CN106283400A - A kind of non-woven fabrics with Aloe delicate fragrance and preparation method thereof - Google Patents

A kind of non-woven fabrics with Aloe delicate fragrance and preparation method thereof Download PDF

Info

Publication number
CN106283400A
CN106283400A CN201610689186.5A CN201610689186A CN106283400A CN 106283400 A CN106283400 A CN 106283400A CN 201610689186 A CN201610689186 A CN 201610689186A CN 106283400 A CN106283400 A CN 106283400A
Authority
CN
China
Prior art keywords
woven fabrics
aloe
delicate fragrance
tourmaline powder
polylactic acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610689186.5A
Other languages
Chinese (zh)
Inventor
汪彦羽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MAANSHAN LAKESIDE NONWOVEN TECHNOLOGY Co Ltd
Original Assignee
MAANSHAN LAKESIDE NONWOVEN TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MAANSHAN LAKESIDE NONWOVEN TECHNOLOGY Co Ltd filed Critical MAANSHAN LAKESIDE NONWOVEN TECHNOLOGY Co Ltd
Priority to CN201610689186.5A priority Critical patent/CN106283400A/en
Publication of CN106283400A publication Critical patent/CN106283400A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of non-woven fabrics with Aloe delicate fragrance and preparation method thereof, it is characterised in that be made up of the raw material of following weight portion: Aloe extraction solution 35, nano-tourmaline powder 48, Oleum Ricini 12, polylactic acid 5 10, polyethylene glycol 200 12, activated carbon 35, Mint Essence 48, coconut shell flour 12, isotactic polypropylene 50 70, kieselguhr 36, dodecyl sodium sulfate 12, Carboxymethyl cellulose sodium is appropriate, and water is appropriate；The present invention adds nano-tourmaline powder in non-woven fabrics, can reach the effect of continuous releasing negative oxygen ion, when being applied to automotive trim, interior space can be made refrigerant comfortable, spirit and QI cleaning, and Mint Essence of arranging in pairs or groups, effect of refreshing oneself is notable；The Aloe extraction solution added makes the non-woven fabrics prepared distribute the delicate fragrance of Aloe, makes people's spiritual happiness.

