CN106210201B - Phone housing processing technology, phone housing and mobile phone - Google Patents
Phone housing processing technology, phone housing and mobile phone Download PDFInfo
- Publication number
- CN106210201B CN106210201B CN201610736538.8A CN201610736538A CN106210201B CN 106210201 B CN106210201 B CN 106210201B CN 201610736538 A CN201610736538 A CN 201610736538A CN 106210201 B CN106210201 B CN 106210201B
- Authority
- CN
- China
- Prior art keywords
- polishing
- thickness
- paint
- range
- antenna
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to phone housing processing technology, phone housing and mobile phone.In phone housing processing technology, by spraying and technique for grinding or by spraying, polishing, Vacuum Deposition and laser carving technique form coated film in one-level appearance, coated film covers the region in antenna and one-level appearance except the antenna, and the thickness of coated film is less than or equal to 65um.Phone housing includes plastic parts, and antenna and coated film are provided with the one-level appearance of plastic parts, and coated film covers the region in antenna and one-level appearance except the antenna, and the thickness of coated film is less than or equal to 65um.The mobile phone of the present invention includes above-mentioned phone housing.The present invention phone housing processing technology can make phone housing integrally have good hardware sense and cost it is relatively low.The phone housing and mobile phone of the present invention has good hardware sense and cost is relatively low.
Description
Technical field
The present invention relates to phone housing processing technology, phone housing and mobile phone.
Background technology
To avoid metallic shield mobile phone signals, now the shell of metal material mobile phone on the market has generally two structure shape
Formula, one kind are all-metal integrative-structures, and upper and lower antenna segment seam plus plastic cement filling, shortcoming are machined to this height;Another is main
Body portion is metal material, and at least upper-lower section is plastic cement material, specifically, after this kind of phone housing may include metal battery
Lid, upper and lower plastic cement ornamental strip and plastic cement center, antenna are arranged on the inside of plastic cement center, it is also possible to including metal battery cover main body
With upper and lower plastic cement ornamental strip (not having plastic cement center), antenna is arranged on the inside of plastic cement ornamental strip, and this phone housing lacks
Point is that upper-lower section plastic portions are wide, and the body-sensing of metal one is not strong, and phone housing entirety hardware sense is poor.
Some existing products, LDS antennas or PDS antennas can be located to the one of plastic parts (plastic cement center/plastic cement ornamental strip)
In level appearance, its process of surface treatment paint thickness typically can just cover in a day stria in 100um, and shortcoming is easy long-pending oil and mobile phone
Seamed edge C angles become R angles, and phone housing entirety hardware sense is poor.
The content of the invention
On the one hand the purpose of the present invention is:It is proposed it is a kind of can make phone housing integrally have good hardware sense and into
This relatively low phone housing processing technology.
The purpose of the present invention further aspect is that:It is proposed a kind of there is good hardware sense and lower-cost phone housing
And mobile phone.
To use following technical scheme up to this purpose, the present invention:
One aspect of the present invention provides a kind of phone housing processing technology, comprises the following steps:Antenna forming step, in plastic cement
Contoured beam antenna in the one-level appearance of part, the thickness of antenna are less than or equal to 13um;Coated film forming step, by spraying and polishing
Technique or by spraying, polishing, Vacuum Deposition and laser carving technique form coated film in one-level appearance, coated film cover antenna with
And the region in one-level appearance except the antenna, the thickness of coated film are less than or equal to 65um, wherein, when plastic parts fills for plastic cement
During panel, using spraying and technique for grinding, when plastic parts is plastic cement center, using spraying, polishing, Vacuum Deposition and laser carving work
Skill.
According to the present invention, in coated film forming step, spraying and technique for grinding include following sub-step:In one-level outward appearance
Spray-applied primer forms prime coat, prime coat parcel antenna on face;The polishing of spraying first paint forms the first polishing paint on prime coat
Layer;The polishing enamelled coating of polishing first, until aerial position is without protrusion feel;Second dozen is sprayed on the first polishing enamelled coating after polishing
Mill paint forms the second polishing enamelled coating;The first colored paint, which is sprayed, on the second polishing enamelled coating forms the first colored paint layer;In the first colored paint layer
The second colored paint of upper spraying forms the second colored paint layer;UV finish paints are sprayed on the second colored paint layer and form UV top coat layers;Wherein, priming paint,
The color of the color and plastic parts of first polishing paint and the second polishing paint belongs to same colour system, the first colored paint and the second colored paint for tool
There is the colored paint of metal-like, UV finish paints are transparent.
According to the present invention, the thickness of prime coat is located in the range of 5-7um;The thickness of first polishing enamelled coating is located at 13-
In the range of 16um;Thickness after first polishing enamelled coating polishing is located in the range of 7-10um;The thickness position of second polishing enamelled coating
In the range of 5-7um;The thickness of first colored paint layer is located in the range of 5-7um;The thickness of second colored paint layer is located at 5-7um's
In the range of;The thickness of UV top coat layers is located in the range of 15-20um.
According to the present invention, in coated film forming step, spraying, polishing, Vacuum Deposition and laser carving technique include following sub-step
Suddenly:Spray-applied primer forms prime coat, prime coat parcel antenna in one-level appearance;The polishing of the spraying first paint shape on prime coat
Into the first polishing enamelled coating;The polishing enamelled coating of polishing first, until aerial position is without protrusion feel;The first polishing enamelled coating after polishing
The upper polishing of spraying second paint forms the second polishing enamelled coating;Colored paint, which is sprayed, on the second polishing enamelled coating forms colored paint layer;In colored paint layer
Upper spraying Vacuum Deposition priming paint forms Vacuum Deposition prime coat;Vacuum Deposition processing is carried out on Vacuum Deposition prime coat and forms vacuum coating
Layer;Sprayed protection paint forms protective paint layer on vacuum coating;The region for needing to show colored paint layer on vacuum coating is led to
Cross the removal of laser laser carving;UV finish paints are sprayed on protective paint layer and form UV top coat layers;Wherein, priming paint, the first polishing paint and second
The color of paint of polishing and the color of plastic parts belong to same colour system, and colored paint is the colored paint with metal-like, Vacuum Deposition priming paint, is protected
Vernix and UV finish paints are transparent.
According to the present invention, the thickness of prime coat is located in the range of 5-7um;The thickness of first polishing enamelled coating is located at 13-
In the range of 16um;Thickness after first polishing enamelled coating polishing is located in the range of 7-10um;The thickness position of second polishing enamelled coating
In the range of 4-5um;The thickness of colored paint layer is located in the range of 5-7um;The thickness of Vacuum Deposition prime coat is located at 15-20um's
In the range of;The thickness of vacuum coating is located in the range of 100-200nm;The thickness of protective paint layer is located in the range of 5-7um;
The thickness of UV top coat layers is located in the range of 25-30um.
