CN106189868A - 一种纺织烘干设备内用防腐涂料 - Google Patents
一种纺织烘干设备内用防腐涂料 Download PDFInfo
- Publication number
- CN106189868A CN106189868A CN201610738470.7A CN201610738470A CN106189868A CN 106189868 A CN106189868 A CN 106189868A CN 201610738470 A CN201610738470 A CN 201610738470A CN 106189868 A CN106189868 A CN 106189868A
- Authority
- CN
- China
- Prior art keywords
- parts
- acid
- inorganic filler
- drying apparatus
- anticorrosive paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种纺织烘干设备内用防腐涂料,其包括以下重量份数的原料:乳胶20~40份、三烯丙基异氰脲酸酯3~8份、三乙烯四胺六乙酸1~4份、聚丁二酸丁二醇酯2~7份、丁二烯树脂成膜剂5~10份、脱氢乙酸0.5~1.5份、乙二胺四乙酸2~7份、麝香草酚溶液1~3份、亚硫酸钠1~4份、抗氧剂DSTDP 1~4份、乙二醇2~6份、对羟苯甲酸异丙酯0.5~1.5份、2,5‑二特丁基对苯二酚1~3份和无机填料10~20份。本发明提供的一种纺织烘干设备内用防腐涂料经涂刷或喷涂在干燥装置内壁,可以很好的起到防腐败现象的发生,使用效果良好。
Description
技术领域
本发明涉及防腐技术领域,具体涉及一种纺织烘干设备内用的防腐涂料。
背景技术
纺织生产中烘干机是必不可少的生产设备之一,烘干设备直接影响纺织物质量的好坏。但中正常的烘干加工过程中,烘干设备内的内壁常因被烘干织物富含纤维、毛絮、色料以及烘干初期的高湿环境等的影响而产生腐败因子,而纺织烘干设备在正常使用时的清理较为困难,在一定程度上影响了其正常使用。
发明内容
针对现有技术不足,本发明提供了一种纺织烘干设备内用防腐涂料。
本发明解决上述技术问题采用的技术方案为:一种纺织烘干设备内用防腐涂料,包括以下重量份数的原料:乳胶20~40份、三烯丙基异氰脲酸酯3~8份、三乙烯四胺六乙酸1~4份、聚丁二酸丁二醇酯2~7份、丁二烯树脂成膜剂5~10份、脱氢乙酸0.5~1.5份、乙二胺四乙酸2~7份、麝香草酚溶液1~3份、亚硫酸钠1~4份、抗氧剂DSTDP 1~4份、乙二醇2~6份、对羟苯甲酸异丙酯0.5~1.5份、2,5-二特丁基对苯二酚1~3份和无机填料10~20份。
作为优选,上述一种纺织烘干设备内用防腐涂料,包括以下重量份数的原料:乳胶30份、三烯丙基异氰脲酸酯5份、三乙烯四胺六乙酸3份、聚丁二酸丁二醇酯4份、丁二烯树脂成膜剂7份、脱氢乙酸1份、乙二胺四乙酸5份、麝香草酚溶液2份、亚硫酸钠3份、抗氧剂DSTDP2份、乙二醇4份、对羟苯甲酸异丙酯1份、2,5-二特丁基对苯二酚2份和无机填料15份。
进一步地,所述无机填料为钛白粉、碳酸钙、滑石粉、凹凸棒土粉中的一种或几种。
与现有技术相比,本发明具备的优点:
本发明提供的一种纺织烘干设备内用防腐涂料经涂刷或喷涂在纺织干燥装置内壁,可以很好的起到防腐败及氧化现象的发生,使用效果良好。
具体实施方式
下面结合具体实施例对本发明做进一步的说明。
实施例1:一种纺织烘干设备内用防腐涂料,包括以下重量份数的原料:乳胶30份、三烯丙基异氰脲酸酯5份、三乙烯四胺六乙酸3份、聚丁二酸丁二醇酯4份、丁二烯树脂成膜剂7份、脱氢乙酸1份、乙二胺四乙酸5份、麝香草酚溶液2份、亚硫酸钠3份、抗氧剂DSTDP 2份、乙二醇4份、对羟苯甲酸异丙酯1份、2,5-二特丁基对苯二酚2份和无机填料15份;所述无机填料为钛白粉、碳酸钙和凹凸棒土粉。
