CN105957907A - High-uniformity paeonol-containing single crystalline silicon solar cell surface texture liquid and preparation method thereof - Google Patents
High-uniformity paeonol-containing single crystalline silicon solar cell surface texture liquid and preparation method thereof Download PDFInfo
- Publication number
- CN105957907A CN105957907A CN201610531648.0A CN201610531648A CN105957907A CN 105957907 A CN105957907 A CN 105957907A CN 201610531648 A CN201610531648 A CN 201610531648A CN 105957907 A CN105957907 A CN 105957907A
- Authority
- CN
- China
- Prior art keywords
- paeonol
- solar cell
- surface texture
- silicon solar
- texture liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses high-uniformity paeonol-containing single crystalline silicon solar cell surface texture liquid. The single crystalline silicon solar cell surface texture liquid is prepared from the following raw materials in parts by weight: 0.05-0.1 part of paeonol, 1.5-2.5 parts of styrene, 1-2 parts of 5-10% ammonium persulfate solution, 0.1-0.2 part of sodium dodecyl sulfate, 0.1-0.15 part of dodecafluoroheptyl-propyl-trimethoxylsilane, 0.1-0.15 part of N-oleoyl-N-methyl sodium taurine, 0.03-0.05 part of carboxymethylcellulose, 3-5 parts of sodium hydroxide, 0.3-0.5 part of citric acid, 0.3-0.5 part of xylitol and 100-120 parts of water. The silicon wafer texture liquid disclosed by the invention is relatively high in reaction speed, moderate in corrosion, small in reduction amount and high in repeating utilization rate, prepared textured surfaces are in pyramid distribution and are uniform in size, particles are smaller, the technology processing quality is high in stability, and silicon wafers are high in surface quality.
Description
Technical field
The present invention relates to technical field of solar batteries, particularly relate to a kind of high uniformity monocrystaline silicon solar cell sheet surface texture liquid containing paeonol and preparation method thereof.
Background technology
Along with world energy sources crisis is more serious, solar energy has become most potential alternative energy source, and solaode is i.e. a kind of electronic component that solar energy is converted directly into electric energy.The main problem hindering solar battery technology development is its high manufacturing cost.At present, for reducing the cost of monocrystaline silicon solar cell and improving electricity conversion, carrying out silicon face texturing is the most easily to realize and the most efficient method.Texture, also known as making herbs into wool, i.e. utilizes and falls into light principle, make incident illumination carry out multiple reflections and extend its propagation path at battery surface, thus improve the solaode absorption efficiency to light.Utilizing the principle of the anisotropic etch of silicon, monocrystalline silicon surface can form similar pyramidal structure, effectively reduces the reflectance of sunlight.
At present, monocrystalline silicon surface texture is most commonly used that chemical corrosion method, it is common to use texture liquid be NaOH/ Isopropanol Solvent, but isopropanol price is high, and evaporation rate is fast, and cost is high and is unfavorable for environmental protection.Patent 201010161287.8 discloses a kind of velvet manufacturing solution of monocrystalline silicon additive, it is made up of alkaline corrosion liquid and surfactant and organic acid or salt, without isopropanol and rapidly and efficiently, but its problem that there is reaction lack of homogeneity, easily cause that silicon face pyramid after texture is bigger than normal and the situation such as local excessive erosion, the quality make silicon chip need improve further.
Summary of the invention
The object of the invention is contemplated to make up the defect of prior art, response speed is fast, uniformity good to provide one, corrodes high uniformity moderate, that Reducing thickness is little, silicon chip surface quality is high monocrystaline silicon solar cell sheet surface texture liquid containing paeonol and preparation method thereof.
The present invention is achieved by the following technical solutions:
A kind of high uniformity monocrystaline silicon solar cell sheet surface texture liquid containing paeonol, it is to be prepared by the raw material of following weight parts:
Paeonol 0.05-0.1; styrene 1.5-2.5; 5-10% ammonium persulfate solution 1-2, sodium lauryl sulphate 0.1-0.2, ten difluoro heptyl propyl trimethoxy silicane 0.1-0.15; N-oleoyl-N methyl taurine sodium 0.1-0.15; carboxymethyl cellulose 0.03-0.05, sodium hydroxide 3-5, citric acid 0.3-0.5; xylitol 0.3-0.5, water 100-120.
The preparation method of a kind of high uniformity monocrystaline silicon solar cell sheet surface texture liquid containing paeonol, comprises the following steps:
(1) raw material is weighed by weight, first sodium lauryl sulphate is added in the water of 1/3-1/2 weight and stir, it is then slowly added into styrene and the mixture of ten difluoro heptyl propyl trimethoxy silicanes and stirs 0.5-1h, finally it is slowly added dropwise ammonium persulfate solution and stirs 2-4h in 70-80 DEG C, cool down after insulation 3-5h, obtain complex emulsions;
(2) sodium hydroxide and citric acid first add stirring in the water of surplus, until being completely dissolved, be subsequently adding paeonol and N-oleoyl-60-70 DEG C of N methyl taurine sodium stirring 0.5-1h, add remaining raw material stirring after cooling uniformly, obtain mixed liquor;
(3) it is slowly added to the complex emulsions in step (1) stir in the mixed liquor in step (2) and in 60-80 DEG C, after being filtered to remove impurity, i.e. obtains the high uniformity monocrystaline silicon solar cell sheet surface texture liquid containing paeonol.
