CN106046805A - Three-dimensional sculpture LED decorative lamp - Google Patents
Three-dimensional sculpture LED decorative lamp Download PDFInfo
- Publication number
- CN106046805A CN106046805A CN201610574287.8A CN201610574287A CN106046805A CN 106046805 A CN106046805 A CN 106046805A CN 201610574287 A CN201610574287 A CN 201610574287A CN 106046805 A CN106046805 A CN 106046805A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- oil
- mixture
- weight
- quintessence oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A stereoscopic sculpture LED decorative lamp comprises a semitransparent stereoscopic sculpture lamp cover body, an LED lighting assembly, a base and a power supply driving device arranged in the base, wherein the lamp cover body is provided with a hollow cavity for arranging the LED lighting assembly, a plurality of radiating holes are formed in the side wall of the hollow cavity, and a radiating coating is coated on the inner surface of the side wall of the hollow cavity.
Description
Technical field
The present invention relates to electron-optical field, particularly relate to a kind of stereoscopic sculpture LED decorative lamp.
Background technology
Along with the continuous change of human being's production technology, as the light fixture of people's daily necessities, its function is also a day crescent
Different；Simultaneously as the environmental protection idea of current people is increasingly stronger, thus the illuminator of environmental protection can be more by people
Favor, therefore, in addition to possessing traditional lighting function, the pursuit of hommization functions more to light fixture, it has also become illuminate now
One development trend in field.
On the one hand, by negative aeroion Technology application in light fixture product, make light fixture discharge for a long time in indoor air bear from
Son, especially negative oxygen ion.Owing to it is structurally similar to ultra-oxygen anion free radical, therefore there is similar biology and live
Property, it is possible to make the biological cell lived electronegative, so that virus loses the attacking ability to cell；Meanwhile, negative oxygen ion energy
The finishing pollution things such as enough and formaldehyde, toluene, TVOC react, and product is nonpoisonous and tasteless carbon dioxide and water, without secondary dirt
The generation of dye, has certain effect purified the air of a room, such as, in artificial air's anion environment, and air after measured
Middle mycete, bacterial population can reduce by more than 90%.After negative oxygen ion is inhaled into human body, neural excitatory state can be regulated, change
The ventilatory of kind lung, improves blood circulation, enhances metabolism, strengthens immune system ability, makes that people is in high spirits, improve work
Making efficiency etc., it also has certain therapeutical effect to numerous diseases such as hypertension, asthma, influenza, insomnia, arthritis, so people
Anion is called " vitamin in air " " long-lived element "；On the other hand, light fixture is made to have the function of certain expelling mosquito, no
Only promote the comfort level of user, also greatly enrich the use function of light fixture.
So far, the Technology design making conventional lamp product simultaneously have expelling mosquito and negative ion-releasing function does not also have
See.
Summary of the invention
The deficiency existed for prior art, the technical problem to be solved is to provide a kind of stereoscopic sculpture LED
Decorative lamp, not only long-term negative ion release, also have certain expelling mosquito effect, also has certain antibacterial work simultaneously
With, there is certain effect removing the finishing pollution things such as formaldehyde, toluene, TVOC simultaneously, there is the effect achieved many things at one stroke, abundant
The use function of conventional lamp.
It is an object of the invention to be achieved through the following technical solutions:
A kind of stereoscopic sculpture LED decorative lamp, including translucent stereoscopic sculpture lamp lampshade, LED illumination assembly, base and
Being placed in the power source drive device in described base, described lamp lampshade has one for disposing in described LED illumination assembly
Cavity body, the sidewall at described hollow cavity is provided with some louvres, and the side wall inner surfaces at described hollow cavity is coated with scattered
Hot coating, wherein, described translucent stereoscopic sculpture lamp lampshade is prepared from according to parts by weight by following component:
Resin 50-65 weight portion；Glass fibre 10-20 weight portion；Fire retardant 5-8 weight portion；Graphene 3-4.5 weight portion；Change
Property aromatic amine curing agent 3-4 weight portion；Fluorescent material 0.1-0.3 weight portion；The good solid 754 light trigger 2-4 weight portions of vapour Ba Yan；Poly-
Ether amines catalyst 0.5-0.7 weight portion；Ceria 0.1-0.15 weight portion；Active mineral matter powder 0.7-1 weight portion；Middle YAOJING
Oil 1-1.2 weight portion；Wherein, described resin is epoxy soybean oil acrylate and the mixture of bisphenol A-type E51 epoxy resin,
The mass ratio of described epoxy soybean oil acrylate and bisphenol A-type E51 epoxy resin is 2:1-3:2, and described fire retardant is poly-phosphorus
Acid ammonium, tripolycyanamide and the mixture of expanded graphites, the quality of described APP, tripolycyanamide and expanded graphites
Ratio 2:1.5:1.3, described fluorescent material is Ce and YAG fluorescent powder mixture, particle diameter≤13 μm of described fluorescent material, described work
Property mineral powder be germanite, fluorite, tourmaline, hexacyclic ring stone by weight the mixture of 2.5:3:3.7:2, wherein tourmaline is magnesium
The mixture of tourmaline and elbaite 5:3 by weight, particle diameter≤13 μm of described active mineral matter powder, described translucent
Stereoscopic sculpture lamp lampshade is made by the steps and forms:
S1, the resin by required parts by weight, fire retardant, Graphene, fluorescent material, vapour Ba Yan are good to be consolidated 754 light triggers and gathers
Ether amines catalyst is placed in blender, mixes well 70-80 DEG C of next part high speed stirring, and mixing time is 15-30 minute, to be mixed
Take out from blender after Jun Yun, i.e. prepare mixture A, standby；
S2, by material Fructus Carpesii 50-60 weight portion, Herba Lycopodii 3-5 weight portion, Herba Artemisiae Scopariae 20-25 weight portion, lavandula angustifolia 15-20 weight
Part, Herba Anemones Hupehensis 3-5 weight portion, Caulis Polygoni Multiflori 3-5 weight portion, Origanum majorana 1.5-2.5 weight portion, Rhizoma Cimicifugae 1-3 weight portion, ten thousand
Longevity chrysanthemum 3-5 weight portion, Folium cinnamomi camphorae 6-8 weight portion decontamination, it is placed in vacuum still 2-3 hour of-20 DEG C together, is placed in micro-the most again
Ripple drying machine carries out pretreatment, and wherein drying time is 30-40 minute, and microwave power is 17kw；
S3, step S2 is processed after material put into together in super micron mill and be crushed to 60 mesh, prepare crude drug powder, standby
With；
S4, by step S3 prepare crude drug powder put into supercritical carbon dioxide extraction apparatus extraction kettle in, regulation extraction
Pressure power 27.65MPa, extraction temperature 45 DEG C, carbon dioxide flow is 1100L/h, and dynamic extraction 2 hours, directly at separating still
Outlet triangular flask collects crude oil, standby；
S5, the crude oil prepared in step S4 is placed in 5 DEG C of environment freezing 70 minutes, then the crude oil after freezing is placed in rotating speed is
The High speed refrigerated centrifuge of 17000r/min is centrifuged 25 minutes, goes the removal of impurity to be placed on 85 DEG C of vacuum tank evacuation 3 hours, i.e.
