CN106149362A - A kind of non-woven fabrics containing Flos Lonicerae extractive solution and preparation method thereof - Google Patents

A kind of non-woven fabrics containing Flos Lonicerae extractive solution and preparation method thereof Download PDF

Info

Publication number
CN106149362A
CN106149362A CN201610709514.3A CN201610709514A CN106149362A CN 106149362 A CN106149362 A CN 106149362A CN 201610709514 A CN201610709514 A CN 201610709514A CN 106149362 A CN106149362 A CN 106149362A
Authority
CN
China
Prior art keywords
flos lonicerae
woven fabrics
solution
lonicerae extractive
extractive solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610709514.3A
Other languages
Chinese (zh)
Inventor
张泽成
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Province Taihu Ze Hong Plastic Co Ltd
Original Assignee
Anhui Province Taihu Ze Hong Plastic Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Province Taihu Ze Hong Plastic Co Ltd filed Critical Anhui Province Taihu Ze Hong Plastic Co Ltd
Priority to CN201610709514.3A priority Critical patent/CN106149362A/en
Publication of CN106149362A publication Critical patent/CN106149362A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of non-woven fabrics containing Flos Lonicerae extractive solution and preparation method thereof, it is characterized in that, it is made up of the raw material of following weight portion: Flos Lonicerae extractive solution 36, bamboo filament fibre powder 37, chitosan 12, nano-tourmaline powder 48, PAMAM solution 49, polylactic acid 5 10, spandex 12, polyethylene glycol 200 12, activated carbon 35, Mint Essence 48, sodium periodate solution 10 15, isotactic polypropylene 50 70, kieselguhr 36, dodecyl sodium sulfate 12, Carboxymethyl cellulose sodium is appropriate, and water is appropriate；In non-woven fabrics, add nano-tourmaline powder, the effect of continuous releasing negative oxygen ion can be reached, when being applied to clothing liner, there is calmness, analgesia, antitussive, antipruritic, increasing appetite, the effect of blood pressure lowering；Coordinate and with the addition of Flos Lonicerae extractive solution, make the non-woven fabrics prepared have the effect such as waterproof and breathable, warming, anthelmintic.

