CN106009860A

CN106009860A - Fadeless mineral pigment for painting

Info

Publication number: CN106009860A
Application number: CN201610498712.XA
Authority: CN
Inventors: 姜曙光
Original assignee: Individual
Current assignee: Individual
Priority date: 2016-06-28
Filing date: 2016-06-28
Publication date: 2016-10-12

Abstract

The invention discloses fadeless mineral pigment for painting. The fadeless mineral pigment is prepared from the following components in percentage by weight: 34.29% of mineral powder, 3.02% of epoxy resin, 0.21% of composite phosphate, 0.52% of superfine barium, 1.20% of leveling agent, 0.80% of modified starch, 0.10% of graphene, 1.2% of titanium dioxide, 0.8% of sea mud, 0.5% of wax powder, 0.5% of sepiolite powder and the balance of deionized water. In the invention, the components are relatively simple, and the preparation method is easy to realize; and by adopting the special-formula pigment, the product does not fade forever.

Description

A kind of drawing uses colour-fast mineral pigment

Technical field

The present invention relates to pigment technology field, be specifically related to a kind of drawing and use colour-fast mineral pigment.

Background technology

China is ancient civilized country, and for thousands of years, the traditional calligraphy artwork of China is liked by the people always deeply Liking, withered pen, the style of calligraphy characterized by hollow strokes, painting etc. of swooning in calligraphy artwork are the elite expressing a width painting and calligraphy pieces, are skills The embodiment of astrologist's individual style, these all can only show on paper for thousands of years.More existing calligraphy decorations Artware, such as painting and calligraphy carved art, it is to carve out pattern on a substrate, has solid Sense, can give expression to the lines of calligraphy artwork, level, but can not reflect the abundant of calligraphy artwork Color, and withered pen, the style of calligraphy characterized by hollow strokes, the traditional art effects such as painting of swooning, its processing technology is numerous tired simultaneously.For another example The arts such as the couplet written on scrolls and hung on the pillars of a hall in horizontal tablet, gardens, shop sign, screen all can not give expression to tradition painting and calligraphy The artistic charm of the art work.

At present, known colour on pottery, enamel, mud watt ceramic handiwork and article of everyday use, increase Aesthetic feeling has become a kind of tradition and outmoded production technology, but the product after its coloring increases U.S. to user Henry is subject to, and appreciating entertaining has the biggest absorbing power.Some especially useful to human body article of everyday use, such as drinking-water work The kettle of skill product, cup, the container products of the application that is filled with water, still do not find that its artware is had normal complexion through retrieval The new technology of color fixative, new pigment.

Summary of the invention

The technical problem to be solved is to provide one to prepare simply, and effective drawing is not with Fade mineral pigment.

The technical problem to be solved realizes by the following technical solutions:

A kind of drawing uses colour-fast mineral pigment, is made up of following components in percentage by weight: mineral powder End 34.29%, epoxy resin 3.02%, composite phosphate 0.21%, ultra-fine barium 0.52%, levelling agent 1.20%, Modified starch 0.80%, Graphene 0.10%, titanium dioxide 1.2%, sea mud 0.8%, wax powder 0.5%, Hai Pao Stone powder 0.5%, surplus is deionized water；

During preparation, above-mentioned pigment formula is weighed raw material by proportioning, by mineral dust, composite phosphate, Ultra-fine barium, modified starch, Graphene, titanium dioxide, sea mud, wax powder and sepiolite powder are in mixing tank Fully premixing, is then extruded jointly by extruder, then after pulverizing, grinding with epoxy resin, Levelling agent and deionized water are sufficiently mixed, packed products.

Above-mentioned mineral dust selects azurite, chessylite, malachite green, malachite, Cinnabaris, Realgar, white mica Etc. one or both and above combination therein, can be configured to the pigment of multiple color.

A kind of technique using above-mentioned mineral pigment that ancient painted pottery is portrayed, its processing step is as follows:

(1) after ceramic body molding, base substrate is sent into cold air drying and arranges, the temperature of 45-55 DEG C Lower cold air drying 10-25 minute；Make billet surface water content reduce, it is simple to the carrying out of follow-up drawing, also make Can must fully be combined with base substrate by pigment when drawing, improve pigment firmness；

(2) carry out the base substrate after cold air drying polishing for the first time, after polishing for the first time, base substrate is sent into Temperature 6-10 DEG C, deposits 4.5-5 hour in the warehouse of humidity 65-75%；After depositing a period of time, Follow-up portray during make lines more smooth；

(3) base substrate in warehouse is taken out, portray in billet surface with cutter, after completing, use hairbrush Clean out unqualified for the mud portraying middle residual, make the lines lines portrayed become apparent from；

(4) base substrate portrayed is put into the indoor of 26-30 DEG C, is stained with mineral pigment to quarter with brush pen The lines drawn carry out painting for the first time, base substrate is sent into after completing cold air drying and arranges, the temperature of 50-53 DEG C Degree lower cold air drying 4-6 minute；

(5) base substrate after cold air drying in step (4) is taken out, be stained with brush pen under normal temperature environment The mineral pigment lines to portraying carry out second time and paint, and are dried in the shade by base substrate after completing, and then carry out the Second polishing；

(6), after second time has polished, coat glaze colours surface layer in billet surface, be then fired i.e. Can.The ceramic color prepared is natural, and the mellow and full smoothness of lines, persistence will not fade.

