CN106079763A - A kind of wallpaper containing white bamboo carbon fiber - Google Patents
A kind of wallpaper containing white bamboo carbon fiber Download PDFInfo
- Publication number
- CN106079763A CN106079763A CN201610443302.5A CN201610443302A CN106079763A CN 106079763 A CN106079763 A CN 106079763A CN 201610443302 A CN201610443302 A CN 201610443302A CN 106079763 A CN106079763 A CN 106079763A
- Authority
- CN
- China
- Prior art keywords
- layer
- white bamboo
- bamboo carbon
- antibacterial
- carbon fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of wallpaper containing white bamboo carbon fiber, including white bamboo, the back side of described white bamboo is provided with waterproof mildew-resistant layer, described white bamboo be arranged above with antibacterial and deodouring layer, described antibacterial and deodouring layer is arranged above with cotton/chitin/white bamboo carbon blend fibre layer, described cotton/chitin/white bamboo carbon blend fibre layer is provided with printed pattern layer, and described printed pattern layer coated thereon has antibacterial and mouldproof layer, described antibacterial and mouldproof layer to be provided with coating layer.The wallpaper safety and environmental protection of the present invention, cheap, economic and practical, there is good mildew-resistant, antibacterial, moisture absorbing and deodorizing, there is promotion and use value.
Description
Technical field
The present invention relates to a kind of wallpaper, a kind of wallpaper containing white bamboo carbon fiber.
Background technology
Wallpaper, also referred to as wallpaper, it is a kind of application house decorative material the most widely.Because it is many that wallpaper has color
Other house decorative materials multiple such as sample, pattern are abundant, luxurious style, safety and environmental protection, easy construction, affordable cannot compare
The feature intended, therefore obtain considerable degree of universal at developed countries and regions such as America and Europe, Southeast Asia, Japan.In recent years, China room
Interior trim finishing is persistently overheating, the wallpaper that had once been given the cold shoulder with its gorgeous new attitude again come into parlor, bedroom, hotel,
Meeting room etc..
In the past, wallpaper comes into the life of people as just a kind of decorative material, and it is required many in dicoration by people
Above aesthetic property, along with the raising of people's living standard, people need the wallpaper wanting high-quality to decorate the life of oneself, people
Other Functional Requirement of wallpaper is also got more and more.
The environment of human living is the significant problem that present society is extremely paid close attention to.In recent years at the construction quality being exposed by the media
In problem, body of wall condensation is gone mouldy and is had become as one of hot issue, and especially China southern Jiangsu, Shanghai one carries, and is in north subtropical
Moistening monsoon climate, the most all can have plum rains season, and plum rain season temperature height, high humidity, air pressure are low, and indoor moisture is dark, ventilates
In the case of poor, can inevitably grow various mycete, according to investigations, between June to November, there is the resident of half in Shanghai
There is Signs of Mould in house, and therefore this is accomplished by the wallpaper mildew resistance to be had for interior decoration, on the one hand can extend wall
Paper service life in wet environment, another convenient protection body of wall, it is to avoid body of wall has wallpaper mouldy, and then avoids the taste of antibacterial
Raw, the environment of the indoor inhabitation of protection, protection resident's is healthy.
Along with improving constantly of people's material and cultural life, people are for the healthy and care of cleaning problems and to gracefulness
The life of peaceful and comfortable equivalent comfort energy is pursued and is also day by day being improved.But, in the middle of daily life, it is impossible to the kitchen avoided, health
Between, hospital ward, bedroom abnormal flavour and the life stink such as Nicotiana tabacum L., body antiperspirant, often affect the comfortableness of people's life.Particularly
Increase along with the arrival of aging society, the aged person of bed and the person of recuperating, for preventing stench, improving the demand of environment also
Increasing therewith, these are desirable that the wallpaper as interior decoration needs to have the functions such as antibacterial, deodorization undoubtedly.
White bamboo carbon fiber is the one in bamboo carbon fiber, has stronger moisture absorbing and deodorizing, purifies air, antibacterial, antibacterial, anti-
The functions such as ultraviolet, current white bamboo carbon fiber is mainly used in field of textiles, there is no application on wallpaper.