Prepare volatile oil B, standby；
S6, by vanilla 1.5-2 weight portion, Herba Portulacae 3-4 weight portion, Radix Salviae Miltiorrhizae 4-4.5 weight portion, Herba polygoni hydropiperis 2-3 weight portion, the leaves of pulse plants
Fragrant 3-4 weight portion, Radix Euphorbiae Fischerianae (Radix Euphorbiae Ebracteolatae) 3-4 weight portion, Radix Stemonae 6-7.5 weight portion, Artemisia argyi Levl. et Van. var. argyi cv. Qiai 3-4 weight portion is cleaned and is dried, puts into ultra micro together
Pulverizer is crushed to 30 mesh, then adds deionized water and soak 5 hours, amount of water by 7 times of immersions crude drug quality, stir
Dispersion is mixed well, and prepares Traditional Chinese drug mixture, standby；
S7, Traditional Chinese drug mixture step S6 prepared decoct 2 hours in 80 DEG C, collect distillate, and add ether extraction, distillation
Liquid is 2.5:1 with the volume ratio of ether, takes upper oil phase, then adds anhydrous sodium sulfate 0.13-0.2 weight portion and be dried, the most prepared
Volatile oil C, standby；
S8, made to step S5 and S7 volatile oil B and volatile oil C are mixed and mixes well prepared miscella, then be sequentially added into while stirring
Radix Paeoniae Alba quintessence oil, cypress quintessence oil, Herba Saussureae Involueratae quintessence oil, eucalyptus quintessence oil and blue Flos Chrysanthemi quintessence oil, be sufficiently stirred for 45 minutes, stand 30 points
Clock, filtering and impurity removing, obtain essential oil of traditional Chinese medicine, wherein, described miscella and Radix Paeoniae Alba quintessence oil, cypress quintessence oil, Herba Saussureae Involueratae quintessence oil, You Jia
The mass ratio of profit quintessence oil and blue Flos Chrysanthemi quintessence oil is 2:0.6:0.5:0.65:0.5:0.45；
The mixture A that S9, essential oil of traditional Chinese medicine step S8 prepared and step S1 prepare, at 70-80 DEG C, concentrates in blender
Stirring mixing 30 minutes, obtains mixture D；
S10, mixture D step S9 prepared put into ball mill, then add active mineral matter powder, ceria, modification
Aromatic amine curing agent and glass fibre, carry out concentrating at 70-80 DEG C and grind 4.5 hours, filters decontamination, i.e. prepares premix
Material；
S11, the premix material of step S10 being put into twin-screw extrusion equipment, wherein, the rotating speed of twin-screw extrusion equipment is 150-
250 revs/min, extrusion temperature is 260-280 ° of C, extrusion, cooling, and pelletizing i.e. obtains needed for manufacturing described lampshade shell
Composite；
S12, the composite that step S11 is prepared through injection machine heating, extruding, molding, cool down, repair, obtain translucent
Stereoscopic sculpture lamp lampshade.
In a preferred embodiment, essential oil of traditional Chinese medicine in step s 8 also includes the component of following weight portion: surface activity
Agent 3 parts, diethyltoluamide 0.2 part, butyl butyrate 1 part, Eucalyptus oil 1.5 parts, chlorhexidine acetate 0.5 part, fatty alcohol-polyoxyethylene ether sulfur
1 part of sodium of acid and sodium benzoate 0.2 part.
It should be noted that the experiment proved that, active mineral matter powder adds appropriate ceria (CeO2), utilize
The emittance of this rare earth element is high, the feature of half degradation period limit for length, and the anion that active mineral matter powder can be significantly increased produces
Rate, its principle is as follows: the Ce in ceria4+Ce is changed under photoenvironment3+, in conversion process, electron-hole
Recombination probability reduces, then in active mineral matter powder under the effect of the material electric field such as tourmaline, part electronics is passively with electric field side
To displacement, electron-hole recombination probability reduces, thus at tourmaline/CeO2Substantial amounts of electricity has been gathered on composite powder surface
The energy of solution air molecule, and then create the negative aeroion of high concentration, Ce simultaneously3+It is oxidized into again Ce4+, then repeat
Aforesaid conversion process；Meanwhile, through practice detection, interpolation titanium dioxide it is being combined in the active mineral matter powder of proportioning through the present invention
Cerium component, higher more than 10 times than the concentration without the active mineral matter powder anion adding ceria, r ray and natural environment
Identical.
The present invention is based on motherland's traditional medicine, with reference to modern Chinese medicine pharmacological research, from the drug screening of existing Chinese medicine with anti-
Reviewing card, give full play to each component synergism, wherein the effect brief introduction of primary raw material is as follows.
Fructus Carpesii: [mongolian medicine] capsule gives a chapter ancient: fruit is used for ascariasis, enterobiasis, skin infection, and joint wound, " illiteracy plants medicine to scrofula
Will " fruit: bitter, pungent, flat.Eliminating stagnated food and killing intestinal worms
Herba Lycopodii: expelling wind and removing dampness, relaxing muscles and tendons and activating QI and blood in the collateral.For joint aches, joint stuffiness.
