CN106319765A - Nonwoven fabric with performances of toughening and retarding flame and capability of releasing negative oxygen ions and preparation method of nonwoven fabric - Google Patents
Nonwoven fabric with performances of toughening and retarding flame and capability of releasing negative oxygen ions and preparation method of nonwoven fabric Download PDFInfo
- Publication number
- CN106319765A CN106319765A CN201610688885.8A CN201610688885A CN106319765A CN 106319765 A CN106319765 A CN 106319765A CN 201610688885 A CN201610688885 A CN 201610688885A CN 106319765 A CN106319765 A CN 106319765A
- Authority
- CN
- China
- Prior art keywords
- parts
- nano
- nonwoven fabric
- negative oxygen
- woven fabrics
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a nonwoven fabric with performances of toughening and retarding flame and capability of releasing negative oxygen ions and a preparation method of the nonwoven fabric. The nonwoven fabric is characterized by being prepared from the following raw materials in parts by weight: 2 to 4 parts of nano-crystalline cellulose, 4 to 8 parts of nano tourmaline powder, 1 to 2 parts of micropowder silica gel, 5 to 10 parts of polylactic acid, 1 to 2 parts of polyethylene glycol 200, 3 to 5 parts of activated carbon, 4 to 8 parts of herba menthae essence, 1 to 2 parts of magnesium hydroxide, 50 to 70 parts of isotatic polypropylene, 3 to 6 parts of diatomite, 1 to 2 parts of sodium dodecyl sulfate, a proper amount of carboxymethyl cellulose sodium and a proper amount of water. According to the nonwoven fabric disclosed by the invention, the nano tourmaline powder is added in the nonwoven fabric, so an effect of continuously releasing the negative oxygen ions can be realized; when the nonwoven fabric is applied to automotive interiors, a space in an automobile can become cool, comfortable and refreshed; by matching with the herba menthae essence, a remarkable refreshing effect is realized; by matching with the added nano-crystalline cellulose and the magnesium hydroxide, a target product is endowed with the functions of toughening and retarding flame.
Description
Technical field
The present invention relates to a kind of non-woven fabrics and preparation method thereof, be specifically related to a kind of toughening flame-proof, can discharge continuously negative
Non-woven fabrics of oxonium ion and preparation method thereof.
Background technology
Non-woven fabrics is a kind of non-weaving cloth, and it is to directly utilize high polymer section, chopped fiber or long filament fiber is passed through gas
Stream or machinery become net, are then passed through spun lacing, acupuncture, or hot rolling and reinforce, and eventually pass the cloth without braiding that Final finishing is formed.Tool
Having softness, the ventilative and tencel goods of planar structure, advantage is not produce Soft flocks, tough, durable, silkiness is soft, also
It is the one of reinforcing material, and the sensation of also cotton, have been widely used for automotive field.But stay in confined space for a long time
In, people can think that dizzy brain rises, when come forest seashore, waterfall etc. local when, we can feel spirit and QI cleaning, and this is just
It it is the effect of negative aeroion.Negative aeroion is also negative oxygen ion, refer to obtain excess electron and electronegative oxygen from
Son.
Jiang Yinggang, in " containing the preparation of bamboo charcoal powder liner cloth and Study on adsorption properties ", utilizes bamboo charcoal powder and non-weaving cloth, logical
Cross coating, the method such as pad, make multiple containing bamboo charcoal powder nonwoven interlining.But, when it is applied to automotive trim, there is also
And be not provided that negative oxygen ion, refrigerant fragrance of refreshing oneself etc. can not be discharged be conducive to traffic safety and driving comfortable space is provided
Weak point.
Summary of the invention
Comprehensive above consideration, the present invention provides a kind of non-woven fabrics and formula thereof, it is therefore intended that solve when non-woven fabrics is applied
When automotive trim, it is impossible to releasing negative oxygen ion continuously, it is provided that the preferably defect of interior space.