Therefore, it is necessary to develop a kind of white bamboo carbon fiber wallpaper with performances such as antibacterial, deodorization, mildew-resistant.
Summary of the invention
Goal of the invention: the invention aims to solve the deficiencies in the prior art, it is provided that a kind of containing white bamboo carbon fiber
Wallpaper.
Technical scheme: in order to realize object above, the present invention is by the following technical solutions.
A kind of wallpaper containing white bamboo carbon fiber, including white bamboo, the back side of described white bamboo is provided with
Waterproof mildew-resistant layer, described white bamboo be arranged above with antibacterial and deodouring layer, described antibacterial and deodouring layer is arranged above with cotton/carapace
Element/white bamboo carbon blend fibre layer, described cotton/chitin/white bamboo carbon blend fibre layer is provided with printed pattern layer, described printing pressure
Flower layer coated thereon has antibacterial and mouldproof layer, described antibacterial and mouldproof layer to be provided with coating layer;Described waterproof mildew-resistant layer is by following quality
The material composition of percentage ratio: modified polyvinylalcohol: 30-35 part, sodium alginate: 6-8 part, 3-iodo-2-propynyl butylamino first
Acid esters: 5-7 part, halloysite nanotubes: 4-6 part, silicone acrylic emulsion: 20-22 part, deionized water: 30-35 part;Described antibacterial and mouldproof
Layer is made up of the material of following mass percent: modified polyvinylalcohol: 20-22 part, zeolite with carrying silver: 0.5-1 part, chitosan: 4-5
Part, calcium lignosulfonate: 4-5 part, camphor leaf extract: 10-15 part, DDAC: 1-1.5 part, pectin with
Sodium lactate compound: 4-5 part, deionized water: 75-80 part.
Preferably, cotton fiber/chitin fiber/white bamboo carbon in described cotton/chitin/white bamboo carbon blend fibre layer
The weight ratio of fiber is 2/2/1.Cotton/chitin/white bamboo carbon blend fibre is by the cotton fiber of environmental protection, chitin fiber, white
Bamboo carbon fiber carries out blending so that it is have cooperative effect, finally makes the blend fibre of three have the moisture absorbing and sweat releasing of excellence, resist
The functions such as bacterium, deodorization, uvioresistant.
Preferably, described pectin and sodium lactate compound are 5mg/mL hawthorn pectin oligosaccharide and 10mg/mL lactic acid
Compound.
Preferably, described antibacterial and deodouring layer is made up of the material of following mass percent: PE:80-90 part, diatom
Soil: 6-8 part, activated carbon: 6-8 part, chitosan: 4-5 part, Hinokitiol: 4-5 part, glass fibre: 4-6 part, organo montmorillonite: 4-6
Part, octaphenyl eight silsesquioxane: 1-2 part, carbon fiber: 1-2 part, PPS:2-4 part, dimethyl fumarate: 1-2 part, meerschaum:
5-7 part, sorbic acid: 1-1.5 part, softening agent: 1-2 part, retention agent: 0.3-0.5 part, wet strength agent: 1-2 part, ethanol: 5-8 part, goes
Ionized water: 30-35 part.
As further preferred scheme, the thickness of described antibacterial and deodouring layer is 0.1-0.3mm;
As further preferred scheme, described softening agent is stearic acid triethanolamine ester quaternary, and retention agent is guar gum, wet by force
Agent is PAE resin.
As further preferred scheme, described organo montmorillonite is 3-hexadecane epoxide-2-hydroxypropyl trimethyl chlorination
The organo montmorillonite that ammonium is modified.
As further preferred version, the preparation method of described organo montmorillonite is: by the inorganic illiteracy that mass ratio is 1:1
De-soil and 3-hexadecane epoxide-2-trimethyl ammonium chloride are dissolved in the ethanol water that mass fraction is 50%, mixing
Uniformly post-heating is to 75 DEG C, reacts 1 hour, filters, filter cake ethanol purge, is drying to obtain described organo montmorillonite.