Herba Artemisiae Scopariae: have significant hepatic cholagogic effect, improves microcirculation, and has blood pressure lowering, blood fat reducing, anticoagulation, diuresis solution
Heat is relievingd asthma, and drives away ascarid and suppresses the effect of multiple pathogenic dermatophytes and antibacterial.
Lavandula angustifolia can remove ant, except roach, acaricide, the when of being placed under wardrobe, medicated pillow, not only can replace camphor ball, moreover it is possible to stay
The fragrance of one people that oozes lower, research finds, lavandula angustifolia has obvious antibacterial action, and the linalool contained in lavandula angustifolia is lavandula angustifolia
Antibacterial main component, it can suppress 17 kinds of antibacterials (including gram-negative bacteria and gram-positive bacteria), the life of 10 kinds of funguses
Long.
Herba Anemones Hupehensis: 1. " Shaanxi Chinese herbal medicine ": " bitter, cool, slightly poisonous." 2. " Chinese herbal medicine is commonly used in Sichuan ": " and toil, temperature,
Slightly poisonous." removing toxic substances, evacuation of pus granulation promoting, dissipating blood stasis of subsiding a swelling, have and kill maggot, wriggler, change long-pending, detumescence, dissipating blood stasis, control stubborn dermatitis, tinea alba, malaria
Disease, infantile malnutrition, dysentery, carbuncle furuncle swells, scrofula, traumatic injury.
Caulis Polygoni Multiflori: Caulis Polygoni Multiflori is put down nontoxic, sweet and slightly bitter taste, enter the heart, Liver Channel, have effect of tranquilizing and blood nourishing, dispelling wind and removing obstruction in the collateral,
Cure mainly the diseases such as deficiency of YIN insufficiency of blood, restlessness of asrhenia type and insomnia, rheumatic arthralgia, itchy skin eruption.
Origanum majorana: can improve that mood is depressed and addictive disease, especially effective to liberal-mindedness and vigorous endurance stress symptom, can expand blood vessel,
Blood pressure lowering, alleviate and burden, help to eliminate cardiopalmus, have the nerve of excellence to pacify and calm function.
Rhizoma Cimicifugae: have antibacterial action, to being permitted blue achorion, Du big belly microspore tinea bacterium, rust microspore tinea bacterium, redness difficult to understand
Epidermophyton, staphylococcus aureus, anthrax bacillus have stronger inhibitory action；To group B streptococcus, diphtheria corynebacterium, typhoid fever bar
Bacterium, bacillus pyocyaneus, escherichia coli, dysentery bacterium also have inhibitory action in various degree, also have calmness, convulsion work simultaneously
With.
Flos Tagetis Erectae: bitter is cool.Removing toxic substances and promoting subsidence of swelling.For upper respiratory tract infection, pertussis, bronchitis, eye keratitis, pharyngitis,
Stomatitis, toothache；Parotitis, mastitis, ulcerative carbuncle toxic swelling are controlled in external.
Vanilla: have special fragrance, has resisting fatigue and mood is gloomy, help hormone secretion, anxiety of releiving and improvement
The effects such as insomnia.There is heart tonifying, supplementing the brain, stomach invigorating, removing toxic substances, wind dispelling, effect of enhancing muscle strength, make aroma type nervous system emerging
Put forth energy agent and kidney-reinforcing drug, be used for treating hysteria, melancholia, sexual impotence, deficiency-heat and rheumatism.
Herba Portulacae: Portulacaceae annual herb plant.Plump succulence, without hair, high 10-30cm, be born in roadside, field and
The area without shade such as ruins, flower garden.All there is distribution domestic various places.This kind is medicine food dual purpose plant.Herb hyoscine, has clearing away heat-damp and promoting diuresis, solution
Poison detumescence, antiinflammatory, quench the thirst, diuresis.
Radix Salviae Miltiorrhizae: nature and flavor are bitter, are slightly cold.GUIXIN, Liver Channel." the southern regions of the Yunnan Province book on Chinese herbal medicine " is recorded: reinforcing the heart sedate, calming heart and tranquilizing mind.Control forgetful seized with terror
Punching, palpitation with fear is insomnia, and has stasis-dispelling and pain-killing, promoting blood circulation to restore menstrual flow, the effect of the relieving restlessness that clears away heart-fire, and for menoxenia, amenorrhea dysmenorrhea, lump in the abdomen amasss
Poly-, chest and abdomen twinge, pyretic arthralgia pain, skin infection.
Herba polygoni hydropiperis: all have inhibitory action, current clinical medicine research to show in test tube to various dysentery bacteriums, Herba polygoni hydropiperis has
There are the effects such as antibacterial, antiviral, antiinflammatory, antioxidation.
Herba Pogostemonis: acrid in the mouth, slightly warm in nature.Effect: removing dampness for regulating stomach, the effect of administration of inducing sweat, solve, cure mainly dampness taste, breast gastral cavity is vexed swollen,
Appetite is the most fragrant, Nausea and vomiting；Summer, heat-damp in summer was sleepy, uncomfortable in chest did not relaxed, and affection of exogenous wind-cold. the diseases such as aversion to cold is uncomfortable in chest, and have and have relatively
Strong Fungistasis and antibacterial action.
The Radix Euphorbiae Fischerianae (Radix Euphorbiae Ebracteolatae): the another name river Radix Euphorbiae Fischerianae (Radix Euphorbiae Ebracteolatae), continuous poison, Radix Stellerae, chervil, vexed fresh idea, Re Jiaba, Herba Senecionis Dianthui, Radix scopoliae sinensis, perfume,
Medicine sieve foretells, raw pull, flourishing bavin headdress flower, monkey root, Gelsemium elegans Benth., in Chinese medicine with its root eliminate the phlegm, pain relieving, removing food stagnancy, parasite killing.
