CN106280801A - A kind of adjustable coating of humidity - Google Patents
A kind of adjustable coating of humidity Download PDFInfo
- Publication number
- CN106280801A CN106280801A CN201610706730.2A CN201610706730A CN106280801A CN 106280801 A CN106280801 A CN 106280801A CN 201610706730 A CN201610706730 A CN 201610706730A CN 106280801 A CN106280801 A CN 106280801A
- Authority
- CN
- China
- Prior art keywords
- parts
- titanium dioxide
- humidity
- calcium carbonate
- adjustable coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of adjustable coating of humidity, including titanium dioxide, kieselguhr, titanium dioxide, magnesium hydroxide, aluminium silicate, acrylic emulsion, Gypsum Fibrosum powder, precipitated calcium carbonate, water, the mass fraction of each component is: titanium dioxide 10 16 parts, 15 30 parts of kieselguhr, titanium dioxide 6 15 parts, 58 parts of magnesium hydroxide, aluminium silicate 8 10 parts, acrylic emulsion 12 19 parts, Gypsum Fibrosum powder 34 parts, precipitated calcium carbonate 36 parts, 40 70 parts of water.The adjustable coating of humidity of the present invention does not contains the heavy metal antimony prohibitted the use of of national regulation, arsenic, barium, cadmium, chromium, lead, hydrargyrum, selenium, do not contain formaldehyde, do not contain Vinyl Chloride Monomer, while there is good antibacterial and deodouring, also there is good humidity regulation, be a environmental type coating on the whole;There is the physicochemical property of excellence, building material is played well protection, decoration function.
Description
Technical field
The present invention relates to a kind of house ornamentation paint field, in particular it relates to a kind of adjustable coating of humidity.
Background technology
Coating is seen everywhere in life, acts primarily as protection and the effect of decoration, and according to different use environment, kind
The most varied.Along with progress and the development of science and technology of society, living environment comfortableness requirement is improved constantly, not only by people
Only Indoor environment temperature is had a higher requirement, indoor wet environment is also had certain requirement simultaneously.There is research table
Bright, in hot environment, higher relative humidity can be further exacerbated by the hotness of people;In low temperature environment, relatively low is relative
Humidity can aggravate the cold sensation of people.
Summary of the invention
For above-mentioned deficiency present in prior art, the technical problem to be solved is to provide a kind of effective
The adjustable coating of humidity.
The technical solution adopted for the present invention to solve the technical problems is: provide a kind of adjustable coating of humidity, including
Titanium dioxide, kieselguhr, titanium dioxide, magnesium hydroxide, aluminium silicate, acrylic emulsion, Gypsum Fibrosum powder, precipitated calcium carbonate, water, each component
Mass fraction be: titanium dioxide 10-16 part, kieselguhr 15-30 part, titanium dioxide 6-15 part, magnesium hydroxide 5-8 part, aluminium silicate
8-10 part, acrylic emulsion 12-19 part, Gypsum Fibrosum powder 3-4 part, precipitated calcium carbonate 3-6 part, water 40-70 part.
As preferably, the adjustable coating of described humidity, it is characterised in that: each component of the adjustable coating of described humidity
Mass fraction be: titanium dioxide 12 parts, 18 parts of kieselguhr, titanium dioxide 15 parts, 7 parts of magnesium hydroxide, aluminium silicate 8 parts, acrylic acid
Emulsion 15 parts, Gypsum Fibrosum powder 4 parts, precipitated calcium carbonate 5 parts, 65 parts of water.
As preferably, the adjustable coating of described humidity, it is characterised in that: described acrylic emulsion solid content is 27-
58wt%。
As preferably, the preparation method of the adjustable coating of described humidity, it is characterised in that comprise the steps:
(1) Gypsum Fibrosum powder, precipitated calcium carbonate and water are added sequentially in stirred tank, under 400 ~ 600r/min speed conditions, stir
Mix 10 ~ 30min, prepare thickening agent;
(2) being sequentially added into residue component, regulate viscosity, under 800 ~ 1000r/min speed conditions, stirring 20 ~ 25min is i.e.
Can.
