CN102756533A - Method for manufacturing curve compact grade laminate - Google Patents
Method for manufacturing curve compact grade laminate Download PDFInfo
- Publication number
- CN102756533A CN102756533A CN2012102838372A CN201210283837A CN102756533A CN 102756533 A CN102756533 A CN 102756533A CN 2012102838372 A CN2012102838372 A CN 2012102838372A CN 201210283837 A CN201210283837 A CN 201210283837A CN 102756533 A CN102756533 A CN 102756533A
- Authority
- CN
- China
- Prior art keywords
- preparation
- weight portion
- adhesive
- crooked
- oven dry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention relates to a method for manufacturing a curve compact grade laminate. The method includes that firstly, a plasticizer, a light stabilizer, an ultraviolet absorber, an antioxidant and an antiaging agent are added in a first adhesive agent, and facial tissues are put into the first adhesive agent to be subjected to steeping and drying; secondly, a diluent agent, the antioxidant, the antiaging agent, the plastizer, dyes and a fire retardant are added in a second adhesive agent, and pieces of kraft paper are put into the second adhesive agent to be subjected to the steeping and the drying; thirdly, a plurality of pieces of dried kraft paper are overlaid, and pieces of dried facial tissues are placed on the upper and lower end surfaces of the overlaid kraft paper respectively; and fourthly, a finished product is formed by compressing the kraft paper and the facial tissues through a press, and the press comprises matched molds which are suitable for compressing U-shaped or arc-shaped compact grade laminates. According to the method, the manufactured curve compact grade laminate has the advantages of being colorful, high in intensity, impact resisting, uvioresistant, water-proofing, weather-proofing, anti-static, anti-fouling and easy to manufacture, so that the manufactured curve compact grade laminate can be widely applied to building outer walls, furniture, facilities, signs and the like, and the problem of splicing of the compact grade laminate at corners can be prevented.
Description
Technical field
The present invention relates to the technical field of architectural constructional materials production method, the preparation method of especially a kind of crooked Kang Beite.
Background technology
Kang Beite comes out at present, and its color is various, and is water-fast; Weather etc. are extensively accepted, and are used for wall decoration (being wallboard), are used for chair furniture etc.; Give a kind of cosy sensation of people, avoid the ice-cold dullness of stone material, but bent angle partly adopts substitutes such as splicing or plastics at present; So very inharmonious, attractive in appearance, and be prone to expand, come off etc.
For solving this technical problem; Invent a kind of crooked Kang Beite; Existing health shellfish characteristic can, promptly have various color, high strength, impact resistance, uvioresistant, weather-proof, antistatic, anti-soil and be prone to the excellent characteristic of processing, make it can be widely used in external wall, furniture, facility and sign etc.; Can bend to various radians again, avoid the problem of corner splicing, thereby make whole structure more perfect, and merge one integrated mass with environment facies.
Summary of the invention
The technical problem that the present invention will solve provides the preparation method of a kind of crooked Kang Beite of water-fast, weather.
For solving the problems of the technologies described above, the invention provides the preparation method of a kind of crooked Kang Beite, may further comprise the steps successively:
(1) in first adhesive, add flexibility agent, light stabilizer, ultra-violet absorber, antioxidant, age resister, get facial tissue and put into wherein dipping back oven dry;
(2) in second adhesive, add diluent, antioxidant, age resister, flexibility agent, dyestuff, fire retardant, get brown paper and put into wherein dipping back oven dry;
(3) brown paper after many said oven dry is stacked, and respectively put a facial tissue after the said oven dry in this stacked brown paper upper and lower end face;
(4) press down at press and process finished product; Said press comprises the matched molds that is suitable for suppressing U type or arc Kang Beite.
In the said step (1), the first adhesive 800-900 weight portion, flexibility agent 100-200 weight portion, light stabilizer 10-30 weight portion, ultra-violet absorber 10-30 weight portion, antioxidant 20-50 weight portion, ageing-resistant dose of 3-10 weight portion; Said facial tissue sun-proof degree reaches eight grades, and the facial tissue spread after the dipping oven dry is 100-130 g/m
2, fugitive constituent is 6-8%.