The Radix Stemonae: can driving away mosquito, resisting pathogenic microbes effect, to beta hemolytic streptococcus, meningococcus, golden yellow
The multiple pathomycetes such as staphylococcus, Staphylococcus albus, Bacillus typhi, pneumobacillus, bacillus pestis, anthrax bacillus have necessarily
Inhibitory action, its infusion all has killing action to mosquitos and flies larva, head louse, clothing louse and Cimex bedbug etc..
Artemisia argyi Levl. et Van. var. argyi cv. Qiai: containing 17 kinds of known compounds, has and relievings asthma, antitussive, eliminates the phlegm and clear scorching effect, reasonable QI and blood, by cold-damp, tune
Through effects such as antiabortive, warming the meridian for stopping bleeding, clearing and antitussive expectorants.Cure mainly cold type of pain in menoxenia, abdomen, vaginal bleeding during pregnancy hematochezia, frequent fetal movement, palace
Cold infertile disease such as grade.
It should be noted that be proven, after carrying out the Radix Salviae Miltiorrhizae of certain part by weight, Herba polygoni hydropiperis and the Radix Stemonae compounding, no
Only it is remarkably improved degerming antibacterial ability, also can produce a kind of delicate fragrance taste having no side effect, refreshing, have certain
Effect of refreshing oneself；, it is proven, by the Fructus Carpesii of certain part by weight, Herba Artemisiae Scopariae, lavandula angustifolia, Folium cinnamomi camphorae, the Radix Euphorbiae Fischerianae (Radix Euphorbiae Ebracteolatae) with break bowl meanwhile
After flower carries out compounding, the mosquito dispersing ability of said composition is made to be significantly improved；It addition, Rhizoma Cimicifugae, Flos Tagetis Erectae, Herba Portulacae and beg
After the components such as Chinese mugwort carry out compatibility, substantially increase the antibacterial degerming ability of compositions, through practice detection, the compositions pair after compounding
Staphylococcus aureus, anthrax bacillus, hemophilus influenza, micrococcus catarrhalis, streptococcus pneumoniae, escherichia coli, group B streptococcus, diphtheria bar
Bacterium, Bacillus typhi, green pus liver bacterium, dysentery bacteriums etc. more than 30 are planted pathogenic bacteria and have certain suppression and killing action.
The effect of the present invention:
The present invention uses Chinese medicinal ingredients to compound with active mineral matter, makes the present invention be possible not only to expelling mosquito, it is also possible to release is negative
Ion, fresh air, simultaneously fragrant odour, there is effect of body-building, anophelifuge, sterilization, in actual applications, also have certain
Remove effect of the finishing pollution things such as formaldehyde, toluene, TVOC, there is the effect achieved many things at one stroke, enrich the use of conventional lamp
Function.
Accompanying drawing explanation
Fig. 1 is overall schematic of the present invention.
Detailed description of the invention
Embodiment 1:
Referring to Fig. 1, a kind of stereoscopic sculpture LED decorative lamp, including translucent stereoscopic sculpture lamp lampshade 1, LED illumination group
Part (not shown), base 2 and be placed in the power source drive device in described base 2, described lamp lampshade 1 has a use
In the hollow cavity of the described LED illumination assembly of arrangement, the sidewall at described hollow cavity is provided with some louvres, in described hollow
The side wall inner surfaces of cavity is coated with heat radiation coating, and wherein, described translucent stereoscopic sculpture lamp lampshade 1 is pressed by following component
It is prepared from according to parts by weight:
Resin 50 weight portion；Glass fibre 20 weight portion；Fire retardant 5 weight portion；Graphene 4.5 weight portion；Modified aromatic amine is solid
Agent 3 weight portion；Fluorescent material 0.3 weight portion；Good solid 754 light trigger 2 weight portions of vapour Ba Yan；Polyetheramine catalyst 0.7 weight
Part；Ceria 0.1 weight portion；Active mineral matter powder 1 weight portion；Essential oil of traditional Chinese medicine 1 weight portion；Wherein, described resin is epoxy
Soybean oil acrylate and the mixture of bisphenol A-type E51 epoxy resin, described epoxy soybean oil acrylate and bisphenol A-type E51
The mass ratio of epoxy resin is 3:2, and described fire retardant is the mixture of APP, tripolycyanamide and expanded graphites, institute
Stating the mass ratio 2:1.5:1.3 of APP, tripolycyanamide and expanded graphites, described fluorescent material is Ce and YAG fluorescence
Powder mixture, particle diameter≤13 μm of described fluorescent material, described active mineral matter powder be germanite, fluorite, tourmaline, hexacyclic ring stone by
The mixture of weight ratio 2.5:3:3.7:2, wherein tourmaline is dravite and the mixture of elbaite 5:3 by weight,
Particle diameter≤13 μm of described active mineral matter powder, described translucent stereoscopic sculpture lamp lampshade be made by the steps and
Become:
S1, the resin by required parts by weight, fire retardant, Graphene, fluorescent material, vapour Ba Yan are good to be consolidated 754 light triggers and gathers
Ether amines catalyst is placed in blender, mixes well in the stirring of 70 DEG C of next part high speeds, and mixing time is 30 minutes, to be mixed uniformly after
Take out from blender, i.e. prepare mixture A, standby；
S2, by material Fructus Carpesii 60 weight portion, Herba Lycopodii 3 weight portion, Herba Artemisiae Scopariae 25 weight portion, lavandula angustifolia 15 weight portion, Hubei anemone
Spend 5 weight portions, Caulis Polygoni Multiflori 3 weight portion, Origanum majorana 2.5 weight portion, Rhizoma Cimicifugae 1 weight portion, Flos Tagetis Erectae 5 weight portion, Folium cinnamomi camphorae 6 weight
Amount part decontamination, is placed in the vacuum still 2 hours of-20 DEG C together, is placed in microwave dryer the most again and carries out pretreatment, be wherein dried
Time is 40 minutes, and microwave power is 17kw；
S3, step S2 is processed after material put into together in super micron mill and be crushed to 60 mesh, prepare crude drug powder, standby
With；
S4, by step S3 prepare crude drug powder put into supercritical carbon dioxide extraction apparatus extraction kettle in, regulation extraction
Pressure power 27.65MPa, extraction temperature 45 DEG C, carbon dioxide flow is 1100L/h, and dynamic extraction 2 hours, directly at separating still
Outlet triangular flask collects crude oil, standby；
S5, the crude oil prepared in step S4 is placed in 5 DEG C of environment freezing 70 minutes, then the crude oil after freezing is placed in rotating speed is
The High speed refrigerated centrifuge of 17000r/min is centrifuged 25 minutes, goes the removal of impurity to be placed on 85 DEG C of vacuum tank evacuation 3 hours, i.e.
