CN106189618A - Ground non-skid coating and preparation method thereof - Google Patents
Ground non-skid coating and preparation method thereof Download PDFInfo
- Publication number
- CN106189618A CN106189618A CN201610571058.0A CN201610571058A CN106189618A CN 106189618 A CN106189618 A CN 106189618A CN 201610571058 A CN201610571058 A CN 201610571058A CN 106189618 A CN106189618 A CN 106189618A
- Authority
- CN
- China
- Prior art keywords
- ground
- content
- skid coating
- parts
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses ground non-skid coating and preparation method thereof, described ground non-skid coating is made up of following raw material: water, silicone acrylic emulsion, anti-wear agent, sclerosing agent, isopropanol, preservative, viscosity stabiliser and bentonite；In parts by weight, wherein, relative to 230 parts of silicone acrylic emulsions, the content of described water is 100 140 parts, the content of anti-wear agent is 30 70 parts, the content of sclerosing agent is 10 40 parts, the content of isopropanol is 30 60 parts, the content of preservative is 10 20 parts, the content of viscosity stabiliser is 30 70 parts, bentonitic content is 15 35 parts.It is good that ground disclosed by the invention non-skid coating has adhesive force, coarse and can be the most anti-skidding characteristic.
Description
Technical field
The present invention relates to coating prepare, be specifically related to ground non-skid coating and preparation method thereof.
Background technology
Coating can be coated in by different construction technologies to be protected or decorated body surface, and can be with coated article shape
Become to adhere to firmly, there is some strength, continuous print solid film.The thin film common name film formed, also known as paint film or coating.Coating
It is typically based on other preparations such as resin, oil, emulsion, cooperation pigment, additives, with formulated the mixing of organic solvent or water
Compound.Currently, having many uses of coating is general, has decoration functions based on coating to be coated on the colored drawing picture of body surface, base
The anticorrosion moisture barrier coatings etc. of body surface it is coated in the defencive function of coating.According to the purposes that coating is different, to coating
Performance has the requirement of different aspect and degree.When coating is for ground, the non-skid property in addition to beautiful decoration, to coating
There are more strict requirements.Currently, for ground especially outdoor ground coating through rainwater drench profit after, coating surface is the wettest
Sliding, it is easily caused when pedestrian walks and slips.
Summary of the invention
It is an object of the invention to provide ground non-skid coating and preparation method thereof, the paint adhesion prepared by the method
Good, coarse and can be the most anti-skidding.
To achieve these goals, the invention provides ground non-skid coating, be made up of following raw material: water, silicone acrylic emulsion,
Anti-wear agent, sclerosing agent, isopropanol, preservative, viscosity stabiliser and bentonite；In parts by weight, wherein, relative to 230 parts of silicon
Acrylic emulsion, the content of described water be 100-140 part, the content of anti-wear agent be 30-70 part, the content of sclerosing agent be 10-40 part, different
The content of propanol be 30-60 part, the content of preservative be 10-20 part, the content of viscosity stabiliser be 30-70 part, bentonitic
Content is 15-35 part.
Present invention also offers the preparation method of above-mentioned ground non-skid coating, the method includes: by 100-140 part water, 230
Part silicone acrylic emulsion and the mixing of 30-60 part isopropanol, obtained solution；Again by 30-70 part anti-wear agent, 10-40 part sclerosing agent, 10-20
Part preservative, 30-70 part viscosity stabiliser and 15-35 part bentonite add in above-mentioned solution, stirring mixing, prepare ground anti-skidding
Coating.
By technique scheme, the present invention by being first stirred mixing in reaction vessel by the feed liquid of each weight portion
Obtained solution, more each powder is added thereto mixing, under agitation it is in close contact between material, react generation association each other
Same-action, thus prepare ground non-skid coating.The method is a kind of with low cost, mild condition, environmental protection and simple to operate
Stirring means, it is good that prepared ground non-skid coating has adhesive force, coarse and can be the most anti-skidding characteristic.
Other features and advantages of the present invention will be described in detail in detailed description of the invention part subsequently.
Detailed description of the invention
Hereinafter the detailed description of the invention of the present invention is described in detail.It should be appreciated that described herein specifically
Embodiment is merely to illustrate and explains the present invention, is not limited to the present invention.
The invention provides ground non-skid coating, be made up of following raw material: be water, silicone acrylic emulsion, anti-wear agent, sclerosing agent, different
Propanol, preservative, viscosity stabiliser and bentonite；In parts by weight, wherein, relative to 230 parts of silicone acrylic emulsions, containing of described water
Amount is 100-140 part, the content of anti-wear agent is 30-70 part, the content of sclerosing agent is 10-40 part, the content of isopropanol is 30-60
Part, the content of preservative be 10-20 part, the content of viscosity stabiliser be 30-70 part, bentonitic content be 15-35 part.
