CN106283401A - A kind of have catalysis, can the non-woven fabrics and preparation method thereof of releasing negative oxygen ion continuously - Google Patents
A kind of have catalysis, can the non-woven fabrics and preparation method thereof of releasing negative oxygen ion continuously Download PDFInfo
- Publication number
- CN106283401A CN106283401A CN201610689187.XA CN201610689187A CN106283401A CN 106283401 A CN106283401 A CN 106283401A CN 201610689187 A CN201610689187 A CN 201610689187A CN 106283401 A CN106283401 A CN 106283401A
- Authority
- CN
- China
- Prior art keywords
- woven fabrics
- nano
- oxygen ion
- negative oxygen
- titanium oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of have catalysis, can the non-woven fabrics and preparation method thereof of releasing negative oxygen ion continuously, it is characterised in that be made up of the raw material of following weight portion: nano titanium oxide 13, nano-tourmaline powder 48, white carbon black 12, polylactic acid 5 10, polyethylene glycol 200 12, activated carbon 35, Mint Essence 48, alginate fibre 12, isotactic polypropylene 50 70, kieselguhr 36, dodecyl sodium sulfate 12, Carboxymethyl cellulose sodium is appropriate, and water is appropriate;The present invention adds nano-tourmaline powder in non-woven fabrics, can reach the effect of continuous releasing negative oxygen ion, when being applied to automotive trim, interior space can be made refrigerant comfortable, spirit and QI cleaning, and Mint Essence of arranging in pairs or groups, effect of refreshing oneself is notable;By adding nano titanium oxide, impart material can light-catalysed function, thus the cleaning of material can be kept.
Description
Technical field
The present invention relates to a kind of non-woven fabrics and preparation method thereof, be specifically related to one and there is catalysis, can discharge continuously
Non-woven fabrics of negative oxygen ion and preparation method thereof.
Background technology
Non-woven fabrics is a kind of non-weaving cloth, and it is to directly utilize high polymer section, chopped fiber or long filament fiber is passed through gas
Stream or machinery become net, are then passed through spun lacing, acupuncture, or hot rolling and reinforce, and eventually pass the cloth without braiding that Final finishing is formed.Tool
Having softness, the ventilative and tencel goods of planar structure, advantage is not produce Soft flocks, tough, durable, silkiness is soft, also
It is the one of reinforcing material, and the sensation of also cotton, have been widely used for automotive field.But stay in confined space for a long time
In, people can think that dizzy brain rises, when come forest seashore, waterfall etc. local when, we can feel spirit and QI cleaning, and this is just
It it is the effect of negative aeroion.Negative aeroion is also negative oxygen ion, refer to obtain excess electron and electronegative oxygen from
Son.
Jiang Yinggang, in " containing the preparation of bamboo charcoal powder liner cloth and Study on adsorption properties ", utilizes bamboo charcoal powder and non-weaving cloth, logical
Cross coating, the method such as pad, make multiple containing bamboo charcoal powder nonwoven interlining.But, when it is applied to automotive trim, there is also
And be not provided that negative oxygen ion, refrigerant fragrance of refreshing oneself etc. can not be discharged be conducive to traffic safety and driving comfortable space is provided
Weak point.
Summary of the invention
Comprehensive above consideration, the present invention provides a kind of non-woven fabrics and formula thereof, it is therefore intended that solve when non-woven fabrics is applied
When automotive trim, it is impossible to releasing negative oxygen ion continuously, it is provided that the preferably defect of interior space.
