CN106087215A - Colored knitting fabric of a kind of wool simulating and preparation method thereof - Google Patents
Colored knitting fabric of a kind of wool simulating and preparation method thereof Download PDFInfo
- Publication number
- CN106087215A CN106087215A CN201610758051.XA CN201610758051A CN106087215A CN 106087215 A CN106087215 A CN 106087215A CN 201610758051 A CN201610758051 A CN 201610758051A CN 106087215 A CN106087215 A CN 106087215A
- Authority
- CN
- China
- Prior art keywords
- fabric
- knitting fabric
- wool
- simulating
- colored knitting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses colored knitting fabric of a kind of wool simulating and preparation method thereof, this fabric includes terry loop layer and ground layer, described terry loop layer is covered on described ground layer by braiding, described terry loop layer obtains through plucking finishing technique, described terry loop layer is made up of the composite filament of cationic polyester fiber filament with polyester filaments, being connected by low nexus between described cationic polyester fiber filament and polyester filaments, described ground layer is made up of hollow polyester fibre long filament.The colored knitting fabric of the wool simulating of the present invention, its pattern fabric effect is notable, and hair sense is strong, the fluffy glutinous hair feel abundant, sliding of fabric, and thermal property is excellent, and preparation method is simple, easy to process, production cost is low.
Description
Technical field
The invention belongs to knitting fabric and preparing technical field thereof, particularly relate to the colored knitting fabric of a kind of wool simulating and
Preparation method.
Background technology
The knitting fabric of hair is expensive for tradition, be difficult to nursing, there is the problem such as shrink and anti-pilling property difference.Existing
Woolen like fabric mainly uses tatting or warp knit or pattern effecting method to process, and generally there is feel the softest, without fluffy sense, warming
Property is poor, and the problem such as pattern is single, with high costs；As Application No. patent CN104233597A discloses anti-hair wool fabric, its
Use the wool top that cotton fiber or chemical fibre are made, use computer jacquard weaving to form；Patent CN2015130515u discloses high-elastic
The preparation method of property hair wool fabric, this fabric includes that water proof Buji rubber layer etc. is interwoven；Patent CN103361878A is open
A kind of warp knit woolen like fabric；Patent CN103388216A discloses the preparation method of a kind of tatting woolen like fabric.
But the knitting fabric of hair is expensive for tradition, be difficult to nursing, there is the problem such as shrink and anti-pilling property difference；And
And, existing woolen like fabric mainly uses tatting or warp knit or pattern effecting method to process, and generally there is feel the softest, without fluffy
Pine sense, warmth retention property is poor, and the problem such as pattern is single, with high costs；As: tatting wool simulating needs warping, and sizing work flow is long,
Relatively costly；There is production and adjust trouble in warp knit wool simulating, exploitation waste is greatly；There is high in cost of production problem in weft jacquard weaving.
Summary of the invention
The present invention solves the problems referred to above of the prior art, a kind of pattern effect of proposition is notable, good warmth retention effect, hair
Colored knitting fabric of the wool simulating that sense is strong and production cost is low and preparation method thereof.
For achieving the above object, the present invention is by the following technical solutions:
The first aspect of the invention is to provide the colored knitting fabric of a kind of wool simulating, including terry loop layer and ground layer, institute
State terry loop layer to be covered on described ground layer by braiding, described terry loop layer through plucking finishing technique obtain, described terry loop layer by
Cationic polyester fiber filament is constituted with the composite filament of polyester filaments, described cationic polyester fiber filament and polyester fiber
Being connected by low nexus between long filament, described ground layer is made up of hollow polyester fibre long filament.
Further, described cationic polyester fiber filament uses autonomous innovation research and development with the composite filament of polyester filaments
Use cationic polyester and the normal polyester complex yarn of low nexus, be characterized in that yarn both can guarantee that the strip wind of fabric
Lattice, and due to the existence of nexus, can guarantee that yarn style during processing is not destroyed；And routine strip style fabric
Owing to the restriction of yarn equipment all uses the yarn without nexus, so there is flower pattern when yarn becomes final products any
The risk of change, seriously limits the quality of big production control.