Wherein: the ethanol water that the inorganic montmorillonite of 1g needs 15-20ml mass fraction to be 50%.
Preferably, the thickness of described waterproof mildew-resistant layer is 0.2-0.4mm.
Preferably, the thickness of described antibacterial and mouldproof layer is 0.1-0.3mm.
Preferably, halloysite nanotubes pipe range is 0.5-1.5 μm.
Preferably, described modified polyvinylalcohol is citric acid-modified polyvinyl alcohol, and its preparation method is: according to matter
Amount number meter, by 9-11 part polyvinyl alcohol, 0.1-0.3 part citric acid, 0.5-1.5 part glycerol, 88-90 part deionized water, 95
At DEG C constant temperature stir 3 hours, then deaerate under-0.1 MPa 1 h, finally at 60 DEG C be dried 3 h i.e. obtain described modification gather
Vinyl alcohol.
Preferably, the preparation method of described camphor leaf extract is as follows: Folium cinnamomi camphorae powder is positioned over quality and divides
In the ethanol water of several 60%, insulated and stirred 2-3 hour at 55 DEG C, then to filter, filter residue, filtrate is in 55 DEG C of decompressions
Distilling and i.e. obtain described camphor leaf extract, during extraction, Folium cinnamomi camphorae powder is V ethanol with the solid-liquid ratio of ethanol water: m tree
Leaf=16: 1.
Preferably, the thickness of described cotton/chitin/white bamboo carbon blend fibre layer is 0.1-0.3mm.
Preferably, described coating layer is polyethylene film, and thickness is 0.2-0.4mm.Polyethylene has excellent
Moisture resistance so that the moisture resistance of wallpaper is the most superior.
The above-mentioned silicone acrylic emulsion used of the present invention uses commercially available, and can be such as that Nantong is raw reaches the limited public affairs of chemical industry
The SD-528 silicone acrylic emulsion that department produces.
Beneficial effect: compared with prior art, the present invention has a following significance beneficial effect:
1, the wallpaper of the present invention, uses white bamboo carbon fiber to do wallpaper basic unit, makes wallpaper have excellent moisture absorbing and deodorizing, purify sky
The functions such as gas, antibacterial, antibacterial, uvioresistant, the most additional cotton/chitin/white bamboo carbon blend fibre layer, further enhancing
The moisture absorbing and sweat releasing of wallpaper, antibacterial, deodorization functions, be simultaneously provided with waterproof mildew-resistant layer, antibacterial and deodouring layer, antibacterial and mouldproof layer, multiple
Ensure the antimildew and antibacterial of wallpaper, made the wallpaper environmental protection of the present invention, economy, it is adaptable to hygrothermal environment has used;It is additionally provided with and covers
Film layer protects wallpaper further, extends the service life of wallpaper;
2, the reagent environmental protection that each layer of the present invention uses, meets the regulation of GB18585-2001, does not contains the taboo of national regulation
Only the heavy metal antimony of use, arsenic, barium, cadmium, chromium, lead, hydrargyrum, selenium, do not contain formaldehyde, do not contain Vinyl Chloride Monomer, do not result in yet
Secondary pollution;
In a word, the wallpaper of the present invention is a mildew-resistant, moisture absorbing and deodorizing, antibacterial, fire-retardant, moistureproof multi-functional environment-protection green wallpaper,
There is promotion and use value.
Accompanying drawing explanation
Fig. 1 is the structural representation of the embodiment of the present invention;
In figure: 1-waterproof mildew-resistant layer, the white bamboo of 2-, 3-antibacterial and deodouring layer, 4-cotton/chitin/white bamboo carbon blend fibre
Layer, 5--printed pattern layer, 6-antibacterial and mouldproof layer, 7-coating layer.
Detailed description of the invention
Below in conjunction with embodiment, technical solution of the present invention is described in further detail and completely.
