CN105969458A - Clean biomass briquette fuel capable of reducing sulfur emission and production method thereof - Google Patents

Abstract

The invention discloses a clean biomass briquette fuel capable of reducing sulfur emission. According to the invention, the pretreated corn straws are taken as a raw material for anaerobic fermentation for 10-20 days, so that mechanical endurance of the briquette fuel is increased, finally, biogas residue is dried and crushed, and then is composited with an anti-slagging agent and an oxidant and other active ingredients for compression moulding under condition of 6MPa. The preparation method has the advantages of fast moulding and less required pressure, and is helpful for reducing equipment wearing. In the invention, magnesium carbonate is taken as the anti-slagging agent, during a combustion process, the Mg element and elements such as Si, K, and Na which are inherent in the corn straws and are capable of slagging are subjected to a reaction, a novel compound K2Mg(SO4)2 is generated and provides anti-slagging performance to the briquette fuel, ammonium bicarbonate and aviation kerosene which are taken as an ignition-assisting agent are capable of increasing the combustion efficiency and heat energy of the fuel, and the produced briquette fuel has the advantages of high desulphuration rate and good fuel performance, waste steel residue can be recycled, and the energy resource is saved.

Description

A kind of clean biometric matter shaped fuel reducing sulphur emissions and preparation method thereof

Technical field

The present invention relates to biomass fuel technical field, particularly relate to a kind of clean biometric matter molding reducing sulphur emissions Fuel and preparation method thereof.

Background technology

Biomass energy because it is renewable, aboundresources, environmental friendliness and become world's fourth largest energy, be also the most permissible Transport and the clean reproducible energy stored, mainly by the biomass energy technology modernized by agricultural wastes, felling Residue, feces of livestock and poultry, MSW, sanitary sewage become biological particles to fire with Raw material processings such as industrial organic waste waters The end products such as material, biodiesel, bio-fuel ethanol.Biomass fuel is discharged almost without SO2 during later-stage utilization, Decrease the acid rain caused by flue gas and the harm of greenhouse effect produced during it utilizes so that biomass energy has The most wide application prospect and development space, thus Developing Biomass fuel has become the mankind and has solved energy problem and improve ring One important means in border and developing direction.China is large agricultural country, and biomass resource enriches, the yield of annual agricultural crop straw More than 700,000,000 t, wherein amount usable is about 5.055 hundred million t, accounts for the 50%-60% of Chinese biological matter total resources, therefore, converts it Utilize significant.The raw materials such as agricultural crop straw exist loosely organized, density is little, distribution is not concentrated, the thermal efficiency is low, inconvenient Many defects such as transport and storage, are unfavorable for utilizing on a large scale, utilize mechanical force that compressed biomass or extruding are become density relatively Greatly, the thermal efficiency is high, it is simple to the solid fuel of transport storage is the most relatively advanced a kind of biomass economy mode.

It is tight to there is equipment attrition for straw compressing and forming in " molding fuel test is prepared in stalk anaerobic fermentation modification " literary composition The antibiont degraded barrier that weight and anaerobic fermentation face, it is proposed that the thinking of shaped fuel is prepared in a kind of stalk anaerobic fermentation modification And carried out experimental study.With corn straw as raw material in literary composition, the anaerobism that raw material carries out 10d and 20 d respectively by a definite date is sent out Ferment, the biogas residue after fermentation size-reduced and dried in 100 DEG C, be compressed into the granular fuel of diameter 10 mm under the conditions of 6 MPa. Result of the test shows: after stalk anaerobic fermentation, and the energy being retained in biogas residue is more than the energy transferred in biogas, straw biogas residue Energy value high, but after fermentation 20 d, straw content of ashes is 3 times of non-fermented stalk, and its clinkering property may be made to increase By force, the shaped fuel calorific value and prepared in literary composition only improves about 5.82% than raw material, it is impossible to meets blast furnace or has high heating value demand Place, and exist when small-sized cooking stove misfire, the problem such as the length duration of ignition and smoke pollution, efficiency of combustion is low, Need in addition modified to obtain high heating value, the novel biomass shaped fuel of resistive connection slag.

