CN106116512A - A kind of health preserving antibacterial domestic ceramic goods - Google Patents
A kind of health preserving antibacterial domestic ceramic goods Download PDFInfo
- Publication number
- CN106116512A CN106116512A CN201610460680.4A CN201610460680A CN106116512A CN 106116512 A CN106116512 A CN 106116512A CN 201610460680 A CN201610460680 A CN 201610460680A CN 106116512 A CN106116512 A CN 106116512A
- Authority
- CN
- China
- Prior art keywords
- powder
- slurry
- ball
- drying
- deionized water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of health preserving antibacterial domestic ceramic goods; flyash is utilized to produce domestic ceramics; reduce production cost; solve the present situation that utilization of fly ash is insufficient, pollute environment; protect ecological environment, and the daily pottery produced has any surface finish, the advantage such as durable in use, additionally it is possible to provide trace element for human body; there is health maintenance effect, be worthy to be popularized.
Description
Technical field
The present invention relates to domestic ceramics technical field, particularly relate to a kind of health preserving antibacterial domestic ceramic goods.
Background technology
China's not only rich in mineral resources, is also coal production state maximum in the world and consumption of coal state, in recent years simultaneously
Coming, China's thermal power generation quickly grows, and wherein great majority are with coal as fuel, and generated energy reaches 1.3 hundred million kW h, shared by thermal power generation
Ratio has reached 79.6%, thus causes flyash discharge capacity to increase year by year.In the end of the year 2010, discharge capacity reaches nearly 300,000,000 tons, in a large number
The discharge of flyash have received to be paid close attention to the most widely.China started just to how utilizing flyash as resource from 1987
The breach of comprehensive utilization, comprehensively utilizes it, becomes a long-range policy of economy and social development.Cullet class thing
Its chemical stability of matter is extremely strong, without putrefaction, does not burns, can not degrade, and substantial amounts of cullet both took up an area, and polluted again environment, reclaimed
Being to save the energy, the optimal path of protection environment with utilizing, and have good economy, the main component of glass is dioxy
SiClx, it is possible to promote the sintering of pottery.In Production of Ceramics, firing temperature is the highest, and firing time is the longest, and energy consumption is the highest, according to
Heat Balance Calculation, firing temperature often reduces by 100 DEG C, then unit product heat consumption can reduce by more than 10%, and firing time often shortens 10%,
Then yield increases by 10%, and heat consumption reduces by 4%, so reduction firing temperature and time have significant energy-saving and emission-reduction social meaning.
Over nearly 20 years, ceramic industry enters developmental stage with rapid changepl. never-ending changes and improvements, new technique, a large amount of uses of new equipment, pottery
Porcelain yield also increases by a fairly big margin.New ceramics, as a kind of new material, solely sets one with the performance of its excellence at Material Field
Flag, is paid much attention to by people.Domestic ceramics occupies an important position at Material Field as traditional ceramics material, because it
Relating to the every aspect of people's life, the development of domestic ceramics is more wanted along with the raising of people's living standard proposes
Asking, the most antibacterial is to propose most common requirement at present.Due to the wilderness demand of porcelain, a large amount of exploitations of china clay resource are just with frightened
The speed of people reduces, and is non-renewable resources, if can not find alternate resources, it is likely that can face No Assets later
The difficult situation that can adopt.Yang Yuwei et al. is at " utilizing the industrial wastes such as flyash to prepare the research of a domestic ceramics " literary composition middle finger
Go out, utilize the flyash of power plant emission, a large amount of useless saggars of ceramic industry generation, useless porcelain powder to utilize Orthogonal Experiment and Design to join
Side, develops cleaning and produces the formula of domestic ceramics, wherein flyash, useless saggar, the content of useless porcelain powder be 10% respectively, 10%,
8%, applying this technology can be that enterprise brings considerable economic benefit, and the recycling for flyash finds an exit, although carry
High Social benefit and economic benefit, but a lot of performance is not reaching to the requirement of people, the most antibacterial, high temperature resistance, freeze proof etc.