According to the present invention, during the polishing enamelled coating of polishing first, first slightly polished with 3000# Sponge sand papers, then with 4000# paper sand paper
Thin polishing.
According to the present invention, the thickness of the coated film formed using spraying and technique for grinding is less than or equal to 55um.
Another aspect of the present invention provides a kind of phone housing, including:Plastic parts, it is provided with the one-level appearance of plastic parts
Antenna and coated film, region except the antenna in coated film covering antenna and one-level appearance, the thickness of antenna are less than etc.
In 13um, the thickness of coated film is less than or equal to 65um;Wherein, when plastic parts is plastic cement ornamental strip, as plastic cement ornamental strip
The width of plastic parts is less than or equal to 4mm;When plastic parts is plastic cement center, the width with the plastic cement ornamental strip of plastic cement center adjoining
Less than or equal to 4mm.
According to the present invention, when plastic parts is plastic cement ornamental strip, coated film includes:It is arranged in one-level appearance by priming paint
The prime coat of formation, prime coat parcel antenna;It is arranged on the first polishing enamelled coating formed on prime coat by the first polishing paint;Set
The the second polishing enamelled coating formed on the first polishing enamelled coating by the second polishing paint;It is arranged on the second polishing enamelled coating by the first colored paint
The the first colored paint layer formed;It is arranged on the second colored paint layer formed on the first colored paint layer by the second colored paint;It is arranged on the second colored paint
The UV top coat layers formed on layer by UV finish paints;Wherein, the face of priming paint, the color of the first polishing paint and the second polishing paint and plastic parts
Color belongs to same colour system, and the first colored paint and the second colored paint are the colored paint with metal-like, and UV finish paints are transparent;Work as plastic parts
For plastic cement center when, coated film includes:It is arranged on the prime coat formed in one-level appearance by priming paint, prime coat parcel antenna;
It is arranged on the first polishing enamelled coating formed on prime coat by the first polishing paint;It is arranged on the first polishing enamelled coating and is painted by the second polishing
The the second polishing enamelled coating formed;It is arranged on the colored paint layer formed on the second polishing enamelled coating by colored paint;It is arranged on colored paint layer by true
The Vacuum Deposition prime coat that sky plating priming paint is formed;It is arranged on the vacuum coating formed on Vacuum Deposition prime coat by vacuum plating
Layer, needed in vacuum coating show colored paint layer region formed by laser laser carving it is jagged;It is arranged on vacuum coating
On the protective paint layer that is formed by protective paint;It is arranged on protective paint layer and UV top coat layers is formed by UV finish paints;Wherein, priming paint, first
The color of the color and plastic parts of polishing paint and the second polishing paint belongs to same colour system, and colored paint is the colored paint with metal-like,
Vacuum Deposition priming paint, protective paint and UV finish paints are transparent.
According to the present invention, when plastic parts is plastic cement ornamental strip:The thickness of coated film is less than or equal to 55um;The thickness of prime coat
Degree is located in the range of 5-7um;The thickness of first polishing enamelled coating is located in the range of 7-10um;The thickness position of second polishing enamelled coating
In the range of 5-7um;The thickness of first colored paint layer is located in the range of 5-7um;The thickness of second colored paint layer is located at 5-7um's
In the range of;The thickness of UV top coat layers is located in the range of 15-20um;When plastic parts is plastic cement center:The thickness position of prime coat
In the range of 5-7um;The thickness of first polishing enamelled coating is located in the range of 7-10um;The thickness of second polishing enamelled coating is located at 4-
In the range of 5um;The thickness of first colored paint layer is located in the range of 5-7um;The thickness of Vacuum Deposition prime coat is located at 15-20um's
In the range of;The thickness of vacuum coating is located in the range of 100-200nm;The thickness of protective paint layer is located in the range of 5-7um;
The thickness of UV top coat layers is located in the range of 25-30um.
Further aspect of the present invention provides a kind of mobile phone, including any of the above-described phone housing.
The above-mentioned technical proposal of the present invention has the following advantages that:
The phone housing processing technology of the present invention comprises the following steps:Antenna forming step, in the one-level outward appearance of plastic parts
Contoured beam antenna on face, the thickness of antenna are less than or equal to 13um;Coated film forming step, by spraying and technique for grinding or pass through spray
Apply, polish, Vacuum Deposition and laser carving technique form coated film, coated film covering antenna and one-level appearance in one-level appearance
In region except the antenna, the thickness of coated film is less than or equal to 65um, wherein, when plastic parts is plastic cement ornamental strip, use
Spraying and technique for grinding, when plastic parts is plastic cement center, using spraying, polishing, Vacuum Deposition and laser carving technique.First, this hair
It is bright that antenna is arranged in the one-level appearance of plastic parts, signal strength is improved, and cause antenna headroom region in cell phone rear cover
Width (i.e. the width of plastic cement ornamental strip) can narrow, for example, narrow to less than or equal to 4mm, and then, metal accounting increases,
Lift the overall hardware sense of phone housing.Secondly, because the thickness of antenna in itself is thinning and because making covering day with technique for grinding
The difficulty of line declines so that the overall thickness of coated film is reduced, and then C the top of the horns Cobalt is carried clearly closer to metal bloom C angles effect
The overall hardware sense of high mobile phone shell, there is the visual effect of novel appearance, lifting Consumer's Experience value.In addition, using this
The phone housing of processing technology be aforementioned body part be metal material, at least upper-lower section be the phone housing of plastic cement material, than
Unitary metallic material phone housing cost is lower.
The phone housing of the present invention includes plastic parts, and antenna and coated film are provided with the one-level appearance of plastic parts, applies
Tunic covers the region in antenna and one-level appearance except the antenna, and the thickness of antenna is less than or equal to 13um, coated film
Thickness is less than or equal to 65um;Wherein, when plastic parts is plastic cement ornamental strip, the width as the plastic parts of plastic cement ornamental strip is less than
Equal to 4mm;When plastic parts is plastic cement center, it is less than or equal to 4mm with the width of the plastic cement ornamental strip of plastic cement center adjoining.It is first
First, antenna is arranged in the one-level appearance of plastic parts by the present invention, improves signal strength, and make it that antenna is net in cell phone rear cover
The width (i.e. the width of plastic cement ornamental strip) of dummy section can be narrowed to less than or equal to 4mm, and then, metal accounting increases, lifting
The overall hardware sense of phone housing.Secondly, the overall thickness of coated film reduces, and then C the top of the horns Cobalt is clearly closer to metal bloom C
Angle effect, the overall hardware sense of phone housing is improved, the visual effect with novel appearance, lifting Consumer's Experience value.In addition,
This phone housing be aforementioned body part be metal material, at least upper-lower section be the phone housing of plastic cement material, than integral gold
It is lower to belong to material phone housing cost.