By using above-mentioned mineral pigment, making institute's draw color enter pottery surface, goods are as smooth as jade, Pattern with pottery body combine, formed multicolour interweave ancient painted pottery, have quaint noble quality quality and High reserve value.

The invention has the beneficial effects as follows: instant component is relatively simple, preparation method is easily achieved, and selects The pigment of formulated so that goods are will never fade.

Detailed description of the invention

For the technological means making the present invention realize, creation characteristic, reach purpose and effect and be readily apparent from Solve, below in conjunction with specific embodiment, the present invention is expanded on further.

Embodiment 1

A kind of drawing uses colour-fast mineral pigment, is made up of following components in percentage by weight: chessylite 34.29%, epoxy resin 3.02%, composite phosphate 0.21%, ultra-fine barium 0.52%, levelling agent 1.20%, Modified starch 0.80%, Graphene 0.10%, titanium dioxide 1.2%, sea mud 0.8%, wax powder 0.5%, Hai Pao Stone powder 0.5%, surplus is deionized water；

During preparation, above-mentioned pigment formula is weighed raw material by proportioning, by chessylite, composite phosphate, surpass Thin barium, modified starch, Graphene, titanium dioxide, sea mud, wax powder and sepiolite powder fill in mixing tank Point premixing, is then extruded jointly by extruder, then after pulverizing, grinding with epoxy resin, stream Flat agent and deionized water are sufficiently mixed, packed products.

Embodiment 2

A kind of drawing uses colour-fast mineral pigment, is made up of following components in percentage by weight: white mica 34.29%, epoxy resin 3.02%, composite phosphate 0.21%, ultra-fine barium 0.52%, levelling agent 1.20%, Modified starch 0.80%, Graphene 0.10%, titanium dioxide 1.2%, sea mud 0.8%, wax powder 0.5%, Hai Pao Stone powder 0.5%, surplus is deionized water；

During preparation, above-mentioned pigment formula is weighed raw material by proportioning, by white mica, composite phosphate, surpass Thin barium, modified starch, Graphene, titanium dioxide, sea mud, wax powder and sepiolite powder fill in mixing tank Point premixing, is then extruded jointly by extruder, then after pulverizing, grinding with epoxy resin, stream Flat agent and deionized water are sufficiently mixed, packed products.

Embodiment 3

A kind of drawing uses colour-fast mineral pigment, is made up of following components in percentage by weight: malachite 34.29%, epoxy resin 3.02%, composite phosphate 0.21%, ultra-fine barium 0.52%, levelling agent 1.20%, Modified starch 0.80%, Graphene 0.10%, titanium dioxide 1.2%, sea mud 0.8%, wax powder 0.5%, Hai Pao Stone powder 0.5%, surplus is deionized water；

During preparation, above-mentioned pigment formula is weighed raw material by proportioning, by malachite, composite phosphate, surpass Thin barium, modified starch, Graphene, titanium dioxide, sea mud, wax powder and sepiolite powder fill in mixing tank Point premixing, is then extruded jointly by extruder, then after pulverizing, grinding with epoxy resin, stream Flat agent and deionized water are sufficiently mixed, packed products.

The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.One's own profession Skilled person will appreciate that of industry, the present invention is not restricted to the described embodiments, above-described embodiment and explanation The principle that the present invention is simply described described in book, without departing from the spirit and scope of the present invention, The present invention also has various changes and modifications, and these changes and improvements both fall within claimed invention model In enclosing.Claimed scope is defined by appending claims and equivalent thereof.

Claims

1. a drawing uses colour-fast mineral pigment, it is characterised in that by the group of following percentage by weight Point make: mineral dust 34.29%, epoxy resin 3.02%, composite phosphate 0.21%, ultra-fine barium 0.52%, Levelling agent 1.20%, modified starch 0.80%, Graphene 0.10%, titanium dioxide 1.2%, sea mud 0.8%, wax Powder 0.5%, sepiolite powder 0.5%, surplus is deionized water.

A kind of drawing the most according to claim 1 uses colour-fast mineral pigment, it is characterised in that Above-mentioned mineral dust selects azurite, and chessylite, malachite green, malachite, Cinnabaris, in Realgar and white mica One or both or two or more combination.

3. the method preparing mineral pigment described in claim 1 or 2, it is characterised in that by above-mentioned Pigment formula weighs raw material by proportioning, by mineral dust, composite phosphate, ultra-fine barium, modified starch, Graphene, titanium dioxide, sea mud, wax powder and sepiolite powder be abundant premixing in mixing tank, then leads to Cross extruder jointly to extrude, then fill with epoxy resin, levelling agent and deionized water after pulverizing, grinding Divide mixing, packed products.

4. use the technique that ancient painted pottery is portrayed by the mineral pigment described in claim 1 or 2, its Being characterised by, processing step is as follows:

(1) after ceramic body molding, base substrate is sent into cold air drying and arranges, the temperature of 45-55 DEG C Lower cold air drying 10-25 minute；

(2) carry out the base substrate after cold air drying polishing for the first time, after polishing for the first time, base substrate is sent into Temperature 6-10 DEG C, deposits 4.5-5 hour in the warehouse of humidity 65-75%；

(6), after second time has polished, coat glaze colours surface layer in billet surface, be then fired i.e. Can.