CN106147613A - A kind of Environment-friendlynon-toxic non-toxic paint - Google Patents
A kind of Environment-friendlynon-toxic non-toxic paint Download PDFInfo
- Publication number
- CN106147613A CN106147613A CN201610805679.0A CN201610805679A CN106147613A CN 106147613 A CN106147613 A CN 106147613A CN 201610805679 A CN201610805679 A CN 201610805679A CN 106147613 A CN106147613 A CN 106147613A
- Authority
- CN
- China
- Prior art keywords
- parts
- resin
- toxic
- paint
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of Environment-friendlynon-toxic non-toxic paint, its component includes the sexual resin of plant 15 25 parts by weight, thermoplastic acrylic resin 10 15 parts, ferrous oxide nanoscale micro mist 25 parts, sodium carboxymethylcellulose 6 12 parts, zinc naphthenate 36 parts, dibutyl tin laurate 14 parts, nano phase ag_2 o 14 parts, nano titanium oxide 5 15 parts, fluorine silicon resin 8 12 parts, 3 10 parts of 5A type molecular sieve, 10 20 parts of radioresistance slurry, epoxy resin 5 15 parts, manufacture craft of the present invention is simple, manufacturing process is environment friendly and pollution-free, the paint environment-protecting asepsis preparing, harmless, can be widely used for various timber, iron material, plastic, paper wood, high-grade coloured furniture, hotel, the finishing of hospital etc.;In addition, its holding time is long, oxidation resistance is strong.
Description
Technical field
The present invention relates to paint preparing technical field, be specially a kind of Environment-friendlynon-toxic non-toxic paint.
Background technology
Paint is that one can firmly cover at body surface, and the chemistry playing protection, decoration, mark and other specific uses mixes
Compound coating.More authoritative " coating process " book of China's coating circle is defined such that " coating is a kind of material, this
Material can be coated in object surface by different construction technologies, formed adhere to firmly, to have some strength, continuous print solid-state thin
Film.The film common name film so being formed, also known as paint film or coating." after current paint is all chemicals especially application, can be constantly
Ground volatile organic compound and episome.Not only produce ozone pollution to the Nature, but also human body can be made to cause headache, whole body
The various diseases such as paralysis, anaemia, cancer, bring serious threat to health, but are that the one being not fee from must material
Material.
Content of the invention
It is an object of the invention to provide a kind of Environment-friendlynon-toxic non-toxic paint, with the problem solving to propose in above-mentioned background technology.
For achieving the above object, the present invention provides following technical scheme: a kind of Environment-friendlynon-toxic non-toxic paint, its component is by weight
Number includes plant sexual resin 15-25 part, thermoplastic acrylic resin 10-15 part, ferrous oxide nanoscale micro mist 2-5 part, carboxylic
Sodium carboxymethylcellulose pyce 6-12 part, zinc naphthenate 3-6 part, dibutyl tin laurate 1-4 part, nano phase ag_2 o 1-4 part, nanometer two
Titanium oxide 5-15 part, fluorine silicon resin 8-12 part, 5A type molecular sieve 3-10 part, radioresistance slurry 10-20 part, epoxy resin 5-15
Part.
Preferably, preferred composition proportion is: the sexual resin of plant 20 parts, thermoplastic acrylic resin 12 parts, titanium dioxide
Iron nanoscale micro mist 3 parts, sodium carboxymethylcellulose 9 parts, zinc naphthenate 5 parts, dibutyl tin laurate 3 parts, nano phase ag_2 o 2
Part, nano titanium oxide 10 parts, fluorine silicon resin 10 parts, 6 parts of 5A type molecular sieve, 15 parts of radioresistance slurry, epoxy resin 10 parts.