Summary of the invention

The object of the invention is contemplated to make up the defect of prior art, it is provided that a kind of clean biometric matter reducing sulphur emissions Shaped fuel and preparation method thereof.

The present invention is achieved by the following technical solutions:

A kind of clean biometric matter shaped fuel reducing sulphur emissions, is prepared by the raw materials in: corn straw 100, Corn starch 10-12, garlicin 1.7-1.9, magnesium carbonate 5.2-5.6, aerial kerosene 7-9, ammonium hydrogen carbonate 2-4, copper oxide 5-7, Magnesium oxide 12-14, slag 20-22, brucite powder 18-20, bamboo charcoal powder 16-18, suitable quantity of water.

The manufacture method of described a kind of clean biometric matter shaped fuel reducing sulphur emissions, comprises the following steps:

(1) ammonium hydrogen carbonate is added water stirring to being completely dissolved, add bamboo charcoal powder impregnate 10-12 hour, take out in 105 DEG C of baking ovens Drying is pulverized, and adds aerial kerosene, corn starch, copper oxide ultrasonic grinding 10-15 minute, be spray-dried prepare combustion-supporting Agent；

(2) brucite powder 5-10wt% hydrochloric acid solution is soaked 1-2 hour, with hot wash to without chloride ion, add water in 80- Ultrasonic Treatment 8-10 minute at 100 DEG C, dries, and adds magnesium oxide roasting 2-4 hour at 850-920 DEG C, is cooled to room temperature Grind and prepare modified brucite powder；

(3) by corn straw with hot-water soak 10-12 hour of 60-70 DEG C, filter and put in fermentation vat, control fermentation vat temperature At 30-50 DEG C, humidity is 50-60%, and anaerobic fermentation processes 20-30 hour, adds modified brucite powder, garlicin, slag stirring Uniformly isolation air continues fermentation 10-20 days, filtering drying, puts into and is crushed to 60-80 mesh in pulverizer；

(4) in step (3) material, add combustion adjuvant, water and the mixing of other residual components, send into single lead screw ex truding briquetting machine, with 6MPa's Briquetting pressure is squeezed into a diameter of 5-8mm, the cylindrical particle of a length of 3-8cm, is dried, discharging.

The invention have the advantage that the anaerobism that the present invention carries out 10-20d by a definite date with pretreated corn straw for raw material is sent out After ferment, the relative amount of stalk hemicellulose and cellulose reduces, and lignin relative amount increases, and volatile matter content reduces, benzene alcohol Extract declines can improve the mechanical endurance of shaped fuel, compound resistive connection slag agent and combustion-supporting after finally biogas residue drying being pulverized Agent and the compression forming under the conditions of 6MPa of other effective ingredient, fast desirable pressure of preparation process molding is little contributes to reduction equipment for this Abrasion；The present invention using magnesium carbonate as resistive connection slag agent, in combustion Mg element intrinsic with corn straw, knot can be caused The elements such as Si, K, Na of slag there occurs reaction, generates new compound K₂Mg(SO₄)₂And make it have anti-slagging properties, with Ammonium hydrogen carbonate, aerial kerosene etc. improve efficiency of combustion and the heat energy of fuel as firing combustion adjuvant, and the shaped fuel of preparation removes Sulfur rate is high, fuel performance is good, by refuse slag regeneration, saves the energy.

Detailed description of the invention

A kind of clean biometric matter shaped fuel reducing sulphur emissions, is prepared by the raw materials in: corn straw 100, corn starch 10, garlicin 1.7, magnesium carbonate 5.2, aerial kerosene 7, ammonium hydrogen carbonate 2, copper oxide 5, magnesium oxide 12, slag 20, brucite powder 18, bamboo charcoal powder 16, suitable quantity of water.

