CN106283830A - 一种提高生活用纸柔软度的方法 - Google Patents

一种提高生活用纸柔软度的方法 Download PDF

Info

Publication number
CN106283830A
CN106283830A CN201610627395.7A CN201610627395A CN106283830A CN 106283830 A CN106283830 A CN 106283830A CN 201610627395 A CN201610627395 A CN 201610627395A CN 106283830 A CN106283830 A CN 106283830A
Authority
CN
China
Prior art keywords
paper
cellulase
mass concentration
daily use
pulp
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610627395.7A
Other languages
English (en)
Inventor
刘洪斌
李传友
郭虎祥
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tianjin University of Science and Technology
Original Assignee
Tianjin University of Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tianjin University of Science and Technology filed Critical Tianjin University of Science and Technology
Priority to CN201610627395.7A priority Critical patent/CN106283830A/zh
Publication of CN106283830A publication Critical patent/CN106283830A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种提高生活用纸柔软度的方法，包括如下的步骤：1)将纤维原料打浆至打浆度为25°SR‑35°SR或进行消潜疏解；得纤维浆料；2)加水调节纤维浆料的质量浓度至3％‑10％，调节pH至5.5‑6.0，加入纤维素酶，使纤维素酶的质量分数为0.2％‑1.0％，在40℃‑60℃，作用30‑120min；3)将步骤(2)获得的材料用水稀释至质量浓度为1％，用抄片器或造纸机抄造生活用纸。本发明采用纤维素酶处理浆料，促使纤维细胞壁结构松弛，降低纤维内聚力，提高纤维分丝帚化程度，提高纤维的柔软性能。纤维素酶由发酵制成，绿色安全，与常规的化学柔软剂相比，有利于人体健康且对环境无污染，生产安全绿色环保。

