CN106277995A - 免烧河沙水泥砖 - Google Patents

免烧河沙水泥砖 Download PDF

Info

Publication number
CN106277995A
CN106277995A CN201610721996.4A CN201610721996A CN106277995A CN 106277995 A CN106277995 A CN 106277995A CN 201610721996 A CN201610721996 A CN 201610721996A CN 106277995 A CN106277995 A CN 106277995A
Authority
CN
China
Prior art keywords
parts
river sand
cement
cement brick
unburned
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610721996.4A
Other languages
English (en)
Inventor
刘兴汉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beihai Jinjiang Cement Products Co Ltd
Original Assignee
Beihai Jinjiang Cement Products Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beihai Jinjiang Cement Products Co Ltd filed Critical Beihai Jinjiang Cement Products Co Ltd
Priority to CN201610721996.4A priority Critical patent/CN106277995A/zh
Publication of CN106277995A publication Critical patent/CN106277995A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种免烧河沙水泥砖，由以下重量份数的组份组成：河沙33‑35份、水泥18‑20份、生石灰8‑12份、石硝6‑10份、砂浆宝8‑10份、石粉2‑4份、炉渣6‑8份、岩砂晶5‑8份、氯化钾0.5‑0.8份、早强剂1‑2份。该水泥砖采用河沙与水泥做为主要原料，原料来源广泛，成本低，降低水泥砖的成本。

Description

免烧河沙水泥砖
技术领域
本发明涉及建筑材料，特别地，涉及一种免烧河沙水泥砖。
背景技术
水泥砖生产过程中主要依靠液压设备的压制而成，而在成型之前则需要将原料进行混合搅拌，最重要的是还需要进行合理的配比，这样才能够制作成为品质非常好的水泥砖。那么水泥砖机的使用原料非常广泛，基本上是以建筑废料和工业废料为主，这些都能够帮助我们合理使用，同时还能够降低生产的成本。那么如何选择合理的原料配比，使水泥砖的性能达到标准要求，同时降低原料成本是业界值得研究的方向。
发明内容
本发明目的在于提供一种免烧河沙水泥砖，以提供一种高强度，低成本的水泥砖。
为实现上述目的，本发明提供一种免烧河沙水泥砖，由以下重量份数的组份组成：河沙33-35份、水泥18-20份、生石灰8-12份、石硝6-10份、砂浆宝8-10份、石粉2-4份、炉渣6-8份、岩砂晶5-8份、氯化钾0.5-0.8份、早强剂1-2份。
进一步地，由以下重量份数的组份组成：所述河沙34份、所述水泥19份、所述生石灰9份、所述石硝7份、所述砂浆宝9份、所述石粉3份、所述炉渣7份、所述岩砂晶6份、所述氯化钾0.7份、所述早强剂1.2份。
本发明具有以下有益效果：
该水泥砖采用河沙与水泥做为主要原料，原料来源广泛，成本低，降低水泥砖的成本。
具体实施方式
以下对本发明的实施例进行详细说明。
本发明的优选实施例提供了一种免烧河沙水泥砖，由以下重量份数的组份组成：河沙33-35份、水泥18-20份、生石灰8-12份、石硝6-10份、砂浆宝8-10份、石粉2-4份、炉渣6-8份、岩砂晶5-8份、氯化钾0.5-0.8份、早强剂1-2份。
优选地，由以下重量份数的组份组成：所述河沙34份、所述水泥19份、所述生石灰9份、所述石硝7份、所述砂浆宝9份、所述石粉3份、所述炉渣7份、所述岩砂晶6份、所述氯化钾0.7份、所述早强剂1.2份。
该水泥砖采用河沙与水泥做为主要原料，原料来源广泛，成本低，降低水泥砖的成本。
实施例1
河沙35份、水泥18份、生石灰12份、石硝6份、砂浆宝10份、石粉2份、炉渣6份、岩砂晶8份、氯化钾0.8份、早强剂1份，上述重量份数的原料研磨成粉，混合均匀后，加适量水直接压制而成。
实施例2
河沙34份、水泥19份、生石灰9份、石硝7份、砂浆宝9份、石粉3份、炉渣7份、岩砂晶6份、氯化钾0.7份、早强剂1.2份，上述重量份数的原料研磨成粉，混合均匀后，加适量水直接压制而成。
实施例3
河沙33份、水泥20份、生石灰8份、石硝10份、砂浆宝8份、石粉4份、炉渣8份、岩砂晶5份、氯化钾0.5份、早强剂2份，上述重量份数的原料研磨成粉，混合均匀后，加适量水直接压制而成。
以上所述仅为本发明的优选实施例而已，并不用于限制本发明；对于本领域的技术人员来说，本发明可以有各种更改和变化。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (2)

1.一种免烧河沙水泥砖，其特征在于，由以下重量份数的组份组成：
河沙33-35份、水泥18-20份、生石灰8-12份、石硝6-10份、砂浆宝8-10份、石粉2-4份、炉渣6-8份、岩砂晶5-8份、氯化钾0.5-0.8份、早强剂1-2份。
2.根据权利要求1所述的免烧河沙水泥砖，其特征在于，由以下重量份数的组份组成：
所述河沙34份、所述水泥19份、所述生石灰9份、所述石硝7份、所述砂浆宝9份、所述石粉3份、所述炉渣7份、所述岩砂晶6份、所述氯化钾0.7份、所述早强剂1.2份。
CN201610721996.4A 2016-08-25 2016-08-25 免烧河沙水泥砖 Pending CN106277995A (zh)