CN106239647A - A kind of manufacture method of carbon fiber ecological ornamental plate - Google Patents
A kind of manufacture method of carbon fiber ecological ornamental plate Download PDFInfo
- Publication number
- CN106239647A CN106239647A CN201610635218.3A CN201610635218A CN106239647A CN 106239647 A CN106239647 A CN 106239647A CN 201610635218 A CN201610635218 A CN 201610635218A CN 106239647 A CN106239647 A CN 106239647A
- Authority
- CN
- China
- Prior art keywords
- carbon fiber
- manufacture method
- plate
- parts
- ecological ornamental
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses the manufacture method of a kind of carbon fiber ecological ornamental plate, the method includes that plate core processes, decorative panel processes, glued three steps of group embryo, add when plate core rubber is closed that the density that carbon fiber can utilize carbon fiber to have is little, intensity is high, good endurance, resistance to corrosion by force, the feature such as strong adaptability to be to improve properties of product；During manufacturing, plate core, decorative panel are carried out fire-retardant, antimicrobial treatment respectively simultaneously, product the most more safety and sanitation can be made, improve product the most more competitive.
Description
Technical field
The present invention relates to field of plate manufacture, be specifically related to the manufacture method of a kind of carbon fiber ecological ornamental plate.
Background technology
Carbon fiber is the tencel material of a kind of phosphorus content high intensity more than 95%, high modulus fibre.It is by
The organic fibers such as flake graphite crystallite are piled up along fiber axial direction and are formed, the microlite obtained through carbonization and graphitization processing
Ink material.Carbon fiber " soft outside but hard inside ", quality is lighter than metallic aluminium, but intensity is higher than iron and steel, and has corrosion-resistant, high-modulus
Characteristic, be all important materials at defence and military and civilian aspect.It not only has the intrinsic intrinsic property of material with carbon element, has both again
The soft machinability of textile fabric, is a new generation's reinforcing fiber.
Carbon fiber has many premium properties, and the axial strength of carbon fiber and modulus are high, and density is low, higher than performance, without compacted
Becoming, superhigh temperature resistant under non-oxidizing atmosphere, fatigue durability is good, specific heat and electric conductivity between nonmetal and metal, thermal expansion system
Number is little and has anisotropy, good corrosion resistance, and X-ray transparent is good.Good electrical and thermal conductivity performance, electromagnetic wave shielding are good
Deng.
Carbon fiber carbon material obtains extensive application in military and civilian industry every field.From space flight, aviation, vapour
The civilian industries such as car, electronics, machinery, chemical industry, light textile are to sports equipment and leisure goods etc..Carbon fiber is in field of plate manufacture also
There is important application, but be applied to heat preservation plate material more at present and prepare, such as the carbon fiber electric heating of Application No. CN00211458.5
Decorative panel, Application No. CN01241498.0 carbon-fiber insulation fire-retardent electrothermal decorative plate, but these application are the most single, and only profit
By the electrical and thermal conductivity performance of carbon fiber, fail to give full play to its effect.
Summary of the invention
For solving above-mentioned technical problem, the invention provides the manufacture method of a kind of carbon fiber ecological ornamental plate.
The present invention is achieved by the following technical programs:
A kind of manufacture method of carbon fiber ecological ornamental plate, the method comprises the following steps:
A, plate core process: plate core is by width 30-60mm, thickness 10-18mm, the plate 3-5 layer of length 500-800mm and 2-
The carbon fiber of 4 layers gluing of interlocking forms, and carries out high-pressure impregnation, then drying and processing with fire retardant, antibacterial, and repeats after gluing
2-3 time；
B, decorative panel process: facing paper is put into and impregnated then drying and processing in cyanurotriamide modified urea resin solution, and
Repeat 3-4 time；Cyanurotriamide modified urea resin solution is cyanurotriamide modified urea resin 10-15 part, purple by parts by weight
Ultraviolet absorbers 0.3-0.6 part, fire retardant 1-2 part, antibacterial 1-2 part, the raw material blending of flexibility agent 0.5-0.8 part are made；
C, group embryo are glued: gluing outside plate core, stick 1-2 layer carbon fiber, then stick decorative panel on two sides, at 0.5-
0.8Mpa, 100-120 DEG C of hot pressing 1-5min, then saw limit, sanding, packaging and warehousing.
