CN107964344A - A kind of environmental protection paint of flame-proof antibiotic and preparation method thereof - Google Patents
A kind of environmental protection paint of flame-proof antibiotic and preparation method thereof Download PDFInfo
- Publication number
- CN107964344A CN107964344A CN201711402642.4A CN201711402642A CN107964344A CN 107964344 A CN107964344 A CN 107964344A CN 201711402642 A CN201711402642 A CN 201711402642A CN 107964344 A CN107964344 A CN 107964344A
- Authority
- CN
- China
- Prior art keywords
- parts
- environmental protection
- protection paint
- flame
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environmental protection paint of flame-proof antibiotic, its component includes by weight：35 48 parts of waterborne polyurethane resin, 22 30 parts of epoxy resin, 15 20 parts of urea formaldehyde resin, 10 16 parts of pitch, 35 parts of sodium salicylate, 35 parts of acetamide, 6 10 parts of antioxidant MB, 36 parts of triethylamine, 58 parts of thickener, 36 parts of Stearyl Amine, 36 parts of higher aliphatic, 2.5 3.5 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, 1.8 3.2 parts of antibacterial salt ion solution, 2.5 3.5 parts of fire retardant, 25 parts of silicone emulsion, appropriate amount of deionized water.Environmental protection paint prepared by the present invention has the advantages that resistance to ag(e)ing, antibacterial, fire-retardant and bond effect are good；The present invention prepares in the raw material of environmental protection paint and adds antibacterial salt ion solution so that environmental protection paint antibacterial ability lifts decades of times；Preparation method is simple, is conducive to industrialized production.
Description
Technical field
The present invention relates to a kind of environmental protection paint, is specifically a kind of environmental protection paint of flame-proof antibiotic and preparation method thereof.
Background technology
Coating, in the entitled paint of Chinese tradition.So-called coating is to be coated in the body surface protected or decorated, and
The continuous film of firm attachment can be formed with coated article, typically based on resin or oil or lotion, adds or does not add face
Material, filler, add corresponding additive, the thick liquid being formulated with organic solvent or water.Paint is to be coated in and is applied
Object surface can simultaneously form the material of the continuous film of firm attachment.It is either inorganic, such as electro-coppering, electronickelling, electricity
It is zinc-plated etc..Can also be organic, such as most high-molecular organic material, high-molecular organic material constitutes current paint city
Field major part.Existing paint adds the organic solvents such as benzene mostly, and harm to the human body is larger, and certain shadow can be also caused to environment
Ring, as people are more and more stronger to the consciousness of environmental protection, this just needs a kind of dependable performance, to the oil of human body and environmental nonpollution
Paint.
Chinese coating circle is more authoritative《Coating process》What one book was defined as：" coating is a kind of material, this material
Material can be coated in object surface with different construction technologies, and it is firm, thin with some strength, continuous solid-state to form adhesion
Film.The film common name film so formed, also known as paint film or coating.The service life of coating is depending on different products, liquid
State reason stone texture product uses modified organic silicone resin lotion as base-material, and with special coating technology, assorted colored paint is overmolding to
Gluey hydrate colour particle, is uniformly and stably suspended in specific water-borne dispersions, and various colored particles form and aspect remain unchanged,
Coloring pigment will not separate out in water.The service life of so this exterior coating is about 15 years.
The quality of currently marketed coating still has much room for improvement, for example, currently marketed coating do not only exist bad adhesion,
The shortcomings that loss of properties on aging, also there are the shortcomings of poor fire and poor antibiotic property, the use of this currently marketed paint vehicle also made
Scope compares limitation.
The content of the invention
In view of the deficiencies of the prior art, the present invention provides a kind of environmental protection paint of flame-proof antibiotic, do not only exist caking property it is good,
The advantages of resistance to ag(e)ing and water-tolerant, also there are good flame resistance, antibiotic property is good and the advantages that high-low temperature resistant.
