CN106634502A - Easy-to-clean aluminum alloy windows and doors and preparation method thereof - Google Patents
Easy-to-clean aluminum alloy windows and doors and preparation method thereof Download PDFInfo
- Publication number
- CN106634502A CN106634502A CN201610884921.8A CN201610884921A CN106634502A CN 106634502 A CN106634502 A CN 106634502A CN 201610884921 A CN201610884921 A CN 201610884921A CN 106634502 A CN106634502 A CN 106634502A
- Authority
- CN
- China
- Prior art keywords
- aluminum alloy
- windows
- preparation
- alloy doors
- easy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of easy-to-clean aluminum alloy windows and doors. The method includes: firstly, stirring polyurethane resin, calcium carbonate, glass fibers, organic silicon oil and 3-(2,3-epoxypropoxy)propyl trimethoxysilane to obtain a coating composition; secondly, polishing, cleaning and drying window bodies and door bodies; finally coating surfaces of the window bodies and the door bodies with the coating composition to obtain the easy-to-clean aluminum alloy windows and doors. The easy-to-clean aluminum alloy windows and doors are easy to clean, and attractiveness and cleanness of the easy-to-clean aluminum alloy windows and doors in long-term use are guaranteed.
Description
Technical field
The present invention relates to door and window manufacture field, in particular it relates to a kind of aluminum alloy doors and windows easy to clean and preparation method thereof
Background technology
In recent years, with expanding economy, the continuous improvement of people's living standard, the species of door and window and its derived product is not
It is disconnected to increase.Such as, closely bound up door is from traditional wooden door during we live, to glass door, composite gate, stainless steel door
And aluminium alloy door.According to people's life, the needs of production, the species of door also varies in increase always.
According to door and window material and function, can substantially be divided into following a few classes:Wood-door window, steel casement door window, revolving door antitheft door, from
Dynamic door, plastic door-window, revolving door, ornamental work of iron door and window, plastic-steel door and window, Door or window made of stainless steel, aluminum alloy doors and windows, glass fiber reinforced plastic door and window.
Aluminum alloy doors and windows, refer to adopt aluminum alloy extrusion section bar for frame, stile, fan material make door.At present, aluminium is closed in life
The use in Jinmen is seen everywhere, aluminum alloy doors and windows because its have the advantages that low cost, weatherability it is strong, it is light be applied to it is various
Place.But, due to the material problem of aluminium alloy, while easy to use extensive, aluminum alloy doors and windows are easily in daily life
Middle residual household stains or environment spot, and be difficult to clean up, had a strong impact in the course of time the attractive in appearance of aluminium alloy door and
Health.
The content of the invention
It is an object of the invention to provide a kind of aluminum alloy doors and windows easy to clean, the aluminum alloy doors and windows easy to clean overcome common
Not easy cleaning problem so that the household stains and environment spot for remaining in door and window surface are easily cleaned, it is ensured that aluminium is closed
Jinmen window cleaning in use, health and attractive in appearance.
To achieve these goals, the invention provides a kind of preparation method of aluminum alloy doors and windows easy to clean:First by poly- ammonia
Ester resin, calcium carbonate, glass fibre, organic silicone oil, 3- (oxygen of 2,3- epoxies third) propyl trimethoxy silicane are stirred
Obtain coating composition;Then aluminum alloy doors and windows main body is polished, is cleaned, being dried;Finally by coating composition in
The surface of aluminum alloy doors and windows main body is obtained aluminum alloy doors and windows easy to clean.
Preferably, relative to the polyurethane resin resin of 100 weight portions, the content of calcium carbonate is 1-19 weight portions, glass
The content of fiber is 6-10 weight portions, and the content of organic silicone oil is 30-50 weight portions, 3- (2,3- the third oxygen of epoxy) propyl group trimethoxy
The content of base silane is 1-10 weight portions.
Preferably, the process of polishing is with sand papering weld until weld light is smooth.
Preferably, the process of cleaning is:Water and ethanol equal-volume ratio are configured into cleaning agent, to aluminium by the way of rinsing
The surface of alloy door and window main body is cleaned.
Preferably, be dried is carried out by the way of air-drying.