Prepare volatile oil B, standby；
S6, by vanilla 2 weight portion, Herba Portulacae 3 weight portion, Radix Salviae Miltiorrhizae 4.5 weight portion, Herba polygoni hydropiperis 2 weight portion, Herba Pogostemonis 4 weight portion,
The Radix Euphorbiae Fischerianae (Radix Euphorbiae Ebracteolatae) 3 weight portion, the Radix Stemonae 7.5 weight portion, Artemisia argyi Levl. et Van. var. argyi cv. Qiai 3 weight portion is cleaned and is dried, and puts in super micron mill together and is crushed to 30 mesh,
Then add deionized water to soak 5 hours, amount of water by 7 times of immersions crude drug quality, dispersed with stirring is mixed well, and prepares Chinese medicine mixed
Compound, standby；
S7, Traditional Chinese drug mixture step S6 prepared decoct 2 hours in 80 DEG C, collect distillate, and add ether extraction, distillation
Liquid is 2.5:1 with the volume ratio of ether, takes upper oil phase, then adds anhydrous sodium sulfate 0.13 weight portion and be dried, and i.e. prepares volatilization
Oil C, standby；
S8, made to step S5 and S7 volatile oil B and volatile oil C are mixed and mixes well prepared miscella, then be sequentially added into while stirring
Radix Paeoniae Alba quintessence oil, cypress quintessence oil, Herba Saussureae Involueratae quintessence oil, eucalyptus quintessence oil and blue Flos Chrysanthemi quintessence oil, be sufficiently stirred for 45 minutes, stand 30 points
Clock, filtering and impurity removing, obtain essential oil of traditional Chinese medicine, wherein, described miscella and Radix Paeoniae Alba quintessence oil, cypress quintessence oil, Herba Saussureae Involueratae quintessence oil, You Jia
The mass ratio of profit quintessence oil and blue Flos Chrysanthemi quintessence oil is 2:0.6:0.5:0.65:0.5:0.45；
The mixture A that S9, essential oil of traditional Chinese medicine step S8 prepared and step S1 prepare, at 80 DEG C, concentrates in blender and stirs
Mix mixing 30 minutes, obtain mixture D；
S10, mixture D step S9 prepared put into ball mill, then add active mineral matter powder, ceria, modification
Aromatic amine curing agent and glass fibre, carry out concentrating at 70 DEG C and grind 4.5 hours, filter decontamination, i.e. prepare premix material；
S11, the premix material of step S10 being put into twin-screw extrusion equipment, wherein, the rotating speed of twin-screw extrusion equipment is 250
Rev/min, extrusion temperature is 260 ° of C, extrusion, cooling, and pelletizing i.e. obtains for manufacturing the composite wood needed for described lampshade shell
Material；
S12, the composite that step S11 is prepared through injection machine heating, extruding, molding, cool down, repair, obtain translucent
Stereoscopic sculpture lamp lampshade.
It should be noted that the experiment proved that, active mineral matter powder adds appropriate ceria (CeO2), utilize
The emittance of this rare earth element is high, the feature of half degradation period limit for length, and the anion that active mineral matter powder can be significantly increased produces
Rate, its principle is as follows: the Ce in ceria4+Ce is changed under photoenvironment3+, in conversion process, electron-hole is multiple
Conjunction probability reduces, then under tourmaline electric field action, part electronics is passively with direction of an electric field displacement, and electron-hole is combined
Probability reduces, thus at tourmaline/CeO2The energy of substantial amounts of electrolysis air molecule has been gathered on composite powder surface, thus produces
The negative aeroion of high concentration, simultaneously Ce are given birth to3+It is oxidized into again Ce4+, then repeat aforesaid conversion process；Meanwhile, through reality
Trampling detection, the active mineral matter powder being combined proportioning through the present invention is higher 10 times than the tourmaline powder negative ion concentration without proportioning
Above, r ray is identical with natural environment.
As preferably, described bisphenol A-type E51 epoxy resin uses the standard bisphenol A-type E51 ring of Yueyang Ba Ling petrochemical iy produced
Epoxy resins；Described epoxy soybean oil acrylate uses the epoxy soybean oil acrylic acid that Zhong Shan Yongfeng Chemical Co., Ltd. produces
Ester；Described APP uses the APP that Yunnan Tian Yao Chemical Co., Ltd. produces；Described expanded graphites uses Qingdao
The expanded graphites that Chen Yang graphite company limited produces.
In a preferred embodiment, essential oil of traditional Chinese medicine in step s 8 also includes the component of following weight portion: surface activity
Agent 3 parts, diethyltoluamide 0.2 part, butyl butyrate 1 part, Eucalyptus oil 1.5 parts, chlorhexidine acetate 0.5 part, fatty alcohol-polyoxyethylene ether sulfur
1 part of sodium of acid and sodium benzoate 0.2 part.
