CN105400244B - A kind of waterborne inorganic einc-rich primer and preparation method - Google Patents

A kind of waterborne inorganic einc-rich primer and preparation method Download PDF

Info

Publication number
CN105400244B
CN105400244B CN201510963889.8A CN201510963889A CN105400244B CN 105400244 B CN105400244 B CN 105400244B CN 201510963889 A CN201510963889 A CN 201510963889A CN 105400244 B CN105400244 B CN 105400244B
Authority
CN
China
Prior art keywords
component
parts
rich
zinc
raw material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201510963889.8A
Other languages
Chinese (zh)
Other versions
CN105400244A (en
Inventor
刘嘉东
王荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Yunhu New Material Technology Co.,Ltd.
Original Assignee
WUXI TAIHU ANTI-CORROSION MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUXI TAIHU ANTI-CORROSION MATERIAL Co Ltd filed Critical WUXI TAIHU ANTI-CORROSION MATERIAL Co Ltd
Priority to CN201510963889.8A priority Critical patent/CN105400244B/en
Publication of CN105400244A publication Critical patent/CN105400244A/en
Application granted granted Critical
Publication of CN105400244B publication Critical patent/CN105400244B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention provides a kind of waterborne inorganic einc-rich primer and preparation method, wherein waterborne inorganic einc-rich primer, including first component and second component;The raw material that the first component includes following parts by weight is constituted:60~95 parts of high mode aqueous inorganic zinc-rich coating resins, 1~20 part of water-compatible amino resin, 0.1~1 part of defoamer;The raw material that the second component includes following parts by weight is constituted:40~90 parts of zinc powder, 10~60 parts of filler, 0.5~10 part of anti-settling agent, wherein filler is nano-calcination-kaolinite, by adding nano-calcination-kaolinite, the anticorrosive property of paint film can be greatly increased, the fine and close paint film formed is participated in by nano-calcination-kaolinite simultaneously, road is painted under energy direct spraying, will not produce bubble and pin hole.Solving traditional waterborne inorganic einc-rich primer spraying intermediate coat or finish paint well needs to be previously added diluent spraying, the problem of increasing VOC emission.

