CN108044747A - A kind of processing method of resistant preserving timber - Google Patents
A kind of processing method of resistant preserving timber Download PDFInfo
- Publication number
- CN108044747A CN108044747A CN201711210120.4A CN201711210120A CN108044747A CN 108044747 A CN108044747 A CN 108044747A CN 201711210120 A CN201711210120 A CN 201711210120A CN 108044747 A CN108044747 A CN 108044747A
- Authority
- CN
- China
- Prior art keywords
- parts
- processing method
- preserving timber
- resistant
- mentioned steps
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of processing method of resistant preserving timber, including following operating procedure：（1）After log is processed into plate, surface carries out grinding process using 400# sand paper, then in wood surface brushing aqueous priming paint；（2）After ten trifluoro monooctyl ester of methacrylic acid, acrylic acid, methyl methacrylate, tetrabutyl ammonium fluoride, polyethylene glycol oxide, deionized water are mixed, persistently stir 40 50min, then the temperature of mixture is risen to 80 85 DEG C, and 36 parts of potassium peroxydisulfates are slowly added dropwise thereto, after being added dropwise to complete, after when isothermal holding 23 is small, fluorine carbon copolymer emulsion is made, then four water kodalks, Crodaret, Polyethylenimine are added in thereto, after mixing, resistant preserving timber coating is made, is squeegeed onto by step（1）The wood surface of processing, is put into baking oven, finished product after drying.By this method treated timber, there is excellent resistant antiseptic property.
Description
Technical field
The invention belongs to wood processing technique fields, and in particular to a kind of processing method of resistant preserving timber.
Background technology
At home and abroad, timber is always widely used in architecture indoor finishing and decoration, it gives the enjoyment of natural beauty, also
The interior space can be made to generate warm and cordial feeling.Timber has its unique advantage due to its characteristic as construction material：Green ring
It protects, it is renewable, it is degradable；Construction is simple, short time limit；It is cool in summer and warm in winter；Excellent earthquake resistance.In the prior art, timber is carried out
Preservative treatment, be using dipping impregnating fluid, this processing mode there is the of high cost and anti-corrosion cycle it is short the defects of, it is existing simultaneously
Some wood surfaces seldom have antifouling performance.
The content of the invention
In order to solve the above technical problem, the present invention provides a kind of processing methods of resistant preserving timber.
The present invention is achieved by the following technical solutions.
A kind of processing method of resistant preserving timber, including following operating procedure：
（1）After log is processed into plate, surface carries out grinding process using 400# sand paper, then aqueous in wood surface brushing
Then timber is put into baking oven by priming paint, be heating and curing paint film, and wherein aqueous priming paint is made of the component of following parts by weight：Water
35-42 parts of emulsion acrylic resin of property, 1-3 parts of four polyethyleneglycol octyl ether, 1-4 parts of ammonium pentaborate, 3-5 parts of spodumene；
（2）By weight, by 31-38 parts of ten trifluoro monooctyl esters of methacrylic acid, 20-27 parts of acrylic acid, 15-20 parts of metering systems
After sour methyl esters, 11-14 part tetrabutyl ammonium fluoride, 3-8 parts of polyethylene glycol oxides, 45-55 parts of deionized water mixing, 40- is persistently stirred
Then the temperature of mixture is risen to 80-85 DEG C, and 3-6 parts of potassium peroxydisulfates is slowly added dropwise thereto by 50min, be added dropwise to complete
Afterwards, after when isothermal holding 2-3 is small, fluorine carbon copolymer emulsion is made, four water for then adding in copolymer emulsion quality 2-4% thereto are inclined
Boratex, 6-10% Crodarets, the Polyethylenimine of 1-5% after mixing, are made resistant preserving timber and apply
Material, is squeegeed onto by step（1）The wood surface of processing, is put into baking oven, finished product after drying.
Specifically, above-mentioned steps（1）In, the solid content of water-based acrylic resin lotion is 54-58%.
Specifically, above-mentioned steps（1）In, the Average Particle Diameters of spodumene are 250-300 mesh.
Specifically, above-mentioned steps（1）In, the temperature of drying is 60-70 DEG C.