The mobile phone of the present invention includes above-mentioned phone housing.In the mobile phone, antenna is arranged in the one-level appearance of plastic parts,
Signal strength is improved, and the width (i.e. the width of plastic cement ornamental strip) in antenna headroom region in cell phone rear cover can be narrowed to
Less than or equal to 4mm, and then, metal accounting increases, the overall hardware sense of lifting phone housing.Secondly, the overall thickness of coated film
Reduce, and then C the top of the horns Cobalt improves the overall hardware sense of phone housing, have outward appearance new clearly closer to metal bloom C angles effect
The visual effect of grain husk, lifting Consumer's Experience value.In addition, this mobile phone is that aforementioned body part is metal material because of its phone housing
Matter, at least upper-lower section are the phone housing of plastic cement material, lower than using the mobile phone cost of unitary metallic material phone housing.
Brief description of the drawings
Fig. 1 is the schematic flow sheet of the one embodiment for the phone housing processing technology that the specific embodiment of the invention provides;
Fig. 2 is the flow signal of the specific steps of the phone housing processing technology floating coat film forming step shown in Fig. 1
Figure;
Fig. 3 is the front view of the phone housing corresponding to the phone housing processing technology in Fig. 1, wherein basically illustrating gold
Belong to battery cover main body, plastic parts (i.e. plastic cement ornamental strip);
Fig. 4 is the top view of the phone housing in Fig. 3, wherein basically illustrating antenna;
Fig. 5 is the upward view of the phone housing in Fig. 3, wherein basically illustrating antenna;
Fig. 6 is the left view of the phone housing in Fig. 3, wherein basically illustrating metal battery cover main body;
Fig. 7 is the right view of the phone housing in Fig. 3, wherein basically illustrating metal battery cover main body;
Fig. 8 is the schematic partial cross-sectional view of the phone housing in Fig. 3, wherein basically illustrating plastic cement ornamental strip and antenna;
Fig. 9 is that the partial cross section for the coated film that the coated film forming step in Fig. 2 is formed on plastic parts and antenna shows
It is intended to;
Figure 10 is the flow signal of another embodiment of the phone housing processing technology that the specific embodiment of the invention provides
Figure;
Figure 11 is that the flow of the specific steps of the phone housing processing technology floating coat film forming step shown in Figure 10 is shown
It is intended to;
Figure 12 is the front view of the phone housing corresponding to the phone housing processing technology in Figure 10, wherein basically illustrating
Metal battery cover main body, plastic cement ornamental strip;
Figure 13 is the top view of the phone housing in Figure 12, wherein basically illustrating antenna;
Figure 14 is the upward view of the phone housing in Figure 12, wherein basically illustrating antenna;
Figure 15 is the right view of the phone housing in Figure 12, wherein basically illustrating plastic parts (i.e. plastic cement center);
Figure 16 is the cross section structure for the coated film that the coated film forming step in Figure 10 is formed on plastic parts and antenna
Schematic diagram;
Figure 17 is the partial cross section for the coated film that the coated film forming step in Figure 10 is formed on plastic parts and antenna
Schematic diagram.
In Fig. 1-Fig. 9:
11:Metal battery cover main body;12、13:Plastic cement ornamental strip;14:Antenna;15:Prime coat;16:First polishing enamelled coating;
17:Second polishing enamelled coating;18:First colored paint layer;19:Second colored paint layer;110:UV top coat layers;a1:Plastic parts (i.e. decorate by plastic cement
Bar) width;b:The thickness of the main body of antenna;c:The thickness of the edge of antenna;
In Figure 10-Figure 17:
21:Metal battery bonnet;22、23:Plastic cement ornamental strip;24:Plastic cement center;25:Antenna;26:Prime coat;27:The
One polishing enamelled coating;28:Second polishing enamelled coating;29:Colored paint layer;210:Vacuum Deposition prime coat;211:Vacuum coating;212:Protection
Enamelled coating;213:UV top coat layers;214:Breach;a2:The width of plastic cement ornamental strip.
Embodiment
Further illustrate technical scheme below in conjunction with the accompanying drawings and by embodiment.
Embodiment one
Referring to figs. 1 to Fig. 8, a kind of phone housing processing technology is provided in the present embodiment, comprised the following steps:
Metal battery cover main body forming step, by metal stock extrusion forming and anodized surface processing is carried out, formed
Metal battery cover main body 11;
Upper and lower two plastic parts (i.e. plastic cement ornamental strip) forming step, plastic-injection mold two plastic parts (i.e. plastic cement
Ornamental strip 12,13), the width a1 of plastic parts (i.e. plastic cement ornamental strip 12,13) are less than or equal to 4mm, in figure, plastic cement above
Ornamental strip is to mark " 12 " to show, underlying plastic cement ornamental strip is to mark " 13 " to show;
Antenna the forming step, (example of contoured beam antenna 14 in the one-level appearance of plastic parts (i.e. plastic cement ornamental strip 12,13)
Such as, printed antenna), specifically, contoured beam antenna on the top surface of the plastic parts (i.e. plastic cement ornamental strip 12,13) of top will be placed on
14 and by contoured beam antenna 14 on the bottom surface of the plastic parts being disposed below (i.e. plastic cement ornamental strip 12,13), antenna 14 is by silver paste
Ink is bakeed 4 hours under conditions of 100 DEG C and formed, and the thickness (the namely maximum gauge of antenna 14) of antenna 14 is less than or equal to
13um, specifically, in the present embodiment, the thickness b of the main body of antenna 14 is less than or equal to 13um, the thickness of the edge of antenna 14
Degree c is less than or equal to 5um, and the part between the main body of antenna 14 and edge is gradually thinning along the direction away from main body;
Coated film forming step, by spraying and technique for grinding outside the one-level of plastic parts (i.e. plastic cement ornamental strip 12,13)
Coated film is formed on sight face, coated film covers the region in addition to antenna 14, coating film thickness in antenna 14 and one-level appearance
Degree is less than or equal to 65um.
By above-mentioned technique, first, antenna 14 is arranged on to the one-level appearance of plastic parts (i.e. plastic cement ornamental strip 12,13)
On, signal strength is improved, and cause width (i.e. the width of the plastic cement ornamental strip 12,13) energy in antenna headroom region in cell phone rear cover
Enough narrow, for example, narrow to less than or equal to 4mm, and then, metal accounting increases, the overall hardware sense of lifting phone housing.Its
It is secondary, because the thickness of antenna 14 itself is thinning and because declining the difficulty of covering antenna 14 with technique for grinding so that coated film
Overall thickness reduces, and then C the top of the horns Cobalt improves the overall hardware sense of phone housing clearly closer to metal bloom C angles effect,
Visual effect with novel appearance, lifting Consumer's Experience value, wherein, the thickness of antenna 14 is thinning to be advantageous to subsequently preferably
Polishing and covering.In addition, it for aforementioned body part is metal material, at least upper-lower section to use the phone housing of this processing technology
It is lower than unitary metallic material phone housing cost for the phone housing of plastic cement material.