Description

A kind of waterborne inorganic einc-rich primer and preparation method
Technical field
The present invention relates to technical field of fine, more particularly to a kind of waterborne inorganic einc-rich primer and preparation method.
Background technology
Aqueous inorganic zinc-enriched coating is one of current service life most long anticorrosive metal paint, because itself environmental protection is special Property and excellent Corrosion Protection, extensive use is achieved in the heavy antisepsis such as air and ocean field.Traditional aqueous inorganic zinc-rich Primed surface is present compared with concrete dynamic modulus, by finish paint to be coated or transition zone paint organic solvent diluting, and spraying closing, allows surface in advance Vesicle overflows, disappeared.Which increase the organic solvent emission amount of Bulk coat, it is difficult to reaches real environmental protection.
The content of the invention
The invention provides a kind of waterborne inorganic einc-rich primer and preparation method, wherein waterborne inorganic einc-rich primer surface is caused It is close, it is not necessary to close, in construction can direct spraying epoxy-based lacquers, polyurethane paint, vinyl paint etc., pin hole will not be produced so that Realize real environmental protection.The technical scheme that the present invention is provided is as follows:
A kind of waterborne inorganic einc-rich primer, including first component and second component;The first component includes the original of following parts by weight Material composition:60~95 parts of high mode aqueous inorganic zinc-rich coating resins, 1~20 part of water-compatible amino resin, 0.1~1 part of defoamer;Institute Raw material of the second component including following parts by weight is stated to constitute:40~90 parts of zinc powder, 10~60 parts of filler, 0.5~10 part of anti-settling agent.
Above-mentioned waterborne inorganic einc-rich primer, wherein, including first component and second component;The first component includes following weight The raw material composition of part:89.5~94.2 parts of high mode aqueous inorganic zinc-rich coating resins, 5~10 parts of water-compatible amino resin, defoamer 0.2~0.5 part;The raw material that the second component includes following parts by weight is constituted:It is 60~80 parts of zinc powder, 20~40 parts of filler, anti-settling 2~5 parts of agent.
Above-mentioned waterborne inorganic einc-rich primer, wherein, including first component and second component;The first component includes following weight The raw material composition of part:92 parts of high mode aqueous inorganic zinc-rich coating resins, 7 parts of water-compatible amino resin, 0.3 part of defoamer;The second The raw material that component includes following parts by weight is constituted:70 parts of zinc powder, 30 parts of filler, 3 parts of anti-settling agent.
Above-mentioned waterborne inorganic einc-rich primer, wherein, the mass ratio of the first component and second component is 3:7.
Above-mentioned waterborne inorganic einc-rich primer, wherein, the defoamer is polyether siloxane copolymer, and the filler is to receive Rice calcined kaolin, the anti-settling agent is modified manometer silicon dioxide.
Above-mentioned waterborne inorganic einc-rich primer, wherein, the model E717 of the high mode aqueous inorganic zinc-rich coating resins Or E707 or E777-3.
A kind of another side of the present invention, preparation method of waterborne inorganic einc-rich primer comprises the following steps:
Water-compatible amino resin is added to be well mixed in high mode aqueous inorganic zinc-rich coating resins and obtains the first mixture;
Defoamer is added in the first mixture and is uniformly mixing to obtain first component;
Zinc powder, filler and anti-settling agent are uniformly mixing to obtain component B;
First component is well mixed with component B and obtains waterborne inorganic einc-rich primer.
Above-mentioned preparation method, wherein, it is described to add to water-compatible amino resin in high mode aqueous inorganic zinc-rich coating resins It is well mixed the step of obtain the first mixture in, by water-compatible amino resin add in high mode aqueous inorganic zinc-rich coating resins with 500 revs/min of stirrings obtain the first mixture in 20-30 minutes.
Above-mentioned preparation method, wherein, described defoamer is added in the first mixture is uniformly mixing to obtain first component The step of in, under conditions of 800 revs/min, disperse 10-15 minutes, obtain first component.
Above-mentioned preparation method, wherein, described be well mixed first component with component B obtains waterborne inorganic einc-rich primer The step of in, wherein the mass ratio of first component and second component is 3:7.
The invention provides a kind of waterborne inorganic einc-rich primer and preparation method, wherein waterborne inorganic einc-rich primer, including First component and second component;The raw material that the first component includes following parts by weight is constituted:High mode aqueous inorganic zinc-rich coating resins 60 ~95 parts, 1~20 part of water-compatible amino resin, 0.1~1 part of defoamer;The raw material that the second component includes following parts by weight is constituted: 40~90 parts of zinc powder, 10~60 parts of filler, 0.5~10 part of anti-settling agent, wherein filler are nano-calcination-kaolinite, are received by addition Rice calcined kaolin, can greatly increase the anticorrosive property of paint film, while the fine and close paint for participating in being formed by nano-calcination-kaolinite Road is painted under film, energy direct spraying, and traditional waterborne inorganic einc-rich primer spraying intermediate coat or finish paint are solved well to be needed in advance The problem of first adding diluent spraying, increase VOC emission.
Embodiment
In the following description, a large amount of concrete details are given to provide more thorough understanding of the invention.So And, it is obvious to the skilled person that the present invention can be able to without one or more of these details Implement.In other examples, in order to avoid obscuring with the present invention, do not enter for some technical characteristics well known in the art Row description.
In order to thoroughly understand the present invention, detailed step and detailed structure will be proposed in following description, so as to Explain technical scheme.Presently preferred embodiments of the present invention is described in detail as follows, but in addition to these detailed descriptions, this Invention can also have other embodiment.
Embodiment 1, a kind of waterborne inorganic einc-rich primer, including first component and second component;First component includes following parts by weight Raw material composition:60 parts of high mode aqueous inorganic zinc-rich coating resins, 1 part of water-compatible amino resin, 0.1 part of defoamer;Second component bag Include the raw material composition of following parts by weight:40 parts of zinc powder, 10 parts of filler, 0.5 part of anti-settling agent, wherein first component and the quality of second component Than for 3:7.
Embodiment 2, a kind of waterborne inorganic einc-rich primer, including first component and second component;First component includes following parts by weight Raw material composition:95 parts of high mode aqueous inorganic zinc-rich coating resins, 20 parts of water-compatible amino resin, 1 part of defoamer;Second component includes The raw material composition of following parts by weight:90 parts of zinc powder, 60 parts of filler, 10 parts of anti-settling agent, wherein first component and the mass ratio of second component For 3:7.
