Abstract

The invention discloses efficient gas-making biomass briquette. A sulfur-fixation combustion improver is added. By cooperation of components in the combustion improver, flue gas generated during the briquette combustion process is turned into coal gas, flame is increased, and emission of lots of fume and harmful gas is reduced. Meanwhile, biomass generated by fermentation is modified with a sodium hydroxide solution, lye releases -OH which enters lignin of biomass' cell walls to destroy pyranoid ring in lignin, separate cellulose and hemicellulose tangled in lignin and relieve a spatial three-dimensional cross-linked network structure of lignin and hemicelluloses. Through recombination, a complex spatial network structure is formed, and cohesiveness is raised, briquetting pressure is then reduced, and abrasion of equipment is relieved. The prepared biomass briquette has high cold and hot strength, will not crack when entering a furnace and will not be dispersed at high temperature. The product has low content of ash and has a good sulfur-fixation effect, and then environmental pollution is reduced. In addition, the product has high fixed carbon content, and then gas output and gas production efficiency are enhanced.

Description

A kind of efficiently gas making biomass coal and preparation method thereof

Technical field

The present invention relates to Filter Tuber For Clean Coal applied technical field, be specifically related to a kind of efficiently gas making biomass coal and preparation method thereof.

Background technology

Biomass such as straw is the primary solids garbage of China's agricultural production, and stacking processes and occupied a large amount of agriculture plantation, and crop straw burning can cause air pollution, and the minimizing degree of compost is low.In order to realize the recycling of garbage, strengthen the dynamics of digestion agricultural stalk, have people to be added in clean moulded coal as binding agent by straw.

Biomass coal is that disposable energy of coal and regenerated biological energy biomass are organically combined; it it is a kind of novel composite fuel; it it is the new product that combines of energy technology, emission-reduction technology and clean coal technology; accelerate biomass coal industrialization; effective new way is opened for agricultural, industrial organic wastes energy; to energy-saving and emission-reduction, preserving the ecological environment has great importance, and meets country and reduces discharging potentiation long-range developmental program.But the biomass coal produced in prior art is due to the defect of biomass self rigidity, easy swelling cracking after extruded with coal dust, and pure inflammable, the burning persistency difference of biomass coal etc., thus take effective technology scheme by addition modified for biomass or add effective additive and improve the function of existing biomass coal, it is achieved reduce discharging CO₂、SO₂, reduce flue dust and PM2.5, save the multiple-effect of coal resources.

" preparation of biomass coal and Micro-Structure Analysis " literary composition is to solve biomass rigidity to cause a difficult problem for biomass coal swelling cracking, microbial fermentation technology is utilized to process biomass straw, using fermenting, modified biomass blend as additive by a certain percentage with fine coal, and cold moudling prepares biomass coal.Result shows: modified biomass quality of fermenting is closely knit, expands compression performance and is improved, and after activation, big particle diameter is the filament being wound around mutually, reuniting, and it is preferable that small particle sprawls effect, and has covering property；Fermentation makes straw tissue become loose, and beneficially coal grain is combined with biomass, it is to avoid biomass have a rigidity and cause moulded coal swelling cracking；After before modified, caloric value change is less, for 0.07kJ/g.Biomass coal optimum proportioning is: coal 80%, fermentation of biomass 15%, bentonite 5%；The comprcssive strength preparing moulded coal reaches 1.4MPa, and drop strength is up to 98.65%, and heat stability reaches 88.4%.

But it is the highest to the utilization rate of biomass in literary composition, briquetting pressure big equipment attrition phenomenon is serious, the modified moulded coal comprcssive strength prepared and drop strength is relatively low is unfavorable for long-term storage and transport, excessive being obviously unfavorable for realizes saving coal resources and reducing discharging CO coal usage ratio₂、SO₂Reduce flue dust and the combustion requirements of PM2.5, blindly increase that the content of biomass inevitably results in again that the smog of moulded coal is big, efficiency of combustion is low, calorific value is little cannot meet thermal discharge and require that high place uses, it is therefore desirable in addition modified to obtain biomass coal fuel energy-conservation, efficient, that clean to existing moulded coal production technology.