More specifically, reference picture 2 is to Fig. 8, and in the present embodiment, in coated film forming step, spray and polish work
Skill includes following sub-step:
S1.1, in one-level appearance spray-applied primer formed prime coat 15, prime coat 15 wrap up antenna 14, rise antenna 14 with
Plastic cement compatible effect, specifically, priming paint are counted including 40% ethylene glycol monobutyl ether, 30% propane diols, 20% in mass ratio
Trimethylolpropane and 10% paraxylene, the color and the color of plastic parts (i.e. plastic cement ornamental strip 12,13) of priming paint belong to
Same colour system, i.e., the two color it is same or similar, the thickness of the prime coat 15 of formation is located in the range of 5-7um;
S1.2, the polishing of spraying first paint forms the first polishing enamelled coating 16 on prime coat 15, and specifically, the first polishing paint is pressed
Mass ratio meter include 40% anatase titanium dioxide, 30% talcum powder TL-45-98GB, 1% tricresyl phosphate and
10% medium oil flax alkyd resin, the color and the color category of plastic parts (i.e. plastic cement ornamental strip 12,13) of the first polishing paint
In same colour system, i.e., the two is same or similar, and the thickness of the first polishing enamelled coating 16 is located in the range of 13-16um;
S1.3, the polishing enamelled coating 16 of polishing first, until the position of antenna 14 is without protrusion feel, it is specifically, first with 3000# sponges
Sand paper is slightly polished, then is carefully polished with 4000# paper sand paper, polishes off 6um thickness, the thickness position after the first polishing polishing of enamelled coating 16
In the range of 7-10um, the first polishing enamelled coating 16 after polishing plays a part of covering antenna 14;
The polishing paint of spraying second forms the second polishing enamelled coating 17 on S1.4, the first polishing enamelled coating 16 after polishing, specifically
Ground, second polishing paint with first polishing paint it is identical, i.e., second polishing paint in mass ratio count include 40% anatase titanium dioxide,
30% talcum powder TL-45-98GB, 1% tricresyl phosphate and 10% medium oil flax alkyd resin, the second polishing paint
The color of color and plastic parts (i.e. plastic cement ornamental strip 12,13) belong to same colour system, i.e., both it is same or similar, the of formation
The thickness of two polishing enamelled coatings 17 is located in the range of 5-7um, plays a part of covering polishing trace and levelling;
S1.5, first colored paint of the spraying with metal-like forms the first colored paint layer 18, tool on the second polishing enamelled coating 17
Body, the first colored paint count in mass ratio including 30% dibatyl phithalate, 30% butyl acetate, 20% butanol,
15% ortho-xylene and 5%, parcel aluminium powder that particle diameter is 3-5um, the thickness of the first colored paint layer 18 is located at 5-7um scope
It is interior;
S1.6, second colored paint of the spraying with metal-like forms the second colored paint layer 19 on the first colored paint layer 18, specifically
Ground, the second colored paint count in mass ratio including 30% dibatyl phithalate, 30% phenol formaldehyde resin, 20% butanol,
15% ortho-xylene and 5%, parcel aluminium powder that particle diameter is 3-5um, the thickness of the second colored paint layer 19 is located at 5-7um scope
It is interior;
S1.7, transparent UV finish paints formation UV top coat layers 110 are sprayed on the second colored paint layer 19, specifically, UV finish paints are pressed
Mass ratio meter includes 30% acrylate, 30% tricresyl phosphate, 10% paraxylene, 20% benzene diformazan
Dibutyl phthalate and 10% butyl acetate, the thickness of UV top coat layers 110 are located in the range of 15-20um.
Preferably, the thickness of the coated film formed using spraying and technique for grinding is less than or equal to 55um.
Embodiment two
With continued reference to Fig. 3 to Fig. 8 a kind of phone housing can be provided in the present embodiment, the phone housing can pass through implementation
What the phone housing processing technology of example one was process, certainly, it can be also made by other method.
Specifically, the phone housing includes metal battery cover main body 11 and upper and lower two plastic parts (i.e. plastic cement ornamental strip
12、13).Be provided with antenna 14 and coated film in the one-level appearance of plastic parts (i.e. plastic cement ornamental strip 12,13), i.e., up
On the top surface of plastic parts (i.e. plastic cement ornamental strip 12,13) contoured beam antenna 14 and lower section plastic parts (i.e. plastic cement ornamental strip 12,
13) contoured beam antenna 14 on bottom surface, coated film cover the region in addition to antenna 14, antenna in antenna 14 and one-level appearance
14 thickness (the namely maximum gauge of antenna 14) is less than or equal to 13um, specifically, in the present embodiment, the main body of antenna 14
Thickness be less than or equal to 13um, the thickness of the edge of antenna 14 is less than or equal to 5um, and the thickness of coated film is less than or equal to
65um, the part between the main body of antenna 14 and edge is gradually thinning along the direction away from main body, and the material of antenna 14 is
Silver paste printing ink, the width a1 of plastic parts (i.e. plastic cement ornamental strip 12,13) are less than or equal to 4mm.
Based on above-mentioned setting, antenna 14 is arranged in the one-level appearance of plastic parts by the present embodiment, improves signal strength,
And cause cell phone rear cover in the empty regions of antenna 14 width (i.e. the width of plastic cement ornamental strip 12,13) can narrow to less than etc.
In 4mm, and then, metal accounting increases, the overall hardware sense of lifting phone housing.Secondly, the overall thickness of coated film reduces, and enters
And C the top of the horns Cobalt improves the overall hardware sense of phone housing clearly closer to metal bloom C angles effect, there is regarding for novel appearance
Feel effect, lifting Consumer's Experience is worth, wherein, the thickness of antenna 14 is thinning to be advantageous to polish and covers.In addition, outside this mobile phone
Shell be aforementioned body part be metal material, at least upper-lower section be the phone housing of plastic cement material, than unitary metallic material mobile phone
Shell cost is lower.
More specifically, in the present embodiment, the thickness of coated film is less than or equal to 55um, coated film include from the bottom to top according to
The polishing polishing of enamelled coating 16, second of prime coat 15, first enamelled coating 17, the first colored paint layer 18, the second colored paint layer 19 and the UV of secondary setting
Top coat layer 110.
Wherein, prime coat 15 is arranged in one-level appearance, and prime coat 15 wraps up antenna 14, and it is compatible with plastic cement to play antenna 14
Effect, the thickness of prime coat 15 are located in the range of 5-7um.Prime coat 15 is formed by priming paint, priming paint count in mass ratio including
40% ethylene glycol monobutyl ether, 30% propane diols, 20% trimethylolpropane and 10% paraxylene, the color of priming paint
Belong to same colour system with the color of plastic parts (i.e. plastic cement ornamental strip 12,13), i.e., the two color it is same or similar.
