天后，用清水冲掉混凝土表面的脱模粉；
(6)保护剂处理：在混凝土表面涂刷保护剂，所述保护剂的用量为0.1-0.4千克/平方米。
所述步骤(1)中混凝土可以采用市售的抗压强度为C30-C80的混凝土，也可以由下述重量份原料组成：PⅡ42.5R水泥95-105份、石灰岩碎石440-540份、聚丙烯酸乳液1-10份、水28-38份。
所述的石灰岩碎石的粒径为5-10mm。
本发明还提供了一种高使用寿命压花地坪，采用上述方法制备而成。
本发明具有整体施工，一次成型、快速固化、维修简便的优点，采用本发明生产的压花地坪具有耐磨、耐腐、致密、抗压、抗折、不起尘，地坪颜色多样，款式多样，色彩鲜艳持久，性价比高、选择面广，使用寿命长达8年以上。
具体实施方式
下面结合实施例对本发明做进一步的说明，以下所述，仅是对本发明的较佳实施例而已，并非对本发明做其他形式的限制，任何熟悉本专业的技术人员可能利用上述揭示的技术内容加以变更为同等变化的等效实施例。凡是未脱离本发明方案内容，依据本发明的技术实质对以下实施例所做的任何简单修改或等同变化，均落在本发明的保护范围内。
实施例中各原料介绍：
P.O 52.5R水泥，采用山东山铝水泥有限公司生产的P.O 52.5R硅酸盐水泥。
PⅡ42.5R水泥，采用南京江南水泥有限公司生产的金宁羊牌PⅡ42.5R(C1)硅酸盐水泥。
石灰岩碎石，粒径7mm。
黄沙，采用湖南天成砂石有限公司提供的细度模数为2.3-3.0，平均粒径为0.35-0.5mm的中砂。
彩色强化剂和脱模粉中的颜料均采用氧化铁红，CAS号：1332-37-2，具体采用上海一品颜料有限公司生产的型号为190的氧化铁红，粒度为400目。
碳酸钙，CAS号：471-34-1，具体采用上海诺成药业股份有限公司生产的D30重质活性碳酸钙。
滑石粉，CAS号：14807-96-6，具体采用灵寿县勇昌矿产品加工厂生产的细度为400目的滑石粉。
硬脂酸钙，CAS号：1592-23-0。
丙烯酸树脂，CAS号：9003-01-4，具体采用江苏三木集团有限公司生产的丙烯酸树脂BS2050，酸值5-8mgKOH/g。
聚丙烯酸乳液，采用专利申请号：201210224666.6中实验一的方法制备。
硬脂酸锌，CAS号：557-05-1。
十六烷酸钙，CAS号：542-42-7。
乙酸正丁酯，CAS号：123-86-4。
乙酸叔丁酯，CAS号：540-88-5。
乙酸异丙酯，CAS号：108-21-4。
实施例1
高使用寿命压花地坪的制备方法，包括下述步骤：
(1)混凝土面找平：将混凝土铺设在地面上，震捣后，在泌水出现前找平至2平方米内落差<3毫米；
(2)彩色强化剂处理：等到混凝土表面没有泌水并且混凝土表面的含水率为5wt％，将彩色强化剂均匀撒在混凝土表面，当强固粉被充分湿润后，颜色开始变深，用铁镘子将撒有强固粉的表面抹平，与混凝土充分结合，第一遍彩色强化剂用量为1.35千克/平方米；当在镘抹撒有彩色强固粉的混凝土表面时，在还有过多的泌水或颜色较浅的地方，再均匀撒一层彩色强固粉，第二遍抛撒的方向应与第一次的方向垂直，第二遍彩色强化剂用量为0.9千克/平方米；当第二遍彩色强固粉已抹均匀并充分湿润后，在局部出现深浅不匀或难以覆盖的地方，再进行第三次撒粉，此次撒粉方向可有的放矢进行，主要根据表面实际深浅状况进行修补，并再用铁镘子仔细镘均匀，第三遍彩色强化剂用量为0.75千克/平方米；
(3)脱模粉处理：将脱模粉均匀撒在混凝土表面，混凝土表面脱模粉的用量为0.25千克/平方米；同时将脱模粉均匀撒在压花模板表面，压花模板表面脱模粉的用量为0.08千克/平方米；
(4)压模：从一个边缘开始，排放第一块压花模板，用夯实器夯压压花模板，将模板上的纹理压印在混凝土的表面，然后将第二块压花模板紧靠在第一块压花模板的边缘，如前所述，夯压模板，直到完成整个表面的压纹处理；压模时要确保所有模板的顶面齐平，以保证压印纹理的深度统一，脱模时，要垂直拿起，否则会损害已压印的纹理和勾缝，在压模过程中如遇到墙柱等障碍物，硬模板不适应时，要采用软模板，压模方法仍同前述；