Specifically, above-mentioned steps（1）In, the molecular weight of above-mentioned Polyethylenimine is 1800, purity 99%.
Specifically, above-mentioned steps（2）In, the temperature of drying is 55-65 DEG C, when the time 3-4 of drying is small.
From the above technical scheme, it can be seen that the beneficial effects of the invention are as follows：
The processing method of resistant preserving timber provided by the invention, easy to operate, of low cost, treated timber, surface are hard
The phenomenon that degree is high, and face coat will not be worn in subsequent process, plate obtained have excellent resistance to soiling
Energy and antiseptic property, anti-corrosion time are long.In the present invention, first aqueous priming paint, water provided by the invention on the external coating of timber
Property priming paint, wood surface have excellent adhesive property, with the present invention resistant preserving timber coating also have it is excellent
Adhesive property, and then effectively promote the adhesive force of film layer of the present invention so that film layer of the invention is less prone to the phenomenon that coming off,
Meanwhile aqueous priming paint provided by the invention, there is extremely excellent compactness, steam outside isolation that can be to a certain extent,
Air enters wood internal so that the parasitic microbe of wood internal cannot breathe air and dead, effectively extend plate
Service life；Resistant preserving timber coating produced by the present invention, surface contain substantial amounts of fluorine element, greatly improve wood
The water contact angle on material surface, and then the effective antifouling property for improving timber；Meanwhile the obtained resistant preserving timber of the present invention applies
Material has both excellent anti-microbial property, can effectively inhibit pathogenic microorganisms in its surface growth and breeding；The addition of polyethylene glycol oxide,
Fluoro-acrylate monomer and remaining substance reaction efficiency can be effectively promoted, overcomes fluoro-acrylate monomer and acrylic acid, first
Poor compatibility between base methyl acrylate, cause reaction inefficiency the problem of；The addition of tetrabutyl ammonium fluoride, except energy
It provides outside fluorine element, there is excellent anti-microbial property simultaneously；Four water kodalks and Crodaret collaboration are made
With rear, the intensity of film surface on the one hand can be effectively promoted, promotes the consistency of film layer, on the other hand, had excellent anti-
Bacterium performance；Polyethylenimine then can effectively promote the adhesion property of film layer.
Specific embodiment
Following embodiment is used for illustrating the present invention, but cannot be used for limiting the scope of the invention, the reality used in embodiment
The condition of applying can be for further adjustments according to the condition of producer, and unaccounted implementation condition is usually conventional laboratory conditions.
Embodiment 1
A kind of processing method of resistant preserving timber, including following operating procedure：
（1）After log is processed into plate, surface carries out grinding process using 400# sand paper, then aqueous in wood surface brushing
Then timber is put into baking oven by priming paint, be heating and curing paint film, and wherein aqueous priming paint is made of the component of following parts by weight：Water
35 parts of emulsion acrylic resin of property, 1 part of four polyethyleneglycol octyl ether, 1 part of ammonium pentaborate, 3 parts of spodumene；
（2）By weight, by 31 parts of ten trifluoro monooctyl esters of methacrylic acid, 20 parts of acrylic acid, 15 parts of methyl methacrylates, 11
After part tetrabutyl ammonium fluoride, 3 parts of polyethylene glycol oxides, 45 parts of deionized waters mixing, 40min is persistently stirred, then by mixture
Temperature rises to 80 DEG C, and 3 parts of potassium peroxydisulfates are slowly added dropwise thereto, after being added dropwise to complete, when isothermal holding 2 is small after, fluorine is made
Then carbon copolymer emulsion adds in four water kodalks of copolymer emulsion quality 2%, 6% Crodaret, 1% thereto
Polyethylenimine, after mixing, resistant preserving timber coating is made, is squeegeed onto by step（1）The timber table of processing
Face is put into baking oven, finished product after drying.
Specifically, above-mentioned steps（1）In, the solid content of water-based acrylic resin lotion is 54%.
Specifically, above-mentioned steps（1）In, the Average Particle Diameters of spodumene are 250 mesh.
Specifically, above-mentioned steps（1）In, the temperature of drying is 60 DEG C.