In the non-skid coating of above-mentioned ground, the concrete kind of anti-wear agent used can select in wide scope, but is
The roughness of further raising ground non-skid coating, it is preferable that anti-wear agent is selected from fluvial sand, corundum, cement and rubber-plastic particle
In one or more.
In the non-skid coating of above-mentioned ground, the concrete kind of sclerosing agent used can select in wide scope, but is
The adhesive force of further raising ground non-skid coating, it is preferable that sclerosing agent is selected from vinyl triamine, diamino-cyclohexane, Asia
One or more in methyl bicycle hexane amine and m-xylene diamine.
In the non-skid coating of above-mentioned ground, the concrete kind of preservative used can select in wide scope, but is
The nonslip properties of further raising ground non-skid coating, it is preferable that preservative is selected from benzyl alcohol, phenethanol and chlorobutanol
In one or more.
In the non-skid coating of above-mentioned ground, the concrete kind of viscosity stabiliser used can select in wide scope, but
It is the effective nonslip properties in order to be further ensured that ground non-skid coating, it is preferable that viscosity stabiliser is selected from polyacrylamide, gathers
One or more in vinylpyrrolidone and polyethylene glycol oxide.
Present invention also offers the preparation method of a kind of above-mentioned ground non-skid coating, the method includes: by described water, silicon third
Emulsion and isopropanol mixing, obtained solution；Again described anti-wear agent, sclerosing agent, preservative, viscosity stabiliser and bentonite are added
Described solution, stirring mixing, prepare described ground non-skid coating.
In above-mentioned preparation method, the temperature of mixing can select, from the preparation of ground non-skid coating in wide scope
Consider on productivity and energy-conserving and environment-protective angle, it is preferable that the temperature of mixing is 10-35 DEG C.
In above-mentioned preparation method, speed and the time of stirring mixing can select in wide scope, but in order to enter
What one step improved ground non-skid coating prepares productivity, it is preferable that the speed of stirring mixing is 1500-2000rpm, and the time is 8-
18h。
Hereinafter will be described the present invention by embodiment.
Embodiment 1
At 10 DEG C, select a reaction vessel, by the raw material of following weight portion: 100 parts of water, 230 parts of silicone acrylic emulsions and 30
Part isopropanol is under the rotating speed of 1500rpm, and stirring mixes, obtained solution；Again by 30 parts of fluvial sand, 10 parts of vinyl triamine, 10 parts
Benzyl alcohol, 30 parts of polyacrylamides and 15 parts of bentonite add described solution, under the rotating speed of 1500rpm, and stirring mixing 18h,
Prepare ground non-skid coating A1.
Embodiment 2
At 35 DEG C, select a reaction vessel, by the raw material of following weight portion: 140 parts of water, 230 parts of silicone acrylic emulsions and 60
Part isopropanol is under the rotating speed of 2000rpm, and stirring mixes, obtained solution；Again by 70 parts of corundum, 40 parts of diamino-cyclohexane,
20 parts of phenethanol, 70 parts of polyvinylpyrrolidones and 35 parts of bentonite add described solution, under the rotating speed of 2000rpm, and stirring
Mixing 10h, prepares ground non-skid coating A2.
Embodiment 3
At 20 DEG C, select a reaction vessel, by the raw material of following weight portion: 120 parts of water, 230 parts of silicone acrylic emulsions and 50
Part isopropanol is under the rotating speed of 1800rpm, and stirring mixes, obtained solution；Again by 50 parts of cement, 25 parts of di-2-ethylhexylphosphine oxide hexamethylene
Amine, 15 parts of chlorobutanols, 50 parts of polyethylene glycol oxides and 20 parts of bentonite add described solution, under the rotating speed of 1800rpm, stir
Mix mixing 12h, prepare ground non-skid coating A3.
Embodiment 4
At 28 DEG C, select a reaction vessel, by the raw material of following weight portion: 110 parts of water, 230 parts of silicone acrylic emulsions and 35
Part isopropanol is under the rotating speed of 1600rpm, and stirring mixes, obtained solution；Again by 40 parts of rubber-plastic particles, 25 parts of m-xylene diamines,
17 parts of benzyl alcohol, 36 parts of polyvinylpyrrolidones and 31 parts of bentonite add described solution, under the rotating speed of 1600rpm, and stirring
Mixing 14h, prepares ground non-skid coating A4.
Comparative example 1
Coating B1 is prepared relative to embodiment 1, except that, the consumption adding fluvial sand is 10 weight portions, vinyl three
The consumption of amine is 5 weight portions.