Said first adhesive is a melmac.
Described melmac is that 30% alkali lye 4 weight portions and water 300 weight portions are synthetic by formaldehyde 1000 weight portions, melamine 600 weight portions, concentration; Its preparation method is: in agitated reactor, throw in formaldehyde and water earlier, transfer more than the pH value to 8.0 with alkali lye, add melamine then; Be warming up to 90 ℃ after stirring; Under this temperature, be incubated then, whole process pH value is not less than 8.0, and 14-18 reduces to room temperature rapidly after second.
In the said step (2), the second adhesive 700-800 weight portion, diluent 100-200 weight portion, antioxidant 30-50 weight portion, age resister 30-50 weight portion, flexibility agent 50-100 weight portion, dyestuff 30-70 weight portion, fire retardant 10-50 weight portion; In the said brown paper, the needle pine is 7:3 with broad-leaved pine part by weight, and the spread of dipping oven dry back brown paper is 45-55 g/m
2, fugitive constituent is 6-8%.
Said second adhesive is a phenolic resins.
Described phenolic resins is that 30% alkali 150 weight portion liquid are synthetic by formaldehyde 1000 weight portions, phenol 780 weight portions and concentration; Its preparation method is: in agitated reactor, throw in formaldehyde and alkali lye earlier; Stir; Slowly be warming up to 90 ℃ then, under this temperature, be incubated, when water-soluble 1:10, dewater rapidly and reduce to room temperature.
In the said step (4), press temperature is 130-155 ℃, and pressure is 5-9MPa, suppresses 90-120 minute.
Technique effect of the present invention: the existing health shellfish of the crooked Kang Beite characteristic that the preparation method of crooked Kang Beite of the present invention is produced can; Have various color, high strength, impact resistance, uvioresistant, water-fast, weather, antistatic, anti-soil and be prone to the excellent characteristic of processing; Make it can be widely used in external wall, furniture, facility and sign etc., avoided the problem of Kang Beite corner splicing again, make whole structure more perfect; And merge one integrated mass with environment facies.
The specific embodiment
Embodiment 1
The preparation method of the crooked Kang Beite of present embodiment may further comprise the steps successively:
(1) in first adhesive, add flexibility agent, light stabilizer, ultra-violet absorber, antioxidant, age resister, get facial tissue and put into wherein dipping back oven dry;
(2) in second adhesive, add diluent, antioxidant, age resister, flexibility agent, dyestuff, fire retardant, get brown paper and put into wherein dipping back oven dry;
(3) brown paper after many said oven dry is stacked, and respectively put a facial tissue after the said oven dry in this stacked brown paper upper and lower end face;
(4) press down at press and process finished product; Said press comprises the matched molds that is suitable for suppressing U type or arc Kang Beite.
In the said step (1), first adhesive, 800 weight portions, flexibility agent 100-weight portion, light stabilizer 10 weight portions, ultra-violet absorber 10 weight portions, antioxidant 20 weight portions, ageing-resistant dose 3 weight portion; The sun-proof degree of said facial tissue reaches eight grades, and the facial tissue spread after the dipping oven dry is 100 g/m
2, fugitive constituent is 6%.
Said first adhesive is a melmac.
Described melmac becomes 300KG by formaldehyde 1000KG, melamine 600KG, alkali lye (30%) 4KG with hydration; Its preparation method is: in agitated reactor, throw in formaldehyde and water earlier, transfer more than the pH value to 8.0 with alkali lye, add melamine then; Be warming up to 90 ℃ after stirring; Under this temperature, be incubated then, whole process pH value is not less than to dewater rapidly after 8.0,14 seconds reduces to room temperature.
In the said step (2), second adhesive, 700 weight portions, diluent 100 weight portions, antioxidant 30 weight portions, age resister 30 weight portions, flexibility agent 50 weight portions, dyestuff 30 weight portions, fire retardant 10kg/ part; In the said brown paper, the needle pine is 7:3 with broad-leaved pine part by weight, and the spread of dipping oven dry back brown paper is 45 g/m
2, fugitive constituent is 6%.
Said second adhesive is a phenolic resins.
