CN106958066B - A kind of double-colored yarn of hydrophily copper ion antibacterial AB and its spinning process - Google Patents
A kind of double-colored yarn of hydrophily copper ion antibacterial AB and its spinning process Download PDFInfo
- Publication number
- CN106958066B CN106958066B CN201710281287.3A CN201710281287A CN106958066B CN 106958066 B CN106958066 B CN 106958066B CN 201710281287 A CN201710281287 A CN 201710281287A CN 106958066 B CN106958066 B CN 106958066B
- Authority
- CN
- China
- Prior art keywords
- yarn
- copper ion
- double
- fibre
- spinning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to yarn field of textiles, more particularly to a kind of double-colored yarn of hydrophily copper ion antibacterial AB, the ultra-fine regenerated celulose fibre of Mai Nuofen including Kapp dragon copper ion anti-bacterial fibre and 92%-96% that weight percent is 4%-8%, above-mentioned fiber is passed through into spinning process spun yarn, it is an advantage of the invention that, table Ganfeng is full, has three-dimensional sense, has both antibiotic property and hygroscopicity, it can be used for high-grade underwear, leisure housing, household textiles etc., meet consumer to functions of textile fabrics, diversified demand.
Description
Technical field
The present invention relates to yarn field of textiles more particularly to a kind of double-colored yarn of hydrophily copper ion antibacterial AB and its spinnings
Yarn process.
Background technique
As the improvement of people's living standards, proposing requirements at the higher level, especially underwear, socks to the antibiotic property of textile
Son, medical textile, home textile articles etc., it is desirable that fabric has antibacterial, antibacterial and bactericidal effect.Antibiotic fabric master currently on the market
Will there are two types of: one is spining technology is used, antibacterial agent is added spinning solution, prepares the fiber with antibacterial functions, then pass through
Textile process obtains antibiotic fabric;Another kind is that antibacterial agent is added in fabric postfinishing process using post-processing technology, is obtained
Antibiotic fabric.First method can obtain the fabric with durable antibiotic function, but when use anti-bacterial fibre progress textile process
Need adjusting process parameter;It is second method simple process, easy to operate, but antibacterial effect can continue in washing and use process
Decline.This project uses anti-bacterial fibre and ultra-fine viscose rayon, and exploitation spinning technique prepares the double-colored yarn of AB.The double-colored yarn of AB is
The rove of two different colours is fed into spinning frame simultaneously, is spinned by drawing-off, twisting, winding shaping.The yarn has
The contrast effect of strand, manufactured fabrics feel soft, table Ganfeng is full, and lines is clear, and color is colourful and has relief view
Feel effect, meets consumer to fabric personalization, fashion-orientation and diversified demand.In addition, with common colour-spun yarns such as colour mixture
Yarn is compared, and the color difference of the double-colored yarn of AB is more difficult to control, and yarn qualities are difficult to ensure.Therefore this project is directed to the performance of anti-bacterial fibre
Feature and the double-colored yarn technical characterstic of AB develop a set of dedicated spinning technique, obtain soft texture, antibacterial bacteriostatic it is double-colored
Yarn.
Summary of the invention
The object of the invention is that providing a kind of hydrophily copper ion antibacterial AB to solve the above-mentioned problems
Double-colored yarn.
The present invention is achieved through the following technical solutions above-mentioned purpose, a kind of double-colored yarn of hydrophily copper ion antibacterial AB
Line, which is characterized in that it includes the Mai Nuofen of Kapp dragon copper ion anti-bacterial fibre and 92%-96% that weight percent is 4%-8%
Above-mentioned fiber is passed through spinning process spun yarn by ultra-fine regenerated celulose fibre.