Further, in a preferred embodiment, described heat radiation coating is prepared from according to parts by weight by following component:
Hybrid resin 65 weight portion, sodium-based montmorillonite 3.5 weight portion, carboxylic styrene butadiene latex 4 weight portion, silicones methyl branch silicon
Oil 1.5 weight portions, Polyethylene Glycol 1 weight portion, pentane 0.9 weight portion, nano silicon 1.5 weight portion, polyacrylonitrile-radical
Carbon fiber 7.5 weight portion, Graphene 5 weight portion, aerosil 1.5 weight portion, fire retardant 6 weight portion, modified aromatic amine
Firming agent 4.5 weight portion, solvent 18 weight portion, ceria 0.12 weight portion, active mineral matter powder 1.5 weight portion, middle YAOJING
Oil 2 weight portions；Wherein, described hybrid resin is the mixture of phenolic resin and epoxy resin, phenolic resin and epoxy resin
Mass ratio is 4:3；The a length of 0.01mm of described polyacrylonitrile-based carbon fibre；Described fire retardant is ammonium polyphosphate, tripolycyanamide
And the mixture of expanded graphites, the mass ratio 3:1.6 of described ammonium polyphosphate, tripolycyanamide and expanded graphites:
1.5；Described solvent is the mixture of DAA and butyl ester, and the mass ratio of described DAA and butyl ester is 3:2；Described
Active mineral matter powder is the mixture of germanite, fluorite, tourmaline, hexacyclic ring stone 2:2:3:1.5 by weight, and wherein tourmaline is magnesium
The mixture of tourmaline and elbaite 3:2 by weight, particle diameter≤15 μm of described active mineral matter powder, described heat radiation coating
It is made by the steps and forms:
S1, weigh hybrid resin, sodium-based montmorillonite, carboxylic styrene butadiene latex, silicones metlyl branching silicone oil, poly-second two by weight
Alcohol, pentane, nano silicon, polyacrylonitrile-based carbon fibre, Graphene, aerosil, fire retardant and solvent are put
In blender, mixing well in the stirring of 80 DEG C of next part high speeds, mixing time is 40 minutes, to be mixed uniformly after take from blender
Go out, i.e. prepare resin compound, standby；
S2, by material fly expelling plum 20 weight portion, Folium Perillae 10 weight portion, Caulis Vernoniae andersonii 7 weight portion, Herba Anemones Hupehensis 3.5 weight
Amount part, Radix Scutellariae 2 weight portion, Origanum majorana 1.5 weight portion, Ambra Grisea 1 weight portion and Moschus 0.7 weight portion, decontamination, together
Putting in super micron mill and be crushed to 100 mesh, then add deionized water and soak 5 hours, amount of water is by being soaked crude drug quality
7 times, dispersed with stirring is mixed well, prepare Traditional Chinese drug mixture, standby；
S3, Traditional Chinese drug mixture step S2 prepared decoct 2 hours in 80 DEG C, collect distillate, and add ether extraction, distillation
Liquid is 3:2 with the volume ratio of ether, takes upper oil phase, then adds anhydrous sodium sulfate 0.13 weight portion and be dried, YAOJING in i.e. preparing
Oil, standby；
The resin compound that S4, essential oil of traditional Chinese medicine step S3 prepared prepare with step S1, at 80 DEG C, concentrates in blender
Stirring mixing 15 minutes, obtains premix material, the most again this premix material is put into ball mill, adds active mineral matter powder, titanium dioxide
Cerium and curing agent, at 85 DEG C, concentrate and grind 5 hours, filter decontamination, i.e. obtain heat radiation coating.
Embodiment 2:
A kind of stereoscopic sculpture LED decorative lamp, a kind of stereoscopic sculpture LED decorative lamp, including translucent stereoscopic sculpture light fixture
Cover body 1, LED illumination assembly (not shown), base 2 and be placed in the power source drive device in described base 2, described lamp
Tool cover body 1 has one for disposing the hollow cavity of described LED illumination assembly, and the sidewall at described hollow cavity is provided with some dissipating
Hot hole, the side wall inner surfaces at described hollow cavity is coated with heat radiation coating, wherein, described translucent stereoscopic sculpture light fixture cover
Body 1 is prepared from according to parts by weight by following component:
Resin 65 weight portion；Glass fibre 15 weight portion；Fire retardant 6 weight portion；Graphene 4 weight portion；Modified aromatic amine solidifies
Agent 3.5 weight portion；Fluorescent material 0.2 weight portion；Good solid 754 light trigger 3 weight portions of vapour Ba Yan；Polyetheramine catalyst 0.6 weight
Part；Ceria 0.15 weight portion；Active mineral matter powder 0.8 weight portion；Essential oil of traditional Chinese medicine 1.2 weight portion；Wherein, described resin is
Epoxy soybean oil acrylate and the mixture of bisphenol A-type E51 epoxy resin, described epoxy soybean oil acrylate and bisphenol-A
The mass ratio of type E51 epoxy resin is 2:1, and described fire retardant is the mixing of APP, tripolycyanamide and expanded graphites
Thing, the mass ratio 2:1.5:1.3 of described APP, tripolycyanamide and expanded graphites, described fluorescent material is Ce and YAG
Phosphor mixture, particle diameter≤13 μm of described fluorescent material, described active mineral matter powder is germanite, fluorite, tourmaline, six rings
Stone is by weight the mixture of 2.5:3:3.7:2, and wherein tourmaline is dravite and the mixing of elbaite 5:3 by weight
Thing, particle diameter≤13 μm of described active mineral matter powder, described translucent stereoscopic sculpture lamp lampshade is made by the steps
Form:
S1, the resin by required parts by weight, fire retardant, Graphene, fluorescent material, vapour Ba Yan are good to be consolidated 754 light triggers and gathers
Ether amines catalyst is placed in blender, mixes well in the stirring of 75 DEG C of next part high speeds, and mixing time is 20 minutes, to be mixed uniformly after
Take out from blender, i.e. prepare mixture A, standby；
S2, by material Fructus Carpesii 50 weight portion, Herba Lycopodii 5 weight portion, Herba Artemisiae Scopariae 20 weight portion, lavandula angustifolia 20 weight portion, Hubei anemone
Spend 3 weight portions, Caulis Polygoni Multiflori 5 weight portion, Origanum majorana 1.5 weight portion, Rhizoma Cimicifugae 3 weight portion, Flos Tagetis Erectae 3 weight portion, Folium cinnamomi camphorae 8 weight
Amount part decontamination, is placed in the vacuum still 2.5 hours of-20 DEG C together, is placed in microwave dryer the most again and carries out pretreatment, Qi Zhonggan
The dry time is 35 minutes, and microwave power is 17kw；
S3, step S2 is processed after material put into together in super micron mill and be crushed to 60 mesh, prepare crude drug powder, standby
With；
S4, by step S3 prepare crude drug powder put into supercritical carbon dioxide extraction apparatus extraction kettle in, regulation extraction
Pressure power 27.65MPa, extraction temperature 45 DEG C, carbon dioxide flow is 1100L/h, and dynamic extraction 2 hours, directly at separating still
Outlet triangular flask collects crude oil, standby；
S5, the crude oil prepared in step S4 is placed in 5 DEG C of environment freezing 70 minutes, then the crude oil after freezing is placed in rotating speed is
The High speed refrigerated centrifuge of 17000r/min is centrifuged 25 minutes, goes the removal of impurity to be placed on 85 DEG C of vacuum tank evacuation 3 hours, i.e.