Described phenolic resins is that 30% alkali lye 150KG is synthetic by formaldehyde 1000KG, phenol 780KG and concentration; Its preparation method is: in agitated reactor, throw in formaldehyde and alkali lye earlier; Stir; Slowly be warming up to 90 ℃ then, under this temperature, be incubated, when water-soluble 1:10, dewater rapidly and reduce to room temperature.
In the said step (4), press temperature is 130 ℃, and pressure is 5MPa, suppresses 120 minutes.
The warp detection UV resistant dry heat resistance of anti-boiling water acid and alkali-resistance etc. meets GB/T7911-1999 and EN438-2 standard.
Embodiment 2
The preparation method of the crooked Kang Beite of present embodiment may further comprise the steps successively:
(1) in first adhesive, add flexibility agent, light stabilizer, ultra-violet absorber, antioxidant, age resister, get facial tissue and put into wherein dipping back oven dry;
(2) in second adhesive, add diluent, antioxidant, age resister, flexibility agent, dyestuff, fire retardant, get brown paper and put into wherein dipping back oven dry;
(3) brown paper after many said oven dry is stacked, and respectively put a facial tissue after the said oven dry in this stacked brown paper upper and lower end face;
(4) press down at press and process finished product.
In the said step (1), first adhesive, 850 weight portions, flexibility agent 150 weight portions, light stabilizer 20 weight portions, ultra-violet absorber 20 weight portions, antioxidant 35 weight portions, ageing-resistant dose 6 weight portion; The sun-proof degree of said facial tissue reaches eight grades, and the facial tissue spread after the dipping oven dry is 115 g/m
2, fugitive constituent is 7%.
Said first adhesive is a melmac.
Described melmac is become by formaldehyde, melamine, alkali lye and hydration; Its preparation method is: in agitated reactor, throw in formaldehyde and water earlier, transfer more than the pH value to 8.0 with alkali lye, add melamine then; Be warming up to 90 ℃ after stirring; Under this temperature, be incubated then, whole process pH value is not less than after 8.0,16 seconds and reduces to room temperature rapidly.
In the said step (2), second adhesive, 750 weight portions, diluent 150 weight portions, antioxidant 40 weight portions, age resister 40 weight portions, flexibility agent 75 weight portions, dyestuff 50 weight portions, fire retardant 30kg/ part; In the said brown paper, the needle pine is 7:3 with broad-leaved pine part by weight, and the spread of dipping oven dry back brown paper is 50 g/m
2, fugitive constituent is 7%.
Said second adhesive is a phenolic resins.
Described phenolic resins is synthetic by formaldehyde, phenol and alkali lye, and its preparation method is: in agitated reactor, throw in formaldehyde and alkali lye earlier, stir, slowly be warming up to 90 ℃ then, under this temperature, be incubated, when water-soluble 1:10, reduce to room temperature rapidly.
In the said step (4), press temperature is 140 ℃, and pressure is 7MPa, suppresses 110 minutes.
The warp detection UV resistant dry heat resistance of anti-boiling water acid and alkali-resistance etc. meets GB/T7911-1999 and EN438-2 standard.
Embodiment 3
The preparation method of a kind of crooked Kang Beite may further comprise the steps successively:
(1) in first adhesive, add flexibility agent, light stabilizer, ultra-violet absorber, antioxidant, age resister, get facial tissue and put into wherein dipping back oven dry;
(2) in second adhesive, add diluent, antioxidant, age resister, flexibility agent, dyestuff, fire retardant, get brown paper and put into wherein dipping back oven dry;
(3) brown paper after many said oven dry is stacked, and respectively put a facial tissue after the said oven dry in this stacked brown paper upper and lower end face;
(4) press down at press and process finished product.
In the said step (1), first adhesive, 900 weight portions, flexibility agent 200 weight portions, light stabilizer 30 weight portions, ultra-violet absorber 30 weight portions, antioxidant 50 weight portions, ageing-resistant dose 10 weight portion; The sun-proof degree of said facial tissue reaches eight grades, and the facial tissue spread after the dipping oven dry is 130 g/m
2, fugitive constituent is 8%.
Said first adhesive is a melmac.