Embodiment 1
A kind of wallpaper containing white bamboo carbon fiber, including white bamboo 2, the back side of described white bamboo 2 is provided with anti-
Water mildew-resistant layer 1, described white bamboo 2 be arranged above with antibacterial and deodouring layer 3, described antibacterial and deodouring layer 3 is arranged above with cotton/first
Shell element/white bamboo carbon blend fibre layer 4, described cotton/chitin/white bamboo carbon blend fibre layer 4 is provided with printed pattern layer 5, described
Printed pattern layer 5 coated thereon has antibacterial and mouldproof layer 6, described antibacterial and mouldproof layer 6 to be provided with coating layer 7.
Wherein:
Waterproof mildew-resistant layer 1 is made up of the material of following mass percent: modified polyvinylalcohol: 30 parts, sodium alginate: 6 parts, 3-
Iodo-2-propynyl butyl carbamate: 5 parts, halloysite nanotubes: 4 parts, silicone acrylic emulsion: 20 parts, deionized water: 30 parts;Anti-
The thickness of water mildew-resistant layer 1 is 0.2mm.
Antibacterial and deodouring layer 3 is made up of the material of following mass percent: PE:80 part, kieselguhr: 6 parts, activated carbon: 6 parts,
Chitosan: 4 parts, Hinokitiol: 4 parts, glass fibre: 4 parts, organo montmorillonite: 4 parts, octaphenyl eight silsesquioxane: 1 part, carbon is fine
Dimension: 1 part, PPS:2 part, dimethyl fumarate: 1 part, meerschaum: 5 parts, sorbic acid: 1 part, softening agent: triethanolamine stearate
Ester quat: 1 part, retention agent: guar gum: 0.3 part, wet strength agent: PAE resin: 1 part, ethanol: 5 parts, deionized water: 30 parts;Anti-
The thickness of bacterium deodorizing layer 3 is 0.3mm.
The thickness of cotton/chitin/white bamboo carbon blend fibre layer 4 is 0.1mm.
Antibacterial and mouldproof layer 6 is made up of the material of following mass percent: modified polyvinylalcohol: 20 parts, zeolite with carrying silver: 0.5
Part, chitosan: 4 parts, calcium lignosulfonate: 4 parts, camphor leaf extract: 10 parts, DDAC: 1 part, pectin
With sodium lactate compound, 4 parts, deionized water: 75 parts;The thickness of antibacterial and mouldproof layer 6 is 0.1mm.
Coating layer 7 is polyethylene film, and thickness is 0.2mm.
Embodiment 2
A kind of wallpaper containing white bamboo carbon fiber, including white bamboo 2, the back side of described white bamboo 2 is provided with anti-
Water mildew-resistant layer 2, described white bamboo 2 be arranged above with antibacterial and deodouring layer 3, described antibacterial and deodouring layer 3 is arranged above with cotton/first
Shell element/white bamboo carbon blend fibre layer 4, described cotton/chitin/white bamboo carbon blend fibre layer 4 is provided with printed pattern layer 5, described
Printed pattern layer 5 coated thereon has antibacterial and mouldproof layer 6, described antibacterial and mouldproof layer 6 to be provided with coating layer 7.
Wherein:
Waterproof mildew-resistant layer 2 is made up of the material of following mass percent: modified polyvinylalcohol: 33 parts, sodium alginate: 7 parts, 3-
Iodo-2-propynyl butyl carbamate: 6 parts, halloysite nanotubes: 5 parts, silicone acrylic emulsion: 21 parts, deionized water: 33 parts;Anti-
The thickness of water mildew-resistant layer 2 is 0.3mm.
Antibacterial and deodouring layer 3 is made up of the material of following mass percent: PE:85 part, kieselguhr: 7 parts, activated carbon: 7 parts,
Chitosan: 4.5 parts, Hinokitiol: 4.5 parts, glass fibre: 5 parts, organo montmorillonite: 5 parts, octaphenyl eight silsesquioxane: 1.5
Part, carbon fiber: 1.5 parts, PPS:3 part, dimethyl fumarate: 1.5 parts, meerschaum: 6 parts, sorbic acid: 1.3 parts, softening agent: hard
Fat acid triethanol amine ester quat: 1.5 parts, retention agent: guar gum: 0.4 part, wet strength agent: PAE resin: 1-.5 part, ethanol: 6.5
Part, deionized water: 33 parts;The thickness of antibacterial and deodouring layer 3 is 0.2mm.