实施例2:一种纺织烘干设备内用防腐涂料,包括以下重量份数的原料:乳胶20份、三烯丙基异氰脲酸酯3份、三乙烯四胺六乙酸1份、聚丁二酸丁二醇酯2份、丁二烯树脂成膜剂5份、脱氢乙酸0.5份、乙二胺四乙酸2份、麝香草酚溶液1份、亚硫酸钠1份、抗氧剂DSTDP 1份、乙二醇2份、对羟苯甲酸异丙酯0.5份、2,5-二特丁基对苯二酚1份和无机填料10份;所述无机填料为钛白粉。
实施例3:一种纺织烘干设备内用防腐涂料,包括以下重量份数的原料:乳胶40份、三烯丙基异氰脲酸酯8份、三乙烯四胺六乙酸4份、聚丁二酸丁二醇酯7份、丁二烯树脂成膜剂10份、脱氢乙酸1.5份、乙二胺四乙酸7份、麝香草酚溶液3份、亚硫酸钠4份、抗氧剂DSTDP4份、乙二醇6份、对羟苯甲酸异丙酯1.5份、2,5-二特丁基对苯二酚3份和无机填料20份;所述无机填料为钛白粉、碳酸钙、滑石粉和凹凸棒土粉。
实施例4:一种纺织烘干设备内用防腐涂料,包括以下重量份数的原料:乳胶20份、三烯丙基异氰脲酸酯8份、三乙烯四胺六乙酸1份、聚丁二酸丁二醇酯7份、丁二烯树脂成膜剂5份、脱氢乙酸0.5份、乙二胺四乙酸7份、麝香草酚溶液1份、亚硫酸钠4份、抗氧剂DSTDP 1份、乙二醇6份、对羟苯甲酸异丙酯0.5份、2,5-二特丁基对苯二酚3份和无机填料10份;所述无机填料为碳酸钙和凹凸棒土粉。
实施例5:一种纺织烘干设备内用防腐涂料,包括以下重量份数的原料:乳胶35份、三烯丙基异氰脲酸酯6份、三乙烯四胺六乙酸2份、聚丁二酸丁二醇酯6份、丁二烯树脂成膜剂8份、脱氢乙酸0.8份、乙二胺四乙酸4份、麝香草酚溶液2份、亚硫酸钠2份、抗氧剂DSTDP 2份、乙二醇5份、对羟苯甲酸异丙酯0.8份、2,5-二特丁基对苯二酚3份和无机填料18份;所述无机填料为钛白粉、滑石粉和凹凸棒土粉。
Claims (5)
1. 一种纺织烘干设备内用防腐涂料,其特征在于,包括以下重量份数的原料:乳胶20~40份、三烯丙基异氰脲酸酯3~8份、三乙烯四胺六乙酸1~4份、聚丁二酸丁二醇酯2~7份、丁二烯树脂成膜剂5~10份、脱氢乙酸0.5~1.5份、乙二胺四乙酸2~7份、麝香草酚溶液1~3份、亚硫酸钠1~4份、抗氧剂DSTDP 1~4份、乙二醇2~6份、对羟苯甲酸异丙酯0.5~1.5份、2,5-二特丁基对苯二酚1~3份和无机填料10~20份。
2. 根据权利要求1所述的一种纺织烘干设备内用防腐涂料,其特征在于,包括以下重量份数的原料:乳胶30份、三烯丙基异氰脲酸酯5份、三乙烯四胺六乙酸3份、聚丁二酸丁二醇酯4份、丁二烯树脂成膜剂7份、脱氢乙酸1份、乙二胺四乙酸5份、麝香草酚溶液2份、亚硫酸钠3份、抗氧剂DSTDP 2份、乙二醇4份、对羟苯甲酸异丙酯1份、2,5-二特丁基对苯二酚2份和无机填料15份。
3. 根据权利要求1所述的一种纺织烘干设备内用防腐涂料,其特征在于,包括以下重量份数的原料:乳胶20份、三烯丙基异氰脲酸酯3份、三乙烯四胺六乙酸1份、聚丁二酸丁二醇酯2份、丁二烯树脂成膜剂5份、脱氢乙酸0.5份、乙二胺四乙酸2份、麝香草酚溶液1份、亚硫酸钠1份、抗氧剂DSTDP 1份、乙二醇2份、对羟苯甲酸异丙酯0.5份、2,5-二特丁基对苯二酚1份和无机填料10份;所述无机填料为钛白粉。
4. 根据权利要求1所述的一种纺织烘干设备内用防腐涂料,其特征在于,包括以下重量份数的原料:乳胶40份、三烯丙基异氰脲酸酯8份、三乙烯四胺六乙酸4份、聚丁二酸丁二醇酯7份、丁二烯树脂成膜剂10份、脱氢乙酸1.5份、乙二胺四乙酸7份、麝香草酚溶液3份、亚硫酸钠4份、抗氧剂DSTDP 4份、乙二醇6份、对羟苯甲酸异丙酯1.5份、2,5-二特丁基对苯二酚3份和无机填料20份;所述无机填料为钛白粉、碳酸钙、滑石粉和凹凸棒土粉。
5.根据权利要求1-4任一项所述的一种纺织烘干设备内用防腐涂料,其特征在于:所述无机填料为钛白粉、碳酸钙、滑石粉、凹凸棒土粉中的一种或几种。