CN106433335A - Easily cleaned aluminum alloy doors and windows and preparation method thereof - Google Patents
Easily cleaned aluminum alloy doors and windows and preparation method thereof Download PDFInfo
- Publication number
- CN106433335A CN106433335A CN201610884895.9A CN201610884895A CN106433335A CN 106433335 A CN106433335 A CN 106433335A CN 201610884895 A CN201610884895 A CN 201610884895A CN 106433335 A CN106433335 A CN 106433335A
- Authority
- CN
- China
- Prior art keywords
- aluminum alloy
- windows
- alloy doors
- preparation
- clean
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for preparing easily cleaned aluminum alloy doors and windows. The method comprises the following steps: stirring polyvinyl chloride resin, titanium dioxide, glass fibers, organic silicone oil, 3-(2,3-epoxypropoxy) propyltrimethoxysilane, thereby obtaining a coating composition; grinding, cleaning and drying the aluminum alloy door and window main body; and finally, coating the coating composition on the surface of the aluminum alloy door and window main body, thereby preparing the easily cleaned aluminum alloy doors and windows. The easily cleaned aluminum alloy doors and windows are easily cleaned, and can be kept attractive and sanitary in the long-term using process.
Description
Technical field
A kind of the present invention relates to door and window manufactures field, in particular it relates to aluminum alloy doors and windows easy to clean and preparation method thereof
Background technology
In recent years, with expanding economy, the continuous improvement of people's living standard, the species of door and window and its derived product is not
Break and increase.Such as, in our lives closely bound up door from traditional wooden door, to glass door, composite gate, stainless steel door
And aluminium alloy door.According to the needs of people's life, production, the species of door also varies in increase always.
According to door and window material and function, following a few class substantially can be divided into:Wood-door window, steel casement door window, revolving door antitheft door, from
Dynamic door, plastic door-window, revolving door, ornamental work of iron door and window, plastic-steel door and window, Door or window made of stainless steel, aluminum alloy doors and windows, glass fiber reinforced plastic door and window.
Aluminum alloy doors and windows, refer to using aluminum alloy extrusion section bar be frame, stile, fan material make door.At present, in life, aluminium closes
The use in Jinmen is seen everywhere, because of it, aluminum alloy doors and windows have the advantages that low cost, weatherability are strong, light and are applied to various
Place.But, due to the material problem of aluminium alloy, while easy to use extensive, aluminum alloy doors and windows are easily in daily life
Middle residual household stains or environment spot, and be difficult to clean up, had a strong impact in the course of time the attractive in appearance of aluminium alloy door and
Health.
Content of the invention
It is an object of the invention to provide a kind of aluminum alloy doors and windows easy to clean, this aluminum alloy doors and windows easy to clean overcomes common
Easy cleaning problem is not so that remain in the household stains on door and window surface and environment spot is easily cleaned it is ensured that aluminium closes
Jinmen window cleaning in use, health and attractive in appearance.
To achieve these goals, the invention provides a kind of preparation method of aluminum alloy doors and windows easy to clean:First by polychlorostyrene
Vinyl, titanium dioxide, glass fibre, organic silicone oil, 3- (2,3- epoxy third oxygen) propyl trimethoxy silicane are stirred
Obtain coating composition;Then aluminum alloy doors and windows main body is carried out polishing, clean, be dried;Finally by coating composition in
The surface of aluminum alloy doors and windows main body is obtained aluminum alloy doors and windows easy to clean.
Preferably, with respect to the Corvic of 100 weight portions, the content of titanium dioxide is 20-30 weight portion, glass
The content of fiber is 1-5 weight portion, and the content of organic silicone oil is 30-50 weight portion, 3- (2,3- epoxy the third oxygen) propyl group trimethoxy
The content of base silane is 1-10 weight portion.
Preferably, the process of polishing is with sand papering weld until weld light is smooth.
Preferably, the process of cleaning is:Water and ethanol equal-volume ratio are configured to cleaning agent, to aluminium by the way of rinsing
The surface of alloy door and window main body is carried out.
Preferably, it is dried and carry out for the mode air-drying.