Also carry out microwave treatment 10-15min while described step a mesohigh dipping, then carry out supersound process 10-
25min, takes out and dries.
After described impregnation process, take out and be placed on 0.5-2h at shady and cool ventilation, then 45-65 DEG C of drying.
Described fire retardant is ultrafine aluminium hydroxide 6-9 part by parts by weight, and phosphonium flame retardant 0.5-3 part is made.
The Traditional Chinese Medicine Anti microbial inoculum of described step a is Radix Artemisia ordosicae 10-15 part, Radix Glycyrrhizae 4-8 part, Aloe 3-6 part, Folium Camelliae sinensis by parts by weight
4-7 part, water 80-100 part are made.
The preparation method of the Traditional Chinese Medicine Anti microbial inoculum of described step a be Radix Artemisia ordosicae, Radix Glycyrrhizae, Aloe, Folium Camelliae sinensis chopping dry, add water big fire
Decoct 15-30min, less fire decocts 5-15min.
In described step b, antibacterial is silver zinc complex antibacterial, and wherein silver is 5-8:1-2 with the weight ratio of zinc.
The beneficial effects of the present invention is: the present invention adds carbon fiber and carbon fiber can be utilized to have when decorative panel gluing
The feature such as density little, intensity is high, good endurance, resistance to corrosion are strong, strong adaptability improve properties of product；Fire-retardant
High-pressure impregnation, microwave treatment, supersound process is comprehensively utilized during agent, antimicrobial impregnated, can be more preferably relative to conventional method
Ground improves dipping effect, makes product anti-flammability and antibiotic property more preferably；Due to fire retardant particle diameter more small specific surface the biggest long-pending fire-retardant effect
Fruit is the best, therefore selects ultrafine aluminium hydroxide to make fire retardant；The mode using Traditional Chinese Medicine Anti microbial inoculum to combine with inorganic antiseptic is kept away
Exempt to use the issuable toxic action of organic antibacterial agent, product the most more safety and sanitation can be made, improve product in city
On field more competitive；The decorative panel of the present invention can make wallboard and implant thereof, it is adaptable to the fields such as building, household.
Detailed description of the invention
Below in conjunction with embodiment, technical scheme is further described, but claimed scope is not limited to
In described.
Embodiment one
A kind of manufacture method of carbon fiber ecological ornamental plate, the method comprises the following steps:
A, plate core process: plate core is interlocked glue by the carbon fiber of width 30mm, thickness 10mm, the plate of length 500mm and 2 layers
Conjunction forms, and carries out high-pressure impregnation with fire retardant, antibacterial after gluing；Microwave treatment 10min is also carried out while high-pressure impregnation,
Carry out supersound process 10min again, after impregnation process, take out and be placed on 0.5h at shady and cool ventilation, then 45 DEG C of drying, and repeat
2 times；Wherein fire retardant is that ultrafine aluminium hydroxide 6 parts, phosphonium flame retardant 0.5 part are made by parts by weight, and antibacterial is by weight portion
Number is made for Radix Artemisia ordosicae 10 parts, 4 parts of Radix Glycyrrhizae, Aloe 3 parts, Folium Camelliae sinensis 4 parts, the raw material of 80 parts of water, and preparation method is Radix Artemisia ordosicae, Radix Glycyrrhizae, reed
Luxuriant growth, Folium Camelliae sinensis chopping are dried, and the big fire that adds water decocts 15min, less fire decocts 5min.
