CN105951253B - The preparation processing method of antibiosis knitting yarn - Google Patents
The preparation processing method of antibiosis knitting yarn Download PDFInfo
- Publication number
- CN105951253B CN105951253B CN201610461327.8A CN201610461327A CN105951253B CN 105951253 B CN105951253 B CN 105951253B CN 201610461327 A CN201610461327 A CN 201610461327A CN 105951253 B CN105951253 B CN 105951253B
- Authority
- CN
- China
- Prior art keywords
- copper ion
- ion fiber
- per minute
- knitting yarn
- kept
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of textile yarn field, especially a kind of preparation processing method of antibiosis knitting yarn；It can reach 3A grades the object of the present invention is to provide a kind of antibacterial effect and also reduce the antibiosis knitting yarn of production cost and its prepare processing method；The first step, the selection of raw material：22~29% wool, 30~45% viscose glue, 25~35% polyamide fibre and 5~7% Kapp dragon copper ion fiber, and always proportioning is 100% etc. for wool, viscose glue, polyamide fibre and Kapp dragon copper ion fiber；A kind of preparation processing method of antibiosis knitting yarn designed by the present invention, by using wool, viscose glue, polyamide fibre and Kapp dragon copper ion fiber, first Kapp dragon copper ion fiber is dyed and reduction treatment, Kapp dragon copper ion fiber is made to reach fastness requirement, the yarn for reaching national 3A grades of antibacterial standard then just can be processed according to specified procedure of processing.
Description
Technical field
The present invention relates to a kind of textile yarn field, especially a kind of preparation processing method of antibiosis knitting yarn.
Background technology
As the improvement of people's living standards, requirement of the people to clothes is higher and higher, consumer chases after since most
That asks warming develops, therefore functional textile comes into being to the directions such as comfortable, beautiful, good for health.
At present, people will also to functional textile other than it should have good moisture absorbing and sweat releasing performance and electric conductivity
It is with good antibiotic property and healthcare function；Because antibacterial fabric can prevent and cut off various disease bacteriums, and can protect
The aridity of body is held, warm and humid skin is avoided to become the good place of bacterial reproduction.
In order to improve the anti-microbial property of fabric, conventional method is functional treatment method, and the finishing method is simple and practicable, but due to
Chemical reagent has been used, there is the feel for damaging fabric and style or even secondary injury has been caused to skin, and cannot keep lasting
Antibiotic property the shortcomings that.And anti-bacterial fibre nearly ten years is broadly divided into natural class, such as chitin, fiber crops, bamboo fibre；Heavy metal
Class, such as silver ion；But not only antibacterial effect is bad, and production cost is higher for existing natural class, heavy metal classes antibiotic fabric.
It is solved in view of the above problems, being badly in need of us.
Invention content
It can reach 3A grades it is an object of the invention to overcome the deficiencies of the prior art and provide a kind of antibacterial effect and also reduce
The preparation processing method of the antibiosis knitting yarn of production cost.
In order to achieve the above object, the preparation processing method of a kind of antibiosis knitting yarn designed by the present invention, step is such as
Under：The first step, the selection of raw material：22~29% wool, 30~45% viscose glue, 25~35% polyamide fibre and 5~7% Kapp dragon
Copper ion fiber, and always proportioning is 100% for wool, viscose glue, polyamide fibre and Kapp dragon copper ion fiber；Second step, dyeing processing：It will
Kapp dragon copper ion fiber is at room temperature with bath raio 1:5~1:8 are matched, and are additionally added the glacial acetic acid of 0.5~1g/L, 0.5
The levelling agent and disperse dyes of~1g/L, the additive amounts of disperse dyes from shallow to deep, and is kept for 5 minutes for 0~6%, then with every
1 DEG C of minute is warming up to 80 DEG C, is then warming up to 120~125 DEG C with 0.8 DEG C per minute, and kept for 45~60 minutes, then stops
Heating makes it be cooled to 80 DEG C with 0.8 DEG C per minute, and is kept for 5 minutes, is then cooled to 50 DEG C with 1 DEG C per minute, finally certainly
So dyeing processing is completed in cooling, and pH value is 5~9 in entire dyeing course；Third walks, reduction treatment：Dyeing is handled well
Kapp dragon copper ion fiber at room temperature with bath raio 1:5~1:8 are matched, and are additionally added the sodium hydrosulfite of 1~2g/L, 1.5
The soda ash of~2g/L and the acidic reduction cleaner of 1~2g/L, and kept for 5 minutes, 100 DEG C are then heated to, is kept for 30 minutes,
Then stop heating, it is made to be cooled to 80 DEG C with 0.8 DEG C per minute, and kept for 5 minutes, be then cooled to 50 with 1 DEG C per minute
DEG C, last natural cooling completes reduction treatment, and pH value is not less than 5 in entire reduction treatment process；The work of the reduction treatment
With being to remove some loose colours, the fastness of Kapp dragon copper ion fiber is promoted；It is prepared by the 4th step, production：By wool, viscose glue, polyamide fibre
With Kapp dragon copper ion fiber pass through and hair → cotton carding → drafting → rove → spun yarn → winder → doubling → double twisting, prepare one
Kind antibiosis knitting yarn.