Embodiment 3, a kind of waterborne inorganic einc-rich primer, including first component and second component;First component includes following parts by weight Raw material composition:94.2 parts of high mode aqueous inorganic zinc-rich coating resins, 10 parts of water-compatible amino resin, 0.5 part of defoamer;Second component Raw material composition including following parts by weight:80 parts of zinc powder, 40 parts of filler, 5 parts of anti-settling agent, wherein first component and the quality of second component Than for 3:7.
Embodiment 4, a kind of waterborne inorganic einc-rich primer, including first component and second component;First component includes following parts by weight Raw material composition:89.5 parts of high mode aqueous inorganic zinc-rich coating resins, 5 parts of water-compatible amino resin, 0.2 part of defoamer;Second component Raw material composition including following parts by weight:60 parts of zinc powder, 20 parts of filler, 2 parts of anti-settling agent, wherein first component and the quality of second component Than for 3:7.
Embodiment 5, a kind of waterborne inorganic einc-rich primer, including first component and second component;First component includes following parts by weight Raw material composition:92 parts of high mode aqueous inorganic zinc-rich coating resins, 7 parts of water-compatible amino resin, 0.3 part of defoamer;The second group Dividing includes the raw material composition of following parts by weight:70 parts of zinc powder, 30 parts of filler, 3 parts of anti-settling agent, wherein first component and the matter of second component Amount is than being 3:7.
In the present invention, defoamer is polyether siloxane copolymer, can reach more preferable defoaming effect, and filler is nanometer Calcined kaolin, by adding nano-calcination-kaolinite, can greatly increase the anticorrosive property of paint film, while calcining kaolinite by nanometer Soil participates in road under the fine and close paint film formed, energy direct spraying and painted, and traditional waterborne inorganic einc-rich primer spray is solved well Applying intermediate coat or finish paint needs to be previously added diluent spraying, and the problem of increasing VOC emission, anti-settling agent is modified nano-silica Silicon, can play more preferable result of prevention, the model E717 or E707 or E777-3 of high mode aqueous inorganic zinc-rich coating resins.
A kind of another side of the present invention, preparation method of waterborne inorganic einc-rich primer comprises the following steps:
Step S1:Water-compatible amino resin is added to be well mixed in high mode aqueous inorganic zinc-rich coating resins and obtains first and mixes Compound, wherein, water-compatible amino resin is added in high mode aqueous inorganic zinc-rich coating resins with 500 revs/min of 20-30 points of stirrings Clock obtains the first mixture;
Step S2:Defoamer is added in the first mixture and is uniformly mixing to obtain first component, wherein, at 800 revs/min Under conditions of, disperse 10-15 minutes, obtain first component;
Step S3:Zinc powder, filler and anti-settling agent are uniformly mixing to obtain component B;
Step S4:First component is well mixed with component B and obtains waterborne inorganic einc-rich primer, wherein, first component and second group The mass ratio divided is 3:7.
The influence situation enumerated below using different fillers to properties of product is as shown in table 1;
Table 1
Filler Salt water resistance (30d) Salt spray resistance Matching
Powdered whiting It is good 550h bubbles There is pin hole
Talcum powder It is good 600h bubbles A large amount of pin holes
Blanc fixe It is good 580h bubbles A small amount of pin hole
Nano-calcination-kaolinite It is excellent 1500h bubbles It is pin-free
In table 1, matching is latter 7 days from doing in spray-applied primer, if has the appearance of pin hole, pin hole such as occurs to spraying Common epoxy micaceous iron intermediate coat has an impact, from table 1 it follows that can be realized in spray-applied primer using nano-calcination-kaolinite After dry after 7 days will not pin hole phenomenon, and the waterborne inorganic einc-rich primer of the present invention has excellent salt spray resistance and salt tolerant It is aqueous, there is obvious advantage compared with other fillers.Specially nano-calcination-kaolinite is because of its unique surface texture, particle More tiny, the atomicity increase of particle surface, the deficiency and high surface energy of Atomic coordinate make these atoms have high activity, It is easy to be combined with other atoms, paint film compares other fillers, very fine and close, so matching and salt fog resistance are very excellent.
Specific implementation of the use of zinc powder consumption and nano-calcination-kaolinite to coating antiseptic performance impact is enumerated below Example, as shown in table 2.
Table 2
W (Zn)/% W (nano kaoline) % Resistance to salt water Salt fog resistance
20-40 60-80 The a small amount of bubblings of 45d 300 hours a large amount of rust spots
50 50 The a small amount of bubblings of 50d 800 hours a small amount of rust spots
60-80 20-40 The a small amount of bubblings of 70d Bubble within 1500 hours
90-100 10-20 The a small amount of bubblings of 35d Bubble within 1000 hours
100 0 The a small amount of bubblings of 30d Bubble within 720 hours
From table 2 it can be seen that when zinc powder is less than 40%, the salt fog resistance of coating is very poor, and zinc content is excessive, is more than When 90%, paint film resistance to salt water is weaker.20-40% nano kaoline is added, salt water resistance and salt fog resistance are optimal.
Total described, the invention provides a kind of waterborne inorganic einc-rich primer and preparation method, wherein aqueous inorganic zinc-rich Priming paint, including first component and second component;The raw material that the first component includes following parts by weight is constituted:High mode aqueous inorganic zinc-rich 60~95 parts of coating resins, 1~20 part of water-compatible amino resin, 0.1~1 part of defoamer;The second component includes following parts by weight Raw material is constituted:40~90 parts of zinc powder, 10~60 parts of filler, 0.5~10 part of anti-settling agent, wherein filler are nano-calcination-kaolinite, By adding nano-calcination-kaolinite, the anticorrosive property of paint film can be greatly increased, while being participated in being formed by nano-calcination-kaolinite Fine and close paint film, can paint in road under direct spraying, solve well traditional waterborne inorganic einc-rich primer spraying intermediate coat or The problem of finish paint needs to be previously added diluent spraying, increase VOC emission, the waterborne inorganic einc-rich primer, excellent combination property, Have a wide range of applications.
Presently preferred embodiments of the present invention is described above.It is to be appreciated that the invention is not limited in above-mentioned Particular implementation, wherein the equipment and structure be not described in detail to the greatest extent are construed as giving reality with the common mode in this area Apply;Any those skilled in the art, without departing from the scope of the technical proposal of the invention, all using the disclosure above Methods and techniques content make many possible variations and modification to technical solution of the present invention, or be revised as equivalent variations etc. Embodiment is imitated, this has no effect on the substantive content of the present invention.Therefore, every content without departing from technical solution of the present invention, foundation The technical spirit of the present invention still falls within the present invention to any simple modifications, equivalents, and modifications made for any of the above embodiments In the range of technical scheme protection.

