CN106048479A - 一种空调散热器铝箔的退火工艺 - Google Patents

一种空调散热器铝箔的退火工艺 Download PDF

Info

Publication number
CN106048479A
CN106048479A CN201610669736.7A CN201610669736A CN106048479A CN 106048479 A CN106048479 A CN 106048479A CN 201610669736 A CN201610669736 A CN 201610669736A CN 106048479 A CN106048479 A CN 106048479A
Authority
CN
China
Prior art keywords
annealing
aluminum foil
aluminium foil
temperature
coil
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610669736.7A
Other languages
English (en)
Inventor
骆宣佐
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI TIANXIANG AIR-CONDITIONER SCIENCE AND TECHNOLOGY Co Ltd
Original Assignee
ANHUI TIANXIANG AIR-CONDITIONER SCIENCE AND TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI TIANXIANG AIR-CONDITIONER SCIENCE AND TECHNOLOGY Co Ltd filed Critical ANHUI TIANXIANG AIR-CONDITIONER SCIENCE AND TECHNOLOGY Co Ltd
Priority to CN201610669736.7A priority Critical patent/CN106048479A/zh
Publication of CN106048479A publication Critical patent/CN106048479A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种空调散热器铝箔的退火工艺，该空调散热器铝箔的退火工艺具体步骤如下：S1：将需要退火的铝箔卷放入退火炉中，S2：启动退火炉对铝箔进行退火处理，S3：退火时鼓风处理，S4：降温处理，S5：铝箔的取出处理。本发明采用炉内降温的方式对铝箔进行退火处理，使得铝箔在退火完成后温度降低缓慢，避免温度骤降，给铝箔的质量带来了保障，提高铝箔的机械性能。

Description

一种空调散热器铝箔的退火工艺
技术领域
本发明涉及空调散热器技术领域，具体为一种空调散热器铝箔的退火工艺。
背景技术
退火是一种金属热处理工艺，指的是将金属缓慢加热到一定温度，保持足够时间，然后以适宜速度冷却。目的是降低硬度，改善切削加工性;消除残余应力，稳定尺寸，减少变形与裂纹倾向;细化晶粒，调整组织，消除组织缺陷。准确的说，退火是一种对材料的热处理工艺，包括金属材料、非金属材料。而且新材料的退火目的也与传统金属退火存在异同。铝箔是空调散热器中的重要部件，铝箔在加工过程中需要进行退火处理，提高铝箔的机械性能。
发明内容
本发明的目的在于提供一种空调散热器铝箔的退火工艺，该空调散热器铝箔的退火工艺具体步骤如下：
S1：将需要退火的铝箔卷放入退火炉中，铝箔卷采用竖直放置的方式，将铝箔卷放在转盘上，转盘转动，铝箔卷在退火炉中转动；
S2：启动退火炉对铝箔进行退火处理，退火炉加热，退火温度控制在600-800℃之间，退火时间控制在20-25分钟之间；
S3：退火时鼓风处理，向退火炉内鼓风，由铝箔卷顶部向下鼓风，使得铝箔上的压延油便捷的由铝箔卷上掉落，避免铝箔上残留过多的压延油对退火造成影响；
S4：降温处理，退火时间到后采用炉内降温的方式降温，关闭退火炉，使得铝箔卷在退火炉内降温，使得温度缓慢降低，避免温度骤降对铝箔造成质量缺陷；
S5：铝箔的取出处理，在步骤S4中，当温度降低至200℃以下后可以将铝箔取出，向铝箔上循环浇冷却液，使得铝箔温度降低至室温即可完成铝箔的退火处理。
所述铝箔卷在退火处理时先经过松动处理，使得每卷之间的间隙不小于2MM。
与现有技术相比，本发明的有益效果是：本发明采用炉内降温的方式对铝箔进行退火处理，使得铝箔在退火完成后温度降低缓慢，避免温度骤降，给铝箔的质量带来了保障，提高铝箔的机械性能。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白，以下结合具体实施例，对本发明进行进一步详细说明。应当理解，此处所描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
实施例1
一种空调散热器铝箔的退火工艺，该空调散热器铝箔的退火工艺具体步骤如下：
S1：将需要退火的铝箔卷放入退火炉中，铝箔卷采用竖直放置的方式，将铝箔卷放在转盘上，转盘转动，铝箔卷在退火炉中转动；
S2：启动退火炉对铝箔进行退火处理，退火炉加热，退火温度控制在600-800℃之间，退火时间控制在20-25分钟之间；
S3：退火时鼓风处理，向退火炉内鼓风，由铝箔卷顶部向下鼓风，使得铝箔上的压延油便捷的由铝箔卷上掉落，避免铝箔上残留过多的压延油对退火造成影响；
S4：降温处理，退火时间到后采用炉内降温的方式降温，关闭退火炉，使得铝箔卷在退火炉内降温，使得温度缓慢降低，避免温度骤降对铝箔造成质量缺陷；
S5：铝箔的取出处理，在步骤S4中，当温度降低至200℃以下后可以将铝箔取出，向铝箔上循环浇冷却液，使得铝箔温度降低至室温即可完成铝箔的退火处理。
所述铝箔卷在退火处理时先经过松动处理，使得每卷之间的间隙不小于2MM。
本发明采用炉内降温的方式对铝箔进行退火处理，使得铝箔在退火完成后温度降低缓慢，避免温度骤降，给铝箔的质量带来了保障，提高铝箔的机械性能。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。

Claims (2)

1.一种空调散热器铝箔的退火工艺，其特征在于：该空调散热器铝箔的退火工艺具体步骤如下：
S1：将需要退火的铝箔卷放入退火炉中，铝箔卷采用竖直放置的方式，将铝箔卷放在转盘上，转盘转动，铝箔卷在退火炉中转动；
S2：启动退火炉对铝箔进行退火处理，退火炉加热，退火温度控制在600-800℃之间，退火时间控制在20-25分钟之间；
S3：退火时鼓风处理，向退火炉内鼓风，由铝箔卷顶部向下鼓风，使得铝箔上的压延油便捷的由铝箔卷上掉落，避免铝箔上残留过多的压延油对退火造成影响；
S4：降温处理，退火时间到后采用炉内降温的方式降温，关闭退火炉，使得铝箔卷在退火炉内降温，使得温度缓慢降低，避免温度骤降对铝箔造成质量缺陷；
S5：铝箔的取出处理，在步骤S4中，当温度降低至200℃以下后可以将铝箔取出，向铝箔上循环浇冷却液，使得铝箔温度降低至室温即可完成铝箔的退火处理。
2.根据权利要求1所述的一种空调散热器铝箔的退火工艺，其特征在于：所述铝箔卷在退火处理时先经过松动处理，使得每卷之间的间隙不小于2MM。
CN201610669736.7A 2016-08-16 2016-08-16 一种空调散热器铝箔的退火工艺 Pending CN106048479A (zh)