CN106243874A - Bathroom aluminium alloy door and preparation method thereof - Google Patents
Bathroom aluminium alloy door and preparation method thereof Download PDFInfo
- Publication number
- CN106243874A CN106243874A CN201610884905.9A CN201610884905A CN106243874A CN 106243874 A CN106243874 A CN 106243874A CN 201610884905 A CN201610884905 A CN 201610884905A CN 106243874 A CN106243874 A CN 106243874A
- Authority
- CN
- China
- Prior art keywords
- aluminium alloy
- alloy door
- bathroom
- door
- content
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of bathroom aluminium alloy door, this bathroom aluminium alloy door is made up of aluminium alloy door's body and resistant coating, and resistant coating is coated on the surface of aluminium alloy door's body;Wherein, resistant coating is to be prepared by following method, first by hydroxy propylene acid resin, nano silicon, organic silicone oil and 3 (2,3 epoxy the third oxygen) propyl trimethoxy silicane carries out being mixed to get coating composition, and coating composition is then formed resistant coating in the surface of aluminium alloy door's body.This bathroom aluminium alloy door can effectively prevent the residual packing of the spot on surface, aluminium alloy door, dirt, and easy to clean, substantially increases aesthetic property and wholesomeness that bathroom aluminium alloy door uses.
Description
Technical field
The present invention relates to door and window and manufacture field, in particular it relates to a kind of bathroom aluminium alloy door and preparation method thereof.
Background technology
In recent years, along with expanding economy, improving constantly of people's living standard, the kind of door and window and derived product thereof is not
Break and increase.Such as, door closely bound up in our life is from traditional wooden door, to glass door, composite gate, stainless steel door
And aluminium alloy door.According to people's life, the needs of production, the kind of door varies in increase the most always.
According to door and window material and function, substantially can be divided into following a few class: Wood-door window, steel casement door window, revolving door antitheft door, from
Dynamic door, plastic door-window, revolving door, ornamental work of iron door and window, plastic-steel door and window, Door or window made of stainless steel, aluminum alloy doors and windows, glass fiber reinforced plastic door and window.
Aluminium alloy door, refers to that using aluminum alloy extrusion section bar is frame, stile, the door of fan material making.At present, aluminium alloy in life
The use of door is seen everywhere, and aluminium alloy door is applied to various field because it has the advantages such as cost is low, weatherability is strong, light
Institute.Wherein, aluminium alloy door is because its rust resistance is good, light, be easy to be processed into all size and become the preferable choosing of Door for bathroom
Select.But, shower door is low-priced to various spots, dirt owing to being easily stained with during using frequent and shower and using.And aluminum closes
The surface in Jinmen is not enough smooth, and long use can remaining and the most easy to clean and cause the surface of door because of its dirt
Unsightly and easily breed bacteria and then affect routine use.
Summary of the invention
It is an object of the invention to provide a kind of bathroom aluminium alloy door, this surface, bathroom aluminium alloy door has the resistant coating can
Effectively to prevent the residual packing of the spot on a surface, dirt and easy to clean, substantially increase what bathroom aluminium alloy door used
Aesthetic property and wholesomeness.
To achieve these goals, the invention provides a kind of bathroom aluminium alloy door, it is characterised in that described bathroom is used
Aluminium alloy door is made up of aluminium alloy door's body and resistant coating, and described resistant coating is coated on the surface of aluminium alloy door's body;Its
In, resistant coating is to be prepared by following method: first by hydroxy propylene acid resin, nano silicon, organic silicone oil and 3-(2,3-rings
Oxygen the third oxygen) propyl trimethoxy silicane carries out being mixed to get coating composition, then by coating composition in aluminium alloy door
The surface of body forms resistant coating.
Preferably, relative to the hydroxy propylene acid resin of 100 weight portions, the content of nano silicon is 20-30 weight, has
The content of machine silicone oil is 30-40 weight portion, and the content of 3-(2,3-epoxy the third oxygen) propyl trimethoxy silicane is 15-35 weight
Part.
Preferably, nano silicon size be 50-80nm.
Present invention also offers the preparation method of a kind of above-mentioned bathroom aluminium alloy door: first by hydroxy propylene acid resin, nanometer
Silicon dioxide, organic silicone oil and 3-(2,3-epoxy the third oxygen) propyl trimethoxy silicane are stirred obtaining coating composition;Connect
Coating composition on the surface of described aluminium alloy door main body with prepared bathroom aluminium alloy door.