B, decorative panel process: facing paper is put in cyanurotriamide modified urea resin solution and impregnated, and then takes out and is placed on
0.5h at shady and cool ventilation, then 45 DEG C of drying, and is repeated 3 times；Cyanurotriamide modified urea resin solution by parts by weight is
Cyanurotriamide modified urea resin 10 parts, UV absorbent 0.3 part, fire retardant 1 part, antibacterial 1 part, flexibility agent 0.5 part
Raw material blending is made；Antibacterial is silver zinc complex antibacterial, and wherein silver is 5:1 with the weight ratio of zinc.
C, group embryo are glued: gluing outside plate core, are pressed into 1 layer of carbon fiber, then stick decorative panel on two sides, 0.5Mpa,
100 DEG C of hot pressing 1min, then saw limit, sanding, packaging and warehousing.
Embodiment two
A kind of manufacture method of carbon fiber ecological ornamental plate, the method comprises the following steps:
A, plate core process: plate core is by width 40mm；Thickness 15mm, the carbon fiber of the plate of length 600mm and 3 layers interlocks glue
Conjunction forms, and carries out high-pressure impregnation with fire retardant, antibacterial after gluing；Microwave treatment 12min is also carried out while high-pressure impregnation, then
Carry out supersound process 18min, after impregnation process, take out and be placed on 1h at shady and cool ventilation, then 55 DEG C of drying, and be repeated 3 times；
Wherein fire retardant is ultrafine aluminium hydroxide 7 parts by parts by weight, and phosphonium flame retardant 1.5 parts is made；Traditional Chinese Medicine Anti microbial inoculum is by weight portion
Number is Radix Artemisia ordosicae 13 parts, 6 parts of Radix Glycyrrhizae, Aloe 5 parts, Folium Camelliae sinensis 5 parts, and 90 parts of water is made；Preparation method is Radix Artemisia ordosicae, Radix Glycyrrhizae, Aloe, Folium Camelliae sinensis
Chopping is dried, and the big fire that adds water decocts 25min, less fire decocts 10min.
B, decorative panel process: facing paper is put in cyanurotriamide modified urea resin solution and impregnated, and then takes out and is placed on
0.5h at shady and cool ventilation, then 55 DEG C of drying, and is repeated 3 times；Cyanurotriamide modified urea resin solution by parts by weight is
Cyanurotriamide modified urea resin 13 parts, UV absorbent 0.5 part, fire retardant 1 part, antibacterial 1 part, flexibility agent 0.7 part
Raw material blending is made；Antibacterial is silver zinc complex antibacterial, and wherein silver is 7:1.5 with the weight ratio of zinc.
C, group embryo are glued: gluing outside plate core, press-in 1-2 layer side carbon fiber, then stick decorative panel on two sides,
0.6Mpa, 110 DEG C of hot pressing 3min, then saw limit, sanding, packaging and warehousing.
Embodiment three
A kind of manufacture method of carbon fiber ecological ornamental plate, the method comprises the following steps:
A, plate core process: plate core is interlocked glue by the carbon fiber of width 60mm, thickness 18mm, the plate of length 800mm and 4 layers
Conjunction forms, and carries out high-pressure impregnation with fire retardant, antibacterial after gluing；Microwave treatment 15min is also carried out while high-pressure impregnation, then
Carry out supersound process 25min, after impregnation process, take out and be placed on 2h at shady and cool ventilation, then 65 DEG C of drying, and be repeated 4 times；
Wherein fire retardant is ultrafine aluminium hydroxide 9 parts by parts by weight, and phosphonium flame retardant 3 parts is made；Traditional Chinese Medicine Anti microbial inoculum is by parts by weight
For Radix Artemisia ordosicae 15 parts, 8 parts of Radix Glycyrrhizae, Aloe 6 parts, Folium Camelliae sinensis 5 parts, 100 parts of water is made, and preparation method is Radix Artemisia ordosicae, Radix Glycyrrhizae, Aloe, Folium Camelliae sinensis
Chopping is dried, and the big fire that adds water decocts 30min, less fire decocts 15min.