Preferably, the temperature of stirring is 30-45 DEG C, and the rotating speed of stirring is 1200-2000rpm, and the time of stirring is 0.5-
1.0h.
Present invention also offers a kind of aluminum alloy doors and windows easy to clean being obtained by above-mentioned preparation method.
By technique scheme, the present invention is by Corvic, titanium dioxide, glass fibre, organic silicone oil, 3-
(2,3- epoxy third oxygen) propyl trimethoxy silicane is stirred obtaining the table in aluminum alloy doors and windows main body for the coating composition
Face makes prepared aluminum alloy doors and windows easy to clean easily clean up it is ensured that aluminum alloy doors and windows are attractive in appearance during Long-Time Service
And health.
Other features and advantages of the present invention will be described in detail in subsequent specific embodiment part.
Specific embodiment
Hereinafter the specific embodiment of the present invention is described in detail.It should be appreciated that it is described herein concrete
Embodiment is merely to illustrate and explains the present invention, is not limited to the present invention.
Hereinafter will be described the present invention by embodiment.
Preparation example 1
By Corvic, titanium dioxide, glass fibre, organic silicone oil, 3- (2,3- epoxy third oxygen) propyl group trimethoxy
Base silane is 100 according to weight proportion:20:1:30:2 are stirred 0.5h under 30 DEG C, 1200rpm rotating speed, prepared coating group
Compound T1.
Preparation example 2
By Corvic, titanium dioxide, glass fibre, organic silicone oil, 3- (2,3- epoxy third oxygen) propyl group trimethoxy
Base silane is 100 according to weight proportion:25:3:40:5 are stirred 0.8h under 35 DEG C, 1600rpm rotating speed, prepared coating group
Compound T2.
Preparation example 3
By Corvic, titanium dioxide, glass fibre, organic silicone oil, 3- (2,3- epoxy third oxygen) propyl group trimethoxy
Base silane is 100 according to weight proportion:30:5:50:10 are stirred 1.0h under 40 DEG C, 2000rpm rotating speed, prepared coating group
Compound T3.
Embodiment 1
First by the weld of sand papering aluminum alloy doors and windows until weld light is smooth;Then, by bodies such as water and ethanol
Long-pending ratio is configured to cleaning agent and rinses the surface of aluminum alloy doors and windows main body and be dried by the way of air-dried;Finally, will prepare
Example 1 be obtained coating composition T1 be sprayed at aluminum alloy doors and windows main body surface naturally dry after be obtained aluminum alloy doors and windows easy to clean
A1.
Embodiment 2
First, by the weld of sand papering aluminum alloy doors and windows until weld light is smooth;Then, by water and ethanol etc.
Volume ratio is configured to cleaning agent and rinses the surface of aluminum alloy doors and windows main body and be dried by the way of air-dried;Finally, will make
The surface being sprayed at aluminum alloy doors and windows main body for the prepared coating composition T2 of example 2 is obtained aluminium alloy door easy to clean after naturally drying
Window A2.
Embodiment 3
First, by the weld of sand papering aluminum alloy doors and windows until weld light is smooth;Then, by water and ethanol etc.
Volume ratio is configured to cleaning agent and rinses the surface of aluminum alloy doors and windows main body and be dried by the way of air-dried;Finally, will make
The surface being sprayed at aluminum alloy doors and windows main body for the prepared coating composition T3 of example 3 is obtained aluminium alloy door easy to clean after naturally drying
Window A3.
Comparative example 1
First coating composition D1 is obtained according to preparation example 1, does not except for the difference that add titanium dioxide;Then according to embodiment 1
Mode the surface that D1 is sprayed at aluminum alloy doors and windows main body is dried naturally after be obtained aluminum alloy doors and windows B1 easy to clean.
Comparative example 2
First coating composition D2 is obtained according to preparation example 2, does not except for the difference that add glass fibre;Then according to embodiment 1
Mode the surface that D2 is sprayed at aluminum alloy doors and windows main body is dried naturally after be obtained aluminum alloy doors and windows B2 easy to clean.
