CN106272737A - A kind of manufacture method of anticorrosion moisture-resisting decoration board - Google Patents

A kind of manufacture method of anticorrosion moisture-resisting decoration board Download PDF

Info

Publication number
CN106272737A
CN106272737A CN201610637452.XA CN201610637452A CN106272737A CN 106272737 A CN106272737 A CN 106272737A CN 201610637452 A CN201610637452 A CN 201610637452A CN 106272737 A CN106272737 A CN 106272737A
Authority
CN
China
Prior art keywords
anticorrosion
manufacture
plate
decoration board
moisture
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610637452.XA
Other languages
Chinese (zh)
Inventor
刘献奇
黄�俊
陶晟
蔡国雄
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HEZHOU HENGDA PANEL Co Ltd
Original Assignee
HEZHOU HENGDA PANEL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HEZHOU HENGDA PANEL Co Ltd filed Critical HEZHOU HENGDA PANEL Co Ltd
Priority to CN201610637452.XA priority Critical patent/CN106272737A/en
Publication of CN106272737A publication Critical patent/CN106272737A/en
Pending legal-status Critical Current

Abstract

The invention discloses the manufacture method of a kind of anticorrosion moisture-resisting decoration board, the method includes plate core anticorrosion damp-proof treatment, decorative panel anticorrosion damp-proof treatment, glued three steps of group embryo, by respectively plate core, decorative panel being carried out anticorrosion damp-proof treatment, improve anticorrosion moisture effect, and while high-pressure impregnation, also use microwave, ultrasonic process, the immersion amount in sheet material can be improved, make decorative panel can have longer service life.