First polishing enamelled coating 16 is arranged on prime coat 15, and the thickness of the first polishing enamelled coating 16 is located at 7-10um scope
It is interior, play a part of covering antenna 14.First polishing enamelled coating 16 is formed by the first polishing paint, the first polishing paint meter bag in mass ratio
Include 40% anatase titanium dioxide, 30% talcum powder TL-45-98GB, 1% tricresyl phosphate and 10% medium oil
Flax alkyd resin, the color and the color of plastic parts (i.e. plastic cement ornamental strip 12,13) of the first polishing paint belong to same colour system, i.e.,
The two is same or similar.
Second polishing enamelled coating 17 is arranged on the first polishing enamelled coating 16, and the thickness of the second polishing enamelled coating 17 is located at 5-7um's
In the range of, play a part of covering polishing trace and levelling.Second polishing enamelled coating 17 by second polishing paint is formed, second polishing paint and
First polishing paint is identical, i.e., the second polishing paint meter in mass ratio includes 40% anatase titanium dioxide, 30% talcum powder TL-
45-98GB, 1% tricresyl phosphate and 10% medium oil flax alkyd resin, the color and plastic parts of the second polishing paint
The color of (i.e. plastic cement ornamental strip 12,13) belongs to same colour system, i.e., the two is same or similar.
First colored paint layer 18 is arranged on the second polishing enamelled coating 17, and the thickness of the first colored paint layer 18 is located at 5-7um scope
It is interior.Specifically, the first colored paint layer 18 is formed by the first colored paint with metal-like, and the first colored paint is counted including 30% in mass ratio
Dibatyl phithalate, 30% butyl acetate, 20% butanol, 15% ortho-xylene and 5%, particle diameter 3-5um
Parcel aluminium powder.
Second colored paint layer 19 is arranged on the first colored paint layer 18, and the thickness of the second colored paint layer 19 is located in the range of 5-7um.
Specifically, the second colored paint layer 19 is formed by the second colored paint with metal-like, and the second colored paint is counted including 30% in mass ratio
Dibatyl phithalate, 30% phenol formaldehyde resin, 20% butanol, 15% ortho-xylene and 5%, particle diameter 3-
5um parcel aluminium powder.
UV top coat layers 110 are arranged on the second colored paint layer 19, and the thickness of UV top coat layers 110 is located in the range of 15-20um.
Specifically, UV top coat layers 110 are formed by transparent UV finish paints, UV finish paints count in mass ratio including 30% acrylate,
30% tricresyl phosphate, 10% paraxylene, 20% dibatyl phithalate and 10% butyl acetate.
Embodiment three
Reference picture 10 provides a kind of phone housing processing technology, the difference with embodiment one in the present embodiment to Figure 17
Part is, in the present embodiment, plastic parts is plastic cement center 24, and phone housing also includes metal battery bonnet 21 and upper and lower plastic cement
Ornamental strip 22,23.
Specifically, the phone housing processing technology of the present embodiment comprises the following steps:
The forming step of metal battery bonnet 21, by metal stock extrusion forming and anodized surface processing is carried out, formed
Metal battery bonnet 21;
Upper and lower two plastic cement ornamental strip forming step, plastic-injection mold two plastic cement ornamental strips 22,23, plastic cement dress
The width a2 of panel 22,23 is less than or equal to 4mm;
Plastic parts (i.e. plastic cement center) forming step, injection molding plastic parts (i.e. plastic cement center 24);
Antenna forming step, in one-level appearance (the i.e. upper and lower end of plastic cement center 24 of plastic parts (i.e. plastic cement center 24)
Appearance) on contoured beam antenna 25 (for example, printed antenna 25), antenna 25 bakees 4 hours by silver paste printing ink under conditions of 100 DEG C
Formed.The thickness (the namely maximum gauge of antenna 25) of antenna 25 is less than or equal to 13um, specifically, in the present embodiment, day
The thickness of the main body of line 25 is less than or equal to 13um, and the thickness of the edge of antenna 25 is less than or equal to 5um, the main body of antenna 25 with
Part between edge is gradually thinning along the direction away from main body;
Coated film forming step, by spraying, polishing, Vacuum Deposition and laser carving technique form coating in one-level appearance
Film, coated film cover the region in addition to antenna 25, thickness in antenna 25 and one-level appearance and are less than or equal to 65um;
Connection Step, metal battery bonnet 21 is pasted onto in the middle part of plastic parts (i.e. plastic cement center 24) by hot melt glue,
Upper and lower two plastic cement ornamental strips 22,23 are passed through into the two-sided upper/lower terminal for being adhesive in plastic parts (i.e. plastic cement center 24).
By above-mentioned technique, first, antenna 25 is arranged in the one-level appearance of plastic parts (i.e. plastic cement center 24), carried
High signal strength, and make it that the width (i.e. the width of plastic cement ornamental strip 22,23) of the empty regions of antenna 25 in cell phone rear cover can
Narrow, for example, narrow to less than or equal to 4mm, and then, metal accounting increases, the overall hardware sense of lifting phone housing.Secondly,
Because the thickness of antenna 25 itself is thinning and because declining the difficulty of covering antenna 25 with technique for grinding so that coated film is whole
The thickness of body reduces, and then C the top of the horns Cobalt improves the overall hardware sense of phone housing, tool clearly closer to metal bloom C angles effect
There is the visual effect of novel appearance, lifting Consumer's Experience is worth, wherein, the thickness of antenna 25 is thinning to be advantageous to subsequently preferably beat
Mill and covering.In addition, to use the phone housing of this processing technology for aforementioned body part be metal material, at least upper-lower section is
The phone housing of plastic cement material is lower than unitary metallic material phone housing cost.
More specifically, reference picture 10 is to Figure 16, in the present embodiment, in coated film forming step, spraying, polishing,
Vacuum Deposition and laser carving technique include following sub-step:
S2.1, in one-level appearance spray-applied primer formed prime coat 26, prime coat 26 wrap up antenna 25, rise antenna 25 with
Plastic cement compatible effect, specifically, priming paint are counted including 40% ethylene glycol monobutyl ether, 30% propane diols, 20% in mass ratio
Trimethylolpropane and 10% paraxylene, the color and the color of plastic parts (i.e. plastic cement center 24) of priming paint belong to of the same colour
System, i.e., the two color it is same or similar, the thickness of the prime coat 26 of formation is located in the range of 5-7um.