The thickness of cotton/chitin/white bamboo carbon blend fibre layer 4 is 0.2mm.
Antibacterial and mouldproof layer 6 is made up of the material of following mass percent: modified polyvinylalcohol: 21 parts, zeolite with carrying silver: 0.8
Part, chitosan: 4.5 parts, calcium lignosulfonate: 4.5 parts, camphor leaf extract: 13 parts, DDAC: 1.3
Part, pectin and sodium lactate compound: 4.5 parts, deionized water: 780 parts;The thickness of antibacterial and mouldproof layer 6 is 0.2mm.
Coating layer 7 is polyethylene film, and thickness is 0.3mm.
Embodiment 3
A kind of wallpaper containing white bamboo carbon fiber, including white bamboo 2, the back side of described white bamboo 2 is provided with anti-
Water mildew-resistant layer 2, described white bamboo 2 be arranged above with antibacterial and deodouring layer 3, described antibacterial and deodouring layer 3 is arranged above with cotton/first
Shell element/white bamboo carbon blend fibre layer 4, described cotton/chitin/white bamboo carbon blend fibre layer 4 is provided with printed pattern layer 5, described
Printed pattern layer 5 coated thereon has antibacterial and mouldproof layer 6, described antibacterial and mouldproof layer 6 to be provided with coating layer 7.
Wherein:
Waterproof mildew-resistant layer 2 is made up of the material of following mass percent: modified polyvinylalcohol: 35 parts, sodium alginate: 8 parts, 3-
Iodo-2-propynyl butyl carbamate: 7 parts, halloysite nanotubes: 6 parts, silicone acrylic emulsion: 22 parts, deionized water: 35
Part;The thickness of waterproof mildew-resistant layer 2 is 0.4mm.
Antibacterial and deodouring layer 3 is made up of the material of following mass percent: PE:90 part, kieselguhr: 8 parts, activated carbon: 8
Part, chitosan: 5 parts, Hinokitiol: 5 parts, glass fibre: 6 parts, organo montmorillonite: 6 parts, octaphenyl eight silsesquioxane:
2 parts, carbon fiber: 2 parts, PPS:4 part, dimethyl fumarate: 2 parts, meerschaum: 7 parts, sorbic acid: 1.5 parts, softening agent:
Stearic acid triethanolamine ester quaternary: 2 parts, retention agent: guar gum: 0.5 part, wet strength agent: PAE resin: 2 parts, ethanol: 8
Part, deionized water: 35 parts;The thickness of antibacterial and deodouring layer 3 is 0.3mm.
The thickness of cotton/chitin/white bamboo carbon blend fibre layer 4 is 0.3mm.
Antibacterial and mouldproof layer 6 is made up of the material of following mass percent: modified polyvinylalcohol: 22 parts, zeolite with carrying silver: 1
Part, chitosan: 5 parts, calcium lignosulfonate: 5 parts, camphor leaf extract: 15 parts, DDAC: 1.5
Part, pectin and sodium lactate compound: 5 parts, deionized water: 80 parts;The thickness of antibacterial and mouldproof layer 6 is 0.3mm.
Coating layer 7 is polyethylene film, and thickness is 0.4mm.
Cotton/chitin in above-described embodiment/white bamboo carbon blend fibre is by cotton fiber, chitin fiber, white bamboo charcoal fibre
Dimension carries out blending according to weight ratio 2/2/1 and obtains.
Modified polyvinylalcohol in above-described embodiment, is to be prepared via a method which and obtain: according to mass fraction meter, by 10
Part polyvinyl alcohol, 0.2 part of citric acid, 1 part of glycerol, 89 parts of deionized waters, at 95 DEG C, constant temperature stirs 3 hours, then-0.1
Deaerate under MPa 1 h, is finally dried 3 h at 60 DEG C and i.e. obtains described modified polyvinylalcohol.