For achieving the above object, technical scheme is as follows:
A kind of have catalysis, can the non-woven fabrics of releasing negative oxygen ion continuously, it is characterised in that by the raw material of following weight portion
Make:
Nano titanium oxide 1-3, nano-tourmaline powder 4-8, white carbon black 1-2, polylactic acid 5-10, polyethylene glycol 200 1-2, activated carbon
3-5, Mint Essence 4-8, alginate fibre 1-2, isotactic polypropylene 50-70, kieselguhr 3-6, dodecyl sodium sulfate 1-2, hydroxyl first
Base sodium cellulosate is appropriate, and water is appropriate;
Described a kind of have catalysis, can the non-woven fabrics and preparation method thereof of releasing negative oxygen ion continuously, it is characterised in that
It is made up of following steps:
A., at 150-200 DEG C, nano-tourmaline powder, nano titanium oxide are joined in polylactic acid, adds Polyethylene Glycol
200, stir, make nano-tourmaline powder, nano titanium oxide evenly spread in polylactic acid, and make polylactic acid be wrapped in receive
Rice tourmaline powder, nano titanium oxide surface, form microsphere, filter and dry;
B. activated carbon, alginate fibre are added in water and be uniformly dispersed, be then added to Mint Essence, continue dispersion, point
Proceed to stand under vacuumized conditions 3-5h after dissipating uniformly, obtain being loaded with the work of Mint Essence by centrifugal, dry, milled processed
Property powdered carbon and the mixture of alginate fibre;
C. isotactic polypropylene, step a thus obtained microsphere, step b gained mixture are added to screw extruder and melt, then
Non-woven fabrics is prepared after spinning, drawing-off, one-tenth net, hot rolling;
D. kieselguhr is added to the water, is stirring evenly and then adding into dodecyl sodium sulfate, be stirring evenly and then adding into methylol fine
Dimension element sodium, white carbon black, adjust modest viscosity, prepare serosity;Step c gained non-woven fabrics is totally submerged in serosity, and puts into ultrasonic
Ultrasonic 5-10min in wave oscillator, takes out, the method using " two leachings two are rolled ", and i.e. fully submergence uses padder mangle, further
Secondary submergence, then with after padder mangle, puts into baker, bakees 2-5min, take out.
Described a kind of have catalysis, can the non-woven fabrics and preparation method thereof of releasing negative oxygen ion continuously, its feature
Being, curer stoving temperature described in step b is 70-110 DEG C.
The invention has the beneficial effects as follows: in non-woven fabrics, add nano-tourmaline powder, can reach to discharge continuously negative oxygen from
The effect of son, when being applied to automotive trim, can make interior space refrigerant comfortable, spirit and QI cleaning, Mint Essence of arranging in pairs or groups, effect of refreshing oneself
Fruit is notable, reduces and contained the harm of fatigue driving;Utilize polylactic acid to wrap up nano-tourmaline powder, not only prevent nanometer
Tourmaline powder broken and coming off, and the appearance promoting tourmaline powder and polypropylene substrate closes and dispersion, polylactic acid tool simultaneously
There are excellent breathability, oxygen permeability, and antibacterial and anti-mildew characteristic, improve the fungus resistance of non-woven fabrics, extend service life;With
Activated carbon loads Mint Essence, adds loading and the air contact area of Mint Essence, reaches more lasting release
Effect, has been simultaneously introduced the characterization of adsorption of activated carbon, increases the function of non-woven fabrics clean air;With kieselguhr serosity to non-woven fabrics
Carry out coating, can effectively remove harmful substance and house pet body odor, the rubbish institutes such as the free formaldehyde in air, benzene, ammonia, VOC
The abnormal flavour produced, solves in-vehicle air pollution, hence it is evident that improve environment inside car comprehensively;By adding nano titanium oxide, impart
Material can light-catalysed function, thus the cleaning of material can be kept.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is further described.