Summary of the invention

It is an object of the invention to provide a kind of efficiently gas making biomass coal and preparation method thereof, to overcome the deficiencies in the prior art.

The object of the present invention is achieved like this:

A kind of efficiently gas making biomass coal, it is characterized in that, be prepared by the raw materials in: coal dust 47-48, corn straw 22-24, wood flour 17-19, residue of monosodium glutamate 5-7, Bayer process red mud 6-8, kieselguhr 11-13, nano zine oxide 1.2-1.4, used oil 2-4, ferrous sulfate 0.4-0.6, calcium acetate 0.5-0.6, yellow sodium prussiate 0.7-0.9, Aqueous Polyurethane Adhesives 9-11, banana fiber 8-10,1wt% sodium hydroxide solution appropriate.

The preparation method of described a kind of efficient gas making biomass coal, it is characterised in that comprise the following steps:

(1) ferrous sulfate, calcium acetate are ground the stirring that adds water to being completely dissolved, add Bayer process red mud to impregnate 10-12 hour, take out and dry in 105 DEG C of baking ovens, add nano zine oxide, used oil, banana fiber mixing, it is warming up to 80-90 DEG C, ultrasonic grinding 10-15 minute, is spray-dried and prepares sulfur-fixating combustion promoter；

(2) kieselguhr is ground 2-4 hour, cross 100 mesh sieves, add yellow sodium prussiate, Aqueous Polyurethane Adhesives and suitable quantity of water high-speed stirring and mix pasty state, put in 60-80 DEG C of water-bath, constant temperature 2-3 hour, is evaporated high-temperature calcination 2-3 hour at 620-720 DEG C, obtains the activated diatomaceous earth of graft modification；

(3) by corn straw with hot-water soak 10-12 hour of 60-70 DEG C, filter and put in fermentation vat, anaerobic fermentation 20-30 hour, add wood flour, residue of monosodium glutamate mixing isolation air continues fermentation 7-10 days, filter, putting in the sodium hydroxide solution of 1wt% and soak 1-2 days, washing is dried to neutral, is crushed to 60-80 mesh；

(4) it is about 3mm by pulverized coal grinding to granularity, add step (3) reaction mass stirring and evenly mixing, it is warming up to 90-100 DEG C and is incubated 30-40 minute, natural cooling adds sulfur-fixating combustion promoter, activated diatomaceous earth, suitable quantity of water stirring and evenly mixing, put in mould compressing under 6MPa pressure, natural curing discharging in 7-8 days.

The present invention has following beneficial effect: the present invention is in order to avoid occurring that blindly increasing biomass content causes the defect that smog is big, efficiency of combustion is low, calorific value is little of moulded coal, the present invention with the addition of sulfur-fixating combustion promoter, cooperate between each component of this combustion adjuvant, the flue gas produced in Coal Briquettes Combustion is become coal gas, make the huge increasing of flame, decrease the discharge of volume of smoke and harmful gas；The biomass that fermentation is produced by the present invention simultaneously are through sodium hydroxide solution modification, alkali liquor discharges in the lignin that-OH enters biomass cells wall, destroy the pyranoid ring among lignin, take cellulose intermeshing with lignin and hemicellulose apart, relieve the space multistory cross-linked structure of lignin and hemicellulose, complicated space net structure is formed through restructuring, improve bonds itself, and then reduction briquetting pressure, equipment attrition phenomenon is eased, the biomass coal cold strength utilizing the present invention to prepare is high, ensure that accumulating is convenient, enter stove the most broken, high temperature does not dissipates；Cinder content is low, and captured sulfur result is good, reduces environmental pollution；Fixed carbon content is high, improves gas production and gas producing efficiency.

Detailed description of the invention

Described a kind of efficiently gas making biomass coal, it is characterized in that, be prepared by the raw materials in: coal dust 47, corn straw 22, wood flour 17, residue of monosodium glutamate 5, Bayer process red mud 6, kieselguhr 11, nano zine oxide 1.2, used oil 2, ferrous sulfate 0.4, calcium acetate 0.5, yellow sodium prussiate 0.7, Aqueous Polyurethane Adhesives 9, banana fiber 8,1wt% sodium hydroxide solution appropriate.

