CN106010760A - Mortar additive for solar slicing as well as preparation method and use method thereof - Google Patents
Mortar additive for solar slicing as well as preparation method and use method thereof Download PDFInfo
- Publication number
- CN106010760A CN106010760A CN201610333225.8A CN201610333225A CN106010760A CN 106010760 A CN106010760 A CN 106010760A CN 201610333225 A CN201610333225 A CN 201610333225A CN 106010760 A CN106010760 A CN 106010760A
- Authority
- CN
- China
- Prior art keywords
- parts
- solar energy
- grout additive
- mortar
- energy section
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a mortar additive for solar slicing as well as a preparation method and a use method thereof. The mortar additive for solar slicing is prepared from the following components in percentage by mass: 1-20 parts of a surfactant, 10-20 parts of a cleaning agent, 1-2 parts of a chelating agent and 10-80 parts of a solvent. The mortar additive can improve the dispersion effect of mortar when used in the mortar, thereby achieving the purpose of reducing agglomeration deposition of the mortar.
Description
Technical field
The present invention relates to a kind of grout additive for solar energy section and preparation method thereof and using method, belong to multi-wire saw technical field.
Background technology
At present, in multi-wire saw industry, the tough material carborundum in cutting adjuvant mortar is attached on the steel wire of high speed rotating the cut product of quickly friction, in the case of multi-wire saw working bench produces normal pressure simultaneously, constantly move with steel wire, roll cavitation, make cut product separately.The Main Function of cutting fluid is cooling, lubrication, suspended dispersed;The Main Function of carborundum is cutting;The Main Function of steel wire is that the mortar that cutting fluid and carborundum blend together by a certain percentage is brought into cutting zone.Mortar is the core of section, and the quality of mortar quality directly determines the quality of chipping qualities;For the carborundum in mortar and cutting fluid, a lot of analysis is had been made in industry and has formulated perfect Con trolling index the most accordingly, but belong to blank for the unite research of deposition of mortar;
Most multi-wire saw enterprises, all can encounter mortar and unite deposition to high-temperature high humidity season, and mortar deposition of uniting shows as mortar poor fluidity, causes multi-line cutting machine filter bag to block in cutting process, and mortar pump cannot be cut by the enough mortar amounts of technique extraction;After having cut, mortar is piled up being cut product surface, poor fluidity, easily causes product and there is edge and collapse limit, part, unfilled corner and cannot clean up and cause dirty.
Summary of the invention
The technical problem to be solved is the defect overcoming prior art, it is provided that a kind of grout additive for solar energy section, and it uses can improve the dispersion effect of mortar in mortar, thus reduces mortar and unite the purpose of deposition.
In order to solve above-mentioned technical problem, the technical scheme is that a kind of grout additive for solar energy section, component and the mass percent of each component that it contains are as follows:
1 part ~ 20 parts of surfactant;
Abluent: 10 parts ~ 20 parts;
Chelating agen: 1 part ~ 2 parts;
Solvent: 10 parts ~ 80 parts.
Further, described surfactant is organic higher polycarboxylic acid ammonium salt.
Further, described abluent is metasilicate pentahydrate sodium.
Further, described chelating agen is hydroxyethylethylene diamine tri-acetic acid.
Further, described solvent is deionized water.
Present invention also offers the preparation method of a kind of grout additive for solar energy section, the step of the method contain:
A () joins after each component being got the raw materials ready according to each constituent mass percentage ratio and is sufficiently stirred in agitator tank, obtain preform;
The performance indications of (b) detection preform, and select the finished product use that performance indications are qualified.
Further, in described step (a), agitator tank is sufficiently stirred for 0.5 ~ 10 hour.
Further, in described step (b), performance indications include density and/or viscosity and/or electrical conductivity and/or pH value.
Present invention also offers the using method of a kind of grout additive for solar energy section, the step of the method contain:
Use after grout additive and mortar are thoroughly mixed;Wherein, the part by weight of grout additive and mortar is 1:100 ~ 1:10.