To achieve the above object, the present invention provides following technical solution：
A kind of environmental protection paint of flame-proof antibiotic, its component include by weight：35-48 parts of waterborne polyurethane resin, epoxy resin
22-30 parts, 15-20 parts of urea formaldehyde resin, 10-16 parts of pitch, 3-5 parts of sodium salicylate, 3-5 parts of acetamide, antioxidant MB 6-10
Part, 3-6 parts of triethylamine, 5-8 parts of thickener, 3-6 parts of Stearyl Amine, 3-6 parts of higher aliphatic, polyoxyethylene polyoxy propyl alcohol amidogen ether
2.5-3.5 parts, 1.8-3.2 parts of antibacterial salt ion solution, 2.5-3.5 parts of fire retardant, 2-5 parts of silicone emulsion, appropriate amount of deionized water.
As the further scheme of the present invention：Its component includes by weight：38 parts of waterborne polyurethane resin, asphalt mixtures modified by epoxy resin
27 parts of fat, 18 parts of urea formaldehyde resin, 14 parts of pitch, 4 parts of sodium salicylate, 4 parts of acetamide, 8 parts of antioxidant MB, 4 parts of triethylamine,
6 parts of thickener, 4 parts of Stearyl Amine, 5 parts of higher aliphatic, 3 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, antibacterial salt ion solution 2
Part, 3 parts of fire retardant, 4 parts of silicone emulsion, 150 parts of deionized water.
As the further scheme of the present invention：The antibacterial metal ions salting liquid selects Ag+、Mn7+And Zn2+Mix molten
Liquid, concentration ratio are：n（Ag+）：n（Mn7+）：n（Zn2+）=8：20：35.
As the further scheme of the present invention：The thickener selects Sodium Polyacrylate, polyethylene glycol oxide, polyvinyl pyrrole
Three kinds in alkanone, polyvinyl alcohol, low-molecular polyethylene wax and polyacrylamide or four kinds.
As the further scheme of the present invention：The fire retardant selects phosphate compound, magnesium hydroxide, hydration boric acid
Two or three in zinc and talcum powder.
A kind of preparation method of the environmental protection paint of flame-proof antibiotic, its preparation method comprise the following steps：
A, waterborne polyurethane resin, epoxy resin, urea formaldehyde resin and pitch are placed in pulverizer respectively and are crushed, then
Ground by grinder, gained each component powder is retained separately, spare；
B, the phenolic resin obtained by step a, epoxy resin, urea formaldehyde resin, pitch and deionized water are added to high-speed stirred
Gu Zhong, is warming up to 80-120 DEG C and stirs 85-110min, obtained component is denoted as blending ingredients A；
C, sodium salicylate, acetamide, antioxidant MB and deionized water are added in liquid material a mixing bowl, and by liquid material a mixing bowl
Vacuumize, and 20-35min is stirred with the speed of 550-660r/min, obtained component is denoted as blending ingredients B；
D, blending ingredients A is added in blending ingredients B, then remaining raw material is added thereto and stirs 50-70min, to obtain the final product
Finished product.
As the further scheme of the present invention：The rotating speed of the step b high speed stirred tanks is 1500-2000r/min.
As the further scheme of the present invention：The temperature in liquid material a mixing bowl in the step c is 120-160 DEG C.
Compared with prior art, the beneficial effects of the invention are as follows：
Environmental protection paint prepared by the present invention has the advantages that resistance to ag(e)ing, antibacterial, fire-retardant and bond effect are good；The present invention prepares environmental protection
Antibacterial salt ion solution is added in the raw material of paint so that environmental protection paint antibacterial ability lifts decades of times；Preparation method is simple, favorably
In industrialized production.
Embodiment
The technical solution of this patent is described in more detail with reference to embodiment.