The manufacture method of described a kind of clean biometric matter shaped fuel reducing sulphur emissions, comprises the following steps:

(1) ammonium hydrogen carbonate is added water stirring to being completely dissolved, add bamboo charcoal powder impregnate 10-12 hour, take out in 105 DEG C of baking ovens Drying is pulverized, and adds aerial kerosene, corn starch, copper oxide ultrasonic grinding 10-15 minute, be spray-dried prepare combustion-supporting Agent；

(2) brucite powder 5-10wt% hydrochloric acid solution is soaked 1-2 hour, with hot wash to without chloride ion, add water in 80- Ultrasonic Treatment 8-10 minute at 100 DEG C, dries, and adds magnesium oxide roasting 2-4 hour at 850-920 DEG C, is cooled to room temperature Grind and prepare modified brucite powder；

(3) by corn straw with hot-water soak 10-12 hour of 60-70 DEG C, filter and put in fermentation vat, control fermentation vat temperature At 30-50 DEG C, humidity is 50-60%, and anaerobic fermentation processes 20-30 hour, adds modified brucite powder, garlicin, slag stirring Uniformly isolation air continues fermentation 10-20 days, filtering drying, puts into and is crushed to 60-80 mesh in pulverizer；

(4) in step (3) material, add combustion adjuvant, water and the mixing of other residual components, send into single lead screw ex truding briquetting machine, with 6MPa's Briquetting pressure is squeezed into a diameter of 5-8mm, the cylindrical particle of a length of 3-8cm, is dried, discharging.

The technical parameter index using the biomass molding fuel of present invention production is as follows:

(1) relaxed density is 1.159g/cm³；

(2) biogas residue lignin quality mark adds 34.5%；

(3) sulfur content: 0.355%；

(4) calorific value: 25.57MJ/kg.

Claims (2)

1. the clean biometric matter shaped fuel that can reduce sulphur emissions, it is characterised in that be prepared by the raw materials in: Corn straw 100, corn starch 10-12, garlicin 1.7-1.9, magnesium carbonate 5.2-5.6, aerial kerosene 7-9, ammonium hydrogen carbonate 2- 4, copper oxide 5-7, magnesium oxide 12-14, slag 20-22, brucite powder 18-20, bamboo charcoal powder 16-18, suitable quantity of water.

The manufacture method of a kind of clean biometric matter shaped fuel reducing sulphur emissions the most according to claim 1, it is special Levy and be to comprise the following steps:

(1) ammonium hydrogen carbonate is added water stirring to being completely dissolved, add bamboo charcoal powder impregnate 10-12 hour, take out in 105 DEG C of baking ovens Drying is pulverized, and adds aerial kerosene, corn starch, copper oxide ultrasonic grinding 10-15 minute, be spray-dried prepare combustion-supporting Agent；

(2) brucite powder 5-10wt% hydrochloric acid solution is soaked 1-2 hour, with hot wash to without chloride ion, add water in 80- Ultrasonic Treatment 8-10 minute at 100 DEG C, dries, and adds magnesium oxide roasting 2-4 hour at 850-920 DEG C, is cooled to room temperature Grind and prepare modified brucite powder；

(3) by corn straw with hot-water soak 10-12 hour of 60-70 DEG C, filter and put in fermentation vat, control fermentation vat temperature At 30-50 DEG C, humidity is 50-60%, and anaerobic fermentation processes 20-30 hour, adds modified brucite powder, garlicin, slag stirring Uniformly isolation air continues fermentation 10-20 days, filtering drying, puts into and is crushed to 60-80 mesh in pulverizer；

(4) in step (3) material, add combustion adjuvant, water and the mixing of other residual components, send into single lead screw ex truding briquetting machine, with 6MPa's Briquetting pressure is squeezed into a diameter of 5-8mm, the cylindrical particle of a length of 3-8cm, is dried, discharging.