CN106189579A - A kind of aqueous, environmental protective primary coat paint - Google Patents
A kind of aqueous, environmental protective primary coat paint Download PDFInfo
- Publication number
- CN106189579A CN106189579A CN201610535375.7A CN201610535375A CN106189579A CN 106189579 A CN106189579 A CN 106189579A CN 201610535375 A CN201610535375 A CN 201610535375A CN 106189579 A CN106189579 A CN 106189579A
- Authority
- CN
- China
- Prior art keywords
- aqueous
- parts
- water
- primary coat
- coat paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of aqueous, environmental protective primary coat paint, it is prepared from by the component of following quality proportioning: water-base resin 440 ~ 450 parts, talc slurry 130 ~ 150 parts, deionization pure water 360 ~ 370 parts, aqueous dispersion 4 ~ 5 parts, aqueous wetting agent 4 ~ 5 parts, aqueous levelling agent 4 ~ 5 parts, aqueous defoamer 3 ~ 4 parts, aqueous drier 15 ~ 18 parts, aqueous adhesive force accelerator 8 ~ 10 parts, aqueous nertralizer 2 ~ 3 parts, water-based pigment colour paste 15 ~ 20 parts.Water-base resin is made up of water-borne acrylic resin and aqueous amino crosslinked resin, and mass ratio is 350:90 ~ 100.Aqueous, environmental protective primary coat paint safety and environmental protection of the present invention, has good levelability, abrasion resistance, adhesive ability and pliability, it is easy to processing, it is adaptable to the roller coat of aluminum alloy coiled materials, metal and steel plate is printed, and has higher use value.
Description
Technical field
The present invention relates to technical field of coatings, particularly relate to a kind of aqueous, environmental protective primary coat paint.
Background technology
Coating is that one is coated on body surface, can be formed under certain condition firm attachment, the liquid of continuous film or
Solid material, primarily to protection, decorative product or make product have insulation, the special role such as antirust, heat-resisting, thus promote
The value of product.
Coating can be divided into oil paint, water paint and powdery paints.
Oil paint contains the volatile organic matter such as benzene, toluene (VOCs), has stronger toxicity and strong impulse gas
Taste, is harmful to the health of human body.Containing combustibles such as benzene, toluene, gasoline in oil paint, produce, circulate and store needs especially
Process, the most easily cause security incident.
Water paint is with water as solvent, containing minimal amount of VOCs, does not produce penetrating odor, is that nonpoisonous and tasteless environmental protection is produced
Product.Water paint is nonflammable, and safety is high, greatly reduces production, the expense circulating and storing.Additionally, water paint also has resistance to
Mill, resistance to flavescence, ageing-resistant, the advantage of fast drying, be developing progressively main product, have higher market value.
At present, some water paints present on market have bad dispersibility, surface tension is big, adhesive force is bad and resistance to water
The shortcoming of difference, these all govern using and developing of water paint.
Summary of the invention
It is an object of the invention to overcome the deficiencies in the prior art, it is provided that a kind of aqueous, environmental protective primary coat paint, improve aqueous ring
Guarantee the minimum japanning levelability, abrasion resistance, adhesive force, pliability so that it is be applicable to aluminum alloy coiled materials, metal and the roller of steel plate
It is coated with and prints.
In order to achieve the above object, the technical solution used in the present invention is: a kind of aqueous basecoat paint, by following quality proportioning
Component be prepared from: water-base resin 440 ~ 450 parts, talc slurry 130 ~ 150 parts, deionization pure water 360 ~ 370 parts, aqueous
Dispersant 4 ~ 5 parts, aqueous wetting agent 4 ~ 5 parts, aqueous levelling agent 4 ~ 5 parts, aqueous defoamer 3 ~ 4 parts；Aqueous drier 15 ~ 18
Part, aqueous adhesive force accelerator 8 ~ 10 parts, aqueous nertralizer 2 ~ 3 parts, water-based pigment colour paste 15 ~ 20 parts.
Further, described water-base resin is made up of water-borne acrylic resin and aqueous amino crosslinked resin, aqueous acrylamide
Acid resin is 350:90 ~ 100 with the mass ratio of aqueous amino crosslinked resin.
Further, described water-borne acrylic resin is the 3322-B that Bang Shi chemical industry Industrial Co., Ltd. of Yingde City produces
Type, solid content is 50 ± 2%, acid value≤80, and viscosity is 2000 ~ 3500Pa s(25 DEG C), pH value is 7 ~ 8.
Further, described talc slurry solid content is 48 ~ 52%, and Pulvis Talci fineness is 6000 mesh.
Further, the pure electrical conductivity of water of described deionization is 10 ~ 20 μ s/cm.
Further, described aqueous dispersion, aqueous wetting agent, aqueous levelling agent, aqueous defoamer, aqueous drier,
Aqueous adhesive force accelerator is good with the described water-base resin compatibility, is not likely to produce muddiness and shrinkage cavity.
Further, described aqueous nertralizer is monoethanolamine, purity > 95%.
By above-mentioned weight portion raw material, mix and blend 25 ~ 30min, fully dispersed after, filter with 300 mesh filter screens, to obtain final product.