Further, the line density of described cationic polyester fiber filament and polyester filaments is 150D-300D, described
The line density of hollow polyester fibre long filament is 50D-100D.
Preferably, the line density of described cationic polyester fiber filament and polyester filaments is 200D-250D, described in
The line density of empty polyester filaments is 65D-75D.
Further, described hollow polyester fibre long filament is super fine denier hollow polyester fibre long filament.
Further, described hollow polyester fibre long filament uses the hollow polyester fibre long filament with far-infrared functional.
Further, described terry loop layer height is 1.8-4.5mm；Preferably, described terry loop layer height is 2.5-4mm；Excellent
Elect 3-3.5mm as.
Further, the colored knitting fabric of described wool simulating is weft knitting Circular Single Terry Machine organizational structure.
The second aspect of the invention is to provide the preparation method of the colored knitting fabric of a kind of wool simulating, including: by wire gauze
With plush yarn use weft knitting plane No. be 19-28G carry out weaving, blank pre-treatment, dyeing, reduction cleaning, auxiliary agent arrangement, plucking,
Carding, cropping, shake grain, open-width sizing, to obtain final product.
Further, described weaving environment is: workshop temperature controls at 25 DEG C, relative humidity 75%.
Further, described dyeing is: temperature is 120-140 DEG C, levelling agent 1-3g/L, and fabric contaminates along looped pile direction
Color.
Preferably, described dyeing is: temperature is 130 DEG C, levelling agent 2g/L, and fabric dyes along looped pile direction.
Further, described auxiliary agent finishing technique is: fabric is placed in the solution that bath raio is 1:6-10 process, and it is whole
Reason agent includes softening agent OH-600 0.5-1.5wt%, smooth, soft agent 0.3-0.8g/L, low complexion changed color fixing agent 3-5wt%.
Preferably, described auxiliary agent finishing technique is: fabric is placed in the solution that bath raio is 1:8 process, its finishing agent
Including softening agent OH-600 1wt%, smooth, soft agent 0.5g/L, low complexion changed color fixing agent 4wt%.
Further, described brushing process is: plane is first drawn 3-6 time, looped pile face post-tensioning 1-3 time.
Preferably, described brushing process is: plane is first drawn 4 times, looped pile face post-tensioning 2 times.
Further, described open-width setting temperature is 120 DEG C-140 DEG C；Preferably, described open-width setting temperature is 130
℃。
The present invention uses technique scheme, compared with prior art, has the following technical effect that
The processing of the colored knitting fabric of the wool simulating of the present invention and preparation technology: fabric has fluffy glutinous hair abundant, sliding
Feel, thermal property is excellent, has good warming effect, and fabric is frivolous, easy to process and with low cost；By using
Through low nexus cationic polyester fiber and the conventional polyester fiber composite silk of special processing, facing material design and colour is effectively ensured
Style is stable；The softening agent that its Final finishing adds can not only well improve the plucking style of fabric, and makes fabric have well
Hair sense.
Accompanying drawing explanation
Fig. 1 is existing conventional FANCY YARNS structure；
Fig. 2 is low nexus cationic polyester fiber and the conventional polyester fiber composite silk of the present invention；
Fig. 3 is the fabric style before the colored knitting fabric plucking of wool simulating of the present invention；
Fig. 4 is the fabric style after the colored knitting fabric plucking of wool simulating of the present invention.
