CN1061613A - 一种酪龙粘合剂的工艺及其配方 - Google Patents

一种酪龙粘合剂的工艺及其配方 Download PDF

Info

Publication number
CN1061613A
CN1061613A CN 91111009 CN91111009A CN1061613A CN 1061613 A CN1061613 A CN 1061613A CN 91111009 CN91111009 CN 91111009 CN 91111009 A CN91111009 A CN 91111009A CN 1061613 A CN1061613 A CN 1061613A
Authority
CN
China
Prior art keywords
casein
food grade
water
minutes
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 91111009
Other languages
English (en)
Other versions
CN1034343C (zh
Inventor
陈望年
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhan Tianma Jiefang Chemical Co., Ltd.
Original Assignee
JIEFANG CHEMICAL FACTORY WUHAN CITY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIEFANG CHEMICAL FACTORY WUHAN CITY filed Critical JIEFANG CHEMICAL FACTORY WUHAN CITY
Priority to CN91111009A priority Critical patent/CN1034343C/zh
Publication of CN1061613A publication Critical patent/CN1061613A/zh
Application granted granted Critical
Publication of CN1034343C publication Critical patent/CN1034343C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

一种酪龙粘合剂的工艺及其配方，本发明属于高 分子合成材料，其主要解决原始干酪素在制革、造纸 应用中存在成膜坚硬，柔软性差，无延伸性，容易断 裂，吸水性高，长霉虫蛀等问题，本发明是将适宜的树 脂单体，如丙烯酸树脂，聚酰胺树脂，丙烯酸丁酯、甲 酯，已内酰胺单体与干酪素分子链中的胺基式羧基进 行化学反应而改性，从而达到调节成膜物的软硬性， 延伸性，此种方式制得的酪龙粘合剂，具有柔软性好， 延伸性好，吸水性小，不长霉虫蛀等特点，其粘度，含 固量超过联邦德国产品。

Description

本发明属于高分子合成技术，具体地说是一种合成酪龙粘合剂的工艺及其配方，酪龙粘合剂主要应用于制革、造纸等行业表面涂饰粘合。
在本发明提出之前，国内未见生产酪龙粘合剂的涂饰材料，更未报道其合成酪龙粘合剂的工艺和配方。因此过去国内制革、造纸行业普遍采用原始干酪素作表面涂饰剂。原始干酪素虽然有涂层光亮及手感好，而且耐高温熨平与磨光，一般能保持皮革的固有卫生性能，但涂饰后成膜坚硬，柔软性差，无延伸性，容易断裂，再则吸水性高，不适于在颜料层的光亮剂中应用，容易长霉虫蛀。国外西德的BASF公司曾有类似本发明的Luron  Binder-u粘合剂的产品报道，但也未曾公布其工艺与配方，按其技术指标，西德粘合剂产品，粘度在200浬泊/15℃内，含固量在14%，而无法满足用户的选择。
本发明的目的在于克服干酪素涂饰剂成膜坚硬，容易断裂，吸水性强，不适于在颜料层的光亮剂中应用，易长霉虫蛀等缺点，提出一种改性的方法制成粘合剂式涂饰材料，即干酪素（或蛋白质）的改性，就是设法通过某种手段将适宜的树脂式单体，如丙烯酸树脂，聚酰胺树脂，丙烯酸丁酯、甲酯，已内酰胺单体与干酪素分子链中的氨基式羧基起化学反应，从而达到调节酪龙粘合剂成膜物的软硬性，而且吸水性小，延伸性好，不会长霉虫蛀，光泽度好的目的。
本发明是通过以下工艺方法及配方而获得酪龙粘合剂的，即将100份干酪素，加入煮沸的冷却至60～70℃的水中（10～15份氨水与400～500份水的溶液）在不断搅拌下，使之全部溶解，再加入适量的乳化剂，继续搅拌30分钟左右，使干酪素中的油脂全部乳化，再加入适量的蓖麻油搅拌30分钟左右，一次性加入适量乙二醇搅拌均匀，再加入用2～3倍水溶化好25份已内酰胺溶液的1/3，升温至70～80℃，然后将剩余的已内酰胺溶液在60分钟内滴加完毕，升温80～90℃，搅拌7～9小时，使白色乳浆转为淡黄色，并具有良好的粘性，最后加入防霉剂BCM和防腐剂，搅拌15分钟，过滤即成酪龙粘合剂式涂饰剂。
本发明的酪龙粘合剂，不仅成膜柔软，吸水性小，延伸性好，不会长霉虫蛀，而且耐干湿擦，并能保持干酪素固有的优点。同时工艺简单，操作方便。与西德同类产品相比，其粘度和含固量均超过西德BASF公司Luron  Binder-u，粘度根据用户要求可在200～300浬泊/15℃范围内任意调节，含固量≥20%。
下面进一步结合工艺流程图，（见附图）列举实施例。
混合45%的丙烯酸丁酯和55%的丙烯酸甲酯，于16～25%的酪素水液中，用氧化-还原系列引发剂聚合。用此种防水性树脂所制得的薄膜，含有20%的乳酪素，微溶于丙酮。此种薄膜与用机械的方法，按同样的比例用共聚树脂和乳酪素混合所得的薄膜相比较，前者有较高的延伸性和抗张强度。电子显微镜证明改性树酯中存在水不溶性颗粒，而颗粒直径分布是趋向的小颗粒，乳酪素中的氨基附有低分子量的接技共聚物体，在反应生成物中显然存在。

Claims (1)

  1. 一种合成酪龙粘合剂的工艺及其配方，是将干酪素(或蛋白质)通过丙烯酸树脂，聚酰胺树脂，丙烯酸丁酯、甲酯，已内酰胺单体与干酪素分子链中的氨基式羧基进行化学反应而改性，其特征在于用100份干酪素，加入煮沸的冷却至60～70℃的水中(10～15份氨水与400～500份水的溶液)在不断搅拌下，使之全部溶解，再加入适量的乳化剂，继续搅拌30分钟左右，使干酪素中的油脂全部乳化，再加入适量的蓖麻油搅拌30分钟左右，一次性加入适量的乙二醇搅拌均匀，再加入用2～3倍水溶化好25份已内酰胺溶液的1/3，升温至70～80℃，然后将剩余的已内酰胺溶液在60分钟内滴加完毕，升温80～90℃，搅拌7～9小时，最后加入防霉剂BCM和防腐剂，搅拌15分钟，过滤。
CN91111009A 1991-12-10 1991-12-10 一种干酪素-尼龙粘合剂的制造方法 Expired - Fee Related CN1034343C (zh)