Compared with prior art, the invention has the beneficial effects as follows: with water-borne acrylic resin and aqueous amino crosslinked resin
Mixed system is base material, and Pulvis Talci is filler, adds aqueous dispersion, aqueous levelling agent, aqueous defoamer, aqueous adhesive force rush
Enter the aqueous basecoat paint that the auxiliary agents such as agent are prepared from, there is good levelability, abrasion resistance, adhesive ability and pliability, easily
In processing；And this aqueous basecoat paint has feature nonpoisonous and tasteless, nonflammable, safety and environmental protection；It is applicable to aluminum alloy coiled materials, gold
Belong to and the roller coat of steel plate is printed；There is higher use value.
Detailed description of the invention
Making the present invention further and explanation below according to specific embodiment, the following stated is only currently preferred reality
Executing mode, embodiments of the present invention are not limited to this.
In embodiment, water-borne acrylic resin used is the 3322-B that Bang Shi chemical industry Industrial Co., Ltd. of Yingde City produces
Type.Raw materials in embodiment, unless otherwise indicated, is commercially available industrial goods.
Embodiment 1
Weighing water-borne acrylic resin 350 parts, aqueous amino acid crosslinks resin 90 parts, solid content is the talc slurry 130 of 48%
Part, deionization pure water 360 parts, aqueous dispersion 4 parts, aqueous wetting agent 4 parts, aqueous levelling agent 4 parts, aqueous defoamer 3 parts；
Aqueous drier 15 parts, aqueous adhesive force accelerator 8 parts, monoethanolamine 2 parts, water-based pigment colour paste 15 parts.
By above-mentioned weight portion raw material, mix and blend 25min, fully dispersed after, filter with 300 mesh filter screens, to obtain final product.
Embodiment 2
Weighing water-borne acrylic resin 350 parts, aqueous amino acid crosslinks resin 95 parts, solid content is the talc slurry 140 of 50%
Part, deionization pure water 365 parts, aqueous dispersion 4.5 parts, aqueous wetting agent 4.5 parts, aqueous levelling agent 4.5 parts, aqueous froth breaking
Agent 3.5 parts；Aqueous drier 16 parts, aqueous adhesive force accelerator 9 parts, monoethanolamine 2.5 parts, water-based pigment colour paste 18 parts.
By above-mentioned weight portion raw material, mix and blend 30min, fully dispersed after, filter with 300 mesh filter screens, to obtain final product.
Embodiment 3
Weighing water-borne acrylic resin 350 parts, aqueous amino acid crosslinks resin 100 parts, solid content is the talc slurry 150 of 52%
Part, deionization pure water 370 parts, aqueous dispersion 5 parts, aqueous wetting agent 5 parts, aqueous levelling agent 5 parts, aqueous defoamer 4 parts；
Aqueous drier 18 parts, aqueous adhesive force accelerator 10 parts, monoethanolamine 3 parts, water-based pigment colour paste 20 parts.
By above-mentioned weight portion raw material, mix and blend 30min, fully dispersed after, filter with 300 mesh filter screens, to obtain final product.
Embodiment 4
Weighing water-borne acrylic resin 350 parts, aqueous amino acid crosslinks resin 90 parts, solid content is the talc slurry 140 of 50%
Part, deionization pure water 365 parts, aqueous dispersion 5 parts, aqueous wetting agent 5 parts, aqueous levelling agent 3 parts, aqueous defoamer 4 parts；
Aqueous drier 15 parts, aqueous adhesive force accelerator 10 parts, monoethanolamine 2 parts, water-based pigment colour paste 18 parts.
By above-mentioned weight portion raw material, mix and blend 30min, fully dispersed after, filter with 300 mesh filter screens, to obtain final product.
By the technical scheme in above example, the present invention is carried out clear, complete description, it is clear that described reality
Execute embodiment rather than whole embodiments that example is a present invention part.Based on the embodiment in the present invention, this area is common
The every other embodiment that technical staff is obtained under not making creative work premise, broadly falls into the model of present invention protection
Enclose.
Claims (6)
1. an aqueous, environmental protective primary coat paint, is characterized in that, the component of following quality proportioning be prepared from: water-base resin 440 ~
450 parts, talc slurry 130 ~ 150 parts, deionization pure water 360 ~ 370 parts, aqueous dispersion 4 ~ 5 parts, aqueous wetting agent 4 ~ 5
Part, aqueous levelling agent 4 ~ 5 parts, aqueous defoamer 3 ~ 4 parts, aqueous drier 15 ~ 18 parts, aqueous adhesive force accelerator 8 ~ 10 parts,
Aqueous nertralizer 2 ~ 3 parts, water-based pigment colour paste 15 ~ 20 parts.
Aqueous, environmental protective primary coat paint the most according to claim 1, is characterized in that, described water-base resin is by water-borne acrylic resin
Forming with aqueous amino crosslinked resin, water-borne acrylic resin is 350:90 ~ 100 with the mass ratio of aqueous amino crosslinked resin.
Aqueous, environmental protective primary coat paint the most according to claim 1 and 2, is characterized in that, described water-borne acrylic resin is Germany and Britain
The 3322-B type that Bang Shi chemical industry Industrial Co., Ltd. of city produces.
Aqueous, environmental protective primary coat paint the most according to claim 1, is characterized in that, described talc slurry solid content is 48 ~ 52%,
Pulvis Talci fineness is 6000 mesh.
Aqueous, environmental protective primary coat paint the most according to claim 1, is characterized in that, the pure electrical conductivity of water of described deionization is 10
~20μs/cm。
Aqueous, environmental protective primary coat paint the most according to claim 1, is characterized in that, described aqueous nertralizer is monoethanolamine, pure
Degree > 95%.