As another aspect of the present invention, a kind of spinning process of the double-colored yarn of hydrophily copper ion antibacterial AB is special
Sign is that the yarn is prepared according to the following steps and obtains:
Mixed processes: Kapp dragon copper ion anti-bacterial fibre and the ultra-fine regenerated celulose fibre of Mai Nuofen are put in proportion into circle
Disk griping cotton machine, when disk is arranged and wrapped, two kinds of fibrous septums interlock and guarantee that two kinds of fiber height are consistent, and gap is filled up;To Kapp
Imperial copper ion anti-bacterial fibre takes double grasp modes, that is, breaks into hard-pressed bale with baling press after grabbing, and then investment disk grabs cotton again
Machine is grabbed;
Shredding process;Carding step;
Mixing in doubling step: using the technological principle pressurizeed again, using three it is mixed simultaneously, 8 and close;
Together: 8 blended slivers being carried out and closed, are led using 8.65 times of total drafts and 1.53 times of back zone
It stretches, roller gauge is 12mm × 7mm × 18mm, quantification of 12.5-13.6g/5m, and cotton net tension is
1.131 times, sliver exporting speed 350m/s;
Two simultaneously: by 8, blended sliver is carried out and is closed afterwards together, after 9.35 times of total drafts and 1.43 times
Area's drawing-off, roller gauge are 12mm × 7mm × 18mm, and quantification of 11.7-12.9g/5m, cotton net tension is 1.131 times, out
Speed is 350m/s;
Three simultaneously: by 8 two and after blended sliver carry out and close, using 10.25 times of total drafts and 1.13 times
Back area draft, roller gauge are 12mm × 7mm × 18mm, and quantification of 10.0-11.3g/5m, cotton net tension is 1.131 times,
Sliver exporting speed is 350m/s;
Roving Frames: spinning tension, the uniform tension in order of large, medium and small yarn and front and rear row yarn are adjusted;
Spinning process: spinning process is carried out in SEILE textile equipment, A, B two will completed the process by coarse sand process
Double-colored yarn passes through the double horn mouth in SEILE textile equipment respectively, while feeding draft area;
Winding procedure.
Preferably, the quantification of 10g/5m-11g/5m of the carded sliver.
Preferably, the speed for grabbing cotton hired roughneck is 15r/min-18r/min, and kirschner beater speed is
220r/min-240r/min。
Preferably, the wind speed of spinning machine is 8.0m/s-13.8m/s;Gauge control in spinning machine between cylinder roller and licker-in
System is between 0.18-0.19mm.
The beneficial effects of the present invention are: table Ganfeng is full, has three-dimensional sense, has both antibiotic property and hygroscopicity, can be used in top grade
Clothing, leisure housing, household textiles etc., meet consumer to functions of textile fabrics, diversified demand, it is most important that, when
Kapp dragon copper ion anti-bacterial fibre and the ultra-fine regenerated celulose fibre of Mai Nuofen containing 5.3% are through spinning process disclosed by the invention
After blended, which shows to large intestine bar the antibacterial Indexs measure of staphylococcus aureus, Candida albicans, Escherichia coli
The sterilizing rate of bacterium reaches 99.3%, reaches 96.2% to the sterilizing rate of Candida albicans, to the sterilizing rate of staphylococcus aureus
Reach 99.1%, it is clear that the ultra-fine regenerated celulose fibre of Mai Nuofen enhances Kapp dragon copper ion anti-bacterial fibre to a certain extent
Anti-microbial property.
Specific embodiment
Below in conjunction with the subordinate list content in the embodiment of the present invention, technical solution in the embodiment of the present invention carries out clear
Chu is fully described by, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.
Based on the embodiments of the present invention, obtained by those of ordinary skill in the art without making creative efforts all
Other embodiments shall fall within the protection scope of the present invention.
Blended using Kapp dragon copper ion anti-bacterial fibre and the ultra-fine regenerated celulose fibre of Mai Nuofen, Kapp dragon copper ion is anti-
Bacterium fiber has strength and lasting antibacterial bacteriostatic, odor eliminating function, and it is that can reach excellent antibacterial effect that content, which is 5%,;
The ultra-fine regenerated celulose fibre good hygroscopicity of Mai Nuofen, softness, gloss are graceful, using mixed yarn product made of both fibers
With durable antibiotic, and soft comfortable, table Ganfeng are expired, clean mark.
Kapp dragon copper ion fiber is a kind of hygroscopicity acrylic fibers rich in copper ion, is in magma polymerization stage, with connecing
Branch copolymerization technique has grafted organic brass chain and high hydrophilic radical on acrylic fibers macromolecule side chain respectively, then through wet spinning technology
Made of New Acrylic.The copper ion of Kapp dragon copper ion fiber is present in fiber firmlyly and non-freely, thus has aobvious
Write and lasting antibacterial bacteriostatic, eliminate peculiar smell, self-cleaning healthy function, antibacterial effect to fungi it is further preferred that.The public affairs of the fiber are returned surely
Damp rate is up to 8%, significantly larger than common acrylic fibers, thus the textile prepared has excellent hygroscopicity and comfort.