Comparative example 3
First coating composition D3 is obtained according to preparation example 3, does not except for the difference that add organic silicone oil;Then according to embodiment 1
Mode the surface that D3 is sprayed at aluminum alloy doors and windows main body is dried naturally after be obtained aluminum alloy doors and windows B3 easy to clean.
Detection example 1
Spray aluminium alloy door A1-A3 and B1- easy to clean that above-described embodiment and comparative example are obtained with same sewage respectively
B3;Spray the sewage of equivalent every time, after spraying 60 times, after A1-A3 and B1-B3 is placed 7 days, use equivalent clear water to rinse door again
Surface, observes the cleannes on A1-A3 and B1-B3 surface;In addition, also using the aluminium alloy door of non-spray-on coating composition (to be denoted as
P1) done same detection;Concrete outcome is shown in Table 1.
Table 1
Embodiment is numbered | Cleannes |
A1 | Cleaning, no obvious spot |
A2 | Cleaning, no obvious spot |
A3 | Cleaning, no obvious spot |
B1 | Relatively clean, have spot |
B2 | Relatively clean, have spot |
B3 | Relatively clean, have spot |
P1 | Unclean, there is obvious spot |
In the present invention, coated by Corvic, titanium dioxide, glass fibers by the body surface in aluminum alloy doors and windows
The coating that dimension, organic silicone oil, 3- (2,3- epoxy third oxygen) propyl trimethoxy silicane are mixed to prepare according to suitable weight proportion
Composition, is obtained aluminum alloy doors and windows easy to clean.Spot residual during Long-Time Service for this door and window can be by the clean guarantor of cleaning
Demonstrate,prove door and window health in use and attractive in appearance.
The preferred embodiment of the present invention described in detail above, but, the present invention is not limited in above-mentioned embodiment
Detail, in the range of the technology design of the present invention, multiple simple variant can be carried out to technical scheme, this
A little simple variant belong to protection scope of the present invention.
It is further to note that each particular technique feature described in above-mentioned specific embodiment, in not lance
In the case of shield, can be combined by any suitable means, in order to avoid unnecessary repetition, the present invention to various can
The combination of energy no longer separately illustrates.
Additionally, can also be combined between the various different embodiment of the present invention, as long as it is without prejudice to this
The thought of invention, it equally should be considered as content disclosed in this invention.
Claims (7)
1. a kind of preparation method of aluminum alloy doors and windows easy to clean is it is characterised in that include:First by Corvic, titanium dioxide
Titanium, glass fibre, organic silicone oil, 3- (2,3- epoxy third oxygen) propyl trimethoxy silicane are stirred obtaining coating composition;
Then aluminum alloy doors and windows main body is carried out polishing, clean, be dried;Finally by coating composition in described aluminum alloy doors and windows master
The surface of body is obtained described aluminum alloy doors and windows easy to clean.
2. preparation method according to claim 1, wherein, with respect to the Corvic of 100 weight portions, described dioxy
The content changing titanium is 20-30 weight portion, and the content of described glass fibre is 1-5 weight portion, and the content of described organic silicone oil is 30-
50 weight portions, the content of described 3- (2,3- epoxy the third oxygen) propyl trimethoxy silicane is 1-10 weight portion.
3. preparation method according to claim 1 and 2, wherein, the process of described polishing is:Straight with sand papering weld
Smooth to weld light.
4. preparation method according to claim 3, wherein, the process of described cleaning is:Water and ethanol equal-volume ratio are joined
It is set to cleaning agent, by the way of rinsing, the surface of described aluminum alloy doors and windows main body is carried out.
5. preparation method according to claim 4, wherein, described drying is that air-dried mode is carried out.
6. the preparation method according to any one in claim 1-5, wherein, the temperature of described stirring is 30-45 DEG C, institute
The rotating speed stating stirring is 1200-2000rpm, and the time of described stirring is 0.5-1.0h.
7. a kind of aluminum alloy doors and windows easy to clean are it is characterised in that described anti-aging aluminum alloy doors and windows are by any in claim 1-6
Preparation method described in one is prepared from.