Description

A kind of non-woven fabrics with Aloe delicate fragrance and preparation method thereof
Technical field
The present invention relates to a kind of non-woven fabrics and preparation method thereof, be specifically related to a kind of non-woven fabrics with Aloe delicate fragrance and Preparation method.
Background technology
Non-woven fabrics is a kind of non-weaving cloth, and it is to directly utilize high polymer section, chopped fiber or long filament fiber is passed through gas Stream or machinery become net, are then passed through spun lacing, acupuncture, or hot rolling and reinforce, and eventually pass the cloth without braiding that Final finishing is formed.Tool Having softness, the ventilative and tencel goods of planar structure, advantage is not produce Soft flocks, tough, durable, silkiness is soft, also It is the one of reinforcing material, and the sensation of also cotton, have been widely used for automotive field.But stay in confined space for a long time In, people can think that dizzy brain rises, when come forest seashore, waterfall etc. local when, we can feel spirit and QI cleaning, and this is just It it is the effect of negative aeroion.Negative aeroion is also negative oxygen ion, refer to obtain excess electron and electronegative oxygen from Son.
Jiang Yinggang, in " containing the preparation of bamboo charcoal powder liner cloth and Study on adsorption properties ", utilizes bamboo charcoal powder and non-weaving cloth, logical Cross coating, the method such as pad, make multiple containing bamboo charcoal powder nonwoven interlining.But, when it is applied to automotive trim, there is also And be not provided that negative oxygen ion, refrigerant fragrance of refreshing oneself etc. can not be discharged be conducive to traffic safety and driving comfortable space is provided Weak point.
Summary of the invention
Comprehensive above consideration, the present invention provides a kind of non-woven fabrics and formula thereof, it is therefore intended that solve when non-woven fabrics is applied When automotive trim, it is impossible to releasing negative oxygen ion continuously, it is provided that the preferably defect of interior space.
For achieving the above object, technical scheme is as follows:
A kind of non-woven fabrics with Aloe delicate fragrance, it is characterised in that be made up of the raw material of following weight portion:
Aloe extraction solution 3-5, nano-tourmaline powder 4-8, Oleum Ricini 1-2, polylactic acid 5-10, polyethylene glycol 200 1-2, activated carbon 3-5, Mint Essence 4-8, coconut shell flour 1-2, isotactic polypropylene 50-70, kieselguhr 3-6, dodecyl sodium sulfate 1-2, methylol Sodium cellulosate is appropriate, and water is appropriate；
Described a kind of non-woven fabrics with Aloe delicate fragrance and preparation method thereof, it is characterised in that be made up of following steps:
A., at 150-200 DEG C, nano-tourmaline powder is joined in polylactic acid, adds polyethylene glycol 200, stir, Make tourmaline powder evenly spread in polylactic acid, and make polylactic acid be wrapped in nano-tourmaline powder surface, form microsphere, filter also Dry；
B. activated carbon and coconut shell flour are added in water and are uniformly dispersed, be then added to Mint Essence and Aloe extraction solution, Continue dispersion, after being uniformly dispersed, proceed to stand under vacuumized conditions 3-5h, be loaded with by centrifugal, dry, milled processed Mint Essence and the activated carbon powder of Aloe extraction solution and coconut shell flour mixture；
C. isotactic polypropylene, step a thus obtained microsphere, step b gained mixture are added to screw extruder and melt, then Non-woven fabrics is prepared after spinning, drawing-off, one-tenth net, hot rolling；
D. kieselguhr is added to the water, is stirring evenly and then adding into dodecyl sodium sulfate, be stirring evenly and then adding into methylol fine Dimension element sodium and Oleum Ricini, adjust modest viscosity, prepares serosity；Step c gained non-woven fabrics is totally submerged in serosity, and puts into super Ultrasonic 5-10min in acoustic wave oscillator, takes out, the method using " two leachings two are rolled ", and padder mangle is used in i.e. fully submergence, then Submergence, then with after padder mangle, puts into baker, bakees 2-5min, take out.
Described a kind of non-woven fabrics with Aloe delicate fragrance and preparation method thereof, it is characterised in that bakee described in step b Machine stoving temperature is 70-110 DEG C.
The invention has the beneficial effects as follows: in non-woven fabrics, add nano-tourmaline powder, can reach to discharge continuously negative oxygen from The effect of son, when being applied to automotive trim, can make interior space refrigerant comfortable, spirit and QI cleaning, Mint Essence of arranging in pairs or groups, effect of refreshing oneself Fruit is notable, reduces and contained the harm of fatigue driving；Utilize polylactic acid to wrap up nano-tourmaline powder, not only prevent nanometer Tourmaline powder broken and coming off, and the appearance promoting tourmaline powder and polypropylene substrate closes and dispersion, polylactic acid tool simultaneously There are excellent breathability, oxygen permeability, and antibacterial and anti-mildew characteristic, improve the fungus resistance of non-woven fabrics, extend service life；With Activated carbon loads Mint Essence, adds loading and the air contact area of Mint Essence, reaches more lasting release Effect, has been simultaneously introduced the characterization of adsorption of activated carbon, increases the function of non-woven fabrics clean air；With kieselguhr serosity to non-woven fabrics Carry out coating, can effectively remove harmful substance and house pet body odor, the rubbish institutes such as the free formaldehyde in air, benzene, ammonia, VOC The abnormal flavour produced, solves in-vehicle air pollution, hence it is evident that improve environment inside car comprehensively；The Aloe extraction solution added makes the nonwoven prepared Cloth distributes the delicate fragrance of Aloe, makes people's spiritual happiness.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is further described.
Embodiment
A kind of non-woven fabrics with Aloe delicate fragrance, it is characterised in that be made up of the raw material of following weight portion:
Aloe extraction solution 5, nano-tourmaline powder 8, Oleum Ricini 2, polylactic acid 10, polyethylene glycol 200 2, activated carbon 5, Mint Essence 8, coconut shell flour 2, isotactic polypropylene 70, kieselguhr 2, dodecyl sodium sulfate 2, Carboxymethyl cellulose sodium is appropriate, and water is appropriate；
Described a kind of non-woven fabrics with Aloe delicate fragrance and preparation method thereof, it is characterised in that be made up of following steps:
A., at 150-200 DEG C, nano-tourmaline powder is joined in polylactic acid, adds polyethylene glycol 200, stir, Make tourmaline powder evenly spread in polylactic acid, and make polylactic acid be wrapped in nano-tourmaline powder surface, form microsphere, filter also Dry；
B. activated carbon and coconut shell flour are added in water and are uniformly dispersed, be then added to Mint Essence and Aloe extraction solution, Continue dispersion, after being uniformly dispersed, proceed to stand under vacuumized conditions 3-5h, be loaded with by centrifugal, dry, milled processed Mint Essence and the activated carbon powder of Aloe extraction solution and coconut shell flour mixture；
C. isotactic polypropylene, step a thus obtained microsphere, step b gained mixture are added to screw extruder and melt, then Non-woven fabrics is prepared after spinning, drawing-off, one-tenth net, hot rolling；
D. kieselguhr is added to the water, is stirring evenly and then adding into dodecyl sodium sulfate, be stirring evenly and then adding into methylol fine Dimension element sodium and Oleum Ricini, adjust modest viscosity, prepares serosity；Step c gained non-woven fabrics is totally submerged in serosity, and puts into super Ultrasonic 5-10min in acoustic wave oscillator, takes out, the method using " two leachings two are rolled ", and padder mangle is used in i.e. fully submergence, then Submergence, then with after padder mangle, puts into baker, bakees 2-5min, take out.
Described a kind of non-woven fabrics with Aloe delicate fragrance and preparation method thereof, it is characterised in that bakee described in step b Machine stoving temperature is 70-110 DEG C.
The technical parameter of the present invention is:
Formaldehyde absorbing rate >=11.09% of Unit Weight non-woven fabrics, benzene adsorption rate >=14.83%, TVOC adsorption rate >=13.42%.