The fiber shows that sterilizing rate is to the antibacterial Indexs measure of staphylococcus aureus, Candida albicans, Escherichia coli
99%, reach the highest AAA grade standard of national textile industry;In practical applications, only need to contain 5% copper ion fiber and its
His general fibre is blended, and after 50 times are washed repeatedly, mixed yarn still maintains excellent antibiotic property.
The ultra-fine regenerated celulose fibre of Mai Nuofen is one kind of ultra-fine regenerated celulose fibre, is made of pure natural raw material,
It is biodegradable;Its fineness is 0.5dtex, can spin high-count yarn, and the comfortable softness of made fabric touch, color are bright
It is beautiful, it is the desirable feedstock of high-quality clothes and home textile product.But the fibre strength is lower, mixed with Kapp dragon copper ion anti-bacterial fibre
After spinning, antibacterial functions can be not only obtained, moreover it is possible to improve yarn strength.
1, mixed processes
Kapp dragon copper ion anti-bacterial fibre and the ultra-fine regenerated celulose fibre of Mai Nuofen are put into according to the ratio of 5:95
Disc bale plucker should accomplish " interleaved, uniformity " when disk is arranged and wrapped, and guarantee that various raw material height are consistent, gap is filled out
It is full.Because Kapp dragon copper ion anti-bacterial fibre ratio is low, to guarantee to be uniformly mixed, double grasp modes are taken, that is, uses and is packaged after grabbing
Machine breaks into hard-pressed bale, and then investment disc bale plucker is grabbed again.Which other mixed cotton mode recruitments that compare are few, production
Efficiency is higher.
2, shredding process
Since the ultra-fine regenerated celulose fibre strength of Mai Nuofen is lower, hygroscopicity is strong, raw material is close, shredding process should be followed
The principle of " short route, low velocity, few strike ", is reduced as far as fibre damage, the kink of fiber is avoided to crumple.It should reduce each
The speed of hired roughneck, prevents excessive velocities from fiber is broken into synnema.In order to which two kinds of fibers are mixed evenly, to avoid since fiber is excessive
Coma caused by rolling.Fibre damage in order to prevent is production technology original with " more pines, less beat, beaten with comb generation, antiwind "
Then, cotton rolling weight should be grasped gently partially, grab cotton hired roughneck, the speed of kirschner beater needs to reduce, and wind speed improves, and gauge is appropriate at strike
Adjustment increases, in order to avoid damage fiber, increases short flannel and cotton knot, volume is sticked when coiled in order to prevent, can choose and several viscose glues are added
Rove.
3, the superiority and inferiority of carding step will have a direct impact on formation yarn nep, so to take into account combing and reduce two side of fibre damage
Face.With trocar cloth and optimize technique according to the performance characteristics of two kinds of raw materials, using flexible recombing technique, to control the carded sliver
Cotton knot and short flannel.The ultra-fine regenerated celulose fibre of Mai Nuofen is very thin, and single fiber strength is relatively small;Kapp dragon copper ion anti-bacterial fibre
It is strongly slightly higher, but because content is very low, so after two kinds of fiber mixing still based on the ultra-fine regenerated celulose fibre of Mai Nuofen, due to
The fibre property and cotton fiber performance are close, and cotton can be used to match trocar cloth.Licker-in speed should be suitably reduced, fiber damage is reduced
Wound;Cover board is suitably tightened with cylinder interval distance, strengthens the combing effect to fiber;Using lower cover plate speed, cover board is reduced
Flower;The moderate grasp of cotton net tension is dry to avoid carded sliver item is influenced;Pay attention to observing cotton net sharpness, accomplishes no clouding and broken hole, weight
Point controls sliver impurity number.
4, mixing in doubling step
In order to be mixed evenly sliver, color is consistent, and is further ensured that blending ratio, at the same guarantee fiber stretch with it is ripe
The item of item is dry uniformly, takes the technological principle of " jogging speed, again pressurization, big gauge, reasonable drawing-off ", takes three draftings, item
The quantitative partially light grasp of son, per pass number of doubling is 8, and extreme trace drafting uses the drawing frame with evereven, can be made each
Fiber blend is reduced than accurately, guaranteeing the color homogeneity of strip, and the extended parallelization of fiber can be improved because of hooked fibre
The cotton knot colluded with and formed.Simultaneously back area draft is bigger than normal for head, and simultaneously back area draft is smaller at end, to improve the uniformity of strip.Drafting work
Phenomena such as sequence should reduce stop frequency to the greatest extent, and cleaning will handle properly, and prevent unsmooth channel, wounded obstruction.