The invention have the advantage that
The present invention utilizes styrene and ten difluoro heptyl propyl trimethoxy silicane emulsions polymerization synthesis complex microsphere, silicon chip surface can be attached to well, play certain etching mask effect, the excessive corrosion of silicon chip can be reduced, promote the uniformity of reaction simultaneously, improve matte quality, be difficult to again remain at silicon chip surface, it is ensured that the spatter property of silicon chip;Simultaneously, by the compounding of the raw materials such as paeonol and potentiation, make the silicon chip texture liquid response speed obtained very fast, corrode moderate, Reducing thickness is little, recycling rate of waterused is high, the distribution of matte pyramid, the size that prepare are uniform, granule is less, and processes quality stability is good, and silicon chip surface quality is high.
Detailed description of the invention
A kind of high uniformity monocrystaline silicon solar cell sheet surface texture liquid containing paeonol, is prepared from by the component raw material of following weight (kg):
Paeonol 0.05, styrene 1.5,5% ammonium persulfate solution 1, sodium lauryl sulphate 0.1; ten difluoro heptyl propyl trimethoxy silicanes 0.1, N-oleoyl-N methyl taurine sodium 0.1, carboxymethyl cellulose 0.03, sodium hydroxide 3; citric acid 0.3, xylitol 0.3, water 100.
The preparation method of a kind of high uniformity monocrystaline silicon solar cell sheet surface texture liquid containing paeonol, comprises the following steps:
(1) raw material is weighed by weight, first sodium lauryl sulphate is added in the water of 1/3 weight and stir, it is then slowly added into styrene and the mixture of ten difluoro heptyl propyl trimethoxy silicanes and stirs 0.5h, finally it is slowly added dropwise ammonium persulfate solution and stirs 2h in 70 DEG C, cool down after insulation 3h, obtain complex emulsions;
(2) sodium hydroxide and citric acid first add stirring in the water of surplus, until being completely dissolved, be subsequently adding paeonol and N-oleoyl-60 DEG C of N methyl taurine sodium stirring 0.5h, add remaining raw material stirring after cooling uniformly, obtain mixed liquor;
(3) it is slowly added to the complex emulsions in step (1) stir in the mixed liquor in step (2) and in 60 DEG C, after being filtered to remove impurity, i.e. obtains the high uniformity monocrystaline silicon solar cell sheet surface texture liquid containing paeonol.
.Through inspection, above-mentioned texture liquid 80 DEG C, uniform small size pyramid structure can be prepared at silicon chip surface under the conditions of 20min, its pyramid prepared is 9.4% at 0.5-1.5 μm, the average reflectance in the range of 300-1100nm, and the amount of silicon being corroded is about 4.7%.
Claims (2)
1. the high uniformity monocrystaline silicon solar cell sheet surface texture liquid containing paeonol, it is characterised in that it is to be prepared by the raw material of following weight parts:
Paeonol 0.05-0.1; styrene 1.5-2.5; 5-10% ammonium persulfate solution 1-2, sodium lauryl sulphate 0.1-0.2, ten difluoro heptyl propyl trimethoxy silicane 0.1-0.15; N-oleoyl-N methyl taurine sodium 0.1-0.15; carboxymethyl cellulose 0.03-0.05, sodium hydroxide 3-5, citric acid 0.3-0.5; xylitol 0.3-0.5, water 100-120.
The preparation method of a kind of high uniformity the most according to claim 1 monocrystaline silicon solar cell sheet surface texture liquid containing paeonol, it is characterised in that comprise the following steps:
(1) raw material is weighed by weight, first sodium lauryl sulphate is added in the water of 1/3-1/2 weight and stir, it is then slowly added into styrene and the mixture of ten difluoro heptyl propyl trimethoxy silicanes and stirs 0.5-1h, finally it is slowly added dropwise ammonium persulfate solution and stirs 2-4h in 70-80 DEG C, cool down after insulation 3-5h, obtain complex emulsions;
(2) sodium hydroxide and citric acid first add stirring in the water of surplus, until being completely dissolved, be subsequently adding paeonol and N-oleoyl-60-70 DEG C of N methyl taurine sodium stirring 0.5-1h, add remaining raw material stirring after cooling uniformly, obtain mixed liquor;
(3) it is slowly added to the complex emulsions in step (1) stir in the mixed liquor in step (2) and in 60-80 DEG C, after being filtered to remove impurity, i.e. obtains the high uniformity monocrystaline silicon solar cell sheet surface texture liquid containing paeonol.