CN106142310A - 一种混凝土成型用脱模剂 - Google Patents
一种混凝土成型用脱模剂 Download PDFInfo
- Publication number
- CN106142310A CN106142310A CN201610519852.0A CN201610519852A CN106142310A CN 106142310 A CN106142310 A CN 106142310A CN 201610519852 A CN201610519852 A CN 201610519852A CN 106142310 A CN106142310 A CN 106142310A
- Authority
- CN
- China
- Prior art keywords
- parts
- releasing agent
- concrete formation
- sodium
- phenethanol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本申请公开了一种混凝土成型用脱模剂,包括硅酸钠10‑30份,碳酸钠15‑35份,氯化钾15‑40份,松香5‑35份,滑石粉20‑55份,木质素磺酸钠15‑45份,增稠剂10‑40份,苯乙醇10‑40份,环氧树脂20‑70份。由此,脱模剂使用后使得脱模容易,改善了劳动强度,避免了污染,产品光亮度高,提高了成品率,降低了成本。
Description
技术领域
本发明涉及汽车脱模剂,尤其涉及一种混凝土成型用脱模剂。
背景技术
现有的脱模剂在使用后,脱模效果并不好,还需要人力辅助,才能很好的脱模,而且污染较为严重,难以处理。
发明内容
本发明的目的提供一种混凝土成型用脱模剂,解决上述现有技术问题中的一个或者多个。
根据本发明的一个方面,提供一种混凝土成型用脱模剂,包括硅酸钠10-30份,碳酸钠15-35份,氯化钾15-40份,松香5-35份,滑石粉20-55份,木质素磺酸钠15-45份,增稠剂10-40份,苯乙醇10-40份,环氧树脂20-70份。
生产时,将上述物料全部加入到搅拌桶中,并向搅拌桶内加入占全部质量60%的水,搅拌均匀,然后再加入到球磨罐中进行球磨,经4h球磨后即得成品。
本发明的脱模剂使用后使得脱模容易,改善了劳动强度,避免了污染,产品光亮度高,提高了成品率,降低了成本。
具体实施方式
实施例1:包括硅酸钠10份,碳酸钠15份,氯化钾15份,松香5份,滑石粉20份,木质素磺酸钠15份,增稠剂10份,苯乙醇10份,环氧树脂20份。
实施例2:包括硅酸钠20份,碳酸钠25份,氯化钾28份,松香22份,滑石粉45份,木质素磺酸钠35份,增稠剂20份,苯乙醇30份,环氧树脂40份。
实施例3:包括硅酸钠30份,碳酸钠35份,氯化钾40份,松香35份,滑石粉55份,木质素磺酸钠45份,增稠剂40份,苯乙醇40份,环氧树脂70份。
生产时,将上述物料全部加入到搅拌桶中,并向搅拌桶内加入占全部质量60%的水,搅拌均匀,然后再加入到球磨罐中进行球磨,经4h球磨后即得成品。
综上所述,本发明的脱模剂使用后使得脱模容易,改善了劳动强度,避免了污染,产品光亮度高,提高了成品率,降低了成本。
以上所述仅是本发明的一种实施方式,应当指出,对于本领域普通技术人员来说,在不脱离本发明创造构思的前提下,还可以做出若干相似的变形和改进,这些也应视为本发明的保护范围之内。
Claims (1)
1.一种混凝土成型用脱模剂,其特征在于:包括硅酸钠10-30份,碳酸钠15-35份,氯化钾15-40份,松香5-35份,滑石粉20-55份,木质素磺酸钠15-45份,增稠剂10-40份,苯乙醇10-40份,环氧树脂20-70份。