Claims (3)

1. a non-woven fabrics with Aloe delicate fragrance, it is characterised in that be made up of the raw material of following weight portion:
Aloe extraction solution 3-5, nano-tourmaline powder 4-8, Oleum Ricini 1-2, polylactic acid 5-10, polyethylene glycol 200 1-2, activated carbon 3-5, Mint Essence 4-8, coconut shell flour 1-2, isotactic polypropylene 50-70, kieselguhr 3-6, dodecyl sodium sulfate 1-2, methylol Sodium cellulosate is appropriate, and water is appropriate.
A kind of non-woven fabrics with Aloe delicate fragrance the most according to claim 1 and preparation method thereof, it is characterised in that by with Lower step is made:
A., at 150-200 DEG C, nano-tourmaline powder is joined in polylactic acid, adds polyethylene glycol 200, stir, Make tourmaline powder evenly spread in polylactic acid, and make polylactic acid be wrapped in nano-tourmaline powder surface, form microsphere, filter also Dry；
B. activated carbon and coconut shell flour are added in water and are uniformly dispersed, be then added to Mint Essence and Aloe extraction solution, Continue dispersion, after being uniformly dispersed, proceed to stand under vacuumized conditions 3-5h, be loaded with by centrifugal, dry, milled processed Mint Essence and the activated carbon powder of Aloe extraction solution and coconut shell flour mixture；
C. isotactic polypropylene, step a thus obtained microsphere, step b gained mixture are added to screw extruder and melt, then Non-woven fabrics is prepared after spinning, drawing-off, one-tenth net, hot rolling；
D. kieselguhr is added to the water, is stirring evenly and then adding into dodecyl sodium sulfate, be stirring evenly and then adding into methylol fine Dimension element sodium and Oleum Ricini, adjust modest viscosity, prepares serosity；Step c gained non-woven fabrics is totally submerged in serosity, and puts into super Ultrasonic 5-10min in acoustic wave oscillator, takes out, the method using " two leachings two are rolled ", and padder mangle is used in i.e. fully submergence, then Submergence, then with after padder mangle, puts into baker, bakees 2-5min, take out.
A kind of non-woven fabrics with Aloe delicate fragrance the most according to claim 2 and preparation method thereof, it is characterised in that step Curer stoving temperature described in b is 70-110 DEG C.
CN201610689186.5A 2016-08-19 2016-08-19 A kind of non-woven fabrics with Aloe delicate fragrance and preparation method thereof Pending CN106283400A (en)