(5)水洗：静置2.5天后，用手提式电动混凝土切割机切割混凝土伸缩缝，然后用软性的尼龙平板刷带水洗刷整个表面，用清水冲掉混凝土表面的脱模粉，待混凝土表面干燥后，在伸缩缝处打上密封硅胶；
(6)保护剂处理：脱模粉清除完毕，等混凝土完全干燥24小时后，在整个混凝土表面上用刷子涂刷涂刷保护剂，保护剂的用量为0.25千克/平方米。
所述步骤(2)中彩色强化剂由下述重量份原料组成：黄沙3份、P.O 52.5R水泥2份、氧化铁红0.05份。将黄沙、P.O 52.5R水泥、氧化铁红搅拌混合均匀即得彩色强化剂。
所述步骤(3)中脱模粉由下述重量份原料组成：碳酸钙2份、滑石粉4份、脂肪酸盐1.2份、氧化铁红0.0035份。将碳酸钙、滑石粉、脂肪酸盐、氧化铁红搅拌混合均匀即得脱模粉。
所述的脂肪酸盐由硬脂酸锌、十六烷酸钙、硬脂酸钙按质量比为1：1：1搅拌混合均匀得到。
所述步骤(6)中保护剂由下述重量份原料组成：有机溶剂1.5份、丙烯酸树脂2份。将有机溶剂、丙烯酸树脂搅拌混合均匀即得保护剂。
所述的有机溶剂由乙酸正丁酯、乙酸叔丁酯、乙酸异丙酯按质量比为1：1：1搅拌混合均匀得到。
所述步骤(1)中混凝土由下述重量份原料组成：PⅡ42.5R水泥100份、石灰岩碎石500份、聚丙烯酸乳液5份、水32份。
混凝土的制备：将聚丙烯酸乳液加入水中搅拌混合均匀，得到混合液；将P.O52.5R水泥、石灰岩碎石加入混凝土搅拌机中搅拌混合均匀，然后加入混合液继续搅拌至混合均匀即得。
实施例2
与实施例1基本相同，区别仅在于：所述的脂肪酸盐由十六烷酸钙、硬脂酸钙按质量比为1：1搅拌混合均匀得到。
实施例3
与实施例1基本相同，区别仅在于：所述的脂肪酸盐由硬脂酸锌、硬脂酸钙按质量比为1：1搅拌混合均匀得到。
实施例4
与实施例1基本相同，区别仅在于：所述的脂肪酸盐由硬脂酸锌、十六烷酸钙按质量比为1：1搅拌混合均匀得到。
实施例5
与实施例1基本相同，区别仅在于：所述的有机溶剂由乙酸叔丁酯、乙酸异丙酯按质量比为1：1搅拌混合均匀得到。
实施例6
与实施例1基本相同，区别仅在于：所述的有机溶剂由乙酸正丁酯、乙酸异丙酯按质量比为1：1搅拌混合均匀得到。
实施例7
与实施例1基本相同，区别仅在于：所述的有机溶剂由乙酸正丁酯、乙酸叔丁酯按质量比为1：1搅拌混合均匀得到。
测试例1
对实施例1-7的压花地坪，在上海8-9月气候条件下进行露天自然养护，观察14天，并记录第14天压花地坪表面产生白霜情况，测定泛白面积占压花地坪整个表面积的百分数，具体测试结果见表1。
表1：泛白面积测试结果表
| 14天泛白面积率(％) | 颜色变化 | |
| 实施例1 | 8.3 | 仍鲜艳 |
| 实施例2 | 19.1 | 色彩难看 |
| 实施例3 | 18.4 | 色彩变淡 |
| 实施例4 | 19.5 | 色彩难看 |
| 实施例5 | 16.5 | 色彩难看 |
| 实施例6 | 15.7 | 色彩变淡 |
| 实施例7 | 16.3 | 色彩变淡 |
比较实施例1与实施例2-4，实施例1(硬脂酸锌、十六烷酸钙、硬脂酸钙复配)测试效果明显优于实施例2-4(硬脂酸锌、十六烷酸钙、硬脂酸钙中任意二者复配)。比较实施例1与实施例5-7，实施例1(乙酸正丁酯、乙酸叔丁酯、乙酸异丙酯复配)测试效果明显优于实施例5-7(乙酸正丁酯、乙酸叔丁酯、乙酸异丙酯中任意二者复配)。
测试例2
对实施例1-7的压花地坪，在上海8-9月气候条件下进行露天自然养护，观察28天，然后进行参照JTG E30-2005水泥混凝土耐磨性试验方法进行耐磨性能测试，具体测试结果见表2。
表2：耐磨性能测试结果表
| 耐磨性能，g/cm<sup>2</sup> | |