Further, the time of stirring mixing is 10 ~ 30 minutes.
After have employed technique scheme, the present invention unites angle of deposit from improving mortar, the method using chemical addition agent, changes mortar and unites the current potential of deposited material so that it is by current potential repelling attack, improves the dispersive property of mortar.Eliminate in cutting process simultaneously and produce the by-products such as metal ion, thus the dispersion effect improving mortar reduces mortar and unites the purpose of deposition.
The method have the advantages that
1, every cutter only needs to add a small amount of additive, the problem that can improve mortar deposition, easy to use, low cost;
2, avoid multi-line cutting machine to block up filter bag and mortar extraction amount deficiency is shut down, cause product and capacity loss;
3, can be effectively improved finished product rate, that reduces product collapses the defective products ratios such as limit, unfilled corner and dirty.
Detailed description of the invention
Being clearly understood to make present disclosure be easier to, below according to specific embodiment, the present invention is further detailed explanation.
Embodiment one
A kind of grout additive for solar energy section, component and the mass percent of each component that it contains are as follows:
20 parts of surfactant;
Abluent: 20 parts;
Chelating agen: 2 parts;
Solvent: 50 parts.
Described surfactant can be organic higher polycarboxylic acid ammonium salt.
Described abluent can be metasilicate pentahydrate sodium.
Described chelating agen can be hydroxyethylethylene diamine tri-acetic acid.
Described solvent can be deionized water, and the particular type of above component is not limited to this.
The step of this preparation method being used for the grout additive that solar energy is cut into slices contains:
A () joins after each component being got the raw materials ready according to each constituent mass percentage ratio and is sufficiently stirred in agitator tank, obtain preform;
The performance indications of (b) detection preform, and select the finished product use that performance indications are qualified, can finished product to container use.
In described step (a), in agitator tank, under room temperature, under the mechanism of blender strength, different classes of component is sufficiently stirred for about 9 hours.
In described step (b), performance indications include density and/or viscosity and/or electrical conductivity and/or pH value.
The step of this using method being used for the grout additive that solar energy is cut into slices contains:
Use after grout additive and mortar are thoroughly mixed;Wherein, the part by weight of grout additive and mortar is 1:10;Measuring of grout additive can use the measurers such as measuring cup;After multi-line cutting machine has been got the raw materials ready, being poured slowly into a mixing bowl, be sufficiently mixed uniformly, incorporation time is about 25 minutes, has mixed rear multi-line cutting machine and can boot up cutting.
Embodiment two
A kind of grout additive for solar energy section, component and the mass percent of each component that it contains are as follows:
1 part of surfactant;
Abluent: 10 parts;
Chelating agen: 1 part;
Solvent: 80 parts.
Described surfactant can be organic higher polycarboxylic acid ammonium salt.
Described abluent can be metasilicate pentahydrate sodium.
Described chelating agen can be hydroxyethylethylene diamine tri-acetic acid.
Described solvent can be deionized water.
The step of this preparation method being used for the grout additive that solar energy is cut into slices contains:
A () joins after each component being got the raw materials ready according to each constituent mass percentage ratio and is sufficiently stirred in agitator tank, obtain preform;
The performance indications of (b) detection preform, and select the finished product use that performance indications are qualified, can finished product to container use.
In described step (a), in agitator tank, under room temperature, under the mechanism of blender strength, different classes of component is sufficiently stirred for about 1 hour.
In described step (b), performance indications include density and/or viscosity and/or electrical conductivity and/or pH value.
The step of this using method being used for the grout additive that solar energy is cut into slices contains:
Use after grout additive and mortar are thoroughly mixed;Wherein, the part by weight of grout additive and mortar is 1:100;Measuring of grout additive can use the measurers such as measuring cup;After multi-line cutting machine has been got the raw materials ready, being poured slowly into a mixing bowl, be sufficiently mixed uniformly, incorporation time is about 15 minutes, has mixed rear multi-line cutting machine and can boot up cutting.