Description

A kind of manufacture method of anticorrosion moisture-resisting decoration board
Technical field
The present invention relates to field of plate manufacture, be specifically related to the manufacture method of a kind of anticorrosion moisture-resisting decoration board.
Background technology
Decorative panel is a kind of artificial board, be by multiple special paper after chemical treatment, use High Temperature High Pressure adhesive The thermosetting laminated plastic made, plate mask has various wood grain or pattern, and light is smooth, bright in colour attractive in appearance, has relatively simultaneously The good physical properties such as high wear-resisting, heat-resisting, cold-resistant, fire prevention.Be applied at present the wall in room, roof, cabinet, cupboard, table, Beds etc. make field.
How anticorrosion is moistureproof the most then to face a difficult problem for the decorative panel that plate core is timber, extends Product service life.Timber is fiber and the resin nature cement of a kind of concrete dynamic modulus, the most easily absorbs, evaporates water Part, thus often change and expansion or shrinkage along with the temperature humidity of environment, thus cause timber deformation, be full of cracks, the most rotten, no Only affect attractive in appearance, also affect the service life of timber.Timber is after preservative treatment, it is possible to expand its range of application and usability Energy.And the preservative treatment of timber on market, mostly use waterborne-type preservation, only possess antiseptic insect-repelling effect, do not possess protection against the tide Performance, due to the natural hygroscopicity of timber, causes preserving timber in use, easily occurs that deformation, warpage, cracking etc. are asked Topic, and cause anti-corrosion function premature failure.Carry out wood internal, outside is impregnated or covers with paint, lacquer, colour wash, etc. anti-blushing agent, is that enhancing timber size is steady One of effective measures qualitatively.
The research that the anti-blushing agent of relevant timber preservative interpolation at present strengthens humidity resistance is less, but along with the increasing of the market demand Long this will become a more prominent inevitable problem, how also to improve it while carrying out wood preservation and prevents Tidal energy power will become the emphasis of Future Development research.
Summary of the invention
For solving above-mentioned technical problem, the invention provides the manufacture method of a kind of anticorrosion moisture-resisting decoration board.
The present invention is achieved by the following technical programs:
A kind of manufacture method of anticorrosion moisture-resisting decoration board, the method comprises the following steps:
A, plate core anticorrosion damp-proof treatment: plate core is by width 30-60mm, thickness 10-18mm, the plate of length 500-800mm Gluing forms, and before gluing by high-pressure impregnation by anticorrosion anti-blushing agent press-in plate, takes out and dries, and repeat 3-4 time;
B, decorative panel anticorrosion damp-proof treatment: facing paper is put in melmac solution and impregnated, and then dries, and repeats 3-4 time;Melmac solution is melmac 8-10 part, UV absorbent 0.3-0.6 part by parts by weight, is prevented Rotten anti-blushing agent 3-7 part, the raw material blending of flexibility agent 0.5-1 part are made;
C, group embryo are glued: gluing on plate core, and decorative panel is sticked on two sides, then carries out hot pressing, saw limit, sanding, packaging and warehousing.
Elder generation application of vacuum 5-10min during described step a mesohigh dipping, adds anticorrosion anti-blushing agent and carries out high-pressure impregnation 10-25min, the most also carries out microwave treatment, supersound process to plate, dries.
Described microwave and supersound process are that high-pressure impregnation processes 10-25min with microwave simultaneously, then carry out supersound process 10- 25min。
After described dipping terminates, take out plate or facing paper is placed on 0.5-2h at shady and cool ventilation, then 45-65 DEG C of baking Dry.
Described anticorrosion anti-blushing agent is that ammonia molten alkylamine trunk 6-10 part, the raw material of anti-blushing agent 4-8 part are dissolved in breast by parts by weight Agent is made.
The beneficial effects of the present invention is: in the present invention, plate core is when anticorrosion damp-proof treatment, using the same of high-pressure impregnation Time, also it is combined with microwave and supersound process, compared to conventional high-pressure impregnation, more anticorrosion anti-blushing agent can be allowed to immerse in plate, Improve its anticorrosion humidity resistance;After dipping terminates, plate, decorative panel are first dried and dries again, beneficially anticorrosion anti-blushing agent Adhere to;And the present invention have also been changed on market sheet material when possessing anti-corrosion function simultaneously, the shortcoming of moisture-proof function, have certain Market value and practicality, can be used for building, the field such as household.
Detailed description of the invention
Below in conjunction with embodiment, technical scheme is further described, but claimed scope is not limited to In described.
Embodiment one
A kind of manufacture method of anticorrosion moisture-resisting decoration board, the method comprises the following steps:
A, plate core anticorrosion damp-proof treatment: plate core is formed by width 30mm, thickness 10mm, the plate gluing of length 500mm, By high-pressure impregnation by anticorrosion anti-blushing agent press-in plate before gluing;Elder generation's application of vacuum 5min during high-pressure impregnation, adds anti- Rotten anti-blushing agent carries out high-pressure impregnation 10min, and time while high-pressure impregnation, row microwave processes simultaneously, then carries out supersound process 10min; After dipping terminates, take out plate and be placed on 0.5h at shady and cool ventilation, then 45 DEG C of drying, and be repeated 3 times;
B, decorative panel anticorrosion damp-proof treatment: facing paper is put in melmac solution and impregnated, after dipping terminates, take out Facing paper is placed on 0.5h at shady and cool ventilation, then 45 DEG C of drying, and is repeated 3 times;Melmac solution is by weight portion Number is melmac 8 parts, UV absorbent 0.3 part, anticorrosion anti-blushing agent 3 parts, the raw material blending system of flexibility agent 0.5 part Become;
C, group embryo are glued: gluing on plate core, and decorative panel is sticked on two sides, then carries out hot pressing, saw limit, sanding, packaging and warehousing.
Anticorrosion anti-blushing agent used is that ammonia molten alkylamine trunk 6 parts, the raw material of anti-blushing agent 4 parts are dissolved in emulsifying agent by parts by weight Make.
Embodiment two
A kind of manufacture method of anticorrosion moisture-resisting decoration board, the method comprises the following steps:
A, plate core anticorrosion damp-proof treatment: plate core is formed by width 40mm, thickness 15mm, the plate gluing of length 680mm, By high-pressure impregnation by anticorrosion anti-blushing agent press-in plate before gluing;Elder generation's application of vacuum 7min during high-pressure impregnation, adds anticorrosion Anti-blushing agent carries out high-pressure impregnation 15min, and time while high-pressure impregnation, row microwave processes simultaneously, then carries out supersound process 20min;Leaching After stain terminates, take out plate and be placed on 1h at shady and cool ventilation, then 50 DEG C of drying, and be repeated 3 times;
B, decorative panel anticorrosion damp-proof treatment: facing paper is put in melmac solution and impregnated, after dipping terminates, take out Facing paper is placed on 1h at shady and cool ventilation, then 50 DEG C of drying, and repeats 3-4 time;Melmac solution is by weight portion Number is melmac 9 parts, UV absorbent 0.5 part, anticorrosion anti-blushing agent 6 parts, the raw material blending system of flexibility agent 0.7 part Become;
C, group embryo are glued: gluing on plate core, and decorative panel is sticked on two sides, then carries out hot pressing, saw limit, sanding, packaging and warehousing.
Anticorrosion anti-blushing agent used is that ammonia molten alkylamine trunk 8 parts, the raw material of anti-blushing agent 6 parts are dissolved in emulsifying agent by parts by weight Make.
Embodiment two
A kind of manufacture method of anticorrosion moisture-resisting decoration board, the method comprises the following steps:
A, plate core anticorrosion damp-proof treatment: plate core is formed by width 60mm, thickness 18mm, the plate gluing of length 800mm, By high-pressure impregnation by anticorrosion anti-blushing agent press-in plate before gluing;Elder generation's application of vacuum 10min during high-pressure impregnation, adds anticorrosion Anti-blushing agent carries out high-pressure impregnation 25min, and time while high-pressure impregnation, row microwave processes simultaneously, then carries out supersound process 25min;Leaching After stain terminates, take out plate or facing paper is placed on 2h at shady and cool ventilation, then 65 DEG C of drying, and be repeated 4 times;
B, decorative panel anticorrosion damp-proof treatment: facing paper is put in melmac solution and impregnated, after dipping terminates, take out Facing paper is placed on 2h at shady and cool ventilation, then 65 DEG C of drying, and is repeated 4 times;Melmac solution is by parts by weight Make for melmac 10 parts, UV absorbent 0.6 part, anticorrosion anti-blushing agent 7 parts, the raw material blending of flexibility agent 1 part;
C, group embryo are glued: gluing on plate core, and decorative panel is sticked on two sides, then carries out hot pressing, saw limit, sanding, packaging and warehousing.
Anticorrosion anti-blushing agent used is that ammonia molten alkylamine trunk 10 parts, the raw material of anti-blushing agent 8 parts are dissolved in emulsifying by parts by weight Agent is made.

