CN106141077A - 一种高透气性消失模铸造用异丙醇基涂料及其制备方法 - Google Patents

一种高透气性消失模铸造用异丙醇基涂料及其制备方法 Download PDF

Info

Publication number
CN106141077A
CN106141077A CN201610766390.2A CN201610766390A CN106141077A CN 106141077 A CN106141077 A CN 106141077A CN 201610766390 A CN201610766390 A CN 201610766390A CN 106141077 A CN106141077 A CN 106141077A
Authority
CN
China
Prior art keywords
breathable
highly
base paint
isopropyl alcohol
powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201610766390.2A
Other languages
English (en)
Inventor
史付建
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FUYANG FUXIN CASTING MACHINERY Co Ltd
Original Assignee
FUYANG FUXIN CASTING MACHINERY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FUYANG FUXIN CASTING MACHINERY Co Ltd filed Critical FUYANG FUXIN CASTING MACHINERY Co Ltd
Priority to CN201610766390.2A priority Critical patent/CN106141077A/zh
Publication of CN106141077A publication Critical patent/CN106141077A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种高透气性消失模铸造用异丙醇基涂料，该涂料以高稳定性、适中挥发速度的异丙醇‑水复合体系作为溶剂载体，配以可再分散乳胶粉‑有机膨润土/聚乙二醇的粘结悬浮体系，以及钢渣、石英砂、硅酸镁、多孔活性碳粉等原料复配而成的高透气性、高耐火、保温型骨料，改善了传统水基或者醇基涂料存在的缺陷，形成的膜层牢固坚韧，保温透气，有效的改善了铸件的表面质量，提高了铸件精度。

Description

一种高透气性消失模铸造用异丙醇基涂料及其制备方法
技术领域
本发明涉及消失模涂料技术领域，尤其涉及一种高透气性消失模铸造用异丙醇基涂料及其制备方法。
背景技术
消失模铸造是泡沫塑料模采用无黏结剂干砂结合抽真空技术的实型铸造，是将与铸件尺寸形状相似的泡沫模型粘结组合成模型簇，刷涂涂料并烘干后，埋在干石英砂中振动造型，在负压下浇注，使模型气化，液体金属占据模型位置，凝固冷却后形成铸件的新型铸造方法。消失模铸造技术较之传统的铸造技术具有突出的优点，是目前最为先进的铸造工艺，国内外称之为21世纪绿色铸造。
在消失模铸造工艺实际应用过程中，使用的消失模涂料性能直接关系到铸件的性能，例如铸件存在的夹砂、气孔、残渣等缺陷均可以通过改善涂料的性能来改善。为了提高涂料的综合性能，技术人员尝试对传统的涂料进行性能改进，其中《消失模铸钢醇基涂料的开发》一文以异丙醇作为载体溶剂，解决了常见的甲醇基、乙醇基以及水基涂料存在的一些缺陷，在实验条件下获得了高品质的铸件，然而异丙醇在空气中容易氧化，增加了保存难度，实际应用还存在一定的困难。
发明内容
本发明目的就是为了弥补已有技术的缺陷，提供一种高透气性消失模铸造用异丙醇基涂料及其制备方法。
本发明是通过以下技术方案实现的：
一种高透气性消失模铸造用异丙醇基涂料，该涂料由以下重量份的原料制成：钢渣粉10-15、石英砂粉20-30、硅酸镁5-8、多孔活性碳粉4-5、有机膨润土0.4-0.5、聚乙二醇0.1-0.2、乙二醇丁醚3-5、可再分散乳胶粉1-2、硫脲0.001-0.002、异丙醇15-20、去离子水5-10。
所述的一种高透气性消失模铸造用异丙醇基涂料的制备方法为：
（1）先将异丙醇、乙二醇丁醚、硫脲与2-3重量份的去离子混合均匀，配制成溶液备用；
（2）将可再分散乳胶粉、有机膨润土投入余量的去离子水中，超声振荡40-50min后加入聚乙二醇，搅拌混合反应30-40min，所得物料备用；
（3）将钢渣粉、石英砂粉、硅酸镁、多孔活性碳粉混料均匀，随后加入步骤（2）制备的物料，搅拌20-30min，最后加入步骤（1）配制的物料，搅拌40-50min后即得。
本发明制备的消失模铸造涂料以高稳定性、适中挥发速度的异丙醇-水复合体系作为溶剂载体，配以可再分散乳胶粉-有机膨润土/聚乙二醇的粘结悬浮体系，以及钢渣、石英砂、硅酸镁、多孔活性碳粉等原料复配而成的高透气性、高耐火、保温型骨料，改善了传统水基或者醇基涂料存在的缺陷，形成的膜层牢固坚韧，保温透气，有效的改善了铸件的表面质量，提高了铸件精度。
具体实施方式
一种高透气性消失模铸造用异丙醇基涂料，该涂料由以下重量份的原料制成：钢渣粉10、石英砂粉20、硅酸镁5、多孔活性碳粉4、有机膨润土0.4、聚乙二醇0.1、乙二醇丁醚3、可再分散乳胶粉1、硫脲0.001、异丙醇15、去离子水5。
该涂料的制备方法为：
（1）先将异丙醇、乙二醇丁醚、硫脲与2重量份的去离子混合均匀，配制成溶液备用；
（2）将可再分散乳胶粉、有机膨润土投入余量的去离子水中，超声振荡40min后加入聚乙二醇，搅拌混合反应30min，所得物料备用；
（3）将钢渣粉、石英砂粉、硅酸镁、多孔活性碳粉混料均匀，随后加入步骤（2）制备的物料，搅拌20min，最后加入步骤（1）配制的物料，搅拌40min后即得。
得到的涂料性能测试结果为：
密度：1.27g/mm3；72h后悬浮率≥95%；粘度：65mP.s；触变率：12%；透气性：27.4cm2.(KPa.min)-1；涂层强度：905g/mm。
将其涂刷在泡沫塑样表面形成厚度为0.5mm的涂料层，随后经干燥处理后进行铸钢件浇注，得到的铸钢件表面光洁，表面粗糙度≤Ra10.5μm，无缩孔、夹砂。

Claims (2)

1.一种高透气性消失模铸造用异丙醇基涂料，其特征在于，该涂料由以下重量份的原料制成：钢渣粉10-15、石英砂粉20-30、硅酸镁5-8、多孔活性碳粉4-5、有机膨润土0.4-0.5、聚乙二醇0.1-0.2、乙二醇丁醚3-5、可再分散乳胶粉1-2、硫脲0.001-0.002、异丙醇15-20、去离子水5-10。
2.如权利要求1所述的一种高透气性消失模铸造用异丙醇基涂料的制备方法，其特征在于，所述的制备方法为：
（1）先将异丙醇、乙二醇丁醚、硫脲与2-3重量份的去离子混合均匀，配制成溶液备用；
（2）将可再分散乳胶粉、有机膨润土投入余量的去离子水中，超声振荡40-50min后加入聚乙二醇，搅拌混合反应30-40min，所得物料备用；
（3）将钢渣粉、石英砂粉、硅酸镁、多孔活性碳粉混料均匀，随后加入步骤（2）制备的物料，搅拌20-30min，最后加入步骤（1）配制的物料，搅拌40-50min后即得。
CN201610766390.2A 2016-08-30 2016-08-30 一种高透气性消失模铸造用异丙醇基涂料及其制备方法 Withdrawn CN106141077A (zh)