Description

A kind of non-woven fabrics containing Flos Lonicerae extractive solution and preparation method thereof
Technical field
The present invention relates to a kind of non-woven fabrics and preparation method thereof, be specifically related to a kind of non-woven fabrics containing Flos Lonicerae extractive solution and Its preparation method.
Background technology
Non-woven fabrics is a kind of non-weaving cloth, and it is to directly utilize high polymer section, chopped fiber or long filament fiber is passed through gas Stream or machinery become net, are then passed through spun lacing, acupuncture, or hot rolling and reinforce, and eventually pass the cloth without braiding that Final finishing is formed.Tool Having softness, the ventilative and tencel goods of planar structure, advantage is not produce Soft flocks, tough, durable, silkiness is soft, and And the sensation of also cotton, have been widely used for garment industry.Along with people's constantly chasing after " ecological, healthy, environmental protection " theory Ask, together with textile has been closely connected with fashion, health environment-friendly, what this fashion reflected the is mankind to the love of self and Concern to living environment, simultaneously because the popularization that ecological textile concept is in the world, and people pursue natural relaxing Suitable, back to nature, the psychology recovered one's original simplicity, Green Textiles has become as the main trend of following textile development.
Jiang Yinggang, in " containing the preparation of bamboo charcoal powder liner cloth and Study on adsorption properties ", utilizes bamboo charcoal powder and non-weaving cloth, logical Cross coating, the method such as pad, make multiple containing bamboo charcoal powder nonwoven interlining.But, there is also and be not provided that negative oxygen ion, no Refrigerant fragrance of refreshing oneself can be discharged and wait healthy, the weak point of resisting fatigue of refreshing oneself being conducive to people.
Summary of the invention
Comprehensive above consideration, the present invention provides a kind of non-woven fabrics and formula thereof, it is therefore intended that solve when non-woven fabrics is applied When automotive trim, it is impossible to releasing negative oxygen ion continuously, it is provided that the preferably defect of interior space.
For achieving the above object, technical scheme is as follows:
A kind of non-woven fabrics containing Flos Lonicerae extractive solution, it is characterised in that be made up of the raw material of following weight portion:
Flos Lonicerae extractive solution 3-6, bamboo filament fibre powder 3-7, chitosan 1-2, nano-tourmaline powder 4-8, PAMAM solution 4-9, poly-breast Acid 5-10, spandex 1-2, polyethylene glycol 200 1-2, activated carbon 3-5, Mint Essence 4-8, sodium periodate solution 10-15, isotactic gathers Propylene 50-70, kieselguhr 3-6, dodecyl sodium sulfate 1-2, Carboxymethyl cellulose sodium is appropriate, and water is appropriate；
The concentration of described sodium periodate solution is 0.1-10g/L；PAMAM solution concentration is 1-10g/L.
Described a kind of non-woven fabrics containing Flos Lonicerae extractive solution and preparation method thereof, it is characterised in that by following steps system Become:
A., at 150-200 DEG C, nano-tourmaline powder is joined in polylactic acid, adds polyethylene glycol 200, stir, Make nano-tourmaline powder evenly spread in polylactic acid, and make polylactic acid be wrapped in nano-tourmaline powder surface, form microsphere, mistake Filter and dry；
B. activated carbon is added in water and be uniformly dispersed, be then added to Mint Essence and Flos Lonicerae extractive solution, continue to divide Dissipate, after being uniformly dispersed, proceed to stand under vacuumized conditions 3-5h, obtain being loaded with minty note by centrifugal, dry, milled processed Essence and the activated carbon powder of Flos Lonicerae extractive solution；
C. bamboo filament fibre powder being placed in lucifuge oxidation reaction 3-5h in sodium periodate solution, reaction temperature is 40-110 DEG C, mistake Filter, wash, dry, obtain aoxidizing bamboo fibre；Oxidation bamboo fibre is immersed in 3-6h in PAMAM solution, reaction temperature 25-85 DEG C, filtering drying also grinds, and obtains PAMAM and is grafted bamboo filament fibre powder；
D. by isotactic polypropylene, step a thus obtained microsphere, step b gained load Mint Essence and the activated carbon of Flos Lonicerae extractive solution Powder, step c gained PAMAM grafting bamboo filament fibre powder, spandex add screw extruder to and melt, then through spinning, drawing-off, one-tenth Non-woven fabrics is prepared after net, hot rolling；
E. kieselguhr is added to the water, is stirring evenly and then adding into dodecyl sodium sulfate and chitosan, is stirring evenly and then adding into Carboxymethyl cellulose sodium, adjusts modest viscosity, prepares serosity；Step d gained non-woven fabrics is totally submerged in serosity, and puts into super Ultrasonic 5-10min in acoustic wave oscillator, takes out, the method using " two leachings two are rolled ", and padder mangle is used in i.e. fully submergence, then Submergence, then with after padder mangle, puts into baker, bakees 2-5min, take out.
Described a kind of non-woven fabrics containing Flos Lonicerae extractive solution and preparation method thereof, it is characterised in that dry described in step b Roasting machine stoving temperature is 70-110 DEG C.
The invention has the beneficial effects as follows: in non-woven fabrics, add nano-tourmaline powder, can reach to discharge continuously negative oxygen from The effect of son, when being applied to clothing liner, has calmness, analgesia, antitussive, antipruritic, increasing appetite, the effect of blood pressure lowering, Herba Menthae of arranging in pairs or groups Essence, can make people's spirit and QI cleaning, resisting fatigue；Utilize polylactic acid to wrap up nano-tourmaline powder, not only prevent nanometer electric Stone powder broken and coming off, and the appearance promoting tourmaline powder and polypropylene substrate closes and dispersion, and polylactic acid has excellent simultaneously Good breathability, oxygen permeability, and antibacterial and anti-mildew characteristic, improve the fungus resistance of non-woven fabrics, extends service life；By activity Charcoal loads Mint Essence, adds loading and the air contact area of Mint Essence, reaches more lasting releasing effect, It is simultaneously introduced the characterization of adsorption of activated carbon, increases the function of non-woven fabrics absorption abnormal flavour；Bamboo filament fibre after sodium periodate oxidation, The oh group on its surface is oxidized to aldehyde radical even carboxyl, crosslinks reaction with the amino on PAMAM surface, thus will PAMAM is grafted on bamboo filament fibre, is possible not only to make bamboo filament fibre more soft fluffy, and enhance bamboo filament fibre with etc. The fusion of isotactic polypropylene substrate；Coordinate with the addition of Flos Lonicerae extractive solution, make the non-woven fabrics prepared have waterproof and breathable, warming, drive The effects such as worm.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is further described.
Embodiment
A kind of non-woven fabrics containing Flos Lonicerae extractive solution, it is characterised in that be made up of the raw material of following weight portion:
Flos Lonicerae extractive solution 6, bamboo filament fibre powder 7, chitosan 2, nano-tourmaline powder 8, PAMAM solution 9, polylactic acid 10, spandex 2, polyethylene glycol 200 2, activated carbon 5, Mint Essence 8, sodium periodate solution 15, isotactic polypropylene 70, kieselguhr 6, dodecane Base sodium sulfonate 2, Carboxymethyl cellulose sodium is appropriate, and water is appropriate；
The concentration of described sodium periodate solution is 0.1-10g/L；PAMAM solution concentration is 1-10g/L.
Described a kind of non-woven fabrics containing Flos Lonicerae extractive solution and preparation method thereof, it is characterised in that by following steps system Become:
A., at 150-200 DEG C, nano-tourmaline powder is joined in polylactic acid, adds polyethylene glycol 200, stir, Make nano-tourmaline powder evenly spread in polylactic acid, and make polylactic acid be wrapped in nano-tourmaline powder surface, form microsphere, mistake Filter and dry；
B. activated carbon is added in water and be uniformly dispersed, be then added to Mint Essence and Flos Lonicerae extractive solution, continue to divide Dissipate, after being uniformly dispersed, proceed to stand under vacuumized conditions 3-5h, obtain being loaded with minty note by centrifugal, dry, milled processed Essence and the activated carbon powder of Flos Lonicerae extractive solution；
C. bamboo filament fibre powder being placed in lucifuge oxidation reaction 3-5h in sodium periodate solution, reaction temperature is 40-110 DEG C, mistake Filter, wash, dry, obtain aoxidizing bamboo fibre；Oxidation bamboo fibre is immersed in 3-6h in PAMAM solution, reaction temperature 25-85 DEG C, filtering drying also grinds, and obtains PAMAM and is grafted bamboo filament fibre powder；
D. by isotactic polypropylene, step a thus obtained microsphere, step b gained load Mint Essence and the activated carbon of Flos Lonicerae extractive solution Powder, step c gained PAMAM grafting bamboo filament fibre powder, spandex add screw extruder to and melt, then through spinning, drawing-off, one-tenth Non-woven fabrics is prepared after net, hot rolling；
E. kieselguhr is added to the water, is stirring evenly and then adding into dodecyl sodium sulfate and chitosan, is stirring evenly and then adding into Carboxymethyl cellulose sodium, adjusts modest viscosity, prepares serosity；Step d gained non-woven fabrics is totally submerged in serosity, and puts into super Ultrasonic 5-10min in acoustic wave oscillator, takes out, the method using " two leachings two are rolled ", and padder mangle is used in i.e. fully submergence, then Submergence, then with after padder mangle, puts into baker, bakees 2-5min, take out.
Described a kind of non-woven fabrics containing Flos Lonicerae extractive solution and preparation method thereof, it is characterised in that dry described in step b Roasting machine stoving temperature is 70-110 DEG C.
The technical parameter of the present invention is:
Formaldehyde absorbing rate >=11.09% of Unit Weight non-woven fabrics, benzene adsorption rate >=14.83%, TVOC adsorption rate >=13.42%.

