CN106947353A - A kind of environment-friendly type waterproof paint and its preparation technology - Google Patents
A kind of environment-friendly type waterproof paint and its preparation technology Download PDFInfo
- Publication number
- CN106947353A CN106947353A CN201710288623.7A CN201710288623A CN106947353A CN 106947353 A CN106947353 A CN 106947353A CN 201710288623 A CN201710288623 A CN 201710288623A CN 106947353 A CN106947353 A CN 106947353A
- Authority
- CN
- China
- Prior art keywords
- parts
- resin
- waterproof paint
- mixture
- tmos
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of environment-friendly type waterproof paint and its preparation technology, waterproof paint component includes 15 30 parts of water soluble resin by weight, 10 20 parts of bisphenol A epoxide resin, 38 parts of zinc oxide, 10 20 parts of calcium stearate, 20 40 parts of hydroxy resin, 5 15 parts of nanometer grade silica, 5 15 parts of Nano titanium dioxide, 2 10 parts of nano magnesia, 4 12 parts of TMOS, 4 12 parts of 28 parts of elastomer and expanded perlite, preparation technology of the present invention is simple, obtained paint water resistance is good, also there is excellent anti-wear performance simultaneously, long service life.
Description
Technical field
The present invention relates to waterproof paint preparing technical field, specially a kind of environment-friendly type waterproof paint and its preparation technology.
Background technology
Paint is that one kind can firmly be covered in body surface, and the chemistry for playing protection, decoration, mark and other specific uses is mixed
Compound coating.The more authoritative book of coating process one of Chinese coating circle is defined as：Coating is a kind of material, this material
Material can be coated in object surface with different implementing process, formed and adhered to firmly, with some strength, continuous solid-state film.
The film common name film so formed, also known as paint film or coating.Belong to organic chemical industry's macromolecular material, the film formed belongs to high
Molecular compound type.The classification for the chemical products passed through according to the modern times, coating belongs to fine chemical product.Now on the market
Paint species various, but the harmful components contained are more, can not only spread out of one pungent taste after painting well, easily open
Split and come off, use for a long time, it is harmful to body, and also waterproof effect is poor, causes paint product service life short.
The content of the invention
It is an object of the invention to provide a kind of environment-friendly type waterproof paint and its preparation technology, to solve above-mentioned background technology
The problem of middle proposition.
To achieve the above object, the present invention provides following technical scheme：A kind of environment-friendly type waterproof paint, waterproof paint component
Include 15-30 parts of water soluble resin, 10-20 parts of bisphenol A epoxide resin, 3-8 parts of zinc oxide, calcium stearate 10-20 by weight
Part, 20-40 parts of hydroxy resin, 5-15 parts of nanometer grade silica, 5-15 parts of Nano titanium dioxide, nano magnesia 2-
4-12 parts of 10 parts, 4-12 parts of TMOS, 2-8 parts of elastomer and expanded perlite.
It is preferred that, the preferred composition proportion of waterproof paint is：22 parts of water soluble resin, 15 parts of bisphenol A epoxide resin, zinc oxide
5 parts, 15 parts of calcium stearate, 30 parts of hydroxy resin, 10 parts of nanometer grade silica, Nano titanium dioxide 10 part, nanometer
8 parts of 6 parts of magnesia, 8 parts of TMOS, 5 parts of elastomer and expanded perlite.
It is preferred that, its preparation technology comprises the following steps：
A, mechanical agitation will be added after water soluble resin, bisphenol A epoxide resin, zinc oxide, calcium stearate, hydroxy mixed with resin
Stirred in kettle, stir speed (S.S.) is 4000 revs/min, and mixing time is 40min, is filtered afterwards, standing obtains mixture A；
B, addition nanometer grade silica, Nano titanium dioxide, nano magnesia, TMOS, elasticity fibre in mixture A
Dimension and expanded perlite, add heating response in heating tank after mixing, heating-up temperature is 130 DEG C, and the heat time is 40min,
Normal temperature is slowly cooled to after constant temperature 20min afterwards, mixture B is obtained；
C, mixture poured into again in stirred tank and stirred, stir speed (S.S.) is 500 revs/min, stirs 10min, that is, obtains dubbin
Paint.