Embodiment 1
A kind of environmental protection paint of flame-proof antibiotic, its component include by weight：35 parts of waterborne polyurethane resin, epoxy resin 22
Part, 15 parts of urea formaldehyde resin, 10 parts of pitch, 3 parts of sodium salicylate, 3 parts of acetamide, 6 parts of antioxidant MB, 3 parts of triethylamine, thickening
5 parts of agent, 3 parts of Stearyl Amine, 3 parts of higher aliphatic, 2.5 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, antibacterial salt ion solution 1.8
Part, 2.5 parts of fire retardant, 2 parts of silicone emulsion, 80 parts of deionized water.
The antibacterial metal ions salting liquid selects Ag+、Mn7+And Zn2+Mixed solution, concentration ratio are：n（Ag+）：n（Mn7 +）：n（Zn2+）=8：20：35.The thickener selects Sodium Polyacrylate, polyethylene glycol oxide, polyvinylpyrrolidone.It is described fire-retardant
Phosphate compound, magnesium hydroxide are selected in agent.
A kind of preparation method of the environmental protection paint of flame-proof antibiotic, its preparation method comprise the following steps：
A, waterborne polyurethane resin, epoxy resin, urea formaldehyde resin and pitch are placed in pulverizer respectively and are crushed, then
Ground by grinder, gained each component powder is retained separately, spare；
B, the phenolic resin obtained by step a, epoxy resin, urea formaldehyde resin, pitch and deionized water are added to high-speed stirred
Gu Zhong, is warming up to 80 DEG C and stirs 85min, obtained component is denoted as blending ingredients A；The rotating speed of high-speed stirred kettle is 1500r/min；
C, sodium salicylate, acetamide, antioxidant MB and deionized water are added in liquid material a mixing bowl, and by liquid material a mixing bowl
Vacuumize, and 20min is stirred with the speed of 550r/min, obtained component is denoted as blending ingredients B；Temperature in liquid material a mixing bowl is
120℃；
D, blending ingredients A is added in blending ingredients B, then remaining raw material is added thereto and stirs 50min, up into
Product.
After tested, the surface drying hardening time of the coating prepared by embodiment 1（25℃）It is for 22h, shear strength
0.91MPa, adhesion strength 0.38MPa, by coating be immersed in 20 DEG C, mass concentration be 3% brine in 720h do not find coating
Generation cracking, aliquation or obscission；Fire resistance test uses UL94 standards, and test result is not occur drip phenomenon；
60 degree of relative humidity stand 72h surface colony numbers in the environment of being 60%（cfu/cm2）For 2.2 grades of ozone aging.
Embodiment 2
A kind of environmental protection paint of flame-proof antibiotic, its component include by weight：48 parts of waterborne polyurethane resin, epoxy resin 30
Part, 20 parts of urea formaldehyde resin, 16 parts of pitch, 5 parts of sodium salicylate, 5 parts of acetamide, 10 parts of antioxidant MB, 6 parts of triethylamine, thickening
8 parts of agent, 6 parts of Stearyl Amine, 6 parts of higher aliphatic, 3.5 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, antibacterial salt ion solution 3.2
Part, 3.5 parts of fire retardant, 5 parts of silicone emulsion, 100 parts of deionized water.
The antibacterial metal ions salting liquid selects Ag+、Mn7+And Zn2+Mixed solution, concentration ratio are：n（Ag+）：n（Mn7 +）：n（Zn2+）=8：20：35.The thickener selects polyvinylpyrrolidone, polyvinyl alcohol, low-molecular polyethylene wax and poly- third
Acrylamide.The fire retardant selects magnesium hydroxide, hydration zinc borate and talcum powder.