Described melmac is become by formaldehyde, melamine, alkali lye and hydration; Its preparation method is: in agitated reactor, throw in formaldehyde and water earlier, transfer more than the pH value to 8.0 with alkali lye, add melamine then; Be warming up to 90 ℃ after stirring; Under this temperature, be incubated then, whole process pH value is not less than after 8.0,18 seconds and reduces to room temperature rapidly.
In the said step (2), second adhesive, 800 weight portions, diluent 200 weight portions, antioxidant 50 weight portions, age resister 50 weight portions, flexibility agent 100 weight portions, dyestuff 70 weight portions, fire retardant 50kg/ part; In the said brown paper, the needle pine is 7:3 with broad-leaved pine part by weight, and the spread of dipping oven dry back brown paper is 55 g/m
2, fugitive constituent is 8%.
Said second adhesive is a phenolic resins.
Described phenolic resins is synthetic by formaldehyde, phenol and alkali lye, and its preparation method is: in agitated reactor, throw in formaldehyde and alkali lye earlier, stir, slowly be warming up to 90 ℃ then, under this temperature, be incubated, when water-soluble 1:10, reduce to room temperature rapidly.
In the said step (4), press temperature is 155 ℃, and pressure is 9MPa, suppresses 90 minutes.
The warp detection UV resistant dry heat resistance of anti-boiling water acid and alkali-resistance etc. meets GB/T7911-1999 and EN438-2 standard.
Embodiment 4
The preparation method of the crooked Kang Beite of present embodiment may further comprise the steps successively:
(1) in first adhesive, add flexibility agent, light stabilizer, ultra-violet absorber, antioxidant, age resister, get facial tissue and put into wherein dipping back oven dry;
(2) in second adhesive, add diluent, antioxidant, age resister, flexibility agent, dyestuff, fire retardant, get brown paper and put into wherein dipping back oven dry;
(3) brown paper after many said oven dry is stacked, and respectively put a facial tissue after the said oven dry in this stacked brown paper upper and lower end face;
(4) press down at press and process finished product.
In the said step (1), first adhesive, 800 weight portions, flexibility agent 100-weight portion, light stabilizer 10 weight portions, ultra-violet absorber 10 weight portions, antioxidant 20 weight portions, ageing-resistant dose 3 weight portion; The sun-proof degree of said facial tissue reaches eight grades, and the facial tissue spread after the dipping oven dry is 100 g/m
2, fugitive constituent is 6%.
Said first adhesive is a melmac.
Described melmac is become by formaldehyde, melamine, alkali lye and hydration; Its preparation method is: in agitated reactor, throw in formaldehyde and water earlier, transfer more than the pH value to 8.0 with alkali lye, add melamine then; Be warming up to 90 ℃ after stirring; Under this temperature, be incubated then, whole process pH value is not less than after 8.0,14 seconds and reduces to room temperature rapidly.
In the said step (2), second adhesive, 700 weight portions, diluent 100 weight portions, antioxidant 30 weight portions, age resister 30 weight portions, flexibility agent 50 weight portions, dyestuff 30 weight portions, fire retardant 10kg/ part; In the said brown paper, the needle pine is 7:3 with broad-leaved pine part by weight, and the spread of dipping oven dry back brown paper is 45 g/m
2, fugitive constituent is 6%.
Said second adhesive is a phenolic resins.
Described phenolic resins is synthetic by formaldehyde, phenol and barium hydroxide, and its preparation method is: in agitated reactor, throw in formaldehyde and barium hydroxide earlier, stir, slowly be warming up to 100 ℃ then, under this temperature, be incubated, room temperature is reduced in dehydration when water-soluble 1:2.
In the said step (4), press temperature is 130 ℃, and pressure is 5MPa, suppresses 120 minutes.
The warp detection UV resistant dry heat resistance of anti-boiling water acid and alkali-resistance etc. meets GB/T7911-1999 and EN438-2 standard.