Camphor leaf extract in above-described embodiment, is to be prepared via a method which and obtain: be positioned over by Folium cinnamomi camphorae powder
In the ethanol water of mass fraction 60%, insulated and stirred 2-3 hour at 55 DEG C, then to filter, filter residue, filtrate is in 55
DEG C decompression distill and is i.e. obtained described camphor leaf extract, and during extraction, the solid-liquid ratio of Folium cinnamomi camphorae powder and ethanol water is V second
Alcohol: m leaves=16: 1.
Organo montmorillonite in above-described embodiment, is to be prepared via a method which and obtain:
Inorganic montmorillonite and 3-hexadecane epoxide-2-trimethyl ammonium chloride that mass ratio is 1:1 are dissolved in quality and divide
Number be 50% ethanol water in (ethanol water that the inorganic montmorillonite of 1g needs 15-20ml mass fraction to be 50%), mixing
Uniformly post-heating is to 75 DEG C, reacts 1 hour, filters, filter cake ethanol purge, is drying to obtain described organo montmorillonite.
The processing technology of the wallpaper of example wallpaper routinely time above-mentioned, through paste producing, coating, is dried, prints, sends out
Bubble, embossing, cooling, trimming, rolling.
The wallpaper prepared according to above-described embodiment meets the regulation of GB18585-2001, do not contain national regulation forbid make
Heavy metal antimony, arsenic, barium, cadmium, chromium, lead, hydrargyrum, selenium, do not contain formaldehyde, do not contain Vinyl Chloride Monomer.
The wallpaper prepared according to above-described embodiment, does basic unit with white bamboo carbon fiber, the most additional cotton/chitin/white bamboo carbon
Blend fibre layer, has excellent moisture absorbing and deodorizing.
The wallpaper prepared according to above-described embodiment, carries out mildew resistance test to it, and concrete method of testing is: by 30x60 milli
The wallpaper of rice be exposed to containing escherichia coli, Salmonella, staphylococcus aureus suspension in, be placed in beneficially mushroom raw
Long environment (temperature 25 DEG C, relative humidity 85%), this environment tackles the wet environment of daily household, including the Huang that south is common
Rainy season gas, after one month, wallpaper surface occurs without macula lutea and mildew, and this explanation wallpaper has superior mildew resistance.
The wallpaper prepared according to above-described embodiment, carries out antibiotic property test to it, with reference to JISZ2801:2000 " antibacterial system
The detection of product anti-microbial property and evaluation)) standard detects, and carries out antibacterial to common escherichia coli, staphylococcus aureus
Test, experimental result display the present invention wallpaper to escherichia coli, staphylococcus aureus bacteriostasis rate all up to 99.99%;Tool
There is superior bacteriostasis antibiosis.
It addition, the wallpaper prepared according to above-described embodiment, carrying out anti-flammability test, test result shows, its UL-94 hangs down
Direct combustion burns and reaches V-0 level, and LOI reaches more than 30, has good anti-flammability.In a word, the wallpaper of the present invention be a mildew-resistant,
Antibacterial, fire-retardant, moisture absorbing and deodorizing, moistureproof multi-functional environment-protection green wallpaper, have promotion and use value.
Finally need it is pointed out here that: be the most only the part preferred embodiment of the present invention, it is impossible to be interpreted as this
The restriction of bright protection domain, some nonessential improvement that those skilled in the art makes according to the foregoing of the present invention and
Adjustment belongs to protection scope of the present invention.
Claims (10)
1. the wallpaper containing white bamboo carbon fiber, it is characterised in that: include white bamboo, described white bamboo
The back side is provided with waterproof mildew-resistant layer, described white bamboo be arranged above with antibacterial and deodouring layer, set above described antibacterial and deodouring layer
Cotton/chitin/white bamboo carbon blend fibre layer, described cotton/chitin/white bamboo carbon blend fibre layer is had to be provided with printed pattern layer,
Described printed pattern layer coated thereon has antibacterial and mouldproof layer, described antibacterial and mouldproof layer to be provided with coating layer;Described waterproof mildew-resistant layer
It is made up of the material of following mass percent: modified polyvinylalcohol: 30-35 part, sodium alginate: 6-8 part, the iodo-2-propynyl of 3-
Butyl carbamate: 5-7 part, halloysite nanotubes: 4-6 part, silicone acrylic emulsion: 20-22 part, deionized water: 30-35 part;Institute
State antibacterial and mouldproof layer to be made up of the material of following mass percent: modified polyvinylalcohol: 20-22 part, zeolite with carrying silver: 0.5-1 part,
Chitosan: 4-5 part, calcium lignosulfonate: 4-5 part, camphor leaf extract: 10-15 part, DDAC: 1-1.5
Part, pectin and sodium lactate compound: 4-5 part, deionized water: 75-80 part.
