CN107312434A - One kind finishing environment-friendly type waterproof paint and preparation method thereof - Google Patents
One kind finishing environment-friendly type waterproof paint and preparation method thereof Download PDFInfo
- Publication number
- CN107312434A CN107312434A CN201710524045.2A CN201710524045A CN107312434A CN 107312434 A CN107312434 A CN 107312434A CN 201710524045 A CN201710524045 A CN 201710524045A CN 107312434 A CN107312434 A CN 107312434A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- friendly type
- finishing
- type waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of finishing environment-friendly type waterproof paint, the paint includes following raw materials：25 45 parts of polyurethane, 12 15 parts of ferrous oxide nanoscale micro mist, 6 10 parts of turpentine oil, 9 12 parts of radioresistance slurry, 8 14 parts of zinc naphthenate, 10 15 parts of gypsum, 6 11 parts of lactic acid, 37 parts of blanc fixe, 24 parts of waterproofing agent, 36 parts of drier, 13 parts of thickener；Manufacture craft of the present invention is simple, and manufacturing process is environment friendly and pollution-free, and obtained paint is environment-protecting and non-poisonous, harmless, can be widely used for the finishing of various timber, iron material, plastic, paper wood, high-grade coloured furniture, hotel, hospital etc.；Ferrous oxide nanoscale micro mist, radioresistance slurry and waterproofing agent are also added with the present invention, it is possible to increase oxidation resistance, capability of resistance to radiation and the waterproof effect of paint, extend the holding time of paint.
Description
Technical field
The present invention relates to paint field, more particularly to a kind of finishing environment-friendly type waterproof paint and preparation method thereof.
Background technology
Paint is that one kind can firmly be covered in body surface, and the chemistry for playing protection, decoration, mark and other specific uses is mixed
Compound coating.Chinese coating circle is more authoritative《Coating process》What one book was defined as：" coating is a kind of material, this
Material can be coated in object surface with different construction technologies, form adhesion firm, thin with some strength, continuous solid-state
Film.The film common name film so formed, also known as paint film or coating.”
The paint of current finishing is all chemicals, can constantly volatile organic compound and episome especially after application.
Ozone pollution not only is produced to the Nature, but also human body can be made to cause the various diseases such as headache, general paralysis, anaemia, cancer,
Carry out serious threat to human body health care belt, but be a kind of unavoidable necessary material.
The content of the invention
In order to solve deficiency of the prior art, it is an object of the invention to provide a kind of finishing environment-friendly type waterproof paint
And preparation method thereof.
The technical solution adopted in the present invention is：One kind finishing environment-friendly type waterproof paint, the paint includes pressing below
The raw material of weight：25-45 parts of polyurethane, 12-15 parts of ferrous oxide nanoscale micro mist, 6-10 parts of turpentine oil, radioresistance
9-12 parts of slurry, 8-14 parts of zinc naphthenate, 10-15 parts of gypsum, 6-11 parts of lactic acid, 3-7 parts of blanc fixe, 2-4 parts of waterproofing agent, urge
Dry 3-6 parts of agent, 1-3 parts of thickener.
Further, the waterproofing agent includes the raw material that following precentagewise is matched：Inorganic potassium salt 30.45%, rosin
8.25%th, sodium hydroxide 18.56%, polyvinylpyrrolidone 3.57%, hydroxymethyl cellulose 21.55%.
Further, the thickener is the mixed of methylcellulose or sodium bentonite or polyvinyl alcohol and gum arabic
Compound, both proportion is 2-3:1.
The preparation method of described finishing environment-friendly type waterproof paint comprises the steps：
1) polyurethane, gypsum and zinc naphthenate are smashed into powder respectively, mixed, radioresistance slurry is added, at 35-50 DEG C
Lower stirring 30-40min, is cooled to room temperature after stirring, add blanc fixe and ferrous oxide nanoscale micro mist, mistake after mixing
At night, the first mixture is obtained, it is standby；
2) lactic acid is added to the first obtained mixture, is heated at 70-85 DEG C after 60-75min, waterproof is added while hot
Agent, drier and thickener, after stirring and evenly mixing, obtain the second mixture；
3) turpentine oil is added into the second obtained mixture, 25-35min is heated at 30-45 DEG C, then carry out ultrasound
Handle after 30-35min, be cooled to room temperature.
Further, the whipping temp in the step 1 is 45 DEG C.
Further, the mixing time in the step 1 is 35min.
Further, the heating-up temperature in the step 2 is 80 DEG C.
Further, the heat time in the step 2 is 65min.
Further, ultrasonic power ultrasonically treated in the step 3 is 750W.
