CN109336402A - A kind of preparation process of sky blue implosion guard product - Google Patents
A kind of preparation process of sky blue implosion guard product Download PDFInfo
- Publication number
- CN109336402A CN109336402A CN201811490686.1A CN201811490686A CN109336402A CN 109336402 A CN109336402 A CN 109336402A CN 201811490686 A CN201811490686 A CN 201811490686A CN 109336402 A CN109336402 A CN 109336402A
- Authority
- CN
- China
- Prior art keywords
- parts
- implosion guard
- glassware
- sky blue
- annealing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation processes of sky blue implosion guard product, the raw material of the sky blue implosion guard product is made of the material of following parts by weight: 100 parts of quartz sand, 7-9 parts of lime stone, 3-5 parts of aluminium oxide, 10-12 parts of soda ash, 5-9 parts of albite, 1-2 parts of potassium feldspar, 2-2.6 parts of mullite crystal whisker, 0.2-0.4 parts of zirconium oxide, 1-1.5 parts of copper oxide, and the step of preparation process of the sky blue implosion guard product is as follows: raw material mixing;Melting: sending obtained mixture into melting furnaces, and make persistently to heat up inside melting furnaces, and controls after the temperature in melting furnaces is 1480 ± 20 degrees Celsius, keeps constant temperature, and further such that mixture is melting into glass metal;Molding;Annealing;Processing polishing: the primary glassware after annealing is placed on polishing table and carries out processing polishing, and finally obtains sapphire implosion guard product.The enhancing of glassware explosion-proof obtained by the present invention is highly-safe, more beautiful;And it is convenient for preparing.
Description
Technical field
The present invention relates to glassmaking art more particularly to a kind of preparation processes of sky blue implosion guard product.
Background technique
Glass is fused together and is formed by silica and other chemical substances.The earliest glass manufacturer in the world is
Ancient Egyptian, and with the development of science and technology, the progress of social productive forces, in today's society, the glass system made of glass
Product are widely used in our life.
Demand with people to glassware becomes more extensively, and the glassware of various characteristics comes into being, and by
People are skilled to be manufactured.Wherein, people are in the case where needing the intensity of glassware higher and using relatively safety, preparation
Implosion guard, people are prepared for the glassware of various colors, people are needing glass when needing glassware more beautiful
Glass is beautiful, intensity is high and using in the case where relatively safety, is then prepared for coloured glassware.However traditional handicraft is being made
When making sky blue implosion guard product, there is processes to be more troublesome, and color is impure, intensity is told somebody what one's real intentions are and what safety was poor asks
Topic, is unfavorable for being promoted.For this purpose, we have proposed a kind of preparation processes of sky blue implosion guard product.
Summary of the invention
The purpose of the present invention is to solve disadvantages existing in the prior art, and a kind of sky blue implosion guard proposed
The preparation process of product.
To achieve the goals above, present invention employs following technical solutions:
A kind of preparation process of sky blue implosion guard product, the raw material of the sky blue implosion guard product is by following heavy
Measure the material composition of part: 100 parts of quartz sand, 7-9 parts of lime stone, 3-5 parts of aluminium oxide, 10-12 parts of soda ash, 5-9 parts of albite, potassium
1-2 parts of feldspar, 2-2.6 parts of mullite crystal whisker, 0.2-0.4 parts of zirconium oxide, 1-1.5 parts of copper oxide, and the explosion-proof glass of the sky blue
The step of preparation process of glass product, is as follows:
Step 1: raw material mixing: according to ingredients by weight part that quartz sand, lime stone, aluminium oxide, soda ash, albite, potassium is long
Stone, mullite crystal whisker, zirconium oxide and copper oxide are sent into mixing plant jointly to be stirred, is uniformly mixed, and obtains mixture;
Step 2: melting: the mixture that step 1 is obtained is sent into melting furnaces, and makes persistently to heat up inside melting furnaces, and control
After temperature in melting furnaces processed is 1480 ± 20 degrees Celsius, constant temperature is kept, and further such that mixture is melting into glass metal;
Step 3: molding: glass metal made from step 2 is clarified, and by after clarification glass metal flow into mold at
Type, and obtain primary glassware;
Step 4: annealing: primary glassware being put into annealing kiln and is made annealing treatment, and then eliminates primary glass system
The thermal stress of product;
Step 5: processing polishing: the primary glassware after annealing in step 4 being placed on polishing table process and is beaten
Mill, and finally obtain sapphire implosion guard product.