Specifically, above-mentioned steps（1）In, the molecular weight of above-mentioned Polyethylenimine is 1800, purity 99%.
Specifically, above-mentioned steps（2）In, the temperature of drying is 55 DEG C, when the time 3 of drying is small.
After furniture is made in plate in the present embodiment, normal use 3 years carries out hydrophobic, oleophobic to its surface and tests,
Middle water contact angle is 158 °, and water roll angle is 4 °, and ethyl alcohol contact angle is 149 °, and ethyl alcohol roll angle is 8 °, it follows that of the invention
Plate obtained, after normal use 3 years, still with excellent hydrophobic oleophobic performance, i.e., with excellent anti-pollution characteristic,
The corrosion-free phenomenon of timber occurs simultaneously.
Embodiment 2
A kind of processing method of resistant preserving timber, including following operating procedure：
（1）After log is processed into plate, surface carries out grinding process using 400# sand paper, then aqueous in wood surface brushing
Then timber is put into baking oven by priming paint, be heating and curing paint film, and wherein aqueous priming paint is made of the component of following parts by weight：Water
38 parts of emulsion acrylic resin of property, 2 parts of four polyethyleneglycol octyl ether, 3 parts of ammonium pentaborate, 4 parts of spodumene；
（2）By weight, by 34 parts of ten trifluoro monooctyl esters of methacrylic acid, 25 parts of acrylic acid, 18 parts of methyl methacrylates, 13
After part tetrabutyl ammonium fluoride, 5 parts of polyethylene glycol oxides, 50 parts of deionized waters mixing, 45min is persistently stirred, then by mixture
Temperature rises to 83 DEG C, and 5 parts of potassium peroxydisulfates are slowly added dropwise thereto, after being added dropwise to complete, when isothermal holding 2.5 is small after, be made
Fluorine carbon copolymer emulsion, then add in thereto four water kodalks of copolymer emulsion quality 3%, 8% Crodaret,
3% Polyethylenimine after mixing, is made resistant preserving timber coating, is squeegeed onto by step（1）The timber of processing
Surface is put into baking oven, finished product after drying.
Specifically, above-mentioned steps（1）In, the solid content of water-based acrylic resin lotion is 56%.
Specifically, above-mentioned steps（1）In, the Average Particle Diameters of spodumene are 280 mesh.
Specifically, above-mentioned steps（1）In, the temperature of drying is 65 DEG C.
Specifically, above-mentioned steps（1）In, the molecular weight of above-mentioned Polyethylenimine is 1800, purity 99%.
Specifically, above-mentioned steps（2）In, the temperature of drying is 60 DEG C, when the time 3.5 of drying is small.
After furniture is made in plate in the present embodiment, normal use 3 years carries out hydrophobic, oleophobic to its surface and tests,
Middle water contact angle is 159 °, and water roll angle is 3.5 °, and ethyl alcohol contact angle is 151 °, and ethyl alcohol roll angle is 8 °, it follows that this hair
Bright plate obtained, after normal use 3 years, still with excellent hydrophobic oleophobic performance, i.e., with excellent resistance to soiling
Can, while the corrosion-free phenomenon of timber occurs.
Embodiment 3
A kind of processing method of resistant preserving timber, including following operating procedure：
（1）After log is processed into plate, surface carries out grinding process using 400# sand paper, then aqueous in wood surface brushing
Then timber is put into baking oven by priming paint, be heating and curing paint film, and wherein aqueous priming paint is made of the component of following parts by weight：Water
42 parts of emulsion acrylic resin of property, 3 parts of four polyethyleneglycol octyl ether, 4 parts of ammonium pentaborate, 5 parts of spodumene；
（2）By weight, by 38 parts of ten trifluoro monooctyl esters of methacrylic acid, 27 parts of acrylic acid, 20 parts of methyl methacrylates, 14
After part tetrabutyl ammonium fluoride, 8 parts of polyethylene glycol oxides, 55 parts of deionized waters mixing, 50min is persistently stirred, then by mixture
Temperature rises to 85 DEG C, and 6 parts of potassium peroxydisulfates are slowly added dropwise thereto, after being added dropwise to complete, when isothermal holding 3 is small after, fluorine is made
Carbon copolymer emulsion, then add in thereto four water kodalks of copolymer emulsion quality 4%, 10% Crodaret,
5% Polyethylenimine after mixing, is made resistant preserving timber coating, is squeegeed onto by step（1）The timber of processing
Surface is put into baking oven, finished product after drying.