The finishing that the present invention is provided is with the beneficial effect of environment-friendly type waterproof paint and preparation method thereof：The present invention makes work
Skill is simple, and manufacturing process is environment friendly and pollution-free, and obtained paint is environment-protecting and non-poisonous, harmless, can be widely used for various timber, iron
The finishing of material, plastic, paper wood, high-grade coloured furniture, hotel, hospital etc.；It is also micro- added with ferrous oxide nanoscale in the present invention
Powder, radioresistance slurry and waterproofing agent, it is possible to increase oxidation resistance, capability of resistance to radiation and the waterproof effect of paint, extend oil
The holding time of paint.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to embodiments, to the present invention
It is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, it is not used to
Limit the present invention.
Embodiment 1
One kind finishing environment-friendly type waterproof paint, the paint includes following raw materials：Polyurethane 30
Part, 14 parts of ferrous oxide nanoscale micro mist, 8 parts of turpentine oil, 11 parts of radioresistance slurry, 12 parts of zinc naphthenate, 13 parts of gypsum, lactic acid
9 parts, 5 parts of blanc fixe, 3 parts of waterproofing agent, 5 parts of drier, 2 parts of thickener.
The waterproofing agent includes the raw material that following precentagewise is matched：Inorganic potassium salt 30.45%, rosin 8.25%, hydrogen-oxygen
Change sodium 18.56%, polyvinylpyrrolidone 3.57%, hydroxymethyl cellulose 21.55%.
The thickener is the mixture of methylcellulose and gum arabic, and both proportion is 2:1.
Described finishing is with the preparation method of environment-friendly type waterproof paint：First by polyurethane, gypsum and zinc naphthenate point
Powder is not smashed into, is mixed, radioresistance slurry is added, stirs 35min at 45 DEG C, room temperature is cooled to after stirring, and is added
Blanc fixe and ferrous oxide nanoscale micro mist, after mixing overnight, obtain the first mixture, standby；Then it is mixed to first obtained
Compound adds lactic acid, is heated at 80 DEG C after 65min, and waterproofing agent, drier and thickener are added while hot, after stirring and evenly mixing, is obtained
Second mixture；Then turpentine oil is added into the second obtained mixture, 30min is heated at 40 DEG C, then carry out ultrasound
32min is handled, ultrasonic power is 750W, is finally cooled to room temperature.
Manufacture craft of the present invention is simple, and manufacturing process is environment friendly and pollution-free, and obtained paint is environment-protecting and non-poisonous, harmless,
It can be widely used for the finishing of various timber, iron material, plastic, paper wood, high-grade coloured furniture, hotel, hospital etc.；Also add in the present invention
Added with ferrous oxide nanoscale micro mist, radioresistance slurry and waterproofing agent, it is possible to increase the oxidation resistance of paint, capability of resistance to radiation
And waterproof effect, extend the holding time of paint.
Embodiment 2
One kind finishing environment-friendly type waterproof paint, the paint includes following raw materials：Polyurethane 25
Part, 12 parts of ferrous oxide nanoscale micro mist, 6 parts of turpentine oil, 9 parts of radioresistance slurry, 8 parts of zinc naphthenate, 10 parts of gypsum, lactic acid 6
Part, 3 parts of blanc fixe, 2 parts of waterproofing agent, 3 parts of drier, 1 part of thickener.
The waterproofing agent includes the raw material that following precentagewise is matched：Inorganic potassium salt 30.45%, rosin 8.25%, hydrogen-oxygen
Change sodium 18.56%, polyvinylpyrrolidone 3.57%, hydroxymethyl cellulose 21.55%.
The thickener is the mixture of sodium bentonite and gum arabic, and both proportion is 2:1.
Described finishing is with the preparation method of environment-friendly type waterproof paint：First by polyurethane, gypsum and zinc naphthenate point
Powder is not smashed into, is mixed, radioresistance slurry is added, stirs 30min at 35 DEG C, room temperature is cooled to after stirring, and is added
Blanc fixe and ferrous oxide nanoscale micro mist, after mixing overnight, obtain the first mixture, standby；Then it is mixed to first obtained
Compound adds lactic acid, is heated at 70 DEG C after 60min, and waterproofing agent, drier and thickener are added while hot, after stirring and evenly mixing, is obtained
Second mixture；Then turpentine oil is added into the second obtained mixture, 25min is heated at 30 DEG C, then carry out ultrasound
30min is handled, ultrasonic power is 750W, is finally cooled to room temperature.
Manufacture craft of the present invention is simple, and manufacturing process is environment friendly and pollution-free, and obtained paint is environment-protecting and non-poisonous, harmless,
It can be widely used for the finishing of various timber, iron material, plastic, paper wood, high-grade coloured furniture, hotel, hospital etc.；Also add in the present invention
Added with ferrous oxide nanoscale micro mist, radioresistance slurry and waterproofing agent, it is possible to increase the oxidation resistance of paint, capability of resistance to radiation
And waterproof effect, extend the holding time of paint.