Detailed description of the invention
As shown in Figure 4, invention provides the colored knitting fabric of a kind of wool simulating, including terry loop layer 2 and ground layer 1, looped pile
Layer 2 is covered on ground layer 1 by braiding, and terry loop layer 2 obtains through plucking finishing technique, and terry loop layer 2 is by cationic polyester fiber
Long filament 21 is constituted with the composite filament of polyester filaments 22, by low between cationic polyester fiber filament and polyester filaments
Nexus 23 connects, and ground layer 1 is made up of hollow polyester fibre long filament, on the premise of fabric keeps inside and outside consistent style,
The thermal property of fabric can also be strengthened.
As in figure 2 it is shown, the cationic polyester fiber filament of the present invention grinds for autonomous innovation with polyester filaments composite filament 2
The cationic polyester using low nexus 23 sent out and normal polyester complex yarn, be characterized in that yarn both can guarantee that the length of fabric
Bar style, and due to the existence of nexus, can guarantee that yarn style during processing is not destroyed；And routine strip style
Fabric all uses the yarn without nexus, as it is shown in figure 1, so become final products at yarn due to the restriction of yarn equipment
Time there is the risk that flower pattern arbitrarily changes, seriously limit the quality of big production control.
Wherein, the line density of cationic polyester fiber filament and polyester filaments is 150D-300D, hollow polyester fibre
The line density of long filament is 50D-100D；Preferably, the line density of cationic polyester fiber filament and polyester filaments is 200D-
250D, the line density of hollow polyester fibre long filament is 65D-75D.Hollow polyester fibre long filament is that super fine denier hollow polyester fibre is long
Silk, it is preferred to use there is the hollow polyester fibre long filament of far-infrared functional.Terry loop layer height is 1.8-4.5mm；Preferably, looped pile
Layer height is 2.5-4mm；It is preferably 3-3.5mm.The colored knitting fabric of this wool simulating is weft knitting Circular Single Terry Machine organizational structure, looped pile
Layer is covered in the two sides of ground layer, is formed with the terry loop layer on two sides as internal layer and outer layer, the wool simulating with ground layer as intermediate layer
Fabric.
Present invention also offers the preparation method of the colored knitting fabric of a kind of wool simulating, including: wire gauze is adopted with plush yarn
With weft knitting plane No. be 19-28G carry out weaving, blank pre-treatment, dyeing, reduction cleaning, auxiliary agent arrangement, plucking, carding, cropping,
Shake grain, open-width sizing, to obtain final product.
Wherein, weaving environment is: workshop temperature controls at 25 DEG C, relative humidity 75%.Dyeing is: temperature is 120-
140 DEG C, levelling agent 1-3g/L, fabric dyes along looped pile direction；Preferably, temperature is 130 DEG C, and levelling agent 2g/L, fabric is along hair
The dyeing of circle direction.Auxiliary agent finishing technique is: fabric is placed in the solution that bath raio is 1:6-10 process, and its finishing agent includes soft
Soft dose of OH-600 0.5-1.5wt%, smooth, soft agent 0.3-0.8g/L, low complexion changed color fixing agent 3-5wt%；Preferably, by fabric
Be placed in the solution that bath raio is 1:8 process, its finishing agent include softening agent OH-600 1wt%, smooth, soft agent 0.5g/L,
Low complexion changed color fixing agent 4wt%.Brushing process is: plane is first drawn 3-6 time, looped pile face post-tensioning 1-3 time；Preferably, plane first draws 4
Secondary, looped pile face post-tensioning 2 times, as shown in Figure 3-4.Open-width setting temperature is 120 DEG C-140 DEG C；It is preferably 130 DEG C.
Below by specific embodiment, the present invention is carried out detailed and concrete introduction, so that being better understood from the present invention,
But following embodiment is not limiting as the scope of the invention.