Prepare volatile oil B, standby；
S6, by vanilla 1.5 weight portion, Herba Portulacae 4 weight portion, Radix Salviae Miltiorrhizae 4 weight portion, Herba polygoni hydropiperis 3 weight portion, Herba Pogostemonis 3 weight portion,
The Radix Euphorbiae Fischerianae (Radix Euphorbiae Ebracteolatae) 4 weight portion, the Radix Stemonae 6 weight portion, Artemisia argyi Levl. et Van. var. argyi cv. Qiai 4 weight portion is cleaned and is dried, and puts in super micron mill together and is crushed to 30 mesh, so
After add deionized water and soak 5 hours, amount of water by 7 times of immersions crude drug quality, dispersed with stirring is mixed well, and prepares Chinese medicine and mixes
Thing, standby；
S7, Traditional Chinese drug mixture step S6 prepared decoct 2 hours in 80 DEG C, collect distillate, and add ether extraction, distillation
Liquid is 2.5:1 with the volume ratio of ether, takes upper oil phase, then adds anhydrous sodium sulfate 0.15 weight portion and be dried, and i.e. prepares volatilization
Oil C, standby；
S8, made to step S5 and S7 volatile oil B and volatile oil C are mixed and mixes well prepared miscella, then be sequentially added into while stirring
Radix Paeoniae Alba quintessence oil, cypress quintessence oil, Herba Saussureae Involueratae quintessence oil, eucalyptus quintessence oil and blue Flos Chrysanthemi quintessence oil, be sufficiently stirred for 45 minutes, stand 30 points
Clock, filtering and impurity removing, obtain essential oil of traditional Chinese medicine, wherein, described miscella and Radix Paeoniae Alba quintessence oil, cypress quintessence oil, Herba Saussureae Involueratae quintessence oil, You Jia
The mass ratio of profit quintessence oil and blue Flos Chrysanthemi quintessence oil is 2:0.6:0.5:0.65:0.5:0.45；
The mixture A that S9, essential oil of traditional Chinese medicine step S8 prepared and step S1 prepare, at 75 DEG C, concentrates in blender and stirs
Mix mixing 30 minutes, obtain mixture D；
S10, mixture D step S9 prepared put into ball mill, then add active mineral matter powder, ceria, modification
Aromatic amine curing agent and glass fibre, carry out concentrating at 75 DEG C and grind 4.5 hours, filter decontamination, i.e. prepare premix material；
S11, the premix material of step S10 being put into twin-screw extrusion equipment, wherein, the rotating speed of twin-screw extrusion equipment is 200
Rev/min, extrusion temperature is 270 ° of C, extrusion, cooling, and pelletizing i.e. obtains for manufacturing the composite wood needed for described lampshade shell
Material；
S12, the composite that step S11 is prepared through injection machine heating, extruding, molding, cool down, repair, obtain translucent
Stereoscopic sculpture lamp lampshade.
Remaining is with embodiment 1.
The test index of Example 1 and Example 2 of the present invention is as follows:
(1) abnormal smells from the patient inspection: sense organ, nonirritant abnormal flavour.
(2) repelling effect test.
Contrast test is carried out according to the repelling effect of ordinary lamp and lantern of the prior art with above-described embodiment 1 and embodiment 2,
Test data ask for an interview table 1.
Conclusion: Example 1 and Example 2 of the present invention, compared with ordinary lamp and lantern on market, is respectively provided with certain anophelifuge and makees
With.
(3) anionic textiles.
Use anion test instrument, be primarily directed to timber, Ore, ceramic material, negative ion powder are made to relevant
The anion quantity that commodity (such as anion medicated clothing, necklace, woollen blanket) etc. are discharged makes measurement.
Test result is shown in Table 2.
Conclusion: the embodiment of the present invention 1, embodiment 2 can be with sustained release negative aeroions, with ordinary lamps of the prior art
Tool compares, and the present invention has obviously advantage.