Preferably, its preparation technology comprises the following steps:
A, by sexual for plant resin, thermoplastic acrylic resin, fluorine silicon resin, radioresistance slurry, epoxy resin mixing after add
Stirring in mixer, mixer rotating speed is 3000-5000 rev/min, and mixing time is 20min-30min, stands and obtains mixture
A;
B, in mixture A add ferrous oxide nanoscale micro mist, sodium carboxymethylcellulose, zinc naphthenate, tin dilaurate two fourth
Ji Xi, nano phase ag_2 o, nano titanium oxide, add heating in reactor after mixing, temperature of reaction kettle is 70 DEG C-90 DEG C, adds
The heat time is 30min, is cooled to normal temperature afterwards, obtains mixture B;
C, in mixture B add 5A type molecular sieve, at normal temperatures stir 30min, afterwards stand 2h, i.e. obtain nontoxic paint.
Compared with prior art, the invention has the beneficial effects as follows: manufacture craft of the present invention is simple, and manufacturing process environmental protection is without dirt
Dye, the paint environment-protecting asepsis preparing, harmless, can be widely used for various timber, iron material, plastic, paper wood, high-grade coloured family
The finishing of tool, hotel, hospital etc.;In addition, the present invention is added with multiple nanometer materials, it is possible to increase the anti-oxidant energy of paint
Power, extends the holding time of paint.
Detailed description of the invention
Below the technical scheme in the embodiment of the present invention is clearly and completely described, it is clear that described embodiment
It is only a part of embodiment of the present invention, rather than whole embodiments.Based on the embodiment in the present invention, the common skill in this area
The every other embodiment that art personnel are obtained under the premise of not making creative work, broadly falls into the model of present invention protection
Enclose.
The present invention provides a kind of technical scheme: a kind of Environment-friendlynon-toxic non-toxic paint, its component includes that plant is sexual by weight
Resin 15-25 part, thermoplastic acrylic resin 10-15 part, ferrous oxide nanoscale micro mist 2-5 part, sodium carboxymethylcellulose 6-
12 parts, zinc naphthenate 3-6 part, dibutyl tin laurate 1-4 part, nano phase ag_2 o 1-4 part, nano titanium oxide 5-15 part,
Fluorine silicon resin 8-12 part, 5A type molecular sieve 3-10 part, radioresistance slurry 10-20 part, epoxy resin 5-15 part.
Embodiment one:
The composition proportion using is: the sexual resin of plant 15 parts, thermoplastic acrylic resin 10 parts, ferrous oxide nanoscale micro mist
2 parts, sodium carboxymethylcellulose 6 parts, zinc naphthenate 3 parts, dibutyl tin laurate 1 part, nano phase ag_2 o 1 part, nano-silica
Change titanium 5 parts, fluorine silicon resin 8 parts, 3 parts of 5A type molecular sieve, 10 parts of radioresistance slurry, epoxy resin 5 parts.
The preparation technology of the present embodiment comprises the following steps:
A, by sexual for plant resin, thermoplastic acrylic resin, fluorine silicon resin, radioresistance slurry, epoxy resin mixing after add
Stirring in mixer, mixer rotating speed is 3000 revs/min, and mixing time is 20min, stands and obtains mixture A;
B, in mixture A add ferrous oxide nanoscale micro mist, sodium carboxymethylcellulose, zinc naphthenate, tin dilaurate two fourth
Ji Xi, nano phase ag_2 o, nano titanium oxide, add heating in reactor after mixing, temperature of reaction kettle is 70 DEG C, the heat time
It for 30min, is cooled to normal temperature afterwards, obtain mixture B;
C, in mixture B add 5A type molecular sieve, at normal temperatures stir 30min, afterwards stand 2h, i.e. obtain nontoxic paint.
Embodiment two:
The composition proportion using is: the sexual resin of plant 25 parts, thermoplastic acrylic resin 15 parts, ferrous oxide nanoscale micro mist
5 parts, sodium carboxymethylcellulose 12 parts, zinc naphthenate 6 parts, dibutyl tin laurate 4 parts, nano phase ag_2 o 4 parts, nano-silica
Change titanium 15 parts, fluorine silicon resin 12 parts, 10 parts of 5A type molecular sieve, 20 parts of radioresistance slurry, epoxy resin 15 parts.