Preferably, relative to the hydroxy propylene acid resin of 100 weight portions, the content of nano silicon is 20-30 weight, has
The content of machine silicone oil is 30-40 weight portion, and the content of 3-(2,3-epoxy the third oxygen) propyl trimethoxy silicane is 15-35 weight
Part.
Preferably, coating is that the mode using spraying is carried out.
Preferably, the temperature of stirring is 30-45 DEG C, and the rotating speed of stirring is 1200-2000rpm, and the time of stirring is 0.5-
1.0h。
By technique scheme, the present invention is resistance to be formed by the surface-coated resistant compositions at aluminium alloy door's body
Dirty coating is so that prepared bathroom aluminium alloy door has good anti-pollution characteristic and property easy to clean.It addition, in this programme
In the preparation method of coated resistant coating: relative to the hydroxy propylene acid resin of 100 weight portions, the content of nano silicon
For 20-30 weight, the content of organic silicone oil is 30-40 weight portion, containing of 3-(2,3-epoxy the third oxygen) propyl trimethoxy silicane
Amount is 15-35 weight portion.The cooperative reinforcing effect of various raw materials makes to prepare resistant coating and can be good at sticking to aluminium alloy door
Surface and make the bathroom aluminium alloy door prepared have good resistant effect, it is ensured that aluminium alloy door's life-time service still U.S.
Sight, health.
Other features and advantages of the present invention will be described in detail in detailed description of the invention part subsequently.
Detailed description of the invention
Hereinafter the detailed description of the invention of the present invention is described in detail.It should be appreciated that described herein specifically
Embodiment is merely to illustrate and explains the present invention, is not limited to the present invention.
Hereinafter will be described the present invention by embodiment.
Preparation example 1
By hydroxy propylene acid resin, nano silicon (50nm), organic silicone oil and 3-(2,3-epoxy the third oxygen) propyl group front three
TMOS according to weight proportion 100:20:30:15 30 DEG C, rotating speed be to be stirred 0.5h under 1200rpm to obtain coating group
Compound T1.
Preparation example 2
By hydroxy propylene acid resin, nano silicon (60nm), organic silicone oil and 3-(2,3-epoxy the third oxygen) propyl group front three
TMOS according to weight proportion 100:25:35:25 30 DEG C, rotating speed be to be stirred 0.8h under 1600rpm to obtain coating group
Compound T2.
Preparation example 3
By hydroxy propylene acid resin, nano silicon (80nm), organic silicone oil and 3-(2,3-epoxy the third oxygen) propyl group front three
TMOS according to weight proportion 100:30:40:35 30 DEG C, rotating speed be to be stirred 1.0h under 2000rpm to obtain coating group
Compound T3.
Embodiment 1
The coating composition that preparation example 1 prepares is sprayed at the surface of aluminium alloy door's main body, after naturally drying, prepares bathroom
It is denoted as A1 with aluminium alloy door.
Embodiment 2
The coating composition that preparation example 2 prepares is sprayed at the surface of aluminium alloy door's main body, after naturally drying, prepares bathroom
It is denoted as A2 with aluminium alloy door.
Embodiment 3
The coating composition that preparation example 3 prepares is sprayed at the surface of aluminium alloy door's main body, after naturally drying, prepares bathroom
It is denoted as A3 with aluminium alloy door.
Comparative example 1
The coating composition first prepared according to preparation example 1, does not except for the difference that enter nano silicon, is denoted as D1;Again by D1
It is sprayed at the surface of aluminium alloy door's main body, prepares bathroom aluminium alloy door after naturally drying, be denoted as B1.
Comparative example 2
The coating composition first prepared according to preparation example 1, does not except for the difference that add organic silicone oil, is denoted as D2;Again D2 is sprayed
It is applied to the surface of aluminium alloy door's main body, prepares bathroom aluminium alloy door after naturally drying, be denoted as B2.
Comparative example 3
The coating composition first prepared according to preparation example 2, does not except for the difference that add organic silicone oil, is denoted as D3;Again D3 is sprayed
It is applied to the surface of aluminium alloy door's main body, prepares bathroom aluminium alloy door after naturally drying, be denoted as B3.