Wallpaper containing white bamboo carbon fiber the most according to claim 1, it is characterised in that: described cotton/chitin/white bamboo carbon
In blend fibre layer, the weight ratio of cotton fiber/chitin fiber/white bamboo carbon fibre is 2/2/1.
Wallpaper containing white bamboo carbon fiber the most according to claim 1, it is characterised in that: described pectin compounds with sodium lactate
Thing is the compound of 5mg/mL hawthorn pectin oligosaccharide and 10mg/mL lactic acid.
Wallpaper containing white bamboo carbon fiber the most according to claim 1, it is characterised in that: PE:80-90 part, kieselguhr: 6-
8 parts, activated carbon: 6-8 part, chitosan: 4-5 part, Hinokitiol: 4-5 part, glass fibre: 4-6 part, organo montmorillonite: 4-6 part, eight
Phenyl eight silsesquioxane: 1-2 part, carbon fiber: 1-2 part, PPS:2-4 part, dimethyl fumarate: 1-2 part, meerschaum: 5-7
Part, sorbic acid: 1-1.5 part, softening agent: 1-2 part, retention agent: 0.3-0.5 part, wet strength agent: 1-2 part, ethanol: 5-8 part, go from
Sub-water: 30-35 part.
Wallpaper containing white bamboo carbon fiber the most according to claim 4, it is characterised in that: described softening agent is stearic acid three
Ethanolamine ester quat, retention agent is guar gum, and wet strength agent is PAE resin.
Wallpaper containing white bamboo carbon fiber the most according to claim 4, it is characterised in that: described organo montmorillonite is 3-ten
The organo montmorillonite that six alkoxyl-2-trimethyl ammonium chloride are modified.
Wallpaper containing white bamboo carbon fiber the most according to claim 6, it is characterised in that: the preparation of described organo montmorillonite
Method is: inorganic montmorillonite and 3-hexadecane epoxide-2-trimethyl ammonium chloride that mass ratio is 1:1 are dissolved in quality
Mark is in the ethanol water of 50%, mix homogeneously post-heating to 75 DEG C, reacts 1 hour, filters, filter cake ethanol purge, dry
Dry i.e. obtain described organo montmorillonite.
Wallpaper containing white bamboo carbon fiber the most according to claim 1, it is characterised in that: described modified polyvinylalcohol is lemon
Lemon acid modified polyvinylalcohol, its preparation method is: according to mass fraction meter, by 9-11 part polyvinyl alcohol, 0.1-0.3 part Fructus Citri Limoniae
Acid, 0.5-1.5 part glycerol, 88-90 part deionized water, at 95 DEG C, constant temperature stirs 3 hours, then degassing 1 under-0.1 MPa
H, is finally dried 3 h at 60 DEG C and i.e. obtains described modified polyvinylalcohol.
Wallpaper containing white bamboo carbon fiber the most according to claim 1, it is characterised in that: the system of described camphor leaf extract
Preparation Method is as follows: being positioned in the ethanol water of mass fraction 60% by Folium cinnamomi camphorae powder, at 55 DEG C, insulated and stirred 2-3 is little
Time, then to filter, filter residue, filtrate is distilled in 55 DEG C of decompressions and is i.e. obtained described camphor leaf extract, Folium cinnamomi camphorae during extraction
Powder is V ethanol with the solid-liquid ratio of ethanol water: m leaves=16: 1.
Wallpaper containing white bamboo carbon fiber the most according to claim 1, it is characterised in that: described coating layer is polyethylene
Thin film.