For achieving the above object, technical scheme is as follows:
A kind of toughening flame-proof, can the non-woven fabrics of releasing negative oxygen ion continuously, it is characterised in that by the raw material system of following weight portion
Become:
Nano-cellulose 2-4, nano-tourmaline powder 4-8, micropowder silica gel 1-2, polylactic acid 5-10, polyethylene glycol 200 1-2, activity
Charcoal 3-5, Mint Essence 4-8, magnesium hydroxide 1-2, isotactic polypropylene 50-70, kieselguhr 3-6, dodecyl sodium sulfate 1-2, hydroxyl
Sodium carboxymethylcellulose pyce is appropriate, and water is appropriate;
Described a kind of toughening flame-proof, can the non-woven fabrics and preparation method thereof of releasing negative oxygen ion continuously, it is characterised in that by
Following steps are made:
A., at 150-200 DEG C, nano-tourmaline powder is joined in polylactic acid, adds polyethylene glycol 200, stir,
Make tourmaline powder evenly spread in polylactic acid, and make polylactic acid be wrapped in nano-tourmaline powder surface, form microsphere, filter also
Dry;
B. activated carbon and nano-cellulose are added in water and be uniformly dispersed, be then added to Mint Essence, continue to divide
Dissipate, after being uniformly dispersed, proceed to stand under vacuumized conditions 3-5h, obtain being loaded with minty note by centrifugal, dry, milled processed
The activated carbon powder of essence and nano-cellulose mixture;
C. isotactic polypropylene, step a thus obtained microsphere, step b gained mixture and micropowder silica gel are added to screw extruder and entered
Row is melted, then prepares non-woven fabrics after spinning, drawing-off, one-tenth net, hot rolling;
D. kieselguhr is added to the water, is stirring evenly and then adding into dodecyl sodium sulfate, be stirring evenly and then adding into methylol fine
Dimension element sodium and magnesium hydroxide, adjust modest viscosity, prepares serosity;Step c gained non-woven fabrics is totally submerged in serosity, and puts into
Ultrasonic 5-10min in ultrasonic oscillator, takes out, the method using " two leachings two are rolled ", and padder mangle is used in i.e. fully submergence,
Submergence again, then with after padder mangle, puts into baker, bakees 2-5min, take out.
Described a kind of toughening flame-proof, can the non-woven fabrics and preparation method thereof of releasing negative oxygen ion continuously, its feature exists
In, curer stoving temperature described in step b is 70-110 DEG C.
The invention has the beneficial effects as follows: in non-woven fabrics, add nano-tourmaline powder, can reach to discharge continuously negative oxygen from
The effect of son, when being applied to automotive trim, can make interior space refrigerant comfortable, spirit and QI cleaning, Mint Essence of arranging in pairs or groups, effect of refreshing oneself
Fruit is notable, reduces and contained the harm of fatigue driving;Utilize polylactic acid to wrap up nano-tourmaline powder, not only prevent nanometer
Tourmaline powder broken and coming off, and the appearance promoting tourmaline powder and polypropylene substrate closes and dispersion, polylactic acid tool simultaneously
There are excellent breathability, oxygen permeability, and antibacterial and anti-mildew characteristic, improve the fungus resistance of non-woven fabrics, extend service life;With
Activated carbon loads Mint Essence, adds loading and the air contact area of Mint Essence, reaches more lasting release
Effect, has been simultaneously introduced the characterization of adsorption of activated carbon, increases the function of non-woven fabrics clean air;With kieselguhr serosity to non-woven fabrics
Carry out coating, can effectively remove harmful substance and house pet body odor, the rubbish institutes such as the free formaldehyde in air, benzene, ammonia, VOC
The abnormal flavour produced, solves in-vehicle air pollution, hence it is evident that improve environment inside car comprehensively;Coordinate the nano-cellulose and hydroxide added
Magnesium gives the function of target product toughening flame-proof.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is further described.