Claims (2)
1. a stereoscopic sculpture LED decorative lamp, it is characterised in that: include translucent stereoscopic sculpture lamp lampshade (1), LED
Light fixture, base (2) and be placed in the power source drive device in described base (2), described lamp lampshade (1) has a use
In the hollow cavity of the described LED illumination assembly of arrangement, the sidewall at described hollow cavity is provided with some louvres, in described hollow
The side wall inner surfaces of cavity is coated with heat radiation coating, and wherein, described translucent stereoscopic sculpture lamp lampshade (1) is by following component
It is prepared from according to parts by weight:
Resin 50-65 weight portion；Glass fibre 10-20 weight portion；Fire retardant 5-8 weight portion；Graphene 3-4.5 weight portion；Change
Property aromatic amine curing agent 3-4 weight portion；Fluorescent material 0.1-0.3 weight portion；The good solid 754 light trigger 2-4 weight portions of vapour Ba Yan；Poly-
Ether amines catalyst 0.5-0.7 weight portion；Ceria 0.1-0.15 weight portion；Active mineral matter powder 0.7-1 weight portion；Middle YAOJING
Oil 1-1.2 weight portion；Wherein, described resin is epoxy soybean oil acrylate and the mixture of bisphenol A-type E51 epoxy resin,
The mass ratio of described epoxy soybean oil acrylate and bisphenol A-type E51 epoxy resin is 2:1-3:2, and described fire retardant is poly-phosphorus
Acid ammonium, tripolycyanamide and the mixture of expanded graphites, the quality of described APP, tripolycyanamide and expanded graphites
Ratio 2:1.5:1.3, described fluorescent material is Ce and YAG fluorescent powder mixture, particle diameter≤13 μm of described fluorescent material, described work
Property mineral powder be germanite, fluorite, tourmaline, hexacyclic ring stone by weight the mixture of 2.5:3:3.7:2, wherein tourmaline is magnesium
The mixture of tourmaline and elbaite 5:3 by weight, particle diameter≤13 μm of described active mineral matter powder, described translucent
Stereoscopic sculpture lamp lampshade is made by the steps and forms:
S1, the resin by required parts by weight, fire retardant, Graphene, fluorescent material, vapour Ba Yan are good to be consolidated 754 light triggers and gathers
Ether amines catalyst is placed in blender, mixes well 70-80 DEG C of next part high speed stirring, and mixing time is 15-30 minute, to be mixed
Take out from blender after Jun Yun, i.e. prepare mixture A, standby；
S2, by material Fructus Carpesii 50-60 weight portion, Herba Lycopodii 3-5 weight portion, Herba Artemisiae Scopariae 20-25 weight portion, lavandula angustifolia 15-20 weight
Part, Herba Anemones Hupehensis 3-5 weight portion, Caulis Polygoni Multiflori 3-5 weight portion, Origanum majorana 1.5-2.5 weight portion, Rhizoma Cimicifugae 1-3 weight portion, ten thousand
Longevity chrysanthemum 3-5 weight portion, Folium cinnamomi camphorae 6-8 weight portion decontamination, it is placed in vacuum still 2-3 hour of-20 DEG C together, is placed in micro-the most again
Ripple drying machine carries out pretreatment, and wherein drying time is 30-40 minute, and microwave power is 17kw；
S3, step S2 is processed after material put into together in super micron mill and be crushed to 60 mesh, prepare crude drug powder, standby
With；
S4, by step S3 prepare crude drug powder put into supercritical carbon dioxide extraction apparatus extraction kettle in, regulation extraction
Pressure power 27.65MPa, extraction temperature 45 DEG C, carbon dioxide flow is 1100L/h, and dynamic extraction 2 hours, directly at separating still
Outlet triangular flask collects crude oil, standby；
S5, the crude oil prepared in step S4 is placed in 5 DEG C of environment freezing 70 minutes, then the crude oil after freezing is placed in rotating speed is
The High speed refrigerated centrifuge of 17000r/min is centrifuged 25 minutes, goes the removal of impurity to be placed on 85 DEG C of vacuum tank evacuation 3 hours, i.e.
Prepare volatile oil B, standby；
S6, by vanilla 1.5-2 weight portion, Herba Portulacae 3-4 weight portion, Radix Salviae Miltiorrhizae 4-4.5 weight portion, Herba polygoni hydropiperis 2-3 weight portion, the leaves of pulse plants
Fragrant 3-4 weight portion, Radix Euphorbiae Fischerianae (Radix Euphorbiae Ebracteolatae) 3-4 weight portion, Radix Stemonae 6-7.5 weight portion, Artemisia argyi Levl. et Van. var. argyi cv. Qiai 3-4 weight portion is cleaned and is dried, puts into ultra micro together
Pulverizer is crushed to 30 mesh, then adds deionized water and soak 5 hours, amount of water by 7 times of immersions crude drug quality, stir
Dispersion is mixed well, and prepares Traditional Chinese drug mixture, standby；
S7, Traditional Chinese drug mixture step S6 prepared decoct 2 hours in 80 DEG C, collect distillate, and add ether extraction, distillation
Liquid is 2.5:1 with the volume ratio of ether, takes upper oil phase, then adds anhydrous sodium sulfate 0.13-0.3 weight portion and be dried, the most prepared
Volatile oil C, standby；
S8, made to step S5 and S7 volatile oil B and volatile oil C are mixed and mixes well prepared miscella, then be sequentially added into while stirring
Radix Paeoniae Alba quintessence oil, cypress quintessence oil, Herba Saussureae Involueratae quintessence oil, eucalyptus quintessence oil and blue Flos Chrysanthemi quintessence oil, be sufficiently stirred for 45 minutes, stand 30 points
Clock, filtering and impurity removing, obtain essential oil of traditional Chinese medicine, wherein, described miscella and Radix Paeoniae Alba quintessence oil, cypress quintessence oil, Herba Saussureae Involueratae quintessence oil, You Jia
The mass ratio of profit quintessence oil and blue Flos Chrysanthemi quintessence oil is 2:0.6:0.5:0.65:0.5:0.45；
The mixture A that S9, essential oil of traditional Chinese medicine step S8 prepared and step S1 prepare, at 70-80 DEG C, concentrates in blender
Stirring mixing 30 minutes, obtains mixture D；
S10, mixture D step S9 prepared put into ball mill, then add active mineral matter powder, ceria, modification
Aromatic amine curing agent and glass fibre, carry out concentrating at 70-80 DEG C and grind 4.5 hours, filters decontamination, i.e. prepares premix
Material；
S11, the premix material of step S10 being put into twin-screw extrusion equipment, wherein, the rotating speed of twin-screw extrusion equipment is 150-
250 revs/min, extrusion temperature is 260-280 ° of C, extrusion, cooling, and pelletizing obtains composite；
S12, the composite that step S11 is prepared through injection machine heating, extruding, molding, cool down, repair, obtain translucent
Stereoscopic sculpture lamp lampshade.
A kind of stereoscopic sculpture LED decorative lamp the most according to claim 1, it is characterised in that: Chinese medicine in step s 8
Quintessence oil also includes the component of following weight portion: 3 parts of surfactant, diethyltoluamide 0.2 part, butyl butyrate 1 part, Eucalyptus oil 1.5 parts,
Chlorhexidine acetate 0.5 part, polyoxyethylenated alcohol sodium sulfate 1 part and sodium benzoate 0.2 part.