Embodiment
A kind of have catalysis, can the non-woven fabrics of releasing negative oxygen ion continuously, it is characterised in that by following weight portion
Raw material is made:
Nano titanium oxide 3, nano-tourmaline powder 8, white carbon black 2, polylactic acid 10, polyethylene glycol 200 2, activated carbon 5, Mint Essence
8, alginate fibre 2, isotactic polypropylene 70, kieselguhr 6, dodecyl sodium sulfate 2, Carboxymethyl cellulose sodium is appropriate, and water is appropriate;
Described a kind of have catalysis, can the non-woven fabrics and preparation method thereof of releasing negative oxygen ion continuously, it is characterised in that
It is made up of following steps:
A., at 150-200 DEG C, nano-tourmaline powder, nano titanium oxide are joined in polylactic acid, adds Polyethylene Glycol
200, stir, make nano-tourmaline powder, nano titanium oxide evenly spread in polylactic acid, and make polylactic acid be wrapped in receive
Rice tourmaline powder, nano titanium oxide surface, form microsphere, filter and dry;
B. activated carbon, alginate fibre are added in water and be uniformly dispersed, be then added to Mint Essence, continue dispersion, point
Proceed to stand under vacuumized conditions 3-5h after dissipating uniformly, obtain being loaded with the work of Mint Essence by centrifugal, dry, milled processed
Property powdered carbon and the mixture of alginate fibre;
C. isotactic polypropylene, step a thus obtained microsphere, step b gained mixture are added to screw extruder and melt, then
Non-woven fabrics is prepared after spinning, drawing-off, one-tenth net, hot rolling;
D. kieselguhr is added to the water, is stirring evenly and then adding into dodecyl sodium sulfate, be stirring evenly and then adding into methylol fine
Dimension element sodium, white carbon black, adjust modest viscosity, prepare serosity;Step c gained non-woven fabrics is totally submerged in serosity, and puts into ultrasonic
Ultrasonic 5-10min in wave oscillator, takes out, the method using " two leachings two are rolled ", and i.e. fully submergence uses padder mangle, further
Secondary submergence, then with after padder mangle, puts into baker, bakees 2-5min, take out.
Described a kind of have catalysis, can the non-woven fabrics and preparation method thereof of releasing negative oxygen ion continuously, its feature
Being, curer stoving temperature described in step b is 70-110 DEG C.
The technical parameter of the present invention is:
Formaldehyde absorbing rate >=11.09% of Unit Weight non-woven fabrics, benzene adsorption rate >=14.83%, TVOC adsorption rate >=13.42%.
Claims (3)
1. one kind have catalysis, can the non-woven fabrics of releasing negative oxygen ion continuously, it is characterised in that former by following weight portion
Material is made:
Nano titanium oxide 1-3, nano-tourmaline powder 4-8, white carbon black 1-2, polylactic acid 5-10, polyethylene glycol 200 1-2, activated carbon
3-5, Mint Essence 4-8, alginate fibre 1-2, isotactic polypropylene 50-70, kieselguhr 3-6, dodecyl sodium sulfate 1-2, hydroxyl first
Base sodium cellulosate is appropriate, and water is appropriate.
The most according to claim 1 a kind of have catalysis, can the non-woven fabrics of releasing negative oxygen ion and preparation thereof continuously
Method, it is characterised in that be made up of following steps:
A., at 150-200 DEG C, nano-tourmaline powder, nano titanium oxide are joined in polylactic acid, adds Polyethylene Glycol
200, stir, make nano-tourmaline powder, nano titanium oxide evenly spread in polylactic acid, and make polylactic acid be wrapped in receive
Rice tourmaline powder, nano titanium oxide surface, form microsphere, filter and dry;
B. activated carbon, alginate fibre are added in water and be uniformly dispersed, be then added to Mint Essence, continue dispersion, point
Proceed to stand under vacuumized conditions 3-5h after dissipating uniformly, obtain being loaded with the work of Mint Essence by centrifugal, dry, milled processed
Property powdered carbon and the mixture of alginate fibre;
C. isotactic polypropylene, step a thus obtained microsphere, step b gained mixture are added to screw extruder and melt, then
Non-woven fabrics is prepared after spinning, drawing-off, one-tenth net, hot rolling;
D. kieselguhr is added to the water, is stirring evenly and then adding into dodecyl sodium sulfate, be stirring evenly and then adding into methylol fine
Dimension element sodium, white carbon black, adjust modest viscosity, prepare serosity;Step c gained non-woven fabrics is totally submerged in serosity, and puts into ultrasonic
Ultrasonic 5-10min in wave oscillator, takes out, the method using " two leachings two are rolled ", and i.e. fully submergence uses padder mangle, further
Secondary submergence, then with after padder mangle, puts into baker, bakees 2-5min, take out.
The most according to claim 2 a kind of have catalysis, can the non-woven fabrics of releasing negative oxygen ion and preparation thereof continuously
Method, it is characterised in that curer stoving temperature described in step b is 70-110 DEG C.