Embodiment three
A kind of grout additive for solar energy section, component and the mass percent of each component that it contains are as follows:
10 parts of surfactant;
Abluent: 15 parts;
Chelating agen: 1 part;
Solvent: 70 parts.
Described surfactant can be organic higher polycarboxylic acid ammonium salt.
Described abluent can be metasilicate pentahydrate sodium.
Described chelating agen can be hydroxyethylethylene diamine tri-acetic acid.
Described solvent can be deionized water.
The step of this preparation method being used for the grout additive that solar energy is cut into slices contains:
A () joins after each component being got the raw materials ready according to each constituent mass percentage ratio and is sufficiently stirred in agitator tank, obtain preform;
The performance indications of (b) detection preform, and select the finished product use that performance indications are qualified, can finished product to container use.
In described step (a), in agitator tank, under room temperature, under the mechanism of blender strength, different classes of component is sufficiently stirred for about 5 hours.
In described step (b), performance indications include density and/or viscosity and/or electrical conductivity and/or pH value.
The step of this using method being used for the grout additive that solar energy is cut into slices contains:
Use after grout additive and mortar are thoroughly mixed;Wherein, the part by weight of grout additive and mortar is 1:55;Measuring of grout additive can use the measurers such as measuring cup;After multi-line cutting machine has been got the raw materials ready, being poured slowly into a mixing bowl, be sufficiently mixed uniformly, incorporation time is about 20 minutes, has mixed rear multi-line cutting machine and can boot up cutting.
Grout additive prepared by three above embodiment, uses in photovoltaic slice factory, finds that it can improve rapidly the phenomenon of mortar deposition, reduces and collapse limit 0.6% ~ 1%, reduces and clean dirty ratio 0.5 ~ 1%, alleviates rapidly workshop circulation pressure, improves slice efficiency;After using grout additive, no shutdown phenomenon, lifting means efficiency 1 ~ 5%.
Particular embodiments described above; to present invention solves the technical problem that, technical scheme and beneficial effect further described; it is it should be understood that; the foregoing is only the specific embodiment of the present invention; it is not limited to the present invention; all within the spirit and principles in the present invention, any modification, equivalent substitution and improvement etc. done, should be included within the scope of the present invention.
Claims (10)
1. the grout additive for solar energy section, it is characterised in that component and the mass parts of each component that it contains are as follows:
1 part ~ 20 parts of surfactant;
Abluent: 10 parts ~ 20 parts;
Chelating agen: 1 part ~ 2 parts;
Solvent: 10 parts ~ 80 parts.
Grout additive for solar energy section the most according to claim 1, it is characterised in that: described surfactant is organic higher polycarboxylic acid ammonium salt.
Grout additive for solar energy section the most according to claim 1, it is characterised in that: described abluent is metasilicate pentahydrate sodium.
Grout additive for solar energy section the most according to claim 1, it is characterised in that: described chelating agen is hydroxyethylethylene diamine tri-acetic acid.
Grout additive for solar energy section the most according to claim 1, it is characterised in that: described solvent is deionized water.
6. the preparation method of the grout additive for solar energy section as according to any one of claim 1 to 5, it is characterised in that contain in the step of the method:
A () joins after each component being got the raw materials ready according to each constituent mass percentage ratio and is sufficiently stirred in agitator tank, obtain preform;
The performance indications of (b) detection preform, and select the finished product use that performance indications are qualified.
Preparation method the most according to claim 6, it is characterised in that: in described step (a), agitator tank is sufficiently stirred for 0.5 ~ 10 hour.
Preparation method the most according to claim 6, it is characterised in that: in described step (b), performance indications include density and/or viscosity and/or electrical conductivity and/or pH value.
9. the using method of the grout additive for solar energy section as according to any one of claim 1 to 5, it is characterised in that contain in the step of the method:
Use after grout additive and mortar are thoroughly mixed;Wherein, the part by weight of grout additive and mortar is 1:100 ~ 1:10.
Using method the most according to claim 9, it is characterised in that: the time of stirring mixing is 10 ~ 30 minutes.