CN106590266A - Water-proof and corrosion-resistant waterborne coating for wine bottle and preparation method of water-proof and corrosion-resistant waterborne coating - Google Patents
Water-proof and corrosion-resistant waterborne coating for wine bottle and preparation method of water-proof and corrosion-resistant waterborne coating Download PDFInfo
- Publication number
- CN106590266A CN106590266A CN201710063517.9A CN201710063517A CN106590266A CN 106590266 A CN106590266 A CN 106590266A CN 201710063517 A CN201710063517 A CN 201710063517A CN 106590266 A CN106590266 A CN 106590266A
- Authority
- CN
- China
- Prior art keywords
- parts
- corrosion
- agent
- water
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a water-proof and corrosion-resistant waterborne coating for a wine bottle and a preparation method of the water-proof and corrosion-resistant waterborne coating and relates to the technical field of coating production and processing. The preparation method comprises the following steps: an acrylic emulsion, rutile type nanometer titania, modified kaolin, polyurethane, a dispersing agent, a wetting agent, a defoamer, a leveling agent, a foam inhibitor, color paste, filler and a surfactant are added to a reactor and are stirred and mixed for 1 h at 45 DEG C and the rotating speed controlled at 1000 r/min; an antibacterial agent, a coalescing agent, mica powder, zirconium phosphate, 2-mercaptobenzimidazole, iron (III) trifluoroacetylacetonate, aluminum triphosphate, rhizoma gastrodiae extract and distilled water are added to the reactor sequentially, and the substances are stirred and mixed for 0.5 h at 45 DEG C and the rotating speed controlled at 1000 r/min. The coating is a special environment-friendly waterborne coating for the wine bottle, not only can meet the conventional requirements for coating the wine bottle, but also is harmless to the environment, and has higher waterproofness and corrosion resistance.
Description
Technical field
The present invention relates to a kind of waterproof anti-corrosion bottle water paint and preparation method thereof, is related to coating material production processing skill
Art field.
Background technology
With the continuous improvement of people's living standard, the consumption figure of bottled wine product has also obtained greatly increasing, tradition
Bottle application mainly use solvent based coating, these solvent based coatings can cause one during coating and follow-up use
Determine the environmental pollution of degree.Meanwhile, the water resistance of this coating is poor, and decay resistance is relatively low, so that consumer exists
A series of inconvenience can be caused using process.
The content of the invention
In order to overcome the above-mentioned technical problem in the presence of prior art, it is an object of the invention to provide a kind of waterproof is resistance to
Corrosion bottle water paint and preparation method thereof.
For achieving the above object, present invention employs technical scheme below：
A kind of waterproof anti-corrosion bottle water paint, is made up of the raw material of following weight portion：
Acrylic emulsion 30-45 parts,
Rutile type nano titanic oxide 10-12 parts,
Modified kaolin 11-15 parts,
Polyurethane 10-13 parts,
Dispersant 9-15 parts,
Wetting agent 10-14 parts,
Defoamer 8.5-15 parts,
Levelling agent 10-15 parts,
Foam inhibitor 7-15 parts,
Mill base 10-16 parts,
Filler 11.50-15 parts,
Surfactant 10-17 parts,
Antibacterial 10-15 parts,
Film former help 10-12 parts,
Mica powder 10.5-15 parts,
Zirconium phosphate 10-14 parts,
2- mercapto benzimidazole 6-15 parts,
Trifluoroacetylacetone (TFA) ferrum 10-17 parts,
Aluminium triphosphate 9.5-15 parts,
Rhizoma Gastrodiae extract 10-16 parts,
Distilled water 20-25 parts.
Preferably, a kind of waterproof anti-corrosion bottle water paint of the invention, is made up of the raw material of following weight portion：
35 parts of acrylic emulsion,
10 parts of rutile type nano titanic oxide,
12 parts of modified kaolin,
13 parts of polyurethane,
14 parts of dispersant,
11 parts of wetting agent,
10 parts of defoamer,
12.5 parts of levelling agent,
13 parts of foam inhibitor,
10 parts of mill base,
13 parts of filler,
11 parts of surfactant,
14 parts of antibacterial,
Film former help 11 parts,
14 parts of mica powder,
11.5 parts of zirconium phosphate,
7 parts of 2- mercaptos benzimidazole,
13.5 parts of trifluoroacetylacetone (TFA) ferrum,
14.5 parts of aluminium triphosphate,
12 parts of Rhizoma Gastrodiae extract,
24 parts of distilled water.