The preparation of the colored knitting fabric of embodiment 1 wool simulating, comprises the following steps:
(1) material choice: terry loop layer uses cationic polyester fiber filament and the polyester filaments with low nexus
Composite filament, line density is 300D；Ground layer uses hollow polyester fibre long filament, and line density is 75D；Control workshop temperature to control
25 DEG C, relative humidity 75%；The carrying out using weft knitting plane No. to be chosen as 24G is weaved, and prepares grey cloth fabric；
(2) fabric Final finishing: the grey cloth fabric of above-mentioned steps (1) is included successively blank pre-treatment, dye, reduce clear
Wash, auxiliary agent arrangement, plucking, carding, cropping, shake grain, open-width sizing, obtain the colored knitting fabric of wool simulating；
Wherein, dyeing is: temperature is 130 DEG C, levelling agent 2g/L；Fabric to dye along looped pile direction, it is to avoid looped pile
Due to high temperature and the effect of dye liquor, make looped pile excessive distortion；
Auxiliary agent finishing technique: fabric is placed in the solution that bath raio is 1:8 process, and its finishing agent is softening agent OH-600
It is 1%, smooth, soft agent 0.5g/L, low complexion changed color fixing agent 4%；
Brushing process is: use plane first to draw 4 times, the technique that looped pile face post-tensioning is 2 times, it is ensured that fabric positive and negative thickness one
Causing, matte is plentiful, outward appearance is magnificent, gloss is graceful to make fabric have, and hair sense is strong, and the terry height after plucking is at least 2.2mm；
And open-width setting temperature is 120 DEG C.
The preparation of the colored knitting fabric of embodiment 2 wool simulating, comprises the following steps:
(3) material choice: terry loop layer uses cationic polyester fiber filament and the polyester filaments with low nexus
Composite filament, line density is 150D；Ground layer uses hollow polyester fibre long filament, and line density is 100D；Control workshop temperature to control
At 25 DEG C, relative humidity 75%；The carrying out using weft knitting plane No. to be chosen as 28G is weaved, and prepares grey cloth fabric；
(4) fabric Final finishing: the grey cloth fabric of above-mentioned steps (1) is included successively blank pre-treatment, dye, reduce clear
Wash, auxiliary agent arrangement, plucking, carding, cropping, shake grain, open-width sizing, obtain the colored knitting fabric of wool simulating；
Wherein, dyeing is: temperature is 120 DEG C, levelling agent 3g/L；Fabric to dye along looped pile direction, it is to avoid looped pile
Due to high temperature and the effect of dye liquor, make looped pile excessive distortion；
Auxiliary agent finishing technique: fabric is placed in the solution that bath raio is 1:10 process, and its finishing agent is softening agent OH-
600 is 0.5%, smooth, soft agent 0.3g/L, low complexion changed color fixing agent 3%；
Brushing process is: use plane first to draw 6 times, the technique that looped pile face post-tensioning is 3 times, it is ensured that fabric positive and negative thickness one
Causing, matte is plentiful, outward appearance is magnificent, gloss is graceful to make fabric have, and hair sense is strong, and the terry height after plucking is at least 4.5mm；
And open-width setting temperature is 140 DEG C.
The preparation of the colored knitting fabric of embodiment 3 wool simulating, comprises the following steps:
(5) material choice: terry loop layer uses cationic polyester fiber filament and the polyester filaments with low nexus
Composite filament, line density is 200D；Ground layer uses hollow polyester fibre long filament, and line density is 50D；Control workshop temperature to control
25 DEG C, relative humidity 75%；The carrying out using weft knitting plane No. to be chosen as 24G is weaved, and prepares grey cloth fabric；
(6) fabric Final finishing: the grey cloth fabric of above-mentioned steps (1) is included successively blank pre-treatment, dye, reduce clear
Wash, auxiliary agent arrangement, plucking, carding, cropping, shake grain, open-width sizing, obtain the colored knitting fabric of wool simulating；
Wherein, dyeing is: temperature is 140 DEG C, levelling agent 1.5g/L；Fabric to dye along looped pile direction, it is to avoid hair
Circle, due to high temperature and the effect of dye liquor, makes looped pile excessive distortion；
Auxiliary agent finishing technique: fabric is placed in the solution that bath raio is 1:6 process, and its finishing agent is softening agent OH-600
It is 1.5%, smooth, soft agent 0.5g/L, low complexion changed color fixing agent 3%；
Brushing process is: use plane first to draw 3 times, the technique that looped pile face post-tensioning is 2 times, it is ensured that fabric positive and negative thickness one
Causing, matte is plentiful, outward appearance is magnificent, gloss is graceful to make fabric have, and hair sense is strong, and the terry height after plucking is at least 2.0mm；
And open-width setting temperature is 130 DEG C.