Description

一种提高生活用纸柔软度的方法
技术领域
本发明涉及一种提高生活用纸柔软度的方法。
技术背景
卫生纸和面巾纸等生活用纸是人们日常生活中必不可少的产品，对于生活用纸来说，柔软度是其成纸的重要性能之一。目前生活用纸提高柔软度主要依靠造纸生产中添加化学柔软剂，化学柔软剂主要作用是干扰纤维之间的结合，它不易降解而且会对人体皮肤产生刺激。添加化学柔软剂不但会影响成纸的强度，而且还不利于人体健康和环境质量。因此，为了保护人体健康以及环境质量，研究和开发一种绿色环保无污染的生活用纸具有重要意义。
发明内容
本发明的目的是克服现有技术的不足，提供一种提高卫生纸柔软度的方法。
本发明的技术方法概述如下：
一种提高生活用纸柔软度的方法，包括如下步骤：
1)将纤维原料打浆至打浆度为25°SR-35°SR或进行消潜疏解；得纤维浆料；
2)加水调节纤维浆料的质量浓度至3％-10％，调节pH至5.5-6.0，加入纤维素酶，使纤维素酶的质量分数为0.2％-1.0％，在40℃-60℃温度条件下，纤维素酶作用30min-120min；
3)将步骤(2)获得的材料用水稀释至质量浓度为1％，用抄片器或造纸机抄造生活用纸。
纤维原料为漂白针叶木硫酸盐浆、漂白阔叶木硫酸盐浆或机械浆。
打浆度优选为30°SR。
纤维浆料的质量浓度为5％。
温度优选为50℃。
纤维素酶作用时间最好是60min。
本发明采用纤维素酶处理浆料，促使纤维细胞壁结构松弛，降低纤维内聚力，提高纤维分丝帚化程度，提高纤维的柔软性能。本发明所涉及的纤维素酶由发酵制的，绿色安全，与常规的化学柔软剂相比，有利于人体健康且对环境无污染，对于生产安全绿色环保的卫生纸具有重要意义。
具体实施方式
下面的实施案例是为了使本领域的技术人员能够更好地理解本发明，但并不以任何方式限制本发明。
各实施案例的纤维素酶的活性为398U/ml。不对本发明作限定。
实施例1
一种提高生活用纸(卫生纸)柔软度的方法，包括如下步骤：
1)将漂白针叶木硫酸盐浆打浆至打浆度为30°SR；得纤维浆料；
2)取六份等质量纤维浆料，分别加水调节纤维浆料的质量浓度至5％，调节pH至6.0，在六份中加入不同量的纤维素酶，使纤维素酶的质量分数分别为0％，0.2％，0.4％，0.6％，0.8％，1.0％，在50℃温度条件下，纤维素酶作用60min；
3)将步骤2)获得的材料用水稀释至质量浓度为1％，用抄片器抄造20g/m2的生活用纸(卫生纸)。见表1、2、3。
表1纤维素酶用量对漂白针叶木硫酸盐浆柔软性能的影响
表2纤维素酶用量对漂白针叶木硫酸盐浆强度性能的影响
表3纤维素酶用量对漂白针叶木硫酸盐浆保水值的影响
实施例2
一种提高生活用纸(卫生纸)柔软度的方法，包括如下步骤：
1)将漂白阔叶木硫酸盐浆打浆至打浆度为35°SR；得纤维浆料；
2)取六份等质量纤维浆料，分别加水调节纤维浆料的质量浓度至10％，调节pH至5.5，在六份中加入不同量的纤维素酶，使纤维素酶的质量分数分别为0％，0.2％，0.4％，0.6％，0.8％，1.0％，在60℃温度条件下，纤维素酶作用30min；
3)将步骤2)获得的材料用水稀释至质量浓度为1％，用抄片器抄造30g/m2的生活用纸(卫生纸)。见表4、5、6。
表4纤维素酶用量对漂白阔叶木硫酸盐浆柔软性能的影响
表5纤维素酶用量对漂白阔叶木硫酸盐浆强度性能的影响
表6纤维素酶用量对漂白阔叶木硫酸盐浆保水值的影响
实施例3
一种提高生活用纸(面巾纸)柔软度的方法，包括如下步骤：
1)将机械浆打浆至打浆度为25°SR；得纤维浆料；
2)取六份等质量纤维浆料，分别加水调节纤维浆料的质量浓度至3％，调节pH至5.5，在六份中加入不同量的纤维素酶，使纤维素酶的质量分数分别为0％，0.2％，0.4％，0.6％，0.8％，1.0％，在40℃温度条件下，纤维素酶作用120min；
3)将步骤2)获得的材料用水稀释至质量浓度为1％，用造纸机抄造30g/m2的生活用纸(面巾纸)。见表7、8、9。
表7纤维素酶用量对机械浆柔软性能的影响
表8纤维素酶用量对机械浆强度性能的影响
表9纤维素酶用量对机械浆保水值的影响

Claims (6)

1.一种提高生活用纸柔软度的方法，其特征是包括如下步骤：
1)将纤维原料打浆至打浆度为25°SR-35°SR或进行消潜疏解；得纤维浆料；
2)加水调节纤维浆料的质量浓度至3％-10％，调节pH至5.5-6.0，加入纤维素酶，使纤维素酶的质量分数为0.2％-1.0％，在40℃-60℃温度条件下，纤维素酶作用30min-120min；
3)将步骤(2)获得的材料用水稀释至质量浓度为1％，用抄片器或造纸机抄造生活用纸。
2.根据权利要求1所述的方法，其特征是所述纤维原料为漂白针叶木硫酸盐浆、漂白阔叶木硫酸盐浆或机械浆。
3.根据权利要求1或2所述的方法，其特征是所述打浆度为30°SR。
4.根据权利要求1或2所述的的方法，其特征是所述纤维浆料的质量浓度为5％。
5.根据权利要求1或2所述的方法，其特征是所述温度为50℃。
6.根据权利要求1或2所述的方法，其特征是纤维素酶作用时间为60min。
CN201610627395.7A 2016-07-29 2016-07-29 一种提高生活用纸柔软度的方法 Pending CN106283830A (zh)