CN104926182A - 一种建筑用复合抗裂防水剂 - Google Patents
一种建筑用复合抗裂防水剂 Download PDFInfo
- Publication number
- CN104926182A CN104926182A CN201410104060.8A CN201410104060A CN104926182A CN 104926182 A CN104926182 A CN 104926182A CN 201410104060 A CN201410104060 A CN 201410104060A CN 104926182 A CN104926182 A CN 104926182A
- Authority
- CN
- China
- Prior art keywords
- parts
- waterproof agent
- crack
- composite anti
- crack waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及精细化工的技术领域，具体地说是一种建筑用复合抗裂防水剂。该抗裂防水剂所述各材料按以下重量组份：石膏20-40份、铝矿粉20-30份、FDN-A减水剂2-5份、硬脂酸0.1-0.3份、多元醇0.1-0.5份。本发明的目的是在于提供一种使用效果理想、适用范围广的建筑用复合抗裂防水剂。
Description
技术领域
本发明涉及精细化工的技术领域，具体地说是一种建筑用复合抗裂防水剂。
背景技术
目前建筑工程中应用最为广泛的是混凝土，它是重要的基础材料。但它存在抗拉强度低、极限拉应变小，在塑性收缩时易形成开裂，导致防渗水能力不足，严重时直接防碍工程的强度指标，所以，抗裂和防渗水是伴随着混凝土应用的一个长期课题。目前所解决的技术方案是在工程施工时，使用到抗裂减水剂产品，但这类抗裂减水剂对早期硬化过程中的塑性收缩的补偿作用均不明显，对特别重大的工程和抢险类工程对强度和防渗有特别要求的地方显然不适用，并且膨胀剂的碱度较高，会导致与混凝土中的碱骨科产生反应导致结合强度的下降。
发明内容
本发明的目的是在于提供一种使用效果理想、适用范围广的建筑用复合抗裂防水剂。
本发明采用的技术方案是，一种建筑用复合抗裂防水剂，所述各材料按以下重量组份：石膏20-40份、铝矿粉20-30份、FDN-A减水剂2-5份、硬脂酸0.1-0.3份、多元醇0.1-0.5份。
本发明的优点是高强度、防渗性强，适用范围广，可用于特别重大工程和抢险类工程。
具体实施方式
本发明结合以下实施例作进一步描述。
实施例1，一种建筑用复合抗裂防水剂，所述各材料按以下重量组份：石膏40份、铝矿粉30份、FDN-A减水剂5份、硬脂酸0.3份、多元醇0.5份。
实施例2，一种建筑用复合抗裂防水剂，所述各材料按以下重量组份：石膏20份、铝矿粉20份、FDN-A减水剂2份、硬脂酸0.1份、多元醇0.1份。
实施例3，一种建筑用复合抗裂防水剂，所述各材料按以下重量组份：石膏30份、铝矿粉25份、FDN-A减水剂4份、硬脂酸0.2份、多元醇0.3份。
应理解，该实施例仅用于说明本发明而不用于限制本发明的范围。此外，应理解，在阅读了本发明讲授的内容之后，本领域技术人员可以对本发明作各种改动或修改，这些等价形式同样落于本申请所附权利要求书所限定的保护范围之内。
Claims (1)
1.一种建筑用复合抗裂防水剂，其特征在于，所述各材料按以下重量组份：石膏20-40份、铝矿粉20-30份、FDN-A减水剂2-5份、硬脂酸0.1-0.3份、多元醇0.1-0.5份。