Manufacture method comprises the following steps:

(1) ferrous sulfate, calcium acetate are ground the stirring that adds water to being completely dissolved, add Bayer process red mud to impregnate 10-12 hour, take out and dry in 105 DEG C of baking ovens, add nano zine oxide, used oil, banana fiber mixing, it is warming up to 80-90 DEG C, ultrasonic grinding 10-15 minute, is spray-dried and prepares sulfur-fixating combustion promoter；

(2) kieselguhr is ground 2-4 hour, cross 100 mesh sieves, add yellow sodium prussiate, Aqueous Polyurethane Adhesives and suitable quantity of water high-speed stirring and mix pasty state, put in 60-80 DEG C of water-bath, constant temperature 2-3 hour, is evaporated high-temperature calcination 2-3 hour at 620-720 DEG C, obtains the activated diatomaceous earth of graft modification；

(3) by corn straw with hot-water soak 10-12 hour of 60-70 DEG C, filter and put in fermentation vat, anaerobic fermentation 20-30 hour, add wood flour, residue of monosodium glutamate mixing isolation air continues fermentation 7-10 days, filter, putting in the sodium hydroxide solution of 1wt% and soak 1-2 days, washing is dried to neutral, is crushed to 60-80 mesh；

(4) it is about 3mm by pulverized coal grinding to granularity, add step (3) reaction mass stirring and evenly mixing, it is warming up to 90-100 DEG C and is incubated 30-40 minute, natural cooling adds sulfur-fixating combustion promoter, activated diatomaceous earth, suitable quantity of water stirring and evenly mixing, put in mould compressing under 6MPa pressure, natural curing discharging in 7-8 days.

The comprcssive strength of this biomass coal reaches 3.4MPa after testing, and drop strength is up to 99.85%, and heat stability reaches 89.35%.

Claims (2)

1. an efficient gas making biomass coal, it is characterized in that, be prepared by the raw materials in: coal dust 47-48, corn straw 22-24, wood flour 17-19, residue of monosodium glutamate 5-7, Bayer process red mud 6-8, kieselguhr 11-13, nano zine oxide 1.2-1.4, used oil 2-4, ferrous sulfate 0.4-0.6, calcium acetate 0.5-0.6, yellow sodium prussiate 0.7-0.9, Aqueous Polyurethane Adhesives 9-11, banana fiber 8-10,1wt% sodium hydroxide solution appropriate.

The manufacture method of a kind of efficient gas making biomass coal the most according to claim 1, it is characterised in that comprise the following steps:

(1) ferrous sulfate, calcium acetate are ground the stirring that adds water to being completely dissolved, add Bayer process red mud to impregnate 10-12 hour, take out and dry in 105 DEG C of baking ovens, add nano zine oxide, used oil, banana fiber mixing, it is warming up to 80-90 DEG C, ultrasonic grinding 10-15 minute, is spray-dried and prepares sulfur-fixating combustion promoter；

(2) kieselguhr is ground 2-4 hour, cross 100 mesh sieves, add yellow sodium prussiate, Aqueous Polyurethane Adhesives and suitable quantity of water high-speed stirring and mix pasty state, put in 60-80 DEG C of water-bath, constant temperature 2-3 hour, is evaporated high-temperature calcination 2-3 hour at 620-720 DEG C, obtains the activated diatomaceous earth of graft modification；

(3) by corn straw with hot-water soak 10-12 hour of 60-70 DEG C, filter and put in fermentation vat, anaerobic fermentation 20-30 hour, add wood flour, residue of monosodium glutamate mixing isolation air continues fermentation 7-10 days, filter, putting in the sodium hydroxide solution of 1wt% and soak 1-2 days, washing is dried to neutral, is crushed to 60-80 mesh；

(4) it is about 3mm by pulverized coal grinding to granularity, add step (3) reaction mass stirring and evenly mixing, it is warming up to 90-100 DEG C and is incubated 30-40 minute, natural cooling adds sulfur-fixating combustion promoter, activated diatomaceous earth, suitable quantity of water stirring and evenly mixing, put in mould compressing under 6MPa pressure, natural curing discharging in 7-8 days.