The adjustable coating of humidity of the present invention do not contain the heavy metal antimony prohibitted the use of of national regulation, arsenic, barium, cadmium,
Chromium, lead, hydrargyrum, selenium, do not contain formaldehyde, do not contain Vinyl Chloride Monomer, while having good antibacterial and deodouring, also has very well
Humidity regulation, be a environmental type coating on the whole;There is the physicochemical property of excellence, building material is played very well
Protection, decoration function.
Detailed description of the invention
The present invention provide the adjustable coating of a kind of humidity, including titanium dioxide, kieselguhr, titanium dioxide, magnesium hydroxide,
Aluminium silicate, acrylic emulsion, Gypsum Fibrosum powder, precipitated calcium carbonate, water, the mass fraction of each component is: titanium dioxide 10-16 part, silicon
Diatomaceous earth 15-30 part, titanium dioxide 6-15 part, magnesium hydroxide 5-8 part, aluminium silicate 8-10 part, acrylic emulsion 12-19 part, Gypsum Fibrosum powder
3-4 part, precipitated calcium carbonate 3-6 part, water 40-70 part.
As preferably, the adjustable coating of described humidity, it is characterised in that: each component of the adjustable coating of described humidity
Mass fraction be: titanium dioxide 12 parts, 18 parts of kieselguhr, titanium dioxide 15 parts, 7 parts of magnesium hydroxide, aluminium silicate 8 parts, acrylic acid
Emulsion 15 parts, Gypsum Fibrosum powder 4 parts, precipitated calcium carbonate 5 parts, 65 parts of water.
As preferably, the adjustable coating of described humidity, it is characterised in that: described acrylic emulsion solid content is 27-
58wt%。
As preferably, the preparation method of the adjustable coating of described humidity, it is characterised in that comprise the steps:
(1) Gypsum Fibrosum powder, precipitated calcium carbonate and water are added sequentially in stirred tank, under 400 ~ 600r/min speed conditions, stir
Mix 10 ~ 30min, prepare thickening agent;
(2) being sequentially added into residue component, regulate viscosity, under 800 ~ 1000r/min speed conditions, stirring 20 ~ 25min is i.e.
Can.
The above, be only to presently preferred embodiments of the present invention, the present invention not do the restriction of other forms, appoints
What those skilled in the art changed possibly also with the technology contents of the disclosure above or be modified as changing on an equal basis etc.
Effect embodiment.Every without departing from the present invention program content, the technical spirit of the foundation present invention is to made for any of the above embodiments any
Simple modification, equivalent variations and remodeling, all fall within protection scope of the present invention.
Claims (4)
1. the adjustable coating of humidity, it is characterised in that: include titanium dioxide, kieselguhr, titanium dioxide, magnesium hydroxide, silicon
Acid aluminum, acrylic emulsion, Gypsum Fibrosum powder, precipitated calcium carbonate, water, the mass fraction of each component is: titanium dioxide 10-16 part, diatom
Soil 15-30 part, titanium dioxide 6-15 part, magnesium hydroxide 5-8 part, aluminium silicate 8-10 part, acrylic emulsion 12-19 part, Gypsum Fibrosum powder 3-4
Part, precipitated calcium carbonate 3-6 part, water 40-70 part.
The adjustable coating of humidity the most according to claim 1, it is characterised in that: each group of the adjustable coating of described humidity
The mass fraction divided is: titanium dioxide 12 parts, 18 parts of kieselguhr, titanium dioxide 15 parts, 7 parts of magnesium hydroxide, aluminium silicate 8 parts, propylene
Yogurt liquid 15 parts, Gypsum Fibrosum powder 4 parts, precipitated calcium carbonate 5 parts, 65 parts of water.
The adjustable coating of humidity the most according to claim 2, it is characterised in that: described acrylic emulsion solid content is
27-58wt%。
4. according to the preparation method of the adjustable coating of humidity described in claim 1, it is characterised in that comprise the steps:
(1) Gypsum Fibrosum powder, precipitated calcium carbonate and water are added sequentially in stirred tank, under 400 ~ 600r/min speed conditions, stir
Mix 10 ~ 30min, prepare thickening agent;
(2) being sequentially added into residue component, regulate viscosity, under 800 ~ 1000r/min speed conditions, stirring 20 ~ 25min is i.e.
Can.