CN105967653A - Acid-resistant ceramic tile - Google Patents
Acid-resistant ceramic tile Download PDFInfo
- Publication number
- CN105967653A CN105967653A CN201610326602.5A CN201610326602A CN105967653A CN 105967653 A CN105967653 A CN 105967653A CN 201610326602 A CN201610326602 A CN 201610326602A CN 105967653 A CN105967653 A CN 105967653A
- Authority
- CN
- China
- Prior art keywords
- ceramic tile
- parts
- acid
- powder
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an acid-resistant ceramic tile, and relates to the technical field of ceramic tile production. The ceramic tile is prepared from the following raw materials in parts by weight: 55-60 parts of quartz powder, 26-31 parts of kaolin, 4-6 parts of feldspar powder, 0.5-1.0 part of iron ore powder and 0.25-0.35 part of titanium dioxide. Compared with the prior art, the acid-assistant ceramic tile has high acid resistance and good temperature and acid resistance, has a water absorption rate of lower than 1.5 percent, cannot be easily oxidized at normal temperature, cannot be easily polluted by mediums, and is suitable for anticorrosive linings of various towers, ponds, tanks and grooves.
Description
Technical field
The present invention relates to ceramic tile manufacturing technology field, especially a kind of acid-proof ceramic tile.
Background technology
Oil, chemical industry, pharmacy, papermaking, weave, smelt, power plant, the industry such as plating, it is applied to the corrosion-proof lining of tower, pond, tank, groove, and in terms of sewage treatment project etc. work place, common ceramic tile can not meet the needs of its corrosion resistance, and it is high to need have acid resistance, Heat-stable is effective, and water absorption rate is low, the most oxidizable, it is difficult to by the ceramic tile of the characteristics such as medium pollution.
Summary of the invention
The technical problem to be solved is to provide one and has acid resistance height, and water absorption rate is low, the most oxidizable, is difficult to by the acid-proof ceramic tile of medium pollution.
In order to solve the problems referred to above, the technical solution used in the present invention is: this acid-proof ceramic tile, including the raw material of following weight portion: silica flour: 55 parts～60 parts, Kaolin: 26 parts～31 parts, feldspar powder: 4 parts～6 parts, Iron Ore Powder: 0.5 part～1.0 parts, titanium dioxide: 0.25 part～0.35 part.
Described silica flour, is a kind of hard, wear-resisting, mineral of stable chemical performance, and its main chemical compositions is SiO2, and after the quartz that goes out from mining is processed, general granularity is crossed the product of 120 mesh sieves and is referred to as silica flour, is mainly used in pottery and refractory material.
Described Kaolin, is a kind of clay based on kaolinite race clay mineral and clay rock, belongs to nonmetallic minerals, because of white and fine and smooth, also known as white clouds soil；There is the physicochemical properties such as good plasticity and fire resistance, be mainly used in papermaking, pottery and refractory material.
Described Anhydrite, is alkali metal or the aluminium silicate minerals of alkaline-earth metal such as potassium, sodium, calcium, barium, and crystal structure belongs to rack-like structure；Its Main Ingredients and Appearance is SiO2, Al2O3, K2O, Na2O, CaO etc..
Described Iron Ore Powder, is through ore dressing, the breeze that crushes, sort, grind etc. processed by the Ore containing ferrum element or iron compound, can be used as coloring earth.
Described titanium dioxide, it it is the Chinese white being mainly composed of titanium dioxide, being widely used in all kinds of body structure surface coating, paper coating and filler, plastics and elastomer, its purposes also includes pottery, glass, catalyst, coated textiles, printing-ink, rolled roof grain and solder flux.
Owing to have employed technique scheme, the present invention compared with prior art has the advantages that
The acid resistance of acid-proof ceramic tile of the present invention is high, and Heat-stable is effective, and water absorption rate is less than 1.5%, the most oxidizable, is difficult to by medium pollution, it is adaptable to various towers, pond, tank, the corrosion-proof lining of groove.
Detailed description of the invention
Below in conjunction with specific embodiment, the invention will be further described:
Embodiment 1
A kind of acid-proof ceramic tile, including the raw material of following weight portion: silica flour: 550 kilograms, Kaolin: 260 kilograms, feldspar powder: 40 kilograms, Iron Ore Powder: 5 kilograms, titanium dioxide: 2.5 kilograms.
Weigh raw material respectively by the weight of above-mentioned each raw material to carry out pulverizing dispensing, add water after screening and make pug, then carry out mixing, molding, be dried, reburn and make this acid-proof ceramic tile.
Embodiment 2
A kind of acid-proof ceramic tile, including the raw material of following weight portion: silica flour: 600 kilograms, Kaolin: 310 kilograms, feldspar powder: 60 kilograms, Iron Ore Powder: 10 kilograms, titanium dioxide: 3.5 kilograms.
Weigh raw material respectively by the weight of above-mentioned each raw material to carry out pulverizing dispensing, add water after screening and make pug, then carry out mixing, molding, be dried, reburn and make this acid-proof ceramic tile.
Claims (1)
1. an acid-proof ceramic tile, it is characterised in that: include the raw material of following weight portion: silica flour: 55 parts～60 parts, Kaolin: 26 parts～31 parts, feldspar powder: 4 parts～6 parts, Iron Ore Powder: 0.5 part～1.0 parts, titanium dioxide: 0.25 part～0.35 part.