Compared with prior art, the beneficial effects of the invention are as follows：Preparation technology of the present invention is simple, obtained paint water proofing property
Can be good, while also having excellent anti-wear performance, long service life；In addition, being added with nanometer grade silica in the present invention, receiving
Meter level titanium dioxide, nano magnesia, can further increase the environmental-protecting performance and resistance to elevated temperatures of paint, extend paint product
Service life.
Embodiment
The technical scheme in the embodiment of the present invention is clearly and completely described below, it is clear that described embodiment
Only it is a part of embodiment of the invention, rather than whole embodiments.Based on the embodiment in the present invention, ordinary skill
The every other embodiment that personnel are obtained under the premise of creative work is not made, belongs to the scope of protection of the invention.
The present invention provides a kind of technical scheme：A kind of environment-friendly type waterproof paint, waterproof paint component includes by weight
15-30 parts of water soluble resin, 10-20 parts of bisphenol A epoxide resin, 3-8 parts of zinc oxide, 10-20 parts of calcium stearate, hydroxy resin
20-40 parts, 5-15 parts of nanometer grade silica, 5-15 parts of Nano titanium dioxide, 2-10 parts of nano magnesia, TMOS 4-
4-12 parts of 12 parts, 2-8 parts of elastomer and expanded perlite.
Embodiment one：
In the present embodiment, waterproof paint component includes 15 parts of water soluble resin, 10 parts of bisphenol A epoxide resin, oxidation by weight
3 parts of zinc, 10 parts of calcium stearate, 20 parts of hydroxy resin, 5 parts of nanometer grade silica, Nano titanium dioxide 5 part, nanometer
4 parts of 2 parts of magnesia, 4 parts of TMOS, 2 parts of elastomer and expanded perlite.
The preparation technology of the present embodiment comprises the following steps：
A, mechanical agitation will be added after water soluble resin, bisphenol A epoxide resin, zinc oxide, calcium stearate, hydroxy mixed with resin
Stirred in kettle, stir speed (S.S.) is 4000 revs/min, and mixing time is 40min, is filtered afterwards, standing obtains mixture A；
B, addition nanometer grade silica, Nano titanium dioxide, nano magnesia, TMOS, elasticity fibre in mixture A
Dimension and expanded perlite, add heating response in heating tank after mixing, heating-up temperature is 130 DEG C, and the heat time is 40min,
Normal temperature is slowly cooled to after constant temperature 20min afterwards, mixture B is obtained；
C, mixture poured into again in stirred tank and stirred, stir speed (S.S.) is 500 revs/min, stirs 10min, that is, obtains dubbin
Paint.
Embodiment two：
In the present embodiment, waterproof paint component includes 30 parts of water soluble resin, 20 parts of bisphenol A epoxide resin, oxidation by weight
8 parts of zinc, 20 parts of calcium stearate, 40 parts of hydroxy resin, 15 parts of nanometer grade silica, 15 parts of Nano titanium dioxide, receive
12 parts of 10 parts of magnesia of rice, 12 parts of TMOS, 8 parts of elastomer and expanded perlite.
The preparation technology of the present embodiment comprises the following steps：
A, mechanical agitation will be added after water soluble resin, bisphenol A epoxide resin, zinc oxide, calcium stearate, hydroxy mixed with resin
Stirred in kettle, stir speed (S.S.) is 4000 revs/min, and mixing time is 40min, is filtered afterwards, standing obtains mixture A；
B, addition nanometer grade silica, Nano titanium dioxide, nano magnesia, TMOS, elasticity fibre in mixture A
Dimension and expanded perlite, add heating response in heating tank after mixing, heating-up temperature is 130 DEG C, and the heat time is 40min,
Normal temperature is slowly cooled to after constant temperature 20min afterwards, mixture B is obtained；
C, mixture poured into again in stirred tank and stirred, stir speed (S.S.) is 500 revs/min, stirs 10min, that is, obtains dubbin
Paint.