The colored knitting fabric of the wool simulating that embodiment of the present invention 1-3 prepares, efficiently solves tradition hair knitting fabric valency
Lattice are expensive, be difficult to nursing, there is the problem such as shrink and anti-pilling property difference.The pattern fabric effect of the colored knitting fabric of this wool simulating
Fruit is notable, and hair sense is strong；Fabric has fluffy glutinous hair feel abundant, sliding, and thermal property is excellent, easy to process and low cost
Honest and clean；There is good warming effect, and fabric is frivolous, applied widely, there is good economic worth.
Being described in detail the specific embodiment of the present invention above, but it is intended only as example, the present invention does not limit
It is formed on particular embodiments described above.To those skilled in the art, any equivalent modifications that the present invention is carried out and
Substitute the most all among scope of the invention.Therefore, the impartial conversion made without departing from the spirit and scope of the invention and
Amendment, all should contain within the scope of the invention.
Claims (10)
1. the colored knitting fabric of wool simulating, it is characterised in that including terry loop layer and ground layer, described terry loop layer is by braiding
Being covered on described ground layer, described terry loop layer obtains through plucking finishing technique, and described terry loop layer is long by cationic polyester fiber
Silk is constituted with the composite filament of polyester filaments, by low net between described cationic polyester fiber filament and polyester filaments
Network point connects, and described ground layer is made up of hollow polyester fibre long filament.
The colored knitting fabric of wool simulating the most according to claim 1, it is characterised in that described cationic polyester fiber filament
It is 150D-300D with the line density of polyester filaments.
The colored knitting fabric of wool simulating the most according to claim 1, it is characterised in that described hollow polyester fibre long filament
Line density is 50D-100D.
The colored knitting fabric of wool simulating the most according to claim 1, it is characterised in that described hollow polyester fibre long filament is adopted
With the hollow polyester fibre long filament with far-infrared functional.
The colored knitting fabric of wool simulating the most according to claim 1, it is characterised in that described terry loop layer height is 1.8-
4.5mm。
6. the preparation method of the colored knitting fabric of wool simulating as described in any one of claim 1-5, it is characterised in that bag
Include:
Wire gauze and plush yarn are used weft knitting plane No. be 19-28G carry out weaving, blank pre-treatment, dyeing, reduction cleaning, auxiliary agent
Arrangement, plucking, carding, cropping, shake grain, open-width sizing, obtain the colored knitting fabric of wool simulating.
The preparation method of the colored knitting fabric of wool simulating the most according to claim 6, it is characterised in that described dyeing
For: temperature is 120-140 DEG C, levelling agent 1-3g/L, and fabric dyes along looped pile direction.
The preparation method of the colored knitting fabric of wool simulating the most according to claim 6, it is characterised in that described auxiliary agent arranges
Technique is: fabric is placed in the solution that bath raio is 1:6-10 process, and its finishing agent includes softening agent OH-600 0.5-
1.5wt%, smooth, soft agent 0.3-0.8g/L, low complexion changed color fixing agent 3-5wt%.
The preparation method of the colored knitting fabric of wool simulating the most according to claim 6, it is characterised in that described brushing process
For: plane is first drawn 3-6 time, looped pile face post-tensioning 1-3 time.
The preparation method of the colored knitting fabric of wool simulating the most according to claim 6, it is characterised in that described open-width is fixed
Type temperature is 120 DEG C-140 DEG C.