Claims (5)

1. the manufacture method of an anticorrosion moisture-resisting decoration board, it is characterised in that: the method comprises the following steps:
A, plate core anticorrosion damp-proof treatment: plate core is by width 30-60mm, thickness 10-18mm, the plate gluing of length 500-800mm Form, before gluing by high-pressure impregnation by anticorrosion anti-blushing agent press-in plate, take out and dry, and repeat 3-4 time;
B, decorative panel anticorrosion damp-proof treatment: facing paper is put in melmac solution and impregnated, and then dries, and repeats 3-4 Secondary;Melmac solution is melmac 8-10 part, UV absorbent 0.3-0.6 part, anticorrosion by parts by weight Anti-blushing agent 3-7 part, the raw material blending of flexibility agent 0.5-1 part are made;
C, group embryo are glued: gluing on plate core, and decorative panel is sticked on two sides, then carries out hot pressing, saw limit, sanding, packaging and warehousing.
The manufacture method of a kind of anticorrosion moisture-resisting decoration board the most according to claim 1, it is characterised in that: in described step a Elder generation's application of vacuum 5-10min during high-pressure impregnation, adds anticorrosion anti-blushing agent and carries out high-pressure impregnation 10-25min, the most also to plate Carry out microwave treatment, supersound process, dry the most again.
The manufacture method of a kind of anticorrosion moisture-resisting decoration board the most according to claim 2, it is characterised in that: described microwave and super Sonication is that high-pressure impregnation processes 10-15min with microwave simultaneously, then carries out supersound process 10-25min.
4. according to the manufacture method of a kind of anticorrosion moisture-resisting decoration board described in claim 1-2, it is characterised in that: described dipping knot Shu Hou, takes out plate or facing paper is placed on 0.5-2h at shady and cool ventilation, then 45-65 DEG C of drying.
The manufacture method of a kind of anticorrosion moisture-resisting decoration board the most according to claim 1, it is characterised in that: described anticorrosion is moistureproof Agent is that ammonia molten alkylamine trunk 6-10 part, the raw material of anti-blushing agent 4-8 part are dissolved in emulsifying agent and make by parts by weight.
CN201610637452.XA 2016-08-05 2016-08-05 A kind of manufacture method of anticorrosion moisture-resisting decoration board Pending CN106272737A (en)