5, Roving Frames
Process of roving takes the technique of " light quantitative, small back area draft, reduces unexpected elongation at slightly larger roving twist factor " former
Then.The ultra-fine regenerated celulose fibre cohesive force of Mai Nuofen is poor, and roving twist factor will reasonably select, bigger than normal to easily cause spun yarn drafting not
It opens, rove less than normal is easy to produce unexpected elongation.Due to the double-colored yarn of AB be two different colours rove on spinning frame simultaneously
Feeding spins, and regular roving feeding should be controlled gently partially, choose rove horn mouth, avoid rove excessively fluffy.Adjust spinning
Tension, it is ensured that the tension of large, medium and small yarn and front and rear row yarn is almost the same, to reduce rove weight unevenness, reduce it is long slightly and
Long spun yarn defect.Under the premise of spun yarn not harmful drafting, roving twist factor grasp bigger than normal as far as possible, to increase the strength of rove, it is ensured that
Spinning process rove is smoothly unwound, and reduces the bad caused details of unwinding, or even break rove phenomenon.
6, spinning process
Spinning process is carried out in SEILE textile equipment, passes through double horn mouth respectively for A, B two, while feeding drawing-off
Area.In order to prevent because two root thickness yarns are fed, drafting force is excessive to be there is drawing-off and does not open phenomenon, spun yarn using " again pressurization, low velocity,
The technological principle of big back zone gauge, small back area draft ".The selection less than normal of spun yarn back area draft increases fibre cohesion, reel cage pressure
It lays particular stress on and grasps, select the reasonable duplex horn mouth of spacing, spacing will be adapted with the suitable for reading of shape tube air draught slot, while be ensured
Spun yarn machinery is in good condition.It should reinforce touring in operation, prevent single-strand spun phenomenon, influence product quality.
Spinning process prevents color fibre pollution from mainly starting with from the following: spinning board first must be from adjacent different product
Kind board is completely isolated, prevents color fibre to be mixed into other kinds and generates pollution;Secondly resultant yarn is it is noted that uneven twist, prevents uneven twist
The color difference of generation prevents spun yarn or rove repiece yarn wrong;Finally after spinning it is noted that carry out ending cleaning,
Necessary anti-pollution measure is taken, spun yarn bellows flower will be recycled individually.
7, winding procedure
Winding procedure requires speed relatively low, and tension is less than normal, to reduce the growth rate of filoplume, reduces broken end number, uses
The technological principle of " small tension receiving coil, low velocity ".Yarn path smooth clean is kept, prevents item is dry from deteriorating, filoplume increases.It rationally designs
Splicer parameter, controls joint quality, and reasonable set electronic clearing parameter especially reinforces details excision, prevents sub-thread from flowing into
Finished product.Reinforce electronic yarn clearer maintenance and cleaning, reduce leakage cut, accidentally cut, cut-in without ball phenomenon.
The double-colored yarn technical indicator of SF2016CM hydrophily copper ion antibacterial AB:
A appearance
1, uniform color, three-dimensional sense are strong;
2, item dry uniform, clean mark, any surface finish;
3, soft comfortable, elastic moderate.The main physical and chemical index of B
1, breaking strength: >=10cN/tex;
2, bar evenness :≤14.5%;
3, ten myriametre yarn defect :≤15;
4, hundred meters of deviation of weights: ± 2.5%;
5, colour fastness to rubbing: >=4 grades;
6, colour fasteness to sunlight: >=4 grades;
7, washing color fastness: >=3-4 grades;
8, colour fastness to perspiration: >=3-4 grades.Embodiment one
The double-colored yarn performance study of hydrophily copper ion antibacterial AB (selects the Kapp dragon copper ion anti-bacterial fibre of 5% weight
And 95% the ultra-fine regenerated celulose fibre of Mai Nuofen)
1, yarn tensile strength, item are dry and yarn defect is tested
According to the GB/T 3916-2013 measurement of yarn single yarn ultimate strength and elongation at break " textile package ",
GB/T 3292.1-2008 " the irregular test method capacitance method of textile Yarn Evenness ", " cotton and chemical fibre are pure by FZ/T 10007-2008
Spin, blended true qualities yarn inspection rule " and " the measurement oven drying of textile material moisture content and regain of GB/T 9995
Method " etc. tested, in view of there is presently no the standard for being directed to the pure spinning of viscose glue or blended dyed yarn, this project is referring to professional standard
FZ/T 12003-2006 " viscose rayon true qualities yarn " is compared.Test result as shown in table 1, this project exploitation
The indices of the double-colored yarn of SF2016CM hydrophily copper ion antibacterial AB are above professional standard.