A kind of preparation method of the environmental protection paint of flame-proof antibiotic, its preparation method comprise the following steps：
A, waterborne polyurethane resin, epoxy resin, urea formaldehyde resin and pitch are placed in pulverizer respectively and are crushed, then
Ground by grinder, gained each component powder is retained separately, spare；
B, the phenolic resin obtained by step a, epoxy resin, urea formaldehyde resin, pitch and deionized water are added to high-speed stirred
Gu Zhong, is warming up to 120 DEG C and stirs 110min, obtained component is denoted as blending ingredients A；The rotating speed of high-speed stirred kettle is 2000r/
min；
C, sodium salicylate, acetamide, antioxidant MB and deionized water are added in liquid material a mixing bowl, and by liquid material a mixing bowl
Vacuumize, and 35min is stirred with the speed of 660r/min, obtained component is denoted as blending ingredients B；Temperature in liquid material a mixing bowl is
160℃；
D, blending ingredients A is added in blending ingredients B, then remaining raw material is added thereto and stirs 70min, up into
Product.
After tested, the surface drying hardening time of the coating prepared by embodiment 2（25℃）It is for 24h, shear strength
0.85MPa, adhesion strength 0.36MPa, by coating be immersed in 20 DEG C, mass concentration be 4% brine in 720h do not find coating
Generation cracking, aliquation or obscission；Fire resistance test uses UL94 standards, and test result is not occur drip phenomenon；
60 degree of relative humidity stand 72h surface colony numbers in the environment of being 60%（cfu/cm2）For 2.2 grades of ozone aging.
Embodiment 3
A kind of environmental protection paint of flame-proof antibiotic, its component include by weight：38 parts of waterborne polyurethane resin, epoxy resin 27
Part, 18 parts of urea formaldehyde resin, 14 parts of pitch, 4 parts of sodium salicylate, 4 parts of acetamide, 8 parts of antioxidant MB, 4 parts of triethylamine, thickening
6 parts of agent, 4 parts of Stearyl Amine, 5 parts of higher aliphatic, 3 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, 2 parts of antibacterial salt ion solution, resistance
Fire 3 parts of agent, 4 parts of silicone emulsion, 150 parts of deionized water.The antibacterial metal ions salting liquid selects Ag+、Mn7+And Zn2+Mixing
Solution, concentration ratio are：n（Ag+）：n（Mn7+）：n（Zn2+）=8：20：35.The thickener select polyethylene glycol oxide, polyvinyl alcohol,
Low-molecular polyethylene wax and polyacrylamide.The fire retardant selects phosphate compound, magnesium hydroxide, hydration zinc borate.
A kind of preparation method of the environmental protection paint of flame-proof antibiotic, its preparation method comprise the following steps：
A, waterborne polyurethane resin, epoxy resin, urea formaldehyde resin and pitch are placed in pulverizer respectively and are crushed, then
Ground by grinder, gained each component powder is retained separately, spare；
B, the phenolic resin obtained by step a, epoxy resin, urea formaldehyde resin, pitch and deionized water are added to high-speed stirred
Gu Zhong, is warming up to 100 DEG C and stirs 95min, obtained component is denoted as blending ingredients A；The rotating speed of high-speed stirred kettle is 1800r/
min；
C, sodium salicylate, acetamide, antioxidant MB and deionized water are added in liquid material a mixing bowl, and by liquid material a mixing bowl
Vacuumize, and 30min is stirred with the speed of 600r/min, obtained component is denoted as blending ingredients B；Temperature in liquid material a mixing bowl is
140℃；
D, blending ingredients A is added in blending ingredients B, then remaining raw material is added thereto and stirs 60min, up into
Product.
After tested, the surface drying hardening time of the coating prepared by embodiment 3（25℃）It is for 23h, shear strength
0.94MPa, adhesion strength 0.42MPa, by coating be immersed in 20 DEG C, mass concentration be 6% brine in 720h do not find coating
Generation cracking, aliquation or obscission；Fire resistance test uses UL94 standards, and test result is not occur drip phenomenon；
60 degree of relative humidity stand 72h surface colony numbers in the environment of being 60%（cfu/cm2）For 2.2 grades of ozone aging.