Further, the SiO2 content in the quartz sand is 98%-99%.
Further, the CaCO in the lime stone3Content is 89%-95%.
Further, the CuO content in the copper oxide is 99.2-99.6%.
Further, in step 2, when melting kiln temperature to 1480 ± 20 degrees Celsius, uphill process continues 8-10 minutes.
Further, in step 4, the step of annealing specifically:
S1: being heated to 1200 degrees Celsius for the glassware in annealing kiln with the heating rate of 20-30 centigrade per minute,
And it is maintained 20-26 minutes under 1200 degrees Celsius;
S2: the temperature in annealing kiln is made to be cooled to 280-320 degrees Celsius with the cooling rate of 10-16 centigrade per minute;
S3: the glassware after step S2 cooling is taken out out of annealing kiln, places indoors and carries out natural cooling.
A kind of preparation process of sky blue implosion guard product proposed by the present invention, beneficial effect are: this programme is made
Glassware its intensity height obtained, and specially mullite crystal whisker and zirconium oxide can enhance its structural strength, i.e., so that glass
The explosion-proof of glass product enhances, i.e., further such that glassware in use highly-safe, and the face of glassware
Colour purity is more beautiful in use process;And glassware, during processing, simple process is easy to operate, convenient for into
Row preparation, and then be conducive to be promoted.
Specific embodiment
Below in conjunction with embodiment, further description of the specific embodiments of the present invention, and following embodiment is only used for more
Add and clearly demonstrate technical solution of the present invention, and not intended to limit the protection scope of the present invention.
Embodiment 1
A kind of preparation process of sky blue implosion guard product, the raw material of the sky blue implosion guard product is by following heavy
Measure part material composition: 100 parts of quartz sand, 7 parts of lime stone, 3 parts of aluminium oxide, 10 parts of soda ash, 5 parts of albite, 1 part of potassium feldspar,
2 parts of mullite crystal whisker, 0.2 part of zirconium oxide, 1 part of copper oxide, and the step of preparation process of the sky blue implosion guard product
It is as follows:
Step 1: raw material mixing: according to ingredients by weight part that quartz sand, lime stone, aluminium oxide, soda ash, albite, potassium is long
Stone, mullite crystal whisker, zirconium oxide and copper oxide are sent into mixing plant jointly to be stirred, is uniformly mixed, and obtains mixture;
Step 2: melting: the mixture that step 1 is obtained is sent into melting furnaces, and makes persistently to heat up inside melting furnaces, and control
After temperature in melting furnaces processed is 1460 degrees Celsius, constant temperature is kept, and further such that mixture is melting into glass metal;
Step 3: molding: glass metal made from step 2 is clarified, and by after clarification glass metal flow into mold at
Type, and obtain primary glassware;
Step 4: annealing: primary glassware being put into annealing kiln and is made annealing treatment, and then eliminates primary glass system
The thermal stress of product;
Step 5: processing polishing: the primary glassware after annealing in step 4 being placed on polishing table process and is beaten
Mill, and finally obtain sapphire implosion guard product.
SiO2 content in the quartz sand is 98%.
CaCO in the lime stone3Content is 89%%.
CuO content in the copper oxide is 99.2%.
In step 2, when melting kiln temperature to 1460 degrees Celsius, uphill process continues 10 minutes.