The preparation technology of the present embodiment comprises the following steps:
A, by sexual for plant resin, thermoplastic acrylic resin, fluorine silicon resin, radioresistance slurry, epoxy resin mixing after add
Stirring in mixer, mixer rotating speed is 5000 revs/min, and mixing time is 30min, stands and obtains mixture A;
B, in mixture A add ferrous oxide nanoscale micro mist, sodium carboxymethylcellulose, zinc naphthenate, tin dilaurate two fourth
Ji Xi, nano phase ag_2 o, nano titanium oxide, add heating in reactor after mixing, temperature of reaction kettle is 90 DEG C, the heat time
It for 30min, is cooled to normal temperature afterwards, obtain mixture B;
C, in mixture B add 5A type molecular sieve, at normal temperatures stir 30min, afterwards stand 2h, i.e. obtain nontoxic paint.
Embodiment three:
The composition proportion using is: the sexual resin of plant 17 parts, thermoplastic acrylic resin 11 parts, ferrous oxide nanoscale micro mist
3 parts, sodium carboxymethylcellulose 7 parts, zinc naphthenate 4 parts, dibutyl tin laurate 2 parts, nano phase ag_2 o 2 parts, nano-silica
Change titanium 7 parts, fluorine silicon resin 9 parts, 4 parts of 5A type molecular sieve, 12 parts of radioresistance slurry, epoxy resin 6 parts.
The preparation technology of the present embodiment comprises the following steps:
A, by sexual for plant resin, thermoplastic acrylic resin, fluorine silicon resin, radioresistance slurry, epoxy resin mixing after add
Stirring in mixer, mixer rotating speed is 3500 revs/min, and mixing time is 22min, stands and obtains mixture A;
B, in mixture A add ferrous oxide nanoscale micro mist, sodium carboxymethylcellulose, zinc naphthenate, tin dilaurate two fourth
Ji Xi, nano phase ag_2 o, nano titanium oxide, add heating in reactor after mixing, temperature of reaction kettle is 75 DEG C, the heat time
It for 30min, is cooled to normal temperature afterwards, obtain mixture B;
C, in mixture B add 5A type molecular sieve, at normal temperatures stir 30min, afterwards stand 2h, i.e. obtain nontoxic paint.
Embodiment four:
The composition proportion using is: the sexual resin of plant 22 parts, thermoplastic acrylic resin 14 parts, ferrous oxide nanoscale micro mist
4 parts, sodium carboxymethylcellulose 11 parts, zinc naphthenate 5 parts, dibutyl tin laurate 3 parts, nano phase ag_2 o 3 parts, nano-silica
Change titanium 14 parts, fluorine silicon resin 11 parts, 9 parts of 5A type molecular sieve, 18 parts of radioresistance slurry, epoxy resin 14 parts.
The preparation technology of the present embodiment comprises the following steps:
A, by sexual for plant resin, thermoplastic acrylic resin, fluorine silicon resin, radioresistance slurry, epoxy resin mixing after add
Stirring in mixer, mixer rotating speed is 4500 revs/min, and mixing time is 28min, stands and obtains mixture A;
B, in mixture A add ferrous oxide nanoscale micro mist, sodium carboxymethylcellulose, zinc naphthenate, tin dilaurate two fourth
Ji Xi, nano phase ag_2 o, nano titanium oxide, add heating in reactor after mixing, temperature of reaction kettle is 85 DEG C, the heat time
It for 30min, is cooled to normal temperature afterwards, obtain mixture B;
C, in mixture B add 5A type molecular sieve, at normal temperatures stir 30min, afterwards stand 2h, i.e. obtain nontoxic paint.