The preparation method of the waterproof anti-corrosion bottle water paint of the present invention, step are as follows：
1), in reactor add acrylic emulsion, rutile type nano titanic oxide, modified kaolin, polyurethane, point
Powder, wetting agent, defoamer, levelling agent, foam inhibitor, mill base, filler, surfactant, it is 1000r/min to control rotating speed, in
Stirring mixing 1 hour at 45 DEG C；
2), antibacterial, film former are helped, mica powder, zirconium phosphate, 2- mercapto benzimidazoles, trifluoroacetylacetone (TFA) ferrum, three
Poly aluminium phosphate, Rhizoma Gastrodiae extract, distilled water are sequentially added into reactor, control rotating speed for 1000r/min, the stirring at 45 DEG C
Mixing 0.5 hour.
Beneficial effects of the present invention are mainly manifested in：
Waterproof anti-corrosion bottle water paint, be for a kind of special environment-friendlywater-based water-based paint of bottle, can not only
Meet conventional bottle application demand, it is often more important that, this coating environmental sound, and its water resistance and decay resistance
It is stronger.
Specific embodiment
Embodiment 1
A kind of waterproof anti-corrosion bottle water paint, is made up of the raw material of following weight portion：
35 parts of acrylic emulsion,
10 parts of rutile type nano titanic oxide,
12 parts of modified kaolin,
13 parts of polyurethane,
14 parts of dispersant,
11 parts of wetting agent,
10 parts of defoamer,
12.5 parts of levelling agent,
13 parts of foam inhibitor,
10 parts of mill base,
13 parts of filler,
11 parts of surfactant,
14 parts of antibacterial,
Film former help 11 parts,
14 parts of mica powder,
11.5 parts of zirconium phosphate,
7 parts of 2- mercaptos benzimidazole,
13.5 parts of trifluoroacetylacetone (TFA) ferrum,
14.5 parts of aluminium triphosphate,
12 parts of Rhizoma Gastrodiae extract (by Rhizoma Gastrodiae plus the water of its 4 times of weight, is decocted, filtrate is condensed into stream leaching after filtration
Cream, is then dried the extract for obtaining powder),
24 parts of distilled water.
The preparation method of waterproof anti-corrosion bottle water paint, step are as follows：
1), in reactor add acrylic emulsion, rutile type nano titanic oxide, modified kaolin, polyurethane, point
Powder, wetting agent, defoamer, levelling agent, foam inhibitor, mill base, filler, surfactant, it is 1000r/min to control rotating speed, in
Stirring mixing 1 hour at 45 DEG C；
2), antibacterial, film former are helped, mica powder, zirconium phosphate, 2- mercapto benzimidazoles, trifluoroacetylacetone (TFA) ferrum, three
Poly aluminium phosphate, Rhizoma Gastrodiae extract, distilled water are sequentially added into reactor, control rotating speed for 1000r/min, the stirring at 45 DEG C
Mixing 0.5 hour.
Embodiment 2
A kind of waterproof anti-corrosion bottle water paint, is made up of the raw material of following weight portion：
45 parts of acrylic emulsion,
10 parts of rutile type nano titanic oxide,
15 parts of modified kaolin,
10 parts of polyurethane,
15 parts of dispersant,
10 parts of wetting agent,
15 parts of defoamer,
10 parts of levelling agent,
15 parts of foam inhibitor,
10 parts of mill base,
15 parts of filler,
10 parts of surfactant,
15 parts of antibacterial,
Film former help 10 parts,
15 parts of mica powder,
10 parts of zirconium phosphate,
15 parts of 2- mercaptos benzimidazole,
10 parts of trifluoroacetylacetone (TFA) ferrum,
15 parts of aluminium triphosphate,
10 parts of Rhizoma Gastrodiae extract,
25 parts of distilled water.