Embodiment 3
One kind finishing environment-friendly type waterproof paint, the paint includes following raw materials：Polyurethane 45
Part, 15 parts of ferrous oxide nanoscale micro mist, 10 parts of turpentine oil, 12 parts of radioresistance slurry, 14 parts of zinc naphthenate, 15 parts of gypsum, breast
11 parts of acid, 7 parts of blanc fixe, 4 parts of waterproofing agent, 6 parts of drier, 3 parts of thickener.
The waterproofing agent includes the raw material that following precentagewise is matched：Inorganic potassium salt 30.45%, rosin 8.25%, hydrogen-oxygen
Change sodium 18.56%, polyvinylpyrrolidone 3.57%, hydroxymethyl cellulose 21.55%.
The thickener is the mixture of polyvinyl alcohol and gum arabic, and both proportion is 3:1.
Described finishing is with the preparation method of environment-friendly type waterproof paint：First by polyurethane, gypsum and zinc naphthenate point
Powder is not smashed into, is mixed, radioresistance slurry is added, stirs 40min at 50 DEG C, room temperature is cooled to after stirring, and is added
Blanc fixe and ferrous oxide nanoscale micro mist, after mixing overnight, obtain the first mixture, standby；Then it is mixed to first obtained
Compound adds lactic acid, is heated at 85 DEG C after 75min, and waterproofing agent, drier and thickener are added while hot, after stirring and evenly mixing, is obtained
Second mixture；Then turpentine oil is added into the second obtained mixture, 35min is heated at 45 DEG C, then carry out ultrasound
35min is handled, ultrasonic power is 750W, is finally cooled to room temperature.
Manufacture craft of the present invention is simple, and manufacturing process is environment friendly and pollution-free, and obtained paint is environment-protecting and non-poisonous, harmless,
It can be widely used for the finishing of various timber, iron material, plastic, paper wood, high-grade coloured furniture, hotel, hospital etc.；Also add in the present invention
Added with ferrous oxide nanoscale micro mist, radioresistance slurry and waterproofing agent, it is possible to increase the oxidation resistance of paint, capability of resistance to radiation
And waterproof effect, extend the holding time of paint.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all essences in the present invention
Any modifications, equivalent substitutions and improvements made within refreshing and principle etc., should be included in protection scope of the present invention.
Claims (9)
1. one kind finishing uses environment-friendly type waterproof paint, it is characterised in that the paint includes following raw materials：
25-45 parts of polyurethane, 12-15 parts of ferrous oxide nanoscale micro mist, 6-10 parts of turpentine oil, 9-12 parts of radioresistance slurry, aphthenic acids
8-14 parts of zinc, 10-15 parts of gypsum, 6-11 parts of lactic acid, 3-7 parts of blanc fixe, 2-4 parts of waterproofing agent, 3-6 parts of drier, thickener
1-3 parts.
2. finishing according to claim 1 uses environment-friendly type waterproof paint, it is characterised in that the waterproofing agent includes pressing below
The raw material of percentage proportioning：Inorganic potassium salt 30.45%, rosin 8.25%, sodium hydroxide 18.56%, polyvinylpyrrolidone
3.57%th, hydroxymethyl cellulose 21.55%.
3. finishing according to claim 1 uses environment-friendly type waterproof paint, it is characterised in that the thickener is Methyl cellulose
The mixture of element or sodium bentonite or polyvinyl alcohol and gum arabic, both proportion is 2-3:1.
4. the preparation method based on any described finishing environment-friendly type waterproof paints of claim 1-3, it is characterised in that described
Method comprises the steps：
1) polyurethane, gypsum and zinc naphthenate are smashed into powder respectively, mixed, added radioresistance slurry, stirred at 35-50 DEG C
30-40min is mixed, room temperature is cooled to after stirring, blanc fixe and ferrous oxide nanoscale micro mist is added, after mixing overnight,
The first mixture is obtained, it is standby；
2) lactic acid is added to the first obtained mixture, is heated at 70-85 DEG C after 60-75min, waterproofing agent is added while hot, is urged
Dry agent and thickener, after stirring and evenly mixing, obtain the second mixture；
3) turpentine oil is added into the second obtained mixture, 25-35min is heated at 30-45 DEG C, then carried out ultrasonically treated
After 30-35min, room temperature is cooled to.
5. the preparation method of finishing environment-friendly type waterproof paint according to claim 4, it is characterised in that the step 1
In whipping temp be 45 DEG C.
6. the preparation method of finishing environment-friendly type waterproof paint according to claim 4, it is characterised in that the step 1
In mixing time be 35min.
7. the preparation method of finishing environment-friendly type waterproof paint according to claim 4, it is characterised in that the step 2
In heating-up temperature be 80 DEG C.
8. the preparation method of finishing environment-friendly type waterproof paint according to claim 4, it is characterised in that the step 2
In heat time be 65min.
9. the preparation method of finishing environment-friendly type waterproof paint according to claim 4, it is characterised in that the step 3
In ultrasonically treated ultrasonic power be 750W.