Specifically, above-mentioned steps（1）In, the solid content of water-based acrylic resin lotion is 58%.
Specifically, above-mentioned steps（1）In, the Average Particle Diameters of spodumene are 300 mesh.
Specifically, above-mentioned steps（1）In, the temperature of drying is 70 DEG C.
Specifically, above-mentioned steps（1）In, the molecular weight of above-mentioned Polyethylenimine is 1800, purity 99%.
Specifically, above-mentioned steps（2）In, the temperature of drying is 65 DEG C, when the time 4 of drying is small.
After furniture is made in plate in the present embodiment, normal use 3 years carries out hydrophobic, oleophobic to its surface and tests,
Middle water contact angle is 161 °, and water roll angle is 3 °, and ethyl alcohol contact angle is 152 °, and ethyl alcohol roll angle is 7 °, it follows that of the invention
Plate obtained, after normal use 3 years, still with excellent hydrophobic oleophobic performance, i.e., with excellent anti-pollution characteristic,
The corrosion-free phenomenon of timber occurs simultaneously.
It should be appreciated that the application of the present invention is not limited to the above, it for those of ordinary skills, can
To be improved or converted according to the above description, all these modifications and variations should all belong to the guarantor of appended claims of the present invention
Protect scope.
Claims (6)
1. a kind of processing method of resistant preserving timber, which is characterized in that including following operating procedure：
（1）After log is processed into plate, surface carries out grinding process using 400# sand paper, then aqueous in wood surface brushing
Then timber is put into baking oven by priming paint, be heating and curing paint film, and wherein aqueous priming paint is made of the component of following parts by weight：Water
35-42 parts of emulsion acrylic resin of property, 1-3 parts of four polyethyleneglycol octyl ether, 1-4 parts of ammonium pentaborate, 3-5 parts of spodumene；
（2）By weight, by 31-38 parts of ten trifluoro monooctyl esters of methacrylic acid, 20-27 parts of acrylic acid, 15-20 parts of metering systems
After sour methyl esters, 11-14 part tetrabutyl ammonium fluoride, 3-8 parts of polyethylene glycol oxides, 45-55 parts of deionized water mixing, 40- is persistently stirred
Then the temperature of mixture is risen to 80-85 DEG C, and 3-6 parts of potassium peroxydisulfates is slowly added dropwise thereto by 50min, be added dropwise to complete
Afterwards, after when isothermal holding 2-3 is small, fluorine carbon copolymer emulsion is made, four water for then adding in copolymer emulsion quality 2-4% thereto are inclined
Boratex, 6-10% Crodarets, the Polyethylenimine of 1-5% after mixing, are made resistant preserving timber and apply
Material, is squeegeed onto by step（1）The wood surface of processing, is put into baking oven, finished product after drying.
A kind of 2. processing method of resistant preserving timber according to claim 1, which is characterized in that above-mentioned steps（1）In,
The solid content of water-based acrylic resin lotion is 54-58%.
A kind of 3. processing method of resistant preserving timber according to claim 1, which is characterized in that above-mentioned steps（1）In,
The Average Particle Diameters of spodumene are 250-300 mesh.
A kind of 4. processing method of resistant preserving timber according to claim 1, which is characterized in that above-mentioned steps（1）In,
The temperature of drying is 60-70 DEG C.
A kind of 5. processing method of resistant preserving timber according to claim 1, which is characterized in that above-mentioned steps（1）In,
The molecular weight of above-mentioned Polyethylenimine is 1800, purity 99%.
A kind of 6. processing method of resistant preserving timber according to claim 1, which is characterized in that above-mentioned steps（2）In,
The temperature of drying is 55-65 DEG C, when the time 3-4 of drying is small.