S2.2, the polishing of spraying first paint forms the first polishing enamelled coating 27 on prime coat 26, and specifically, the first polishing paint is pressed
Mass ratio meter include 40% anatase titanium dioxide, 30% talcum powder TL-45-98GB, 1% tricresyl phosphate and
10% medium oil flax alkyd resin, the color of the first polishing paint and plastic parts (i.e. plastic cement center 24) belong to same colour system,
I.e. the two color it is same or similar, now formed first polishing enamelled coating 27 thickness be located in the range of 13-16um.
S2.3, the polishing enamelled coating 27 of polishing first, until the position of antenna 25 is without protrusion feel, it is specifically, first with 3000# sponges
Sand paper is slightly polished, then is carefully polished with 4000# paper sand paper, polishes off 6um thickness, the thickness position after the first polishing polishing of enamelled coating 27
In the range of 7-10um, the first polishing enamelled coating 27 after polishing plays a part of covering antenna 25.
The polishing paint of spraying second forms the second polishing enamelled coating 28 on S2.4, the first polishing enamelled coating 27 after polishing, specifically
Ground, second polishing paint with first polishing paint it is identical, second polishing paint in mass ratio count include 40% anatase titanium dioxide,
30% talcum powder TL-45-98GB, 1% tricresyl phosphate and 10% medium oil flax alkyd resin, the second polishing paint
The color of color and plastic parts (i.e. plastic cement center) belong to same colour system, i.e., the two is same or similar, and second polishes the face painted
The color of color and plastic parts (i.e. plastic cement center) belongs to same colour system, i.e., the two is same or similar, the second polishing enamelled coating of formation
28 thickness is located in the range of 4-5um, plays a part of covering polishing trace and levelling.
S2.5, colored paint of the spraying with metal-like forms colored paint layer 29, specifically, colored paint on the second polishing enamelled coating 28
In mass ratio meter include 30% dibatyl phithalate, 30% butyl acetate, 20% butanol, 15% ortho-xylene and
5%, parcel aluminium powder that particle diameter is 3-5um, colored paint can be golden paint, play metal sanding texture.The colored paint layer 29 of formation
Thickness be located in the range of 5-7um.
S2.6, transparent Vacuum Deposition priming paint formation Vacuum Deposition prime coat 210, specifically, vacuum are sprayed on colored paint layer 29
Priming paint is plated by mass including 40% acrylate, 15% nitrocellulose, 15% low degree of etherification melamine
Resin, 10% dibatyl phithalate, 10% butanol and 10% toluene.The thickness of the Vacuum Deposition prime coat 210 of formation
In the range of 15-20um, the effect of furling plating carrier.
S2.7, carry out on Vacuum Deposition prime coat 210 Vacuum Deposition processing and form vacuum coating 211, used in Vacuum Deposition
Material is indium metal, purity 99.99%.The thickness of the vacuum coating 211 of formation is located in the range of 100-200nm, rises
The effect of bloom bright border.
S2.8, transparent protective paint formation protective paint layer 212 is sprayed on vacuum coating 211, specifically, protective paint is pressed
Mass ratio meter includes 15% styrene, 30% dibatyl phithalate, 35% acrylamide and 20% acrylic acid.Shape
Into protective paint layer 212 thickness be located at 5-7um in the range of, mainly play protective coating and be easy to laser carving.
S2.9, the region for needing to show colored paint layer 29 on vacuum coating 211 removed by laser laser carving.
S2.10, transparent UV finish paints formation UV top coat layers 213 are sprayed on protective paint layer 212, specifically, UV finish paints are pressed
Mass ratio includes 30% acrylate, 30% dibatyl phithalate, 10% paraxylene, 20% benzene diformazan
Dibutyl phthalate and 10% butyl acetate.The thickness of the UV top coat layers 213 of formation is located in the range of 25-30um, rises under protection
The effect of finishing coat.
Example IV
With continued reference to Figure 11 to Figure 17 a kind of phone housing can be provided in the present embodiment, the phone housing can pass through reality
Apply what the phone housing processing technology of example three was process, certainly, can be also made by other method.
Specifically, phone housing include metal battery bonnet 21, plastic parts (i.e. plastic cement center 24) and with plastic cement center 24
Adjacent plastic cement ornamental strip.In one-level appearance (the i.e. upper and lower end outward appearance of plastic cement center 24 of plastic parts (i.e. plastic cement center 24)
Face) it is provided with antenna 25 and coated film.The material of antenna 25 can be silver paste printing ink, and the thickness of the main body of antenna 25 is less than or equal to
13um, the thickness (the namely maximum gauge of antenna 25) of antenna 25 are less than or equal to 13um, specifically, in the present embodiment, day
The thickness of the edge of line 25 is less than or equal to 5um, and the part between the main body of antenna 25 and edge is along away from main body
Direction is gradually thinning.Coated film covers the region in addition to antenna 25, the thickness of coated film in antenna 25 and one-level appearance
Less than or equal to 65um.The width of plastic cement ornamental strip is less than or equal to 4mm.
First, antenna 25 is arranged in the one-level appearance of plastic parts (i.e. plastic cement center 24) by the present embodiment, improves news
Number intensity, and cause the width (i.e. the width of plastic cement ornamental strip) of the empty regions of antenna 25 in cell phone rear cover can narrow to be less than
Equal to 4mm, and then, metal accounting increases, the overall hardware sense of lifting phone housing.Secondly, the overall thickness of coated film reduces,
And then C the top of the horns Cobalt improves the overall hardware sense of phone housing, has novel appearance clearly closer to metal bloom C angles effect
Visual effect, lifting Consumer's Experience value, wherein, the thickness of antenna 25 is thinning to be advantageous to follow-up preferably polishing and covers.This
Outside, this phone housing be aforementioned body part be metal material, at least upper-lower section be the phone housing of plastic cement material, than one
Metal material phone housing cost is lower.
Specifically, coated film includes the polishing polishing paint of enamelled coating 27, second of prime coat 26, first set gradually from bottom to top
Layer 28, colored paint layer 29, Vacuum Deposition prime coat 210, vacuum coating 211, protective paint layer 212 and UV top coat layers 213.
Wherein, prime coat 26 is arranged in one-level appearance, and prime coat 26 wraps up antenna 25, and it is compatible with plastic cement to play antenna 25
Effect.Specifically, the thickness of prime coat 26 is located in the range of 5-7um, and prime coat 26 is formed by priming paint, and priming paint is counted in mass ratio
Including 40% ethylene glycol monobutyl ether, 30% propane diols, 20% trimethylolpropane and 10% paraxylene, priming paint
The color of color and plastic parts (i.e. plastic cement center 24) belongs to same colour system, i.e., the two color it is same or similar.
First polishing enamelled coating 27 is arranged on prime coat 26, and the thickness of the first polishing enamelled coating 27 is located at 7-10um scope
It is interior.Specifically, the first polishing enamelled coating 27 is formed by the first polishing paint, and the first polishing paint meter in mass ratio includes 40% anatase
Type titanium dioxide, 30% talcum powder TL-45-98GB, 1% tricresyl phosphate and 10% medium oil flax alkyd resin,
First polishing paint and the color of plastic parts (i.e. plastic cement center 24) belong to same colour system, i.e., the two color it is same or similar.