The shortcoming that performance is the highest, service life is not grown.
Summary of the invention
The object of the invention is contemplated to make up the defect of prior art, it is provided that a kind of health preserving antibacterial domestic ceramic goods.
The present invention is achieved by the following technical solutions:
A kind of health preserving antibacterial domestic ceramic goods, are made up of the raw material of following weight portion: ferrous sulfate 2-3, nanometer fluorite
15-18, Dehua Ore 20-24, diatom ooze 6-8, rutile titanium dioxide 2-3, shale powder 11-13,2-imidazolidinone 0.5-3,
Ammonium dihydrogen phosphate 3-4, activated zinc oxide 9-11, gelatin 3-4, Cortex Cinnamomi powder 8-9, flyash 40-45, white glaze ball 35-40, cullet
6-8, Maifanitum 10-14, green tea 21-25, Pericarpium citri sinensis 14-17, conch meal 6-8, shrimp shell meal 4-6, polyvinyl alcohol 0.2-0.3, phosphorus
Acid tributyl 0.2-0.3, deionized water are appropriate.
Described a kind of health preserving antibacterial domestic ceramic goods, are made up of following concrete steps:
(1) being mixed by the deionized water of gelatin, Cortex Cinnamomi powder and 40-50 times amount, heated and stirred forms pastel, adds 2-imidazoles
Alkanone, ammonium dihydrogen phosphate, activated zinc oxide continue stirring, grind the even complex antimicrobials that obtains, drying for standby after vacuum defoamation;
(2) by Maifanitum clean dry after wear into fine powder, by green tea, Pericarpium citri sinensis, conch meal, shrimp shell meal mixing be added to 75% second
In alcoholic solution, decoct 20-30min when 50-60 DEG C, be continuously heating to when 90-100 DEG C decoct 10-20min, be cooled to room temperature
After carry out centrifugation, take after its supernatant concentration and polyvinyl alcohol, medical stone powder, tributyl phosphate ball milling 30-40min, knot
While being stirred continuously slurry with direct current drive blender after bundle, it is standby that spray drying makes nano medical stone microsphere;
(3) cullet is cleaned up post-drying to crush, be then added to ground 100-200 mesh sieve in colloid mill, by glass
Glass powder and flyash, nanometer fluorite, Dehua Ore, diatom ooze are mixed to get dry material, add and account for dry material gross mass 40-50%
Deionized water, obtained the slurry of 300-400 mesh through ball mill pulverizing;
(4) the slurry magnetic separator that step (3) obtains is carried out iron removal by magnetic separation, make content≤0.2% of ferrum in slurry, by slurry
It is added to drying and moulding in forming machine and obtains base substrate, base substrate is put in the sintering furnace that in-furnace temperature is 100-200 DEG C, at 1200-
Carrying out at a temperature of 1280 DEG C calcining 5-7h, after being cooled to room temperature, polishing is scraped standby;
(5) antibacterial mixing white glaze ball, ferrous sulfate, rutile titanium dioxide, shale powder and step (1) obtained, is added to
Ball mill carries out wet ball grinding, adds the deionized water of material gross weight 45-55%, the glaze slip after ball milling is crossed respectively 200
Mesh, 300 mesh sieves, remove the removal of impurity and coarse granule, obtains thin glaze slip, by glaze slip glazing on biscuit prepared by step (4),
4-5h is sintered at 1180-1250 DEG C;
(6) nano medical stone microsphere and the phosphoric acid hydrogen al binder step (2) prepared mix according to 2-3:1 ratio, are coated in
Ceramic surface prepared by step (5), after drying in the shade, at 120-140 DEG C, constant temperature 2h is the most available.