Embodiment 5
The preparation method of the crooked Kang Beite of present embodiment may further comprise the steps successively:
(1) in first adhesive, add flexibility agent, light stabilizer, ultra-violet absorber, antioxidant, age resister, get facial tissue and put into wherein dipping back oven dry;
(2) in second adhesive, add diluent, antioxidant, age resister, flexibility agent, dyestuff, fire retardant, get brown paper and put into wherein dipping back oven dry;
(3) brown paper after many said oven dry is stacked, and respectively put a facial tissue after the said oven dry in this stacked brown paper upper and lower end face;
(4) press down at press and process finished product.
In the said step (1), first adhesive, 850 weight portions, flexibility agent 150 weight portions, light stabilizer 20 weight portions, ultra-violet absorber 20 weight portions, antioxidant 35 weight portions, ageing-resistant dose 6 weight portion; The sun-proof degree of said facial tissue reaches eight grades, and the facial tissue spread after the dipping oven dry is 115 g/m
2, fugitive constituent is 7%.
Said first adhesive is a melmac.
Described melmac is become by formaldehyde, melamine, alkali lye and hydration; Its preparation method is: in agitated reactor, throw in formaldehyde and water earlier, transfer more than the pH value to 8.0 with alkali lye, add melamine then; Be warming up to 90 ℃ after stirring; Under this temperature, be incubated then, whole process pH value is not less than after 8.0,16 seconds and reduces to room temperature rapidly.
In the said step (2), second adhesive, 750 weight portions, diluent 150 weight portions, antioxidant 40 weight portions, age resister 40 weight portions, flexibility agent 75 weight portions, dyestuff 50 weight portions, fire retardant 30kg/ part; In the said brown paper, the needle pine is 7:3 with broad-leaved pine part by weight, and the spread of dipping oven dry back brown paper is 50 g/m
2, fugitive constituent is 7%.
Said second adhesive is a phenolic resins.
Described phenolic resins is synthetic by formaldehyde, phenol and barium hydroxide, and its preparation method is: in agitated reactor, throw in formaldehyde and barium hydroxide earlier, stir, slowly be warming up to 100 ℃ then, under this temperature, be incubated, room temperature is reduced in dehydration when water-soluble 1:2.
In the said step (4), press temperature is 140 ℃, and pressure is 7MPa, suppresses 110 minutes.
The warp detection UV resistant dry heat resistance of anti-boiling water acid and alkali-resistance etc. meets GB/T7911-1999 and EN438-2 standard.
Embodiment 6
The preparation method of a kind of crooked Kang Beite may further comprise the steps successively:
(1) in first adhesive, add flexibility agent, light stabilizer, ultra-violet absorber, antioxidant, age resister, get facial tissue and put into wherein dipping back oven dry;
(2) in second adhesive, add diluent, antioxidant, age resister, flexibility agent, dyestuff, fire retardant, get brown paper and put into wherein dipping back oven dry;
(3) brown paper after many said oven dry is stacked, and respectively put a facial tissue after the said oven dry in this stacked brown paper upper and lower end face;
(4) press down at press and process finished product.
In the said step (1), first adhesive, 900 weight portions, flexibility agent 200 weight portions, light stabilizer 30 weight portions, ultra-violet absorber 30 weight portions, antioxidant 50 weight portions, ageing-resistant dose 10 weight portion; The sun-proof degree of said facial tissue reaches eight grades, and the facial tissue spread after the dipping oven dry is 130 g/m
2, fugitive constituent is 8%.
Said first adhesive is a melmac.
Described melmac is become by formaldehyde, melamine, alkali lye and hydration; Its preparation method is: in agitated reactor, throw in formaldehyde and water earlier, transfer more than the pH value to 8.0 with alkali lye, add melamine then; Be warming up to 90 ℃ after stirring; Under this temperature, be incubated then, whole process pH value is not less than after 8.0,18 seconds and reduces to room temperature rapidly.
In the said step (2), second adhesive, 800 weight portions, diluent 200 weight portions, antioxidant 50 weight portions, age resister 50 weight portions, flexibility agent 100 weight portions, dyestuff 70 weight portions, fire retardant 50 weight portions; In the said brown paper, the needle pine is 7:3 with broad-leaved pine part by weight, and the spread of dipping oven dry back brown paper is 55 g/m
2, fugitive constituent is 8%.