Preparation method is with embodiment 1.
Embodiment 3
A kind of waterproof anti-corrosion bottle water paint, is made up of the raw material of following weight portion：
30 parts of acrylic emulsion,
12 parts of rutile type nano titanic oxide,
11 parts of modified kaolin,
13 parts of polyurethane,
9 parts of dispersant,
14 parts of wetting agent,
8.5 parts of defoamer,
15 parts of levelling agent,
7 parts of foam inhibitor,
16 parts of mill base,
11.5 parts of filler,
17 parts of surfactant,
10 parts of antibacterial,
Film former help 12 parts,
10.5 parts of mica powder,
14 parts of zirconium phosphate,
6 parts of 2- mercaptos benzimidazole,
17 parts of trifluoroacetylacetone (TFA) ferrum,
9.5 parts of aluminium triphosphate,
16 parts of Rhizoma Gastrodiae extract,
20 parts of distilled water.
Preparation method is with embodiment 1.
Below with reference to embodiment, the present invention is described in detail.But, embodiment content is only to this
Bright example and explanation, affiliated those skilled in the art do various repairing to described specific embodiment
Change or supplement or using similar mode substitute, without departing from invent design or surmount defined in the claims
Scope, all should belong to protection scope of the present invention.
Claims (3)
1. a kind of waterproof anti-corrosion bottle water paint, it is characterised in that：It is made up of the raw material of following weight portion：
Acrylic emulsion 30-45 parts,
Rutile type nano titanic oxide 10-12 parts,
Modified kaolin 11-15 parts,
Polyurethane 10-13 parts,
Dispersant 9-15 parts,
Wetting agent 10-14 parts,
Defoamer 8.5-15 parts,
Levelling agent 10-15 parts,
Foam inhibitor 7-15 parts,
Mill base 10-16 parts,
Filler 11.50-15 parts,
Surfactant 10-17 parts,
Antibacterial 10-15 parts,
Film former help 10-12 parts,
Mica powder 10.5-15 parts,
Zirconium phosphate 10-14 parts,
2- mercapto benzimidazole 6-15 parts,
Trifluoroacetylacetone (TFA) ferrum 10-17 parts,
Aluminium triphosphate 9.5-15 parts,
Rhizoma Gastrodiae extract 10-16 parts,
Distilled water 20-25 parts.
2. a kind of waterproof anti-corrosion bottle water paint as claimed in claim 1, it is characterised in that by following weight portion
Raw material is made：
35 parts of acrylic emulsion,
10 parts of rutile type nano titanic oxide,
12 parts of modified kaolin,
13 parts of polyurethane,
14 parts of dispersant,
11 parts of wetting agent,
10 parts of defoamer,
12.5 parts of levelling agent,
13 parts of foam inhibitor,
10 parts of mill base,
13 parts of filler,
11 parts of surfactant,
14 parts of antibacterial,
Film former help 11 parts,
14 parts of mica powder,
11.5 parts of zirconium phosphate,
7 parts of 2- mercaptos benzimidazole,
13.5 parts of trifluoroacetylacetone (TFA) ferrum,
14.5 parts of aluminium triphosphate,
12 parts of Rhizoma Gastrodiae extract,
24 parts of distilled water.
3. a kind of method for preparing waterproof anti-corrosion bottle water paint as claimed in claim 1 or 2, it is characterised in that step
It is rapid as follows：
1), addition acrylic emulsion, rutile type nano titanic oxide, modified kaolin, polyurethane, dispersion in reactor
Agent, wetting agent, defoamer, levelling agent, foam inhibitor, mill base, filler, surfactant, it is 1000r/min to control rotating speed, in 45
Stirring mixing 1 hour at DEG C；
2), antibacterial, film former are helped, mica powder, zirconium phosphate, 2- mercapto benzimidazoles, trifluoroacetylacetone (TFA) ferrum, trimerization phosphorus
Sour aluminum, Rhizoma Gastrodiae extract, distilled water are sequentially added into reactor, control rotating speed for 1000r/min, the stirring mixing at 45 DEG C
0.5 hour.