CN106145671A - A kind of preparation method of material exquisiteness coloured glaze - Google Patents
A kind of preparation method of material exquisiteness coloured glaze Download PDFInfo
- Publication number
- CN106145671A CN106145671A CN201610640520.8A CN201610640520A CN106145671A CN 106145671 A CN106145671 A CN 106145671A CN 201610640520 A CN201610640520 A CN 201610640520A CN 106145671 A CN106145671 A CN 106145671A
- Authority
- CN
- China
- Prior art keywords
- raw material
- continues
- coloured glaze
- preparation
- exquisiteness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the preparation method of a kind of material exquisiteness coloured glaze, it is characterised in that including: weigh raw material;Raw material refines;Raw material preheats, and pre-heating temperature is maintained at 250 300 DEG C, continues 23 hours;Raw material melts, and melt temperature controls at 1500 DEG C, continues 20 hours;High temperature is clarified, and clarifying temp is 1,650 1700 DEG C, continues 18 hours;Mould molding;Cooling refine;Annealing, annealing temperature controls at 500 DEG C, continues 5 hours;Secondary fine repaiies above-mentioned steps.By the way, the present invention is obtained in that material is fine and smooth, bright, the coloured glaze product that texture is splendid.
Description
Technical field
The present invention relates to coloured glaze casting technique field, particularly relate to the preparation method of a kind of matter exquisiteness coloured glaze.
Background technology
Coloured glaze, also making " glass " is that the synthetic quartz with shades of colour (color is to be formed by various rare metals) is (containing 24%
Lead oxide brown) be raw material, be more than 1000 degree high temperature under fire.Its color stream cloud drenches coloured silk;Its quality is sparkling and crystal-clear picks
Thoroughly, bright and glittering, ancient Chinese manufactures coloured glaze and initially makes the material of coloured glaze, is when bronze ware cast the side-product of generation
Obtain, then make coloured glaze through refining processing.The color of coloured glaze is varied, and ancients are also its " five colored stones ".Ancient times by
Hardly result among the people, so people even regard coloured glaze as more precious than jadeware at that time, how to make colored glaze product material more
Add fine and smooth perfect, be a problem needing research.
Summary of the invention
The technical problem that present invention mainly solves is to provide the preparation method of a kind of material exquisiteness coloured glaze, it is possible to obtain material
Exquisiteness, bright, the coloured glaze product that texture is splendid.
For solving above-mentioned technical problem, the technical scheme that the present invention uses is: provide a kind of material exquisiteness coloured glaze
Preparation method, it is characterised in that including: weigh raw material;Raw material refines;Raw material preheats, and pre-heating temperature is maintained at 250-300
DEG C, continue 2-3 hour;Raw material melts, and melt temperature controls at 1500 DEG C, continues 20 hours;High temperature is clarified, and clarifying temp is
1650-1700 DEG C, continue 18 hours;Mould molding;Cooling refine;Annealing, annealing temperature controls at 500 DEG C, continues 5 hours;
The steps such as secondary refine.
In a preferred embodiment of the present invention, described raw material includes quartz sand, oxidant, clarifier, coloring agent.
In a preferred embodiment of the present invention, described raw material fine grinding is to be ground raw material by high accuracy grinder
Beat thin.
In a preferred embodiment of the present invention, mould molding mould therefor is high temperature resistant casting gypsum powder mould.
The invention has the beneficial effects as follows: the present invention is obtained in that material is fine and smooth, bright, the coloured glaze product that texture is splendid
Product.
Detailed description of the invention
Below presently preferred embodiments of the present invention is described in detail so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that thus protection scope of the present invention is made apparent clear and definite defining.
The embodiment of the present invention includes:
The preparation method of a kind of material exquisiteness coloured glaze, it is characterised in that including: weigh raw material;Raw material refines;Raw material preheats,
Pre-heating temperature is maintained at 250-300 DEG C, continues 2-3 hour;Raw material melts, and melt temperature controls at 1500 DEG C, continues 20 little
Time;High temperature is clarified, and clarifying temp is 1650-1700 DEG C, continues 18 hours;Mould molding;Cooling refine;Annealing, annealing temperature
Control at 500 DEG C, continue 5 hours;The steps such as secondary refine.
Further illustrating, described raw material includes quartz sand, oxidant, clarifier, coloring agent;By rational proportion, by former
Expect into subassembly and reach best of breed.
Further illustrating, described raw material fine grinding is to be ground beating carefully to raw material by high accuracy grinder;By height
The grinding of precision grinder, makes feedstock particle size be maintained at 0.1-0.2mm, it is ensured that raw material exquisiteness degree.
Illustrating further, mould molding mould therefor is high temperature resistant casting gypsum powder mould;Can with resistance to 1800 DEG C of high temperature,
Guarantee the molding of colored glaze product.
The present invention is obtained in that material is fine and smooth, bright, the coloured glaze product that texture is splendid.
The foregoing is only embodiments of the invention, not thereby limit the scope of the claims of the present invention, every utilize this
Equivalent structure or equivalence flow process that bright description is made convert, or are directly or indirectly used in other relevant technology necks
Territory, is the most in like manner included in the scope of patent protection of the present invention.
Claims (4)
1. the preparation method of a material exquisiteness coloured glaze, it is characterised in that including: weigh raw material;Raw material refines;Raw material pre-add
Heat, pre-heating temperature is maintained at 250-300 DEG C, continues 2-3 hour;Raw material melts, and melt temperature controls at 1500 DEG C, continues 20
Hour;High temperature is clarified, and clarifying temp is 1650-1700 DEG C, continues 18 hours;Mould molding;Cooling refine;Annealing, annealing temperature
Degree controls at 500 DEG C, continues 5 hours;The steps such as secondary refine.
The preparation method of material exquisiteness coloured glaze the most according to claim 1, it is characterised in that described raw material includes quartz
Sand, oxidant, clarifier, coloring agent.
The preparation method of material exquisiteness coloured glaze the most according to claim 1, it is characterised in that described raw material fine grinding is to pass through
Raw material is ground beating carefully by grinder in high precision.
The preparation method of material exquisiteness coloured glaze the most according to claim 1, it is characterised in that mould molding mould therefor is
High temperature resistant casting gypsum powder mould.