Preferably, the sodium hydrosulfite in third step is sodium dithionite.
By a kind of preparation processing method of antibiosis knitting yarn designed by the present invention, it can process and reach 3A grades national
The yarn of antibacterial standard.
Specific embodiment
Embodiment 1：
A kind of preparation processing method of antibiosis knitting yarn of the present embodiment description, step are as follows：The first step, the choosing of raw material
It selects：25% wool, 40% viscose glue, 30% polyamide fibre and 5% Kapp dragon copper ion fiber；Second step, dyeing processing：By 5%
Kapp dragon copper ion fiber is at room temperature with bath raio 1:5 are matched, and are additionally added the level dyeing of the glacial acetic acid of 0.5g/L, 0.5g/L
Agent and disperse dyes, the additive amounts of disperse dyes from shallow to deep, and are kept for 5 minutes for 2%, are then warming up to 80 with 1 DEG C per minute
DEG C, 120 DEG C then are warming up to 0.8 DEG C per minute, and kept for 45 minutes, then stop heating, make it with 0.8 DEG C per minute drop
Temperature is kept for 5 minutes to 80 DEG C, is then cooled to 50 DEG C with 1 DEG C per minute, and last natural cooling is completed dyeing and handled, and
PH value is 5 in entire dyeing course；Third walks, reduction treatment：Kapp dragon copper ion fiber after dyeing is handled is in room temperature
Under with bath raio 1:5 are matched with water, and are additionally added the acidity of the sodium dithionite of 1.5g/L, the soda ash of 1.5g/L and 1g/L
Reduction cleaner, and kept for 5 minutes, 100 DEG C are then heated to, is kept for 30 minutes, is then stopped heating, make it with per minute
0.8 DEG C is cooled to 80 DEG C, and is kept for 5 minutes, is then cooled to 50 DEG C with 1 DEG C per minute, last natural cooling completes also original place
Reason, and pH value is 5 in entire reduction treatment process, the effect of the reduction treatment is to remove some loose colours, promotes Kapp dragon copper
The fastness of ion fiber；It is prepared by the 4th step, production：By 25% wool, 40% viscose glue, 30% polyamide fibre and 5% Kapp dragon copper
Ion fiber by with hair → cotton carding → drafting → rove → spun yarn → winder → doubling → double twisting, prepare a kind of antibiosis knitting
Yarn.