Comparative example 2
Coating B2 is prepared relative to embodiment 2, except that, the consumption adding phenethanol is 5 weight portions, polyethylene pyrrole
The consumption of pyrrolidone is 15 weight portions.
Detection example 1
The coating preparing above-described embodiment and comparative example uses portable pendulum tester to measure coefficient of sliding resistance, and concrete outcome is shown in Table 1.
Detection example 2
The coating preparing above-described embodiment and comparative example uses paint film adhesion algoscopy, marks according to GB1720-1979
Standard, detects relevant parameter, and concrete outcome is shown in Table 1.
Table 1
| A1 | A2 | A3 | A4 | B1 | B2 | |
| Coating state in a reservoir | Without caking | Without caking | Without caking | Without caking | Caking | Caking |
| Mohs' hardness | 6 | 7 | 7 | 6 | 4 | 4 |
| Skid resistance, BPN value | 50 | 55 | 45 | 50 | 30 | 35 |
| Paint Adhesion (method of drawing a circle) | 3 | 3 | 3 | 2 | 5 | 6 |
Wherein, BPN represents portable pendulum tester, is used for representing coefficient of sliding resistance, is the evaluation index of antiskid performance, and BPN value answers 45,
Skidproof effect can be reached；The non-skid coating Mohs' hardness that GB1720-1979 standard specifies answers 6, tack (method of drawing a circle)
Answer 4；By above-mentioned detection example, the ground non-skid coating that the present invention provides meets GB1720-1979 standard, has attachment
Power is good, coarse and can be the most anti-skidding effect, and preparation method is simple.
The preferred embodiment of the present invention described in detail above, but, the present invention is not limited in above-mentioned embodiment
Detail, in the technology concept of the present invention, technical scheme can be carried out multiple simple variant, this
A little simple variant belong to protection scope of the present invention.
It is further to note that each the concrete technical characteristic described in above-mentioned detailed description of the invention, at not lance
In the case of shield, can be combined by any suitable means, in order to avoid unnecessary repetition, the present invention to various can
The compound mode of energy illustrates the most separately.
Additionally, combination in any can also be carried out between the various different embodiment of the present invention, as long as it is without prejudice to this
The thought of invention, by the raw material of each weight portion being stirred in reaction vessel mixing, the tightst between material
Contact, react generation synergism each other, thus obtains ground non-skid coating, and it is public that it should be considered as present invention institute equally
The content opened.
Claims (8)
1. a ground non-skid coating, it is characterised in that be made up of following raw material: water, silicone acrylic emulsion, anti-wear agent, sclerosing agent, different
Propanol, preservative, viscosity stabiliser and bentonite；
In parts by weight, wherein, relative to 230 parts of silicone acrylic emulsions, the content of described water is 100-140 part, described anti-wear agent
Content is 30-70 part, and the content of described sclerosing agent is 10-40 part, and the content of described isopropanol is 30-60 part, described preservative
Content be 10-20 part, the content of described viscosity stabiliser is 30-70 part, and described bentonitic content is 15-35 part.
Ground the most according to claim 1 non-skid coating, wherein, described anti-wear agent is selected from fluvial sand, corundum, cement and rubber
Mould one or more in granule.
Ground the most according to claim 1 non-skid coating, wherein, described sclerosing agent is selected from vinyl triamine, diamino basic ring
One or more in hexane, di-2-ethylhexylphosphine oxide hexamethylene alkanamine and m-xylene diamine.
Ground the most according to claim 1 non-skid coating, wherein, described preservative is selected from benzyl alcohol, phenethanol and trichlorine
One or more in the tert-butyl alcohol.
Ground the most according to claim 1 non-skid coating, wherein, described viscosity stabiliser is selected from polyacrylamide, poly-second
One or more in alkene pyrrolidone and polyethylene glycol oxide.
6. the preparation method of the ground non-skid coating as described in any one in claim 1-5, it is characterised in that described
Preparation method includes: described water, silicone acrylic emulsion and isopropanol are mixed, obtained solution；Again by described anti-wear agent, sclerosing agent, prevent
Rotten agent, viscosity stabiliser and bentonite add described solution, stirring mixing, prepare described ground non-skid coating.
The preparation method of ground the most according to claim 6 non-skid coating, wherein, the temperature of described mixing is 10-35 DEG C,
In described mixing, using the mode of stirring to mix, the speed of described stirring is 1500-2000rpm.
The preparation method of ground the most according to claim 6 non-skid coating, wherein, the speed of described stirring mixing is
1500-2000rpm, the time of described stirring mixing is 8-18h.