Second polishing enamelled coating 28 is arranged on the first polishing enamelled coating 27, plays a part of covering polishing trace and levelling.Second
The thickness of polishing enamelled coating 28 is located in the range of 4-5um.Second polishing enamelled coating 28 by second polishing paint is formed, second polishing paint and
First polishing paint is identical, and the second polishing paint meter in mass ratio includes 40% anatase titanium dioxide, 30% talcum powder TL-
45-98GB, 1% tricresyl phosphate and 10% medium oil flax alkyd resin, the color and plastic parts of the second polishing paint
The color of (i.e. plastic cement center) belongs to same colour system, i.e., the two is same or similar, and the color of the second polishing paint (is moulded with plastic parts
Glue center) color belong to same colour system, i.e., the two is same or similar.
Colored paint layer 29 is arranged on the second polishing enamelled coating 28, and the thickness of colored paint layer 29 is located in the range of 5-7um.Colored paint layer
29 are formed by the colored paint with metal-like, and colored paint counts the acetic acid including 30% dibatyl phithalate, 30% in mass ratio
Butyl ester, 20% butanol, 15% ortho-xylene and 5%, parcel aluminium powder that particle diameter is 3-5um, colored paint can be golden paint, rise
Metal sanding texture acts on.
Vacuum Deposition prime coat 210 is arranged on colored paint layer 29, and the thickness of Vacuum Deposition prime coat 210 is located at 15-20um model
In enclosing, the effect of furling plating carrier.Vacuum Deposition prime coat 210 is formed by transparent Vacuum Deposition priming paint, and Vacuum Deposition priming paint presses quality
Meter include 40% acrylate, 15% nitrocellulose, 15% low degree of etherification melmac, 10% benzene
Dibutyl carboxylic acid, 10% butanol and 10% toluene.
Vacuum coating 211 is arranged on Vacuum Deposition prime coat 210, passes through vacuum by indium metal (purity 99.99%)
Plating is formed, and the thickness of vacuum coating 211 is located in the range of 100-200nm, plays bloom bright border.Wherein, exist
The region for needing to show colored paint layer 29 in vacuum coating 211 forms jagged 214 by laser laser carving.
Protective paint layer 212 is arranged on vacuum coating 211, and the thickness of protective paint layer 212 is located in the range of 5-7um,
Mainly play protective coating and be easy to laser carving.Protective paint layer 212 is formed by transparent protective paint, and protective paint is counted in mass ratio
Including 15% styrene, 30% dibatyl phithalate, 35% acrylamide and 20% acrylic acid.
UV top coat layers 213 are arranged on protective paint layer, and the thickness of UV top coat layers 213 is located in the range of 25-30um, are risen and are protected
The effect of the lower finishing coat of shield.UV top coat layers 213 are formed by transparent UV finish paints, and UV finish paints include 30% acrylic acid in mass ratio
Ester resin, 30% dibatyl phithalate, 10% paraxylene, 20% dibatyl phithalate and 10% acetic acid fourth
Ester.
Embodiment five
A kind of mobile phone is provided in the present embodiment, phone housing of the mobile phone described in including embodiment two or example IV.
Specifically, set in the phone housing of the mobile phone in the one-level appearance of plastic parts (plastic cement ornamental strip 12,13/ plastic cement center 24)
There are antenna 25 and coated film, coated film covers the region in addition to antenna 25 in antenna 25 and one-level appearance, antenna 25
The thickness of main body is less than or equal to 13um, and the thickness of the edge of antenna 25 is less than or equal to 5um, and the thickness of coated film is less than or equal to
65um;Wherein, when plastic parts is plastic cement ornamental strip 12,13, the width as the plastic parts of plastic cement ornamental strip 12,13 is less than etc.
In 4mm;When plastic parts is plastic cement center 24, the width of the plastic cement ornamental strip abutted with plastic cement center 24 is less than or equal to 4mm.
In the mobile phone, antenna 25 is arranged in the one-level appearance of plastic parts, improves signal strength, and cause cell phone rear cover
The width (i.e. the width of plastic cement ornamental strip) of the middle empty regions of antenna 25 can be narrowed to less than or equal to 4mm, and then, metal accounting
Increase, the overall hardware sense of lifting phone housing.Secondly, the overall thickness of coated film reduces, and then C the top of the horns Cobalt is clearly closer
Metal bloom C angles effect, the overall hardware sense of phone housing is improved, the visual effect with novel appearance, lift Consumer's Experience
Value.In addition, this mobile phone because its phone housing be aforementioned body part be metal material, at least upper-lower section be plastic cement material
Phone housing is lower than using the mobile phone cost of unitary metallic material phone housing.
The technical principle of the present invention is described above in association with specific embodiment.These descriptions are intended merely to explain the present invention's
Principle, and limiting the scope of the invention can not be construed in any way.Based on explanation herein, the technology of this area
Personnel would not require any inventive effort the other embodiments that can associate the present invention, and these modes are fallen within
Within protection scope of the present invention.
Claims (10)
1. a kind of phone housing processing technology, it is characterised in that comprise the following steps:
Antenna forming step, the contoured beam antenna in the one-level appearance of plastic parts, the thickness of the antenna are less than or equal to 13um;
Coated film forming step, by spraying and technique for grinding or by spraying, polishing, Vacuum Deposition and laser carving technique be described one
Coated film is formed in level appearance, the coated film covers the area in the antenna and the one-level appearance except the antenna
Domain, the thickness of the coated film are less than or equal to 65um, wherein, when the plastic parts is plastic cement ornamental strip, using the spraying
And technique for grinding, when the plastic parts is plastic cement center, using the spraying, polishing, Vacuum Deposition and laser carving technique.
2. phone housing processing technology according to claim 1, it is characterised in that
In the coated film forming step, the spraying and technique for grinding include following sub-step:
Spray-applied primer forms prime coat in the one-level appearance, and the prime coat wraps up the antenna;
The polishing of spraying first paint forms the first polishing enamelled coating on the prime coat;
Polish it is described first polishing enamelled coating, until aerial position without protrusion feel;
The polishing paint of spraying second forms the second polishing enamelled coating on the first polishing enamelled coating after polishing;
The first colored paint, which is sprayed, on the described second polishing enamelled coating forms the first colored paint layer;
The second colored paint is sprayed on the first colored paint layer and forms the second colored paint layer;
UV finish paints are sprayed on the second colored paint layer and form UV top coat layers;
Wherein, the priming paint, the color of the first polishing paint and the second polishing paint and the color of the plastic parts belong to
Same colour system, first colored paint and second colored paint are the colored paint with metal-like, and the UV finish paints are transparent.