B, decorative panel process: facing paper put in cyanurotriamide modified urea resin solution impregnate, then take out and be placed on
2h at shady and cool ventilation, then 65 DEG C of drying, is repeated 4 times；Cyanurotriamide modified urea resin solution is trimerization by parts by weight
Cyanamide modified urea-formaldehyde resin 15 parts, UV absorbent 0.6 part, fire retardant 2 parts, antibacterial 2 parts, the raw material of flexibility agent 0.8 part
Mixing is made；Wherein antibacterial is silver zinc complex antibacterial, and wherein silver is 8:2 with the weight ratio of zinc.
C, group embryo are glued: gluing outside plate core, are pressed into 2 side carbon fibers, then stick decorative panel on two sides, 0.8Mpa,
120 DEG C of hot pressing 5min, then saw limit, sanding, packaging and warehousing.
Claims (7)
1. the manufacture method of a carbon fiber ecological ornamental plate, it is characterised in that: the method comprises the following steps:
A, plate core process: plate core is by width 30-60mm, thickness 10-18mm, the plate 3-5 layer of length 500-800mm and layer 2-4
Carbon fiber gluing of interlocking form, carry out high-pressure impregnation, then drying and processing with fire retardant, antibacterial, and repeat 2-3 after gluing
Secondary；
B, decorative panel process: facing paper is put in cyanurotriamide modified urea resin solution and impregnated, then drying and processing, and repeats
3-4 time；Cyanurotriamide modified urea resin solution is cyanurotriamide modified urea resin 10-15 part, ultraviolet by parts by weight
Absorbent 0.3-0.6 part, fire retardant 1-2 part, antibacterial 1-2 part, the raw material blending of flexibility agent 0.5-0.8 part are made；
C, group embryo are glued: gluing outside plate core, stick 1-2 layer carbon fiber, then stick decorative panel on two sides, at 0.5-
0.8Mpa, 100-120 DEG C of hot pressing 1-5min, then saw limit, sanding, packaging and warehousing.
The manufacture method of a kind of carbon fiber ecological ornamental plate the most according to claim 1, it is characterised in that: described step a
Also carry out microwave treatment 10-15min while mesohigh dipping, then carry out supersound process 10-25min, take out and dry.
3. according to the manufacture method of a kind of carbon fiber ecological ornamental plate described in claim 1-2, it is characterised in that: described dipping
After process, take out and be placed on 0.5-2h at shady and cool ventilation, then 45-65 DEG C of drying.
The manufacture method of a kind of carbon fiber ecological ornamental plate the most according to claim 1, it is characterised in that: described fire retardant
Being ultrafine aluminium hydroxide 6-9 part by parts by weight, the raw material of phosphonium flame retardant 0.5-3 part is made.
The manufacture method of a kind of carbon fiber ecological ornamental plate the most according to claim 1, it is characterised in that: described step a
Traditional Chinese Medicine Anti microbial inoculum be Radix Artemisia ordosicae 10-15 part, Radix Glycyrrhizae 4-8 part, Aloe 3-6 part, Folium Camelliae sinensis 4-7 part by parts by weight, water 80-100 part
Raw material make.
The manufacture method of a kind of carbon fiber ecological ornamental plate the most according to claim 5, it is characterised in that: described step a
The preparation method of Traditional Chinese Medicine Anti microbial inoculum be that Radix Artemisia ordosicae, Radix Glycyrrhizae, Aloe, Folium Camelliae sinensis chopping are dried, the big fire that adds water decocts 15-30min, less
Fire decocts 5-15min.
The manufacture method of a kind of carbon fiber ecological ornamental plate the most according to claim 1, it is characterised in that: described step b
Middle antibacterial is silver zinc complex antibacterial, and wherein silver is 5-8:1-2 with the weight ratio of zinc.