Claims (3)

1. the non-woven fabrics containing Flos Lonicerae extractive solution, it is characterised in that be made up of the raw material of following weight portion:
Flos Lonicerae extractive solution 3-6, bamboo filament fibre powder 3-7, chitosan 1-2, nano-tourmaline powder 4-8, PAMAM solution 4-9, poly-breast Acid 5-10, spandex 1-2, polyethylene glycol 200 1-2, activated carbon 3-5, Mint Essence 4-8, sodium periodate solution 10-15, isotactic gathers Propylene 50-70, kieselguhr 3-6, dodecyl sodium sulfate 1-2, Carboxymethyl cellulose sodium is appropriate, and water is appropriate；
The concentration of described sodium periodate solution is 0.1-10g/L；PAMAM solution concentration is 1-10g/L.
A kind of non-woven fabrics containing Flos Lonicerae extractive solution the most according to claim 1 and preparation method thereof, it is characterised in that by Following steps are made:
A., at 150-200 DEG C, nano-tourmaline powder is joined in polylactic acid, adds polyethylene glycol 200, stir, Make nano-tourmaline powder evenly spread in polylactic acid, and make polylactic acid be wrapped in nano-tourmaline powder surface, form microsphere, mistake Filter and dry；
B. activated carbon is added in water and be uniformly dispersed, be then added to Mint Essence and Flos Lonicerae extractive solution, continue to divide Dissipate, after being uniformly dispersed, proceed to stand under vacuumized conditions 3-5h, obtain being loaded with minty note by centrifugal, dry, milled processed Essence and the activated carbon powder of Flos Lonicerae extractive solution；
C. bamboo filament fibre powder being placed in lucifuge oxidation reaction 3-5h in sodium periodate solution, reaction temperature is 40-110 DEG C, mistake Filter, wash, dry, obtain aoxidizing bamboo fibre；Oxidation bamboo fibre is immersed in 3-6h in PAMAM solution, reaction temperature 25-85 DEG C, filtering drying also grinds, and obtains PAMAM and is grafted bamboo filament fibre powder；
D. by isotactic polypropylene, step a thus obtained microsphere, step b gained load Mint Essence and the activated carbon of Flos Lonicerae extractive solution Powder, step c gained PAMAM grafting bamboo filament fibre powder, spandex add screw extruder to and melt, then through spinning, drawing-off, one-tenth Non-woven fabrics is prepared after net, hot rolling；
E. kieselguhr is added to the water, is stirring evenly and then adding into dodecyl sodium sulfate and chitosan, is stirring evenly and then adding into Carboxymethyl cellulose sodium, adjusts modest viscosity, prepares serosity；Step d gained non-woven fabrics is totally submerged in serosity, and puts into super Ultrasonic 5-10min in acoustic wave oscillator, takes out, the method using " two leachings two are rolled ", and padder mangle is used in i.e. fully submergence, then Submergence, then with after padder mangle, puts into baker, bakees 2-5min, take out.
A kind of non-woven fabrics containing Flos Lonicerae extractive solution the most according to claim 2 and preparation method thereof, it is characterised in that step Described in rapid b, curer stoving temperature is 70-110 DEG C.
CN201610709514.3A 2016-08-24 2016-08-24 A kind of non-woven fabrics containing Flos Lonicerae extractive solution and preparation method thereof Pending CN106149362A (en)