Embodiment three：
In the present embodiment, waterproof paint component includes 18 parts of water soluble resin, 12 parts of bisphenol A epoxide resin, oxidation by weight
4 parts of zinc, 12 parts of calcium stearate, 25 parts of hydroxy resin, 6 parts of nanometer grade silica, Nano titanium dioxide 6 part, nanometer
5 parts of 4 parts of magnesia, 5 parts of TMOS, 3 parts of elastomer and expanded perlite.
The preparation technology of the present embodiment comprises the following steps：
A, mechanical agitation will be added after water soluble resin, bisphenol A epoxide resin, zinc oxide, calcium stearate, hydroxy mixed with resin
Stirred in kettle, stir speed (S.S.) is 4000 revs/min, and mixing time is 40min, is filtered afterwards, standing obtains mixture A；
B, addition nanometer grade silica, Nano titanium dioxide, nano magnesia, TMOS, elasticity fibre in mixture A
Dimension and expanded perlite, add heating response in heating tank after mixing, heating-up temperature is 130 DEG C, and the heat time is 40min,
Normal temperature is slowly cooled to after constant temperature 20min afterwards, mixture B is obtained；
C, mixture poured into again in stirred tank and stirred, stir speed (S.S.) is 500 revs/min, stirs 10min, that is, obtains dubbin
Paint.
Example IV：
In the present embodiment, waterproof paint component includes 28 parts of water soluble resin, 18 parts of bisphenol A epoxide resin, oxidation by weight
7 parts of zinc, 18 parts of calcium stearate, 35 parts of hydroxy resin, 12 parts of nanometer grade silica, 13 parts of Nano titanium dioxide, receive
11 parts of 8 parts of magnesia of rice, 10 parts of TMOS, 7 parts of elastomer and expanded perlite.
The preparation technology of the present embodiment comprises the following steps：
A, mechanical agitation will be added after water soluble resin, bisphenol A epoxide resin, zinc oxide, calcium stearate, hydroxy mixed with resin
Stirred in kettle, stir speed (S.S.) is 4000 revs/min, and mixing time is 40min, is filtered afterwards, standing obtains mixture A；
B, addition nanometer grade silica, Nano titanium dioxide, nano magnesia, TMOS, elasticity fibre in mixture A
Dimension and expanded perlite, add heating response in heating tank after mixing, heating-up temperature is 130 DEG C, and the heat time is 40min,
Normal temperature is slowly cooled to after constant temperature 20min afterwards, mixture B is obtained；
C, mixture poured into again in stirred tank and stirred, stir speed (S.S.) is 500 revs/min, stirs 10min, that is, obtains dubbin
Paint.
Embodiment five：
In the present embodiment, waterproof paint component includes 23 parts of water soluble resin, 16 parts of bisphenol A epoxide resin, oxidation by weight
6 parts of zinc, 16 parts of calcium stearate, 32 parts of hydroxy resin, 12 parts of nanometer grade silica, 12 parts of Nano titanium dioxide, receive
10 parts of 6 parts of magnesia of rice, 10 parts of TMOS, 6 parts of elastomer and expanded perlite.
The preparation technology of the present embodiment comprises the following steps：
A, mechanical agitation will be added after water soluble resin, bisphenol A epoxide resin, zinc oxide, calcium stearate, hydroxy mixed with resin
Stirred in kettle, stir speed (S.S.) is 4000 revs/min, and mixing time is 40min, is filtered afterwards, standing obtains mixture A；
B, addition nanometer grade silica, Nano titanium dioxide, nano magnesia, TMOS, elasticity fibre in mixture A
Dimension and expanded perlite, add heating response in heating tank after mixing, heating-up temperature is 130 DEG C, and the heat time is 40min,
Normal temperature is slowly cooled to after constant temperature 20min afterwards, mixture B is obtained；
C, mixture poured into again in stirred tank and stirred, stir speed (S.S.) is 500 revs/min, stirs 10min, that is, obtains dubbin
Paint.