Claims (6)

1. a kind of waterborne inorganic einc-rich primer, it is characterised in that including first component and second component;The first component includes following heavy Measure the raw material composition of part:60~95 parts of high mode aqueous inorganic zinc-rich coating resins, 1~20 part of water-compatible amino resin, defoamer 0.1 ~1 part;The raw material that the second component includes following parts by weight is constituted:40~90 parts of zinc powder, 10~60 parts of filler, anti-settling agent 0.5 ~10 parts, the mass ratio of the first component and second component is 3:7, the defoamer is polyether siloxane copolymer, the filler For nano-calcination-kaolinite, the anti-settling agent is modified manometer silicon dioxide;The high mode aqueous inorganic zinc-rich coating resins Model E717 or E707 or E777-3.
2. a kind of waterborne inorganic einc-rich primer as claimed in claim 1, it is characterised in that including first component and second component;Institute Raw material of the first component including following parts by weight is stated to constitute:89.5~94.2 parts of high mode aqueous inorganic zinc-rich coating resins, aqueous ammonia 5~10 parts of base resin, 0.2~0.5 part of defoamer;The raw material that the second component includes following parts by weight is constituted:Zinc powder 60~80 Part, 20~40 parts of filler, 2~5 parts of anti-settling agent.
3. a kind of waterborne inorganic einc-rich primer as claimed in claim 1, it is characterised in that including first component and second component;Institute Raw material of the first component including following parts by weight is stated to constitute:92 parts of high mode aqueous inorganic zinc-rich coating resins, water-compatible amino resin 7 Part, 0.3 part of defoamer;The raw material that the second component includes following parts by weight is constituted:70 parts of zinc powder, 30 parts of filler, anti-settling agent 3 Part.
4. a kind of preparation method of waterborne inorganic einc-rich primer as claimed in claim 3, it is characterised in that including following step Suddenly:
Water-compatible amino resin is added to be well mixed in high mode aqueous inorganic zinc-rich coating resins and obtains the first mixture;
Defoamer is added in the first mixture and is uniformly mixing to obtain first component;
Zinc powder, filler and anti-settling agent are uniformly mixing to obtain component B;
First component is well mixed with component B and obtains waterborne zinc-rich primer.
5. the preparation method of waterborne inorganic einc-rich primer as claimed in claim 4, it is characterised in that:It is described by aqueous amino tree Fat is added in high mode aqueous inorganic zinc-rich coating resins and is well mixed in the step of obtaining the first mixture, by water-compatible amino resin Add in high mode aqueous inorganic zinc-rich coating resins and to obtain the first mixture within 20-30 minutes with 500 revs/min of stirrings.
6. the preparation method of waterborne inorganic einc-rich primer as claimed in claim 5, it is characterised in that:It is described to add defoamer In the step of first component is uniformly mixing to obtain into the first mixture, under conditions of 800 revs/min, disperse 10-15 minutes, Obtain first component.
CN201510963889.8A 2015-12-21 2015-12-21 A kind of waterborne inorganic einc-rich primer and preparation method Active CN105400244B (en)