In step 4, the step of annealing specifically:
S1: being heated to 1200 degrees Celsius for the glassware in annealing kiln with the heating rate of 20 centigrade per minutes, and
It is maintained 20 minutes under 1200 degrees Celsius;
S2: the temperature in annealing kiln is made to be cooled to 280 degrees Celsius with the cooling rate of 10 centigrade per minutes;
S3: the glassware after step S2 cooling is taken out out of annealing kiln, places indoors and carries out natural cooling.
Embodiment 2
A kind of preparation process of sky blue implosion guard product, the raw material of the sky blue implosion guard product is by following heavy
Measure the material composition of part: 100 parts of quartz sand, 8 parts of lime stone, 4 parts of aluminium oxide, 11 parts of soda ash, 7 parts of albite, potassium feldspar 1.5
Part, 2.3 parts of mullite crystal whisker, 0.3 part of zirconium oxide, 1.25 parts of copper oxide, and the preparation work of the sky blue implosion guard product
The step of skill, is as follows:
Step 1: raw material mixing: according to ingredients by weight part that quartz sand, lime stone, aluminium oxide, soda ash, albite, potassium is long
Stone, mullite crystal whisker, zirconium oxide and copper oxide are sent into mixing plant jointly to be stirred, is uniformly mixed, and obtains mixture;
Step 2: melting: the mixture that step 1 is obtained is sent into melting furnaces, and makes persistently to heat up inside melting furnaces, and control
After temperature in melting furnaces processed is 1480 degrees Celsius, constant temperature is kept, and further such that mixture is melting into glass metal;
Step 3: molding: glass metal made from step 2 is clarified, and by after clarification glass metal flow into mold at
Type, and obtain primary glassware;
Step 4: annealing: primary glassware being put into annealing kiln and is made annealing treatment, and then eliminates primary glass system
The thermal stress of product;
Step 5: processing polishing: the primary glassware after annealing in step 4 being placed on polishing table process and is beaten
Mill, and finally obtain sapphire implosion guard product.
SiO2 content in the quartz sand is 98.5%.
CaCO in the lime stone3Content is 92%.
CuO content in the copper oxide is 99.4%.
In step 2, when melting kiln temperature to 1480 degrees Celsius, uphill process continues 9 minutes.
In step 4, the step of annealing specifically:
S1: being heated to 1200 degrees Celsius for the glassware in annealing kiln with the heating rate of 25 centigrade per minutes, and
It is maintained 23 minutes under 1200 degrees Celsius;
S2: the temperature in annealing kiln is made to be cooled to 300 degrees Celsius with the cooling rate of 13 centigrade per minutes;
S3: the glassware after step S2 cooling is taken out out of annealing kiln, places indoors and carries out natural cooling.
Embodiment 3
A kind of preparation process of sky blue implosion guard product, the raw material of the sky blue implosion guard product is by following heavy
Measure part material composition: 100 parts of quartz sand, 9 parts of lime stone, 5 parts of aluminium oxide, 12 parts of soda ash, 9 parts of albite, 2 parts of potassium feldspar,
2.6 parts of mullite crystal whisker, 0.4 part of zirconium oxide, 1.5 parts of copper oxide, and the preparation process of the sky blue implosion guard product
Steps are as follows:
Step 1: raw material mixing: according to ingredients by weight part that quartz sand, lime stone, aluminium oxide, soda ash, albite, potassium is long
Stone, mullite crystal whisker, zirconium oxide and copper oxide are sent into mixing plant jointly to be stirred, is uniformly mixed, and obtains mixture;
Step 2: melting: the mixture that step 1 is obtained is sent into melting furnaces, and makes persistently to heat up inside melting furnaces, and control
After temperature in melting furnaces processed is 1500 degrees Celsius, constant temperature is kept, and further such that mixture is melting into glass metal;
Step 3: molding: glass metal made from step 2 is clarified, and by after clarification glass metal flow into mold at
Type, and obtain primary glassware;
Step 4: annealing: primary glassware being put into annealing kiln and is made annealing treatment, and then eliminates primary glass system
The thermal stress of product;
Step 5: processing polishing: the primary glassware after annealing in step 4 being placed on polishing table process and is beaten
Mill, and finally obtain sapphire implosion guard product.