Embodiment
A kind of toughening flame-proof, can the non-woven fabrics of releasing negative oxygen ion continuously, it is characterised in that former by following weight portion
Material is made:
Nano-cellulose 4, nano-tourmaline powder 8, micropowder silica gel 2, polylactic acid 10, polyethylene glycol 200 2, activated carbon 5, minty note
Essence 8, magnesium hydroxide 2, isotactic polypropylene 70, kieselguhr 6, dodecyl sodium sulfate 2, Carboxymethyl cellulose sodium is appropriate, and water is appropriate;
Described a kind of toughening flame-proof, can the non-woven fabrics and preparation method thereof of releasing negative oxygen ion continuously, it is characterised in that by
Following steps are made:
A., at 150-200 DEG C, nano-tourmaline powder is joined in polylactic acid, adds polyethylene glycol 200, stir,
Make tourmaline powder evenly spread in polylactic acid, and make polylactic acid be wrapped in nano-tourmaline powder surface, form microsphere, filter also
Dry;
B. activated carbon and nano-cellulose are added in water and be uniformly dispersed, be then added to Mint Essence, continue to divide
Dissipate, after being uniformly dispersed, proceed to stand under vacuumized conditions 3-5h, obtain being loaded with minty note by centrifugal, dry, milled processed
The activated carbon powder of essence and nano-cellulose mixture;
C. isotactic polypropylene, step a thus obtained microsphere, step b gained mixture and micropowder silica gel are added to screw extruder and entered
Row is melted, then prepares non-woven fabrics after spinning, drawing-off, one-tenth net, hot rolling;
D. kieselguhr is added to the water, is stirring evenly and then adding into dodecyl sodium sulfate, be stirring evenly and then adding into methylol fine
Dimension element sodium and magnesium hydroxide, adjust modest viscosity, prepares serosity;Step c gained non-woven fabrics is totally submerged in serosity, and puts into
Ultrasonic 5-10min in ultrasonic oscillator, takes out, the method using " two leachings two are rolled ", and padder mangle is used in i.e. fully submergence,
Submergence again, then with after padder mangle, puts into baker, bakees 2-5min, take out.
Described a kind of toughening flame-proof, can the non-woven fabrics and preparation method thereof of releasing negative oxygen ion continuously, its feature exists
In, curer stoving temperature described in step b is 70-110 DEG C.
The technical parameter of the present invention is:
Formaldehyde absorbing rate >=11.09% of Unit Weight non-woven fabrics, benzene adsorption rate >=14.83%, TVOC adsorption rate >=13.42%.
Claims (3)
1. a toughening flame-proof, can the non-woven fabrics of releasing negative oxygen ion continuously, it is characterised in that by the raw material of following weight portion
Make:
Nano-cellulose 2-4, nano-tourmaline powder 4-8, micropowder silica gel 1-2, polylactic acid 5-10, polyethylene glycol 200 1-2, activity
Charcoal 3-5, Mint Essence 4-8, magnesium hydroxide 1-2, isotactic polypropylene 50-70, kieselguhr 3-6, dodecyl sodium sulfate 1-2, hydroxyl
Sodium carboxymethylcellulose pyce is appropriate, and water is appropriate.
A kind of toughening flame-proof the most according to claim 1, can the non-woven fabrics of releasing negative oxygen ion and preparation side thereof continuously
Method, it is characterised in that be made up of following steps:
A., at 150-200 DEG C, nano-tourmaline powder is joined in polylactic acid, adds polyethylene glycol 200, stir,
Make tourmaline powder evenly spread in polylactic acid, and make polylactic acid be wrapped in nano-tourmaline powder surface, form microsphere, filter also
Dry;
B. activated carbon and nano-cellulose are added in water and be uniformly dispersed, be then added to Mint Essence, continue to divide
Dissipate, after being uniformly dispersed, proceed to stand under vacuumized conditions 3-5h, obtain being loaded with minty note by centrifugal, dry, milled processed
The activated carbon powder of essence and nano-cellulose mixture;
C. isotactic polypropylene, step a thus obtained microsphere, step b gained mixture and micropowder silica gel are added to screw extruder and entered
Row is melted, then prepares non-woven fabrics after spinning, drawing-off, one-tenth net, hot rolling;
D. kieselguhr is added to the water, is stirring evenly and then adding into dodecyl sodium sulfate, be stirring evenly and then adding into methylol fine
Dimension element sodium and magnesium hydroxide, adjust modest viscosity, prepares serosity;Step c gained non-woven fabrics is totally submerged in serosity, and puts into
Ultrasonic 5-10min in ultrasonic oscillator, takes out, the method using " two leachings two are rolled ", and padder mangle is used in i.e. fully submergence,
Submergence again, then with after padder mangle, puts into baker, bakees 2-5min, take out.
A kind of toughening flame-proof the most according to claim 2, can the non-woven fabrics of releasing negative oxygen ion and preparation side thereof continuously
Method, it is characterised in that curer stoving temperature described in step b is 70-110 DEG C.