3. phone housing processing technology according to claim 2, it is characterised in that
The thickness of the prime coat is located in the range of 5-7um;
The thickness of the first polishing enamelled coating is located in the range of 13-16um;
Thickness after the first polishing enamelled coating polishing is located in the range of 7-10um;
The thickness of the second polishing enamelled coating is located in the range of 5-7um;
The thickness of the first colored paint layer is located in the range of 5-7um;
The thickness of the second colored paint layer is located in the range of 5-7um;
The thickness of the UV top coat layers is located in the range of 15-20um.
4. phone housing processing technology according to claim 1, it is characterised in that
In the coated film forming step, the spraying, polishing, Vacuum Deposition and laser carving technique include following sub-step:
Spray-applied primer forms prime coat in the one-level appearance, and the prime coat wraps up the antenna;
The polishing of spraying first paint forms the first polishing enamelled coating on the prime coat;
Polish it is described first polishing enamelled coating, until aerial position without protrusion feel;
The polishing paint of spraying second forms the second polishing enamelled coating on the first polishing enamelled coating after polishing;
Colored paint, which is sprayed, on the described second polishing enamelled coating forms colored paint layer;
Vacuum Deposition priming paint is sprayed on the colored paint layer and forms Vacuum Deposition prime coat;
Vacuum Deposition processing is carried out on the Vacuum Deposition prime coat and forms vacuum coating;
Sprayed protection paint forms protective paint layer on the vacuum coating;
The region for needing to show the colored paint layer on the vacuum coating is removed by laser laser carving;
UV finish paints are sprayed on the protective paint layer and form UV top coat layers;
Wherein, the priming paint, the color of the first polishing paint and the second polishing paint and the color of the plastic parts belong to
Same colour system, the colored paint are the colored paint with metal-like, and the Vacuum Deposition priming paint, the protective paint and the UV finish paints are equal
It is transparent.
5. phone housing processing technology according to claim 4, it is characterised in that
The thickness of the prime coat is located in the range of 5-7um;
The thickness of the first polishing enamelled coating is located in the range of 13-16um;
Thickness after the first polishing enamelled coating polishing is located in the range of 7-10um;
The thickness of the second polishing enamelled coating is located in the range of 4-5um;
The thickness of the colored paint layer is located in the range of 5-7um;
The thickness of the Vacuum Deposition prime coat is located in the range of 15-20um;
The thickness of the vacuum coating is located in the range of 100-200nm;
The thickness of the protective paint layer is located in the range of 5-7um;
The thickness of the UV top coat layers is located in the range of 25-30um.
6. the phone housing processing technology according to claim 2 or 4, it is characterised in that
Polish the first polishing enamelled coating when, first slightly polished, then carefully polished with 4000# paper sand paper with 3000# Sponge sand papers.
7. phone housing processing technology according to claim 1, it is characterised in that
The thickness of the coated film formed using the spraying and technique for grinding is less than or equal to 55um.
A kind of 8. phone housing, it is characterised in that including:
Plastic parts, is provided with antenna and coated film in the one-level appearance of the plastic parts, and the coated film covers the antenna
And the region in the one-level appearance except the antenna, the thickness of the antenna are less than or equal to 13um, the coated film
Thickness is less than or equal to 65um;
Wherein, when the plastic parts is plastic cement ornamental strip, the width as the plastic parts of plastic cement ornamental strip is less than or equal to
4mm;When the plastic parts is plastic cement center, it is less than or equal to 4mm with the width of the plastic cement ornamental strip of plastic cement center adjoining;
When the plastic parts is plastic cement ornamental strip, the coated film includes:
The prime coat formed in the one-level appearance by priming paint is arranged on, the prime coat wraps up the antenna;
It is arranged on the first polishing enamelled coating formed on the prime coat by the first polishing paint;
It is arranged on the second polishing enamelled coating formed on the first polishing enamelled coating by the second polishing paint;
It is arranged on the first colored paint layer formed on the second polishing enamelled coating by the first colored paint;
It is arranged on the second colored paint layer formed on the first colored paint layer by the second colored paint;
It is arranged on the UV top coat layers formed on the second colored paint layer by UV finish paints;
Wherein, the priming paint, the color of the first polishing paint and the second polishing paint and the color of the plastic parts belong to
Same colour system, first colored paint and second colored paint are the colored paint with metal-like, and the UV finish paints are transparent;
When the plastic parts is plastic cement center, the coated film includes:
The prime coat formed in the one-level appearance by priming paint is arranged on, the prime coat wraps up the antenna;
It is arranged on the first polishing enamelled coating formed on the prime coat by the first polishing paint;
It is arranged on the second polishing enamelled coating formed on the first polishing enamelled coating by the second polishing paint;
It is arranged on the colored paint layer formed on the second polishing enamelled coating by colored paint;
It is arranged on the Vacuum Deposition prime coat formed on the colored paint layer by Vacuum Deposition priming paint;
The vacuum coating formed on the Vacuum Deposition prime coat by vacuum plating is arranged on, in the vacuum coating
Need to show the colored paint layer region formed by laser laser carving it is jagged;
It is arranged on the protective paint layer formed on the vacuum coating by protective paint;
It is arranged on the protective paint layer and UV top coat layers is formed by UV finish paints;
Wherein, the priming paint, the color of the first polishing paint and the second polishing paint and the color of the plastic parts belong to
Same colour system, the colored paint are the colored paint with metal-like, and the Vacuum Deposition priming paint, the protective paint and the UV finish paints are equal
It is transparent.
9. phone housing according to claim 8, it is characterised in that
When the plastic parts is plastic cement ornamental strip:
The thickness of the coated film is less than or equal to 55um;
The thickness of the prime coat is located in the range of 5-7um;
The thickness of the first polishing enamelled coating is located in the range of 7-10um;
The thickness of the second polishing enamelled coating is located in the range of 5-7um;
The thickness of the first colored paint layer is located in the range of 5-7um;
The thickness of the second colored paint layer is located in the range of 5-7um;
The thickness of the UV top coat layers is located in the range of 15-20um;
When the plastic parts is plastic cement center:
The thickness of the prime coat is located in the range of 5-7um;
The thickness of the first polishing enamelled coating is located in the range of 7-10um;
The thickness of the second polishing enamelled coating is located in the range of 4-5um;
The thickness of the first colored paint layer is located in the range of 5-7um;
The thickness of the Vacuum Deposition prime coat is located in the range of 15-20um;
The thickness of the vacuum coating is located in the range of 100-200nm;
The thickness of the protective paint layer is located in the range of 5-7um;
The thickness of the UV top coat layers is located in the range of 25-30um.
10. a kind of mobile phone, it is characterised in that including the phone housing described in claim any one of 8-9.