| 实施例1 | 0.02 |
| 实施例2 | 0.05 |
| 实施例3 | 0.04 |
| 实施例4 | 0.04 |
| 实施例5 | 0.05 |
| 实施例6 | 0.03 |
| 实施例7 | 0.05 |
比较实施例1与实施例2-4，实施例1(硬脂酸锌、十六烷酸钙、硬脂酸钙复配)耐磨性能明显优于实施例2-4(硬脂酸锌、十六烷酸钙、硬脂酸钙中任意二者复配)。比较实施例1与实施例5-7，实施例1(乙酸正丁酯、乙酸叔丁酯、乙酸异丙酯复配)耐磨性能明显优于实施例5-7(乙酸正丁酯、乙酸叔丁酯、乙酸异丙酯中任意二者复配)。
测试例3
对实施例1的压花地坪，进行理化指标测试，具体测试结果见表3。
表3：理化指标测试结果表
| 指标 | 数据 |
| 防滑系数 | 0.82OSHA |
| 冲击功(小颗粒) | 0.21J |
| 抗压强度 | 78MPa(28天) |
| 抗折强度 | 13.7MPa(28天) |
本发明具有整体施工，一次成型、快速固化、维修简便的优点，采用本发明生产的压花地坪具有耐磨、耐腐、致密、抗压、抗折、不起尘，地坪颜色多样，款式多样，色彩鲜艳持久，性价比高、选择面广，使用寿命长达8年以上。
Claims (6)
1.一种高使用寿命压花地坪的制备方法，其特征在于，包括下述步骤：
(1)混凝土面找平：将混凝土铺设在地面上，震捣、找平；
(2)彩色强化剂处理；
(3)脱模粉处理；
(4)压模；
(5)水洗；
(6)保护剂处理；
所述步骤(3)中的脱模粉由下述重量份原料组成：碳酸钙1-3份、滑石粉3-5份、脂肪酸盐0.2-1.8份、颜料0.002-0.007份；
所述的脂肪酸盐由硬脂酸锌、十六烷酸钙、硬脂酸钙混合而成，所述硬脂酸锌、十六烷酸钙、硬脂酸钙的质量比为(1-3)：(1-3)：(1-3)；
所述步骤(6)中保护剂由下述重量份原料组成：有机溶剂1-3份、丙烯酸树脂1-3份；
所述的有机溶剂由乙酸正丁酯、乙酸叔丁酯、乙酸异丙酯混合而成，所述乙酸正丁酯、乙酸叔丁酯、乙酸异丙酯的质量比为(1-3)：(1-3)：(1-3)；
所述的丙烯酸树脂为丙烯酸树脂BS1206、丙烯酸树脂BS108、丙烯酸树脂BS2050、丙烯酸树脂BS2350、丙烯酸树脂BS1880、丙烯酸树脂BS1863中一种或多种的混合物；
所述步骤(2)中的彩色强化剂由下述重量份原料组成：黄沙2-4份、水泥1-3份、颜料0.03-0.07份。
2.如权利要求1所述的高使用寿命压花地坪的制备方法，其特征在于：所述彩色强化剂中的水泥为P.C 32.5水泥、P.O 42.5水泥、P.O 42.5R水泥、P.O 52.5水泥、P.O 52.5R水泥中一种或多种的混合物。
3.如权利要求1所述的高使用寿命压花地坪的制备方法，其特征在于：所述彩色强化剂中的颜料为氧化铁黄、氧化铁红、氧化铁棕、氧化铁黑、复合颜料蓝、复合颜料绿中一种或多种的混合物。
4.如权利要求1所述的高使用寿命压花地坪的制备方法，其特征在于：所述脱模粉中颜料为氧化铁黄、氧化铁红、氧化铁棕、氧化铁黑、复合颜料蓝、复合颜料绿中一种或多种的混合物。
5.如权利要求1所述的高使用寿命压花地坪的制备方法，其特征在于，包括下述步骤：
(1)混凝土面找平：将混凝土铺设在地面上，震捣、找平；
(2)彩色强化剂处理：将彩色强化剂均匀撒在混凝土表面，整平、拉光，所述彩色强化剂的用量为1-4千克/平方米；
(3)脱模粉处理：将脱模粉均匀撒在混凝土表面，所述脱模粉的用量为0.1-0.4千克/平方米；
(4)压模：用压花模板覆盖在混凝土表面，压模；
(5)水洗：静置2-3天后，用清水冲掉混凝土表面的脱模粉；
(6)保护剂处理：在混凝土表面涂刷保护剂，所述保护剂的用量为0.1-0.4千克/平方米。
6.一种高使用寿命压花地坪，其特征在于：采用权利要求1-5中任一项所述方法制备而成。