Preferably, the temperature of stirring is 30-45 DEG C, and the rotating speed of stirring is 1200-2000rpm, and the time of stirring is 0.5-
1.0h。
Present invention also offers one kind aluminum alloy doors and windows easy to clean by obtained in above-mentioned preparation method.
It is of the invention by polyurethane resin resin, calcium carbonate, glass fibre, organic silicone oil, 3- by above-mentioned technical proposal
(oxygen of 2,3- epoxies third) propyl trimethoxy silicane is stirred the table for obtaining coating composition in aluminum alloy doors and windows main body
Face makes obtained aluminum alloy doors and windows easy to clean easily clean up, it is ensured that aluminum alloy doors and windows are attractive in appearance during Long-Time Service
And health.
Other features and advantages of the present invention will be described in detail in subsequent specific embodiment part.
Specific embodiment
The specific embodiment of the present invention is described in detail below.It should be appreciated that described herein concrete
Embodiment is merely to illustrate and explains the present invention, is not limited to the present invention.
Hereinafter will be described the present invention by embodiment.
Preparation example 1
By polyurethane resin resin, calcium carbonate, glass fibre, organic silicone oil, 3- (oxygen of 2,3- epoxies third) propyl group trimethoxy
Base silane is 100 according to weight proportion:19:6:30:2 are stirred 0.5h under 30 DEG C, 1200rpm rotating speeds, and coating group is obtained
Compound T1.
Preparation example 2
By polyurethane resin resin, calcium carbonate, glass fibre, organic silicone oil, 3- (oxygen of 2,3- epoxies third) propyl group trimethoxy
Base silane is 100 according to weight proportion:10:8:40:5 are stirred 0.8h under 35 DEG C, 1600rpm rotating speeds, and coating group is obtained
Compound T2.
Preparation example 3
By polyurethane resin resin, calcium carbonate, glass fibre, organic silicone oil, 3- (oxygen of 2,3- epoxies third) propyl group trimethoxy
Base silane is 100 according to weight proportion:3:10:50:10 are stirred 1.0h under 40 DEG C, 2000rpm rotating speeds, and coating group is obtained
Compound T3.
Embodiment 1
First by the weld of sand papering aluminum alloy doors and windows until weld light is smooth;Then, by bodies such as water and ethanol
Product ratio is configured to cleaning agent and rinses the surface of aluminum alloy doors and windows main body and be dried by the way of air-drying;Finally, will prepare
Coating composition T1 obtained in example 1 is sprayed at after the surface of aluminum alloy doors and windows main body is dried naturally and aluminum alloy doors and windows easy to clean is obtained
A1。
Embodiment 2
First, by the weld of sand papering aluminum alloy doors and windows until weld light is smooth;Then, by water and ethanol etc.
Volume ratio is configured to cleaning agent and rinses the surface of aluminum alloy doors and windows main body and be dried by the way of air-drying;Finally, will make
Coating composition T2 obtained in standby example 2 is sprayed at after the surface of aluminum alloy doors and windows main body is dried naturally and aluminium alloy door easy to clean is obtained
Window A2.
Embodiment 3
First, by the weld of sand papering aluminum alloy doors and windows until weld light is smooth;Then, by water and ethanol etc.
Volume ratio is configured to cleaning agent and rinses the surface of aluminum alloy doors and windows main body and be dried by the way of air-drying;Finally, will make
Coating composition T3 obtained in standby example 3 is sprayed at after the surface of aluminum alloy doors and windows main body is dried naturally and aluminium alloy door easy to clean is obtained
Window A3.
Comparative example 1
First coating composition D1 is obtained according to preparation example 1, does not except for the difference that add calcium carbonate;Then according to embodiment 1
D1 is sprayed at after the surface of aluminum alloy doors and windows main body is dried naturally and aluminum alloy doors and windows B1 easy to clean is obtained by mode.
Comparative example 2
First coating composition D2 is obtained according to preparation example 2, does not except for the difference that add glass fibre;Then according to embodiment 1
Mode by D2 be sprayed at after the surface of aluminum alloy doors and windows main body is dried naturally be obtained aluminum alloy doors and windows B2 easy to clean.