Detection example 1
With same sanitary sewage spray respectively bathroom aluminium alloy door A1-A3 that above-described embodiment and comparative example prepare and
B1-B3;Spray the sewage of equivalent every time, after spraying 60 times, rinse with equivalent clear water again after A1-A3 and B1-B3 is placed 7 days
Door surface, observes the cleannes on A1-A3 and B1-B3 surface;It addition, also with the aluminium alloy door not spraying resistant coating composition
(being denoted as P1) has done same detection;Concrete outcome is shown in Table 1.
Table 1
Numbering | Cleannes |
A1 | Cleaning, without obvious spot |
A2 | Cleaning, without obvious spot |
A3 | Cleaning, without obvious spot |
B1 | Relatively clean, have spot |
B2 | Relatively clean, have spot |
B3 | Relatively clean, have spot |
P1 | Unclean, there is obvious spot |
According to the testing result of table 1, the surface-coated resistant compositions of the aluminium alloy door's body provided in the present invention
To form resistant coating so that prepared bathroom aluminium alloy door has good anti-pollution characteristic and property easy to clean.It addition,
Cooperative reinforcing effect between each raw material of the resistant coating composition of coating makes to prepare resistant coating and can be good at sticking to
The surface of aluminium alloy door also makes the bathroom aluminium alloy door prepared have good resistant effect, it is ensured that aluminium alloy door makes for a long time
By the most attractive in appearance, health.
The preferred embodiment of the present invention described in detail above, but, the present invention is not limited in above-mentioned embodiment
Detail, in the technology concept of the present invention, technical scheme can be carried out multiple simple variant, this
A little simple variant belong to protection scope of the present invention.
It is further to note that each the concrete technical characteristic described in above-mentioned detailed description of the invention, at not lance
In the case of shield, can be combined by any suitable means, in order to avoid unnecessary repetition, the present invention to various can
The compound mode of energy illustrates the most separately.
Additionally, combination in any can also be carried out between the various different embodiment of the present invention, as long as it is without prejudice to this
The thought of invention, it should be considered as content disclosed in this invention equally.
Claims (7)
1. bathroom aluminium alloy door, it is characterised in that described bathroom aluminium alloy door is coated with by aluminium alloy door's body and resistant
Layer composition, described resistant coating is coated on the surface of aluminium alloy door's body;
Wherein, described resistant coating is to be prepared by following method: first by hydroxy propylene acid resin, nano silicon, organic silicone oil
Carry out being mixed to get coating composition, then by coating composition with 3-(2,3-epoxy the third oxygen) propyl trimethoxy silicane
Described resistant coating is formed in the surface of described aluminium alloy door body.
Bathroom the most according to claim 1 aluminium alloy door, wherein, relative to the hydroxy propylene acid resin of 100 weight portions, institute
The content stating nano silicon is 20-30 weight, and the content of described organic silicone oil is 30-40 weight portion, described 3-(2,3-rings
Oxygen the third oxygen) content of propyl trimethoxy silicane is 15-35 weight portion.
Bathroom the most according to claim 1 and 2 aluminium alloy door, wherein, described nano silicon size be 50-
80nm。
4. the preparation method of the bathroom aluminium alloy door as described in any one in claim 1-3, it is characterised in that bag
Include: first hydroxy propylene acid resin, nano silicon, organic silicone oil and 3-(2,3-epoxy the third oxygen) propyl trimethoxy silicane are entered
Row stirring obtains coating composition;Then by described coating composition on the surface of described aluminium alloy door main body with prepared bath
Room aluminium alloy door.
Preparation method the most according to claim 4, wherein, relative to the hydroxy propylene acid resin of 100 weight portions, described nanometer
The content of silicon dioxide is 20-30 weight, and the content of described organic silicone oil is 30-40 weight portion, described 3-(2,3-epoxies third
Oxygen) content of propyl trimethoxy silicane is 15-35 weight portion.
Preparation method the most according to claim 5, wherein, described coating is that the mode using spraying is carried out.
Preparation method the most according to claim 6, wherein, the temperature of described stirring is 30-45 DEG C, the rotating speed of described stirring
For 1200-2000rpm, the time of described stirring is 0.5-1.0h.