Embodiment five:
The composition proportion using is: the sexual resin of plant 20 parts, thermoplastic acrylic resin 12 parts, ferrous oxide nanoscale micro mist
3 parts, sodium carboxymethylcellulose 9 parts, zinc naphthenate 5 parts, dibutyl tin laurate 3 parts, nano phase ag_2 o 2 parts, nano-silica
Change titanium 10 parts, fluorine silicon resin 10 parts, 6 parts of 5A type molecular sieve, 15 parts of radioresistance slurry, epoxy resin 10 parts.
The preparation technology of the present embodiment comprises the following steps:
A, by sexual for plant resin, thermoplastic acrylic resin, fluorine silicon resin, radioresistance slurry, epoxy resin mixing after add
Stirring in mixer, mixer rotating speed is 4000 revs/min, and mixing time is 25min, stands and obtains mixture A;
B, in mixture A add ferrous oxide nanoscale micro mist, sodium carboxymethylcellulose, zinc naphthenate, tin dilaurate two fourth
Ji Xi, nano phase ag_2 o, nano titanium oxide, add heating in reactor after mixing, temperature of reaction kettle is 80 DEG C, the heat time
It for 30min, is cooled to normal temperature afterwards, obtain mixture B;
C, in mixture B add 5A type molecular sieve, at normal temperatures stir 30min, afterwards stand 2h, i.e. obtain nontoxic paint.
Manufacture craft of the present invention is simple, and manufacturing process is environment friendly and pollution-free, the paint environment-protecting asepsis preparing, harmless,
Can be widely used for the finishing of various timber, iron material, plastic, paper wood, high-grade coloured furniture, hotel, hospital etc.;In addition, the present invention
In be added with multiple nanometer materials, it is possible to increase the oxidation resistance of paint, extend the holding time of paint.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, permissible
Understand and multiple change, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention
And modification, the scope of the present invention be defined by the appended.
Claims (3)
1. an Environment-friendlynon-toxic non-toxic paint, it is characterised in that: its component includes plant sexual resin 15-25 part, heat by weight
Plastic propene's acid resin 10-15 part, ferrous oxide nanoscale micro mist 2-5 part, sodium carboxymethylcellulose 6-12 part, zinc naphthenate 3-
6 parts, dibutyl tin laurate 1-4 part, nano phase ag_2 o 1-4 part, nano titanium oxide 5-15 part, fluorine silicon resin 8-12 part,
5A type molecular sieve 3-10 part, radioresistance slurry 10-20 part, epoxy resin 5-15 part.
2. a kind of Environment-friendlynon-toxic non-toxic paint according to claim 1, it is characterised in that: preferred composition proportion is: plant has
Property resin 20 parts, thermoplastic acrylic resin 12 parts, ferrous oxide nanoscale micro mist 3 parts, sodium carboxymethylcellulose 9 parts, cycloalkanes
5 parts of zinc of acid, dibutyl tin laurate 3 parts, nano phase ag_2 o 2 parts, nano titanium oxide 10 parts, fluorine silicon resin 10 parts, 5A type
6 parts of molecular sieve, 15 parts of radioresistance slurry, epoxy resin 10 parts.
3. a kind of Environment-friendlynon-toxic non-toxic paint according to claim 1, it is characterised in that: its preparation technology comprises the following steps:
A, by sexual for plant resin, thermoplastic acrylic resin, fluorine silicon resin, radioresistance slurry, epoxy resin mixing after add
Stirring in mixer, mixer rotating speed is 3000-5000 rev/min, and mixing time is 20min-30min, stands and obtains mixture
A;
B, in mixture A add ferrous oxide nanoscale micro mist, sodium carboxymethylcellulose, zinc naphthenate, tin dilaurate two fourth
Ji Xi, nano phase ag_2 o, nano titanium oxide, add heating in reactor after mixing, temperature of reaction kettle is 70 DEG C-90 DEG C, adds
The heat time is 30min, is cooled to normal temperature afterwards, obtains mixture B;
C, in mixture B add 5A type molecular sieve, at normal temperatures stir 30min, afterwards stand 2h, i.e. obtain nontoxic paint.