Said second adhesive is a phenolic resins.
Described phenolic resins is synthetic by formaldehyde, phenol and barium hydroxide, and its preparation method is: in agitated reactor, throw in formaldehyde and barium hydroxide earlier, stir, slowly be warming up to 100 ℃ then, under this temperature, be incubated, room temperature is reduced in dehydration when water-soluble 1:2.
In the said step (4), press temperature is 155 ℃, and pressure is 9MPa, suppresses 90 minutes.
The warp detection UV resistant dry heat resistance of anti-boiling water acid and alkali-resistance etc. meets GB/T7911-1999 and EN438-2 standard.
Claims (9)
1. the preparation method of a crooked Kang Beite is characterized in that may further comprise the steps successively:
(1) in first adhesive, add flexibility agent, light stabilizer, ultra-violet absorber, antioxidant, age resister, get facial tissue and put into wherein dipping back oven dry;
(2) in second adhesive, add diluent, antioxidant, age resister, flexibility agent, dyestuff, fire retardant, get brown paper and put into wherein dipping back oven dry;
(3) brown paper after many said oven dry is stacked, and respectively put a facial tissue after the said oven dry in this stacked brown paper upper and lower end face;
(4) press down at press and process finished product; Said press comprises the matched molds that is suitable for suppressing U type or arc Kang Beite.
2. the preparation method of crooked Kang Beite as claimed in claim 1; It is characterized in that: in the said step (1), the first adhesive 800-900 weight portion, flexibility agent 100-200 weight portion; Light stabilizer 10-30 weight portion; Ultra-violet absorber 10-30 weight portion, antioxidant 20-50 weight portion, ageing-resistant dose of 3-10 weight portion; Said facial tissue sun-proof degree reaches eight grades, and the facial tissue spread after the dipping oven dry is 100-130 g/m
2, fugitive constituent is 6-8%.
3. the preparation method of crooked Kang Beite as claimed in claim 2, it is characterized in that: said first adhesive is a melmac.
4. the preparation method of crooked Kang Beite as claimed in claim 3, it is characterized in that: described melmac is become by formaldehyde, melamine, alkali lye and hydration, and its preparation method is: input formaldehyde and water in the agitated reactor earlier; Transfer more than the pH value to 8.0 with alkali lye; Add melamine then, be warming up to 90 ℃ after stirring, under this temperature, be incubated then; Whole process pH value is not less than 8.0, and 14-18 reduces to room temperature rapidly after second.
5. the preparation method of crooked Kang Beite as claimed in claim 1 is characterized in that: in the said step (2), and the second adhesive 700-800 weight portion; Diluent 100-200 weight portion; Antioxidant 30-50 weight portion, age resister 30-50 weight portion, flexibility agent 50-100 weight portion; Dyestuff 30-70 weight portion, fire retardant 10-50 weight portion; In the said brown paper, the needle pine is 7:3 with broad-leaved pine part by weight, and the spread of dipping oven dry back brown paper is 45-55 g/m
2, fugitive constituent is 6-8%.
6. the preparation method of crooked Kang Beite as claimed in claim 5, it is characterized in that: said second adhesive is a phenolic resins.
7. the preparation method of crooked Kang Beite as claimed in claim 6; It is characterized in that: described phenolic resins is synthetic by formaldehyde, phenol and alkali lye; Its preparation method is: in agitated reactor, throw in formaldehyde and alkali lye earlier, stir, slowly be warming up to 90 ℃ then; Under this temperature, be incubated, when water-soluble 1:10, reduce to room temperature rapidly.
8. the preparation method of crooked Kang Beite as claimed in claim 6; It is characterized in that: described phenolic resins is synthetic by formaldehyde, phenol and barium hydroxide; Its preparation method is: in agitated reactor, throw in formaldehyde and barium hydroxide earlier, stir, slowly be warming up to 100 ℃ then; Under this temperature, be incubated, room temperature is reduced in dehydration when water-soluble 1:2.
9. the preparation method of crooked Kang Beite as claimed in claim 1, it is characterized in that: in the said step (4), press temperature is 130-155 ℃, and pressure is 5-9MPa, suppresses 90-120 minute.