Embodiment six：
In the present embodiment, waterproof paint component includes 22 parts of water soluble resin, 15 parts of bisphenol A epoxide resin, oxidation by weight
5 parts of zinc, 15 parts of calcium stearate, 30 parts of hydroxy resin, 10 parts of nanometer grade silica, 10 parts of Nano titanium dioxide, receive
8 parts of 6 parts of magnesia of rice, 8 parts of TMOS, 5 parts of elastomer and expanded perlite.
The preparation technology of the present embodiment comprises the following steps：
A, mechanical agitation will be added after water soluble resin, bisphenol A epoxide resin, zinc oxide, calcium stearate, hydroxy mixed with resin
Stirred in kettle, stir speed (S.S.) is 4000 revs/min, and mixing time is 40min, is filtered afterwards, standing obtains mixture A；
B, addition nanometer grade silica, Nano titanium dioxide, nano magnesia, TMOS, elasticity fibre in mixture A
Dimension and expanded perlite, add heating response in heating tank after mixing, heating-up temperature is 130 DEG C, and the heat time is 40min,
Normal temperature is slowly cooled to after constant temperature 20min afterwards, mixture B is obtained；
C, mixture poured into again in stirred tank and stirred, stir speed (S.S.) is 500 revs/min, stirs 10min, that is, obtains dubbin
Paint.
Preparation technology of the present invention is simple, and obtained paint water resistance is good, while also having excellent anti-wear performance, uses
Long lifespan；In addition, nanometer grade silica, Nano titanium dioxide, nano magnesia are added with the present invention, can be further
Increase the environmental-protecting performance and resistance to elevated temperatures of paint, extend the service life of paint product.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understand and these embodiments can be carried out without departing from the principles and spirit of the present invention a variety of changes, modification, replace
And modification, the scope of the present invention is defined by the appended.
Claims (3)
1. a kind of environment-friendly type waterproof paint, it is characterised in that：Waterproof paint component includes water soluble resin 15-30 by weight
Part, 10-20 parts of bisphenol A epoxide resin, 3-8 parts of zinc oxide, 10-20 parts of calcium stearate, 20-40 parts of hydroxy resin, nanometer
5-15 parts of grade silicon dioxide, 5-15 parts of Nano titanium dioxide, 2-10 parts of nano magnesia, 4-12 parts of TMOS, elasticity are fine
Tie up 2-8 parts and 4-12 parts of expanded perlite.
2. a kind of environment-friendly type waterproof paint according to claim 1, it is characterised in that：The preferred composition proportion of waterproof paint
For：22 parts of water soluble resin, 15 parts of bisphenol A epoxide resin, 5 parts of zinc oxide, 15 parts of calcium stearate, 30 parts of hydroxy resin, receive
0 part of meter level silica 1,10 parts of Nano titanium dioxide, 6 parts of nano magnesia, 8 parts of TMOS, 5 parts of elastomer and
8 parts of expanded perlite.
3. a kind of environment-friendly type waterproof paint according to claim 1, it is characterised in that：Its preparation technology includes following step
Suddenly：
A, mechanical agitation will be added after water soluble resin, bisphenol A epoxide resin, zinc oxide, calcium stearate, hydroxy mixed with resin
Stirred in kettle, stir speed (S.S.) is 4000 revs/min, and mixing time is 40min, is filtered afterwards, standing obtains mixture A；
B, addition nanometer grade silica, Nano titanium dioxide, nano magnesia, TMOS, elasticity fibre in mixture A
Dimension and expanded perlite, add heating response in heating tank after mixing, heating-up temperature is 130 DEG C, and the heat time is 40min,
Normal temperature is slowly cooled to after constant temperature 20min afterwards, mixture B is obtained；
C, mixture poured into again in stirred tank and stirred, stir speed (S.S.) is 500 revs/min, stirs 10min, that is, obtains dubbin
Paint.