The invention have the advantage that the present invention utilizes waste resource flyash as Ceramic Material, reduce the dirt to environment
Dye, and wherein silicon oxide, alumina content are higher, and specific grain surface is long-pending big in loose structure, easily grinds, can reduce system
The firing temperature of product, reaches energy-conservation purpose, and discarded glass, with flyash sintering process, melts at low temperatures, is formed
Glass phase, plays the effect of bonding agent, reduces firing temperature, and it is smooth, freeze proof, easy to clean, anti-to improve ceramic surface
The performance of the aspects such as impact, by the antibacterial of synthesis and glaze mixing glazing on biscuit of ceramics surface, improves ceramic antibacterial
Performance, reduces the danger coefficient that the mankind are ill, and uses the decoction of green tea, Pericarpium citri sinensis, conch meal, shrimp shell meal to extract trace
Element Maifanitum cladding forms nano medical stone microsphere, utilizes binding agent to be bonded in ceramic surface, solvable by being heated for a long time
Going out the multiple trace element useful to human body, the body for people provides nutrition, building body, regulates metabolism, to human body
Benefit, the present invention utilize flyash produce domestic ceramics, reduce production cost, solve utilization of fly ash insufficient,
Pollute the present situation of environment, protect ecological environment, and the daily pottery produced has any surface finish, the advantage such as durable in use, also
Trace element can be provided for human body, there is health maintenance effect, be worthy to be popularized.
Detailed description of the invention
A kind of health preserving antibacterial domestic ceramic goods, are made up of the raw material of following weight portion (kilogram): ferrous sulfate 2,
Nanometer fluorite 15, Dehua Ore 20, diatom ooze 6, rutile titanium dioxide 2, shale powder 11,2 imidazolidinone 0.5, biphosphate
Ammonium 3, activated zinc oxide 9, gelatin 3, Cortex Cinnamomi powder 8, flyash 40, white glaze ball 35, cullet 6, Maifanitum 10, green tea 21, Fructus Citri junoris
Skin 14, conch meal 6, shrimp shell meal 4, polyvinyl alcohol 0.2, tributyl phosphate 0.2, deionized water are appropriate.
Described a kind of health preserving antibacterial domestic ceramic goods, are made up of following concrete steps:
(1) being mixed by the deionized water of gelatin, Cortex Cinnamomi powder and 40 times amount, heated and stirred forms pastel, adds 2 imidazolidines
Ketone, ammonium dihydrogen phosphate, activated zinc oxide continue stirring, grind the even complex antimicrobials that obtains, drying for standby after vacuum defoamation;
(2) by Maifanitum clean dry after wear into fine powder, by green tea, Pericarpium citri sinensis, conch meal, shrimp shell meal mixing be added to 75% second
In alcoholic solution, decoct 20min when 50 DEG C, when being continuously heating to 90 DEG C, decoct 10min, be centrifuged after being cooled to room temperature point
From, take after its supernatant concentration and polyvinyl alcohol, medical stone powder, tributyl phosphate ball milling 30min, after terminating, use unidirectional current
Slurry is stirred continuously by dynamic blender, and it is standby that spray drying makes nano medical stone microsphere;
(3) cullet is cleaned up post-drying to crush, be then added to ground 100 mesh sieves in colloid mill, by glass dust
It is mixed to get dry material with flyash, nanometer fluorite, Dehua Ore, diatom ooze, adds the deionization accounting for dry material gross mass 40%
Water, obtained the slurry of 300 mesh through ball mill pulverizing;
(4) the slurry magnetic separator that step (3) obtains is carried out iron removal by magnetic separation, make content≤0.2% of ferrum in slurry, by slurry
It is added to drying and moulding in forming machine and obtains base substrate, base substrate is put in the sintering furnace that in-furnace temperature is 100 DEG C, 1200 DEG C of temperature
Under carry out calcine 5h, after being cooled to room temperature polishing scrape standby;
(5) antibacterial mixing white glaze ball, ferrous sulfate, rutile titanium dioxide, shale powder and step (1) obtained, is added to
Ball mill carries out wet ball grinding, adds the deionized water of material gross weight 45%, the glaze slip after ball milling is crossed respectively 200 mesh,
300 mesh sieves, remove the removal of impurity and coarse granule, obtain thin glaze slip, by glaze slip glazing on biscuit prepared by step (4), at 1180 DEG C
Lower sintering 4h;
(6) nano medical stone microsphere and the phosphoric acid hydrogen al binder step (2) prepared mix according to 2:1 ratio, are coated in step
Suddenly the ceramic surface that prepared by (5), after drying in the shade, at 120 DEG C, constant temperature 2h is the most available.