1 yarn indices test result of table
* note: without same class standard.2, color fastness is tested
The yarn that this project is developed is made into knitted fabric sample, according to GB/T 651-2016 " textile color stability test examination
Test general rule ", GB/T 3920-2008 " textile color stability test colour fastness to rubbing ", GB/T8427-2008 " textile it is resistance to
The test of artificial light color fastness " and GB/T 12490-2007 " the resistance to family of textile and commercial laundering color fastness test method ",
Colour fastness to rubbing, colour fasteness to sunlight, washing color fastness and colour fastness to perspiration are tested respectively, as a result such as 2 institute of table
Show, the double-colored yarn of SF2016CM hydrophily copper ion antibacterial AB of this project exploitation, color fastness has been more than that national A class produces
Product standard.
The 2 double-colored yarn color fastness of SF2016CM hydrophily copper ion antibacterial AB of table
Stamp color fastness | The fabric that this project yarn is made into | National standard A class |
Colour fastness to rubbing/grade | 5 | 4 |
Colour fasteness to sunlight/grade | 5 | 4 |
Washing color fastness/grade | 4-5 | 3-4 |
Colour fastness to perspiration/grade | 4-5 | 3-4 |
Note: national standard refers to " GB 18401-2010 " national general safety technical code for textile products " ".3, antibiotic property
Energy
It is tested according to FZ/T 73023-2006 " antibiosis knitting product ", as a result as shown in table 3.Referring to GB/T
20944.3-2008 " evaluation of antibacterial textile performance ": the bacteriostasis rate to staphylococcus aureus and Escherichia coli is more than
70%, it is more than 60% to the bacteriostasis rate of Candida albicans, that is, shows that sample has antibacterial effect.Therefore, this project is developed
The SF2016CM hydrophily double-colored yarn of copper ion antibacterial AB has excellent antibiotic property.
The bacteriostasis rate of the 3 double-colored yarn of SF2016CM hydrophily copper ion antibacterial AB of table
Escherichia coli | Staphylococcus aureus | Candida albicans | |
Bacteriostasis rate/% | 99% | 99% | 96% |
The research and development success of the double-colored yarn of SF2016CM hydrophily copper ion antibacterial AB, it is with good economic efficiency and social
Benefit.The capability of independent innovation for greatly strengthening my company, further improves technology management level, promotes company's production warp
Battalion reaches a new level.The new product can satisfy the demand of domestic and international different clients.
The project can increase employee 50 newly after going into operation, and be made that contribution to maintain social stability.This project is original
Colour-spun yarns production line on the basis of reorganization and expansion form, not will form new waste, discharge of wastewater source.Company will be to the project construction
The waste yarn, the useless fiber that generate in the process etc. are outer to sell comprehensive utilization, and solid waste realizes zero-emission.
According to market analysis, the SF2016CM hydrophily double-colored yarn of copper ion antibacterial AB is by test marketing, very by client
It welcomes, cost advantage is obvious, and competitiveness is strong, economic benefits.After new product is gone into operation, annual output is up to 500 tons, factory
4.5 ten thousand yuan/ton of average sales price, it can be achieved 22,500,000 yuan of annual sales revenue year, 7,590,000 yuan of annual profits tax.SF2016CM parent
The double-colored yarn function admirable of aqueous copper ion antibacterial AB, cheap, development prospect is very optimistic.
