CN106243413A - 用于超大扭力挖泥船舶弹性联轴节的胶料 - Google Patents

用于超大扭力挖泥船舶弹性联轴节的胶料 Download PDF

Info

Publication number
CN106243413A
CN106243413A CN201610631609.8A CN201610631609A CN106243413A CN 106243413 A CN106243413 A CN 106243413A CN 201610631609 A CN201610631609 A CN 201610631609A CN 106243413 A CN106243413 A CN 106243413A
Authority
CN
China
Prior art keywords
sizing material
torsion
boats
ships
elastic coupling
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610631609.8A
Other languages
English (en)
Inventor
靳温学
申会杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TIANJIN BAOBOTE SEALING TECHNOLOGY Co Ltd
Original Assignee
TIANJIN BAOBOTE SEALING TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIANJIN BAOBOTE SEALING TECHNOLOGY Co Ltd filed Critical TIANJIN BAOBOTE SEALING TECHNOLOGY Co Ltd
Priority to CN201610631609.8A priority Critical patent/CN106243413A/zh
Publication of CN106243413A publication Critical patent/CN106243413A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种用于超大扭力挖泥船舶弹性联轴节的胶料，组分如下：以下均为重量份数：天然胶60‑80、顺丁橡胶20‑30、丁苯胶10‑20、硬脂酸1‑2、防老剂1‑2、纳米氧化锌3‑5、稻壳灰1‑6、助剂及炭黑。本发明胶料中含有稻壳灰，稻壳灰中内含有类二氧化硅成分，类二氧化硅成分能够将扭力产生的热量从内部迅速导出，有效降低橡胶内部的扭力热，延长了使用寿命。

Description

用于超大扭力挖泥船舶弹性联轴节的胶料
技术领域
本发明属于橡胶领域，涉及一种用于超大扭力挖泥船舶弹性联轴节的胶料。
背景技术
联轴节，又名联轴器，是用来联接不同机构中的两根轴(主动轴和从动轴)使之共同旋转以传递扭矩的机械零件，起衔接作用。在高速重载的动力传动中，有些联轴器还有缓冲、减振和提高轴系动态性能的作用。联轴器由两半部分组成，分别与主动轴和从动轴联接。一般动力机大都借助于联轴器与工作机相联接。
在例如挖泥船的铰刀轴的联轴节承受巨大的扭力，扭力大会产生较大动态热、挤压热以及摩擦热，因此联轴节的密封垫内部容易老化，导致密封性下降。
通过检索发现，如下与本申请相关的专利文献，具体公开的内容如下：
一种矿井机械用弹性联轴节的材料及其制备方法(CN104893280A)公开了一种矿井机械用弹性联轴节的材料由如下质量百分比的组分组成：88～92％热塑性聚氨酯、5～8％阻燃剂、2～4％抗静电剂和0.5～1.5％色母；其制备步骤为：配合剂预混；挤出造粒；干燥及注塑成型。本发明制备的弹性联轴节材料在保持其固有高硬度、高强度、高韧性、高耐磨等机械性能的基础上，同时又具有优异的阻燃性和抗静电性能，可以满足矿井机械的使用要求，且其抗静电性能具有永久性，大大降低了矿井中粉尘爆炸的可能性。
通过比较发现，本申请与对比文件差异较大，产品使用效果不及本申请。
发明内容
本发明的目的在于克服现有技术的不足之处，提供一种用于超大扭力挖泥船舶弹性联轴节的胶料及其制备方法，本发明提供的密封橡胶适合联轴节的密封垫使用，能够克服巨大扭力产生的摩擦热、动态热以及挤压热产生的橡胶内部老化问题。
本发明实现目的的技术方案是：
一种用于超大扭力挖泥船舶弹性联轴节的胶料，组分如下：以下均为重量份数
而且，所述炭黑的组成如下：
炭黑N214 10
炭黑N550 40。
本发明的优点和有益效果为：
1、本发明提供的胶料有效的解决了弹性联轴节在大扭力、大偏转角时产生的升温老化问题，从而延长了弹性联轴节的使用寿命，超过了国内外同类产品的水平。
2、本发明胶料中含有稻壳灰，稻壳灰中内含有类二氧化硅成分，类二氧化硅成分能够将扭力产生的热量从内部迅速导出，有效降低橡胶内部的扭力热，延长了使用寿命。
具体实施方式
下面通过具体实施例对本发明作进一步详述，以下实施例只是描述性的，不是限定性的，不能以此限定本发明的保护范围。
实施例1：
一种用于超大扭力挖泥船舶弹性联轴节的胶料，组分如下：以下均为重量份数
上述材料的其制备方法如下：
⑴加入天然胶(烟片)、顺丁橡胶、丁苯胶、单独塑炼，按照原料配比取料，在开炼机混合，混均匀后开始混炼。
⑵混炼在密炼机内进行，上顶栓加压0.8兆帕，最高温度设定110度，加料顺序：步骤⑴获得的胶料、硬脂酸、防老剂、纳米氧化锌、稻壳灰、炭黑，混炼9分钟，下料开炼机出片，冷却到60度以下。
⑶将上述胶片投入到密炼机，加入硫磺、助交联剂、促进剂、2,6-二叔丁基对甲酚加压混合3分钟后下片，冷却，设定最高温度90度，下片在开炼机进行，先经过三次落盘后，包棍下片，冷却存放。
⑷制品硫化条件175度10分钟。
对本实施例加工出的胶料进行性能试验检测，检测结果如下：
国标 实测性能
扯断强度MPa ≥18-22 ≥31
伸长率％ 500-700 ≥730
硬度邵尔A 75±5 76
压缩永久形变 ≤28-22 ≤18

Claims (2)

1.一种用于超大扭力挖泥船舶弹性联轴节的胶料，其特征在于：组分如下：以下均为重量份数
。
2.根据权利要求1所述的用于超大扭力挖泥船舶弹性联轴节的胶料，其特征在于：所述炭黑的组成如下：
炭黑N214 10
炭黑N550 40。
CN201610631609.8A 2016-08-02 2016-08-02 用于超大扭力挖泥船舶弹性联轴节的胶料 Pending CN106243413A (zh)