It is that list is compared by the thread blended fabric of antibacterial stocking yarn and the performance indicator of common cotton below：
Embodiment 2：
A kind of preparation processing method of antibiosis knitting yarn of the present embodiment description, step are as follows：The first step, the choosing of raw material
It selects：25% wool, 38% viscose glue, 30% polyamide fibre and 7% Kapp dragon copper ion fiber；Second step, dyeing processing：By 7%
Kapp dragon copper ion fiber is at room temperature with bath raio 1:8 are matched, and be additionally added the glacial acetic acid of 1g/L, 1g/L levelling agent and
Disperse dyes, the additive amounts of disperse dyes from shallow to deep, and are kept for 5 minutes for 3%, are then warming up to 80 DEG C with 1 DEG C per minute,
Then 125 DEG C are warming up to 0.8 DEG C per minute, and are kept for 60 minutes, then stop heating, make it with 0.8 DEG C per minute cooling
It to 80 DEG C, and is kept for 5 minutes, is then cooled to 50 DEG C with 1 DEG C per minute, last natural cooling completes dyeing processing, and whole
PH value is 9 in a dyeing course；Third walks, reduction treatment：Kapp dragon copper ion fiber after 7 dyeing are handled is at room temperature
With bath raio 1:8 are matched, and are additionally added the acidic reduction cleaning of the sodium dithionite of 2g/L, the soda ash of 2g/L and 2g/L
Agent, and kept for 5 minutes, 100 DEG C are then heated to, is kept for 30 minutes, then stops heating, makes it with 0.8 DEG C per minute cooling
It to 80 DEG C, and is kept for 5 minutes, is then cooled to 50 DEG C with 1 DEG C per minute, last natural cooling completes reduction treatment, and whole
PH value is 5 in a reduction treatment process, and the effect of the reduction treatment is to remove some loose colours, promotes Kapp dragon copper ion fiber
Fastness；It is prepared by the 4th step, production：25% wool, 38% viscose glue, 30% polyamide fibre and 7% Kapp dragon copper ion fiber are led to
It crosses and hair → cotton carding → drafting → rove → spun yarn → winder → doubling → double twisting, prepares a kind of antibiosis knitting yarn.
It is that list is compared by the thread blended fabric of antibacterial stocking yarn and the performance indicator of common cotton below：
By the performance indicator in above two embodiment this it appears that blended being knitted by the way that antibacterial stocking yarn is thread
The effect of object anti-Staphylococcus aureus, escherichia coli and Candida albicans than the antibacterial effect of common cotton well very
It is more, and when what wool, 38% viscose glue, 30% polyamide fibre and 7% Kapp dragon copper ion fiber using 25% produced and processed out resists
The best results of bacterium hosiery yarns anti-candida albicans.
Claims (3)
1. a kind of preparation processing method of antibiosis knitting yarn, it is characterised in that：The first step, the selection of raw material：22~29% sheep
Hair, 30~45% viscose glue, 25~35% polyamide fibre and 5~7% Kapp dragon copper ion fiber, and wool, viscose glue, polyamide fibre and card
Always proportioning is 100% to general dragon copper ion fiber；Second step, dyeing processing：By Kapp dragon copper ion fiber at room temperature with bath raio 1:
5~1:8 are matched, and are additionally added the glacial acetic acid of 0.5~1g/L, the levelling agent of 0.5~1g/L and additive amount as 0~6% by shallow
It to deep disperse dyes, and is kept for 5 minutes, is then warming up to 80 DEG C with 1 DEG C per minute, is then warming up to 0.8 DEG C per minute
120~125 DEG C, and kept for 45~60 minutes, then stop heating, it is made to be cooled to 80 DEG C with 0.8 DEG C per minute, and keep 5
Minute, 50 DEG C then are cooled to 1 DEG C per minute, last natural cooling completes dyeing processing, and the PH in entire dyeing course
Be worth is 5~9；Third walks, reduction treatment：The Kapp dragon copper ion fiber handled well will be dyed at room temperature with bath raio 1:5~1:8
It is matched, and is additionally added the acidic reduction cleaner of the sodium hydrosulfite of 1~2g/L, the soda ash of 1.5~2g/L and 1~2g/L, and
It is kept for 5 minutes, then heats to 100 DEG C, kept for 30 minutes, then stop heating, it is made to be cooled to 80 with 0.8 DEG C per minute
DEG C, and kept for 5 minutes, 50 DEG C then are cooled to 1 DEG C per minute, last natural cooling completes reduction treatment, and is entirely going back
PH value is not less than 5 during the reason of original place；It is prepared by the 4th step, production：Wool, viscose glue, polyamide fibre and Kapp dragon copper ion fiber are passed through
It crosses and hair → cotton carding → drafting → rove → spun yarn → winder → doubling → double twisting, prepares a kind of antibiosis knitting yarn.
2. a kind of preparation processing method of antibiosis knitting yarn according to claim 1, it is characterised in that：In the first step,
The proportioning of raw material is 25% wool：38% viscose glue：30% polyamide fibre：7% Kapp dragon copper ion fiber.
3. a kind of preparation processing method of antibiosis knitting yarn according to claim 1, it is characterised in that：In third step
Sodium hydrosulfite is sodium dithionite.