Test data:
Product appearance is regular, and glaze is smooth;Thermal shock resistance test reaches heat exchange in 20 DEG C of water of 200 DEG C of inputs and does not splits;Machine
Tool intensity >=141mp2;Glaze vickers microhardness >=6.4GPa;Sunlight germicidal efficiency >=71% of lower 1 hour;Shock resistance is strong
Degree >=1.6J/cm2.
Claims (2)
1. health preserving antibacterial domestic ceramic goods, it is characterised in that be made up of the raw material of following weight portion: ferrous sulfate
2-3, nanometer fluorite 15-18, Dehua Ore 20-24, diatom ooze 6-8, rutile titanium dioxide 2-3, shale powder 11-13,2-miaow
Oxazolidone 0.5-3, ammonium dihydrogen phosphate 3-4, activated zinc oxide 9-11, gelatin 3-4, Cortex Cinnamomi powder 8-9, flyash 40-45, white glaze ball
35-40, cullet 6-8, Maifanitum 10-14, green tea 21-25, Pericarpium citri sinensis 14-17, conch meal 6-8, shrimp shell meal 4-6, polyethylene
Alcohol 0.2-0.3, tributyl phosphate 0.2-0.3, deionized water are appropriate.
A kind of health preserving antibacterial domestic ceramic goods, it is characterised in that prepared by following concrete steps
Make:
(1) being mixed by the deionized water of gelatin, Cortex Cinnamomi powder and 40-50 times amount, heated and stirred forms pastel, adds 2-imidazoles
Alkanone, ammonium dihydrogen phosphate, activated zinc oxide continue stirring, grind the even complex antimicrobials that obtains, drying for standby after vacuum defoamation;
(2) by Maifanitum clean dry after wear into fine powder, by green tea, Pericarpium citri sinensis, conch meal, shrimp shell meal mixing be added to 75% second
In alcoholic solution, decoct 20-30min when 50-60 DEG C, be continuously heating to when 90-100 DEG C decoct 10-20min, be cooled to room temperature
After carry out centrifugation, take after its supernatant concentration and polyvinyl alcohol, medical stone powder, tributyl phosphate ball milling 30-40min, knot
While being stirred continuously slurry with direct current drive blender after bundle, it is standby that spray drying makes nano medical stone microsphere;
(3) cullet is cleaned up post-drying to crush, be then added to ground 100-200 mesh sieve in colloid mill, by glass
Glass powder and flyash, nanometer fluorite, Dehua Ore, diatom ooze are mixed to get dry material, add and account for dry material gross mass 40-50%
Deionized water, obtained the slurry of 300-400 mesh through ball mill pulverizing;
(4) the slurry magnetic separator that step (3) obtains is carried out iron removal by magnetic separation, make content≤0.2% of ferrum in slurry, by slurry
It is added to drying and moulding in forming machine and obtains base substrate, base substrate is put in the sintering furnace that in-furnace temperature is 100-200 DEG C, at 1200-
Carrying out at a temperature of 1280 DEG C calcining 5-7h, after being cooled to room temperature, polishing is scraped standby;
(5) antibacterial mixing white glaze ball, ferrous sulfate, rutile titanium dioxide, shale powder and step (1) obtained, is added to
Ball mill carries out wet ball grinding, adds the deionized water of material gross weight 45-55%, the glaze slip after ball milling is crossed respectively 200
Mesh, 300 mesh sieves, remove the removal of impurity and coarse granule, obtains thin glaze slip, by glaze slip glazing on biscuit prepared by step (4),
4-5h is sintered at 1180-1250 DEG C;
(6) nano medical stone microsphere and the phosphoric acid hydrogen al binder step (2) prepared mix according to 2-3:1 ratio, are coated in
Ceramic surface prepared by step (5), after drying in the shade, at 120-140 DEG C, constant temperature 2h is the most available.