SiO2 content in the quartz sand is 99%.
CaCO in the lime stone3Content is 95%.
CuO content in the copper oxide is 99.6%.
In step 2, when melting kiln temperature to 1500 degrees Celsius, uphill process continues 8 minutes.
In step 4, the step of annealing specifically:
S1: being heated to 1200 degrees Celsius for the glassware in annealing kiln with the heating rate of 30 centigrade per minutes, and
It is maintained 26 minutes under 1200 degrees Celsius;
S2: the temperature in annealing kiln is made to be cooled to 320 degrees Celsius with the cooling rate of 16 centigrade per minutes;
S3: the glassware after step S2 cooling is taken out out of annealing kiln, places indoors and carries out natural cooling.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, hair according to the technique and scheme of the present invention
Bright design is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (6)
1. a kind of preparation process of sky blue implosion guard product, which is characterized in that the original of the sky blue implosion guard product
Material is made of the material of following parts by weight: 100 parts of quartz sand, 7-9 parts of lime stone, 3-5 parts of aluminium oxide, 10-12 parts of soda ash, sodium are long
5-9 parts of stone, 1-2 parts of potassium feldspar, 2-2.6 parts of mullite crystal whisker, 0.2-0.4 parts of zirconium oxide, 1-1.5 parts of copper oxide, and the day
The step of preparation process of blue implosion guard product, is as follows:
Step 1: raw material mixing: according to ingredients by weight part by quartz sand, lime stone, aluminium oxide, soda ash, albite, potassium feldspar, not
Come stone crystal whisker, zirconium oxide and copper oxide and be sent into mixing plant jointly be stirred, be uniformly mixed, and obtains mixture;
Step 2: melting: the mixture that step 1 is obtained is sent into melting furnaces, and makes persistently to heat up inside melting furnaces, and controls molten
After temperature in kiln is 1480 ± 20 degrees Celsius, constant temperature is kept, and further such that mixture is melting into glass metal;
Step 3: molding: clarifying glass metal made from step 2, and the glass metal after clarification is flowed into in-mold molding,
And obtain primary glassware;
Step 4: annealing: primary glassware being put into annealing kiln and is made annealing treatment, and then eliminates primary glassware
Thermal stress;
Step 5: processing polishing: the primary glassware after annealing in step 4 being placed on polishing table and carries out processing polishing, and
Finally obtain sapphire implosion guard product.
2. a kind of preparation process of sky blue implosion guard product according to claim 1, which is characterized in that the quartz
SiO2 content in sand is 98%-99%.
3. a kind of preparation process of sky blue implosion guard product according to claim 1, which is characterized in that the lime
CaCO in stone3Content is 89%-95%.
4. a kind of preparation process of sky blue implosion guard product according to claim 1, which is characterized in that the oxidation
CuO content in copper is 99.2-99.6%.
5. a kind of preparation process of sky blue implosion guard product according to claim 1, which is characterized in that in step 2
In, when melting kiln temperature to 1480 ± 20 degrees Celsius, uphill process continues 8-10 minutes.
6. a kind of preparation process of sky blue implosion guard product according to claim 1, which is characterized in that in step 4
In, the step of the described annealing specifically:
S1: being heated to 1200 degrees Celsius for the glassware in annealing kiln with the heating rate of 20-30 centigrade per minute, and
It is maintained 20-26 minutes under 1200 degrees Celsius;
S2: the temperature in annealing kiln is made to be cooled to 280-320 degrees Celsius with the cooling rate of 10-16 centigrade per minute;
S3: the glassware after step S2 cooling is taken out out of annealing kiln, places indoors and carries out natural cooling.