Comparative example 3
First coating composition D3 is obtained according to preparation example 3, does not except for the difference that add organic silicone oil;Then according to embodiment 1
Mode by D3 be sprayed at after the surface of aluminum alloy doors and windows main body is dried naturally be obtained aluminum alloy doors and windows B3 easy to clean.
Detection example 1
Aluminium alloy door A1-A3 and B1- easy to clean obtained in above-described embodiment and comparative example is sprayed respectively with same sewage
B3;Every time the sewage of spray equivalent, after spraying 60 times, uses again equivalent clear water to rinse door after A1-A3 and B1-B3 is placed 7 days
Surface, observes the cleannes on A1-A3 and B1-B3 surfaces;In addition, also making of the aluminium alloy door (P1) of non-spray-on coating composition
Same detection;Concrete outcome is shown in Table 1.
Table 1
Embodiment is numbered | Cleannes |
A1 | Cleaning, without obvious spot |
A2 | Cleaning, without obvious spot |
A3 | Cleaning, without obvious spot |
B1 | Relatively clean, there is spot |
B2 | Relatively clean, there is spot |
B3 | Relatively clean, there is spot |
P1 | It is unclean, there is obvious spot |
In the present invention, coated by polyurethane resin resin, calcium carbonate, glass fibers by the body surface in aluminum alloy doors and windows
The coating that dimension, organic silicone oil, 3- (oxygen of 2,3- epoxies third) propyl trimethoxy silicane are mixed to prepare according to suitable weight proportion
Composition, is obtained aluminum alloy doors and windows easy to clean.Spot residual of the door and window during Long-Time Service can be by the clean guarantor of cleaning
Door and window health in use and attractive in appearance is demonstrate,proved.
The preferred embodiment of the present invention described in detail above, but, the present invention is not limited in above-mentioned embodiment
Detail, the present invention range of the technology design in, various simple variants can be carried out to technical scheme, this
A little simple variants belong to protection scope of the present invention.
It is further to note that each particular technique feature described in above-mentioned specific embodiment, in not lance
In the case of shield, can be combined by any suitable means, in order to avoid unnecessary repetition, the present invention to it is various can
The combination of energy is no longer separately illustrated.
Additionally, can also be combined between a variety of embodiments of the present invention, as long as it is without prejudice to this
The thought of invention, it should equally be considered as content disclosed in this invention.
Claims (7)
1. a kind of preparation method of aluminum alloy doors and windows easy to clean, it is characterised in that include:First by polyurethane resin resin, carbonic acid
Calcium, glass fibre, organic silicone oil, 3- (oxygen of 2,3- epoxies third) propyl trimethoxy silicane are stirred and obtain coating composition;
Then aluminum alloy doors and windows main body is polished, is cleaned, being dried;Finally by coating composition in the aluminum alloy doors and windows master
The surface of body is obtained the aluminum alloy doors and windows easy to clean.
2. preparation method according to claim 1, wherein, relative to the polyurethane resin resin of 100 weight portions, the carbon
The content of sour calcium is 1-19 weight portions, and the content of the glass fibre is 6-10 weight portions, and the content of the organic silicone oil is 30-
50 weight portions, the content of 3- (2,3- the third oxygen of the epoxy) propyl trimethoxy silicane is 1-10 weight portions.
3. preparation method according to claim 1 and 2, wherein, the process of the polishing is:It is straight with sand papering weld
It is smooth to weld light.
4. preparation method according to claim 3, wherein, the process of the cleaning is:Water and ethanol equal-volume ratio are matched somebody with somebody
Cleaning agent is set to, the surface of the aluminum alloy doors and windows main body is cleaned by the way of rinsing.
5. preparation method according to claim 4, wherein, the drying is that air-dried mode is carried out.
6. the preparation method according to any one in claim 1-5, wherein, the temperature of the stirring is 30-45 DEG C, institute
The rotating speed for stating stirring is 1200-2000rpm, and the time of the stirring is 0.5-1.0h.
7. a kind of aluminum alloy doors and windows easy to clean, it is characterised in that the anti-aging aluminum alloy doors and windows by claim 1-6 arbitrarily
Preparation method described in one is prepared from.