CN103232201A - 建筑用免烧砖 - Google Patents
建筑用免烧砖 Download PDFInfo
- Publication number
- CN103232201A CN103232201A CN2013101693629A CN201310169362A CN103232201A CN 103232201 A CN103232201 A CN 103232201A CN 2013101693629 A CN2013101693629 A CN 2013101693629A CN 201310169362 A CN201310169362 A CN 201310169362A CN 103232201 A CN103232201 A CN 103232201A
- Authority
- CN
- China
- Prior art keywords
- brick
- baking
- grinding tool
- cement
- coal ash
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
建筑用免烧砖,用以下材料配比和加工方法完成,材料配比:用岩棉保温材料废弃物60%至70%、水泥10%至20%、矿山碎石硝10%至20%、发电厂及工业用锅炉排放后的煤灰物2%至5%、粘合剂1%至3%和适量的水。优质材料配比:用65%岩棉保温材料废弃物、水泥15%、矿山碎石硝15%、发电厂及工业用锅炉排放后的煤灰物5%和适量的水。将以上材料配比或优质材料配比放入搅拌机搅拌混合均匀后,注或放入磨具,在磨具内进行振动加压,脱胎成砖,再经自然晾干而成。本发明的用料因80%左右是废弃物,这样及合理利用了废弃物,又保护了环境,本发明与现有的技术相比,具有压力强,抗碱化、又节能、又环保的特点。
Description
技术领域
本发明涉及一种建筑用砖,特别是一种建筑用免烧砖,属于建筑用砖方面的技术领域。
背景技术
针对河北省河间市、任丘市、大城县一带,有上万家的岩棉保温材料厂,更有大量的岩棉保温材料废弃物无从处理,造成了很大的环境污染。在建筑工程施工中,砖是不可缺少的建材,如果利用好这些岩棉保温材料废弃物的话,及能为国家的环境污染出一份力量又可以变废为宝。
发明内容
针对上述技术的不足,本发明是为解决一种建筑用免烧砖。
建筑用免烧砖,其特征在于:用以下材料配比和加工方法完成,材料配比:用岩棉保温材料废弃物60%至70%、水泥10%至20%、矿山碎石硝10%至20%、发电厂及工业用锅炉排放后的煤灰物2%至5%、粘合剂1%至3%和适量的水。多加入水泥1%至3%或发电厂及工业用锅炉排放后的煤灰物1%至3%,可不加入粘合剂。
优质材料配比:用65%岩棉保温材料废弃物、水泥15%、矿山碎石硝15%、发电厂及工业用锅炉排放后的煤灰物5%和适量的水。多加入水泥1%至3%或发电厂及工业用锅炉排放后的煤灰物1%至3%,可不加入粘合剂。
将以上材料配比或优质材料配比放入搅拌机搅拌混合均匀后,注或放入磨具,在磨具内进行振动加压,脱胎成砖,再经自然晾干而成。
在砖体(1)上设有五至十个砖孔(2),砖孔(2)是圆形或方形或长方形,砖孔(2)并排均匀设置,所述的砖孔(2)贯通于砖体(1)。
本发明的用料因80%左右是废弃物,这样及合理利用了废弃物,又保护了环境,本发明与现有的技术相比,具有压力强,抗碱化、又节能、又环保的特点。
附图说明
图1是本发明的立体结构示意图。
图中:1砖体、2砖孔。
具体实施方式
如图1所示,一种建筑用免烧砖,砖体1可做成方形或长方形,在砖体1上设有砖孔2。砖孔2是圆形或方形或长方形。也可在砖体1上设有并排的八至十个砖孔2。所述的砖孔2贯通于砖体1。
建筑用免烧砖,用以下材料配比完成:
优质材料配比,用65%岩棉保温材料废弃物、(标号为42.5号)水泥15%、矿山碎石硝15%、发电厂及工业用锅炉排放后的煤灰物3%、粘合剂2%和适量的水。多加入水泥2%或发电厂及工业用锅炉排放后的煤灰物2%,可不加入粘合剂。放入搅拌机搅拌混合均匀后,注或放入磨具,在磨具内进行振动加压,脱胎成砖,再经自然晾干而成。
一般材料配比,用岩棉保温材料废弃物60%至70%、(标号为42.5号)水泥10%至20%、矿山碎石硝10%至20%、发电厂及工业用锅炉排放后的煤灰物2%至5%、粘合剂1%至3%和适量的水。多加入水泥1%至3%或发电厂及工业用锅炉排放后的煤灰物1%至3%,可不加入粘合剂。放入搅拌机搅拌混合均匀后,注入或放入磨具,在磨具内进行振动加压,脱胎成砖,再经自然晾干而成。可不加入粘合剂使用。
Claims (4)
1.建筑用免烧砖,其特征在于:用以下材料配比和加工方法完成,材料配比:用岩棉保温材料废弃物60%至70%、水泥10%至20%、矿山碎石硝10%至20%、发电厂及工业用锅炉排放后的煤灰物2%至5%、粘合剂1%至3%和适量的水,放入搅拌机搅拌混合均匀后,注入或放入磨具,在磨具内进行振动加压,脱胎成砖,再经自然晾干而成。
2.根据权利要求1所述的免烧砖,其特征在于:用以下材料配比和加工方法完成,优质材料配比:用65%岩棉保温材料废弃物、水泥15%、矿山碎石硝15%、发电厂及工业用锅炉排放后的煤灰物5%和适量的水,放入搅拌机搅拌混合均匀后,注或放入磨具,在磨具内进行振动加压,脱胎成砖,再经自然晾干而成。
3.根据权利要求1或2所述的免烧砖,其特征在于:多加入水泥1%至3%或发电厂及工业用锅炉排放后的煤灰物1%至3%,可不加入粘合剂。
4.根据权利要求1或2所述的免烧砖,其特征在于:在砖体(1)上设有五至十个砖孔(2),砖孔(2)是圆形或方形或长方形,砖孔(2)并排均匀设置,所述的砖孔(2)贯通于砖体(1)。