The better embodiment of this patent is explained in detail above, but this patent is not limited to above-mentioned embodiment party
Formula, can also be on the premise of this patent objective not be departed from the knowledge that one skilled in the relevant art possesses
Make a variety of changes.
Claims (8)
1. a kind of environmental protection paint of flame-proof antibiotic, it is characterised in that its component includes by weight：Waterborne polyurethane resin 35-
48 parts, 22-30 parts of epoxy resin, 15-20 parts of urea formaldehyde resin, 10-16 parts of pitch, 3-5 parts of sodium salicylate, 3-5 parts of acetamide,
6-10 parts of antioxidant MB, 3-6 parts of triethylamine, 5-8 parts of thickener, 3-6 parts of Stearyl Amine, 3-6 parts of higher aliphatic, polyoxy second
2.5-3.5 parts of alkene polyoxy propyl alcohol amidogen ether, 1.8-3.2 parts of antibacterial salt ion solution, 2.5-3.5 parts of fire retardant, silicone emulsion 2-5
Part, appropriate amount of deionized water.
2. the environmental protection paint of flame-proof antibiotic according to claim 1, it is characterised in that its component includes by weight：Water
38 parts of polyurethane resin of property, 27 parts of epoxy resin, 18 parts of urea formaldehyde resin, 14 parts of pitch, 4 parts of sodium salicylate, 4 parts of acetamide,
8 parts of antioxidant MB, 4 parts of triethylamine, 6 parts of thickener, 4 parts of Stearyl Amine, 5 parts of higher aliphatic, polyoxyethylene polyoxy Propanolamine
3 parts of ether, 2 parts of antibacterial salt ion solution, 3 parts of fire retardant, 4 parts of silicone emulsion, 150 parts of deionized water.
3. the preparation method of the environmental protection paint of flame-proof antibiotic according to claim 1, it is characterised in that the antibacterial metal from
Alite solution selects Ag+、Mn7+And Zn2+Mixed solution, concentration ratio are：n（Ag+）：n（Mn7+）：n（Zn2+）=8：20：35.
4. the preparation method of the environmental protection paint of flame-proof antibiotic according to claim 1, it is characterised in that the thickener is selected
In Sodium Polyacrylate, polyethylene glycol oxide, polyvinylpyrrolidone, polyvinyl alcohol, low-molecular polyethylene wax and polyacrylamide
Three kinds or four kinds.
5. the preparation method of the environmental protection paint of flame-proof antibiotic according to claim 1, it is characterised in that the fire retardant is selected
Two or three in phosphate compound, magnesium hydroxide, hydration zinc borate and talcum powder.
6. the preparation method of the environmental protection paint of a kind of flame-proof antibiotic as described in claim 1-5 is any, it is characterised in that it is prepared
Method comprises the following steps：
A, waterborne polyurethane resin, epoxy resin, urea formaldehyde resin and pitch are placed in pulverizer respectively and are crushed, then
Ground by grinder, gained each component powder is retained separately, spare；
B, the phenolic resin obtained by step a, epoxy resin, urea formaldehyde resin, pitch and deionized water are added to high-speed stirred
Gu Zhong, is warming up to 80-120 DEG C and stirs 85-110min, obtained component is denoted as blending ingredients A；
C, sodium salicylate, acetamide, antioxidant MB and deionized water are added in liquid material a mixing bowl, and by liquid material a mixing bowl
Vacuumize, and 20-35min is stirred with the speed of 550-660r/min, obtained component is denoted as blending ingredients B；
D, blending ingredients A is added in blending ingredients B, then remaining raw material is added thereto and stirs 50-70min, to obtain the final product
Finished product.
7. the preparation method of the environmental protection paint of flame-proof antibiotic according to claim 6, it is characterised in that high in the step b
The rotating speed of fast stirred tank is 1500-2000r/min.
8. the preparation method of the environmental protection paint of flame-proof antibiotic according to claim 6, it is characterised in that in the step c
Temperature in liquid material a mixing bowl is 120-160 DEG C.