Economic Efficiency is as follows:
Production cost: 3.5 ten thousand yuan/ton average
Newly-increased income from sales: 4.5 × 500=2250, the ten thousand yuan/year new profit: 4.5 × 500-3.5 × 5,00=,500 ten thousand
Member/Nian Xinzeng tax: 2250 × 11.5%=259, ten thousand yuan/year
Newly-increased profits tax: ten thousand yuan/year of 500+259=759
Embodiment two (select 5.3% weight Kapp dragon copper ion anti-bacterial fibre and 94.7% Mai Nuofen it is ultra-fine again
Raw cellulose fibre)
4 yarn indices test result of table
5 bacteriostasis rate of table
Escherichia coli | Staphylococcus aureus | Candida albicans | |
Bacteriostasis rate/% | 99.3% | 99.1% | 96.2% |
Embodiment three (selects the Kapp dragon copper ion anti-bacterial fibre of 4% weight and the 96% ultra-fine regeneration fibre of Mai Nuofen
Cellulose fiber)
6 yarn indices test result of table
7 bacteriostasis rate of table
Escherichia coli | Staphylococcus aureus | Candida albicans | |
Bacteriostasis rate/% | 98.6% | 98.2% | 95.3% |
Example IV (selects the Kapp dragon copper ion anti-bacterial fibre of 8% weight and the 92% ultra-fine regeneration fibre of Mai Nuofen
Cellulose fiber)
8 yarn indices test result of table
9 bacteriostasis rate of table
Escherichia coli | Staphylococcus aureus | Candida albicans | |
Bacteriostasis rate/% | 98.9% | 96.7% | 93.2% |
By table 4-5 it is found that when the ultra-fine regenerated cellulose of Kapp dragon copper ion anti-bacterial fibre and Mai Nuofen for containing 5.3% is fine
For dimension after spinning process disclosed by the invention is blended, which resists staphylococcus aureus, Candida albicans, Escherichia coli
Bacterium Indexs measure shows to reach 99.3% to the sterilizing rate of Escherichia coli, reaches 96.2% to the sterilizing rate of Candida albicans, right
The sterilizing rate of staphylococcus aureus reaches 99.1%, it is clear that the ultra-fine regenerated celulose fibre of Mai Nuofen enhances to a certain extent
The anti-microbial property of Kapp dragon copper ion anti-bacterial fibre, produces unexpected effect, it is most important that, when fineness of yarn is
When 10tex, breaking strength reaches 19.6 cN/tex, that is to say, that when containing 5.3% Kapp dragon copper ion anti-bacterial fibre with
The ultra-fine regenerated celulose fibre of Mai Nuofen is after spinning process disclosed by the invention is blended, not only without reducing breaking strength, and
Other various aspects all have a certain upgrade, and produce unexpected effect.
The present invention is applicant's numerous experiments, selected as a result, therefore having significant progress.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Benefit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent elements of the claims
Variation is included within the present invention.Any subordinate list content in claim should not be construed as limiting the claims involved.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (1)
1. a kind of spinning process of the double-colored yarn of hydrophily copper ion antibacterial AB, it includes that weight percent is 4%-8%
The ultra-fine regenerated celulose fibre of Mai Nuofen of Kapp dragon copper ion anti-bacterial fibre and 92%-96%, passes through spinning for above-mentioned fiber
Technique spun yarn, which is characterized in that the yarn is prepared according to the following steps and obtains:
Mixed processes: Kapp dragon copper ion anti-bacterial fibre and the ultra-fine regenerated celulose fibre of Mai Nuofen are put in proportion into disk and grabbed
Cotton machine, when disk is arranged and wrapped, two kinds of fibrous septums interlock and guarantee that two kinds of fiber height are consistent, and gap is filled up;To Kapp dragon copper
Ion antibacterial fiber takes double grasp modes, that is, breaks into hard-pressed bale with baling press after grabbing, then again investment disc bale plucker into
Row crawl;
Shredding process;Carding step;
Mixing in doubling step: using the technological principle pressurizeed again, using three it is mixed simultaneously, 8 and close;Together: by 8 blended slivers into
It goes and closes, using 8.65 times of total draft
And 1.53 times of back area draft, roller gauge are 12mm × 7mm × 18mm, quantification of 12.5-13.6g/5m, cotton
Net tension is 1.131 times, sliver exporting speed 350m/s;
Two simultaneously: by 8, blended sliver is carried out and is closed afterwards together, is led using 9.35 times of total drafts and 1.43 times of back zone
It stretches, roller gauge is 12mm × 7mm × 18mm, and quantification of 11.7-12.9g/5m, cotton net tension is 1.131 times, shaping speed
Degree is 350m/s;
Three simultaneously: by 8 two and rear blended sliver is carried out and is closed, using 10.25 times of total drafts and 1.13 times of back zone
Drawing-off, roller gauge are 12mm × 7mm × 18mm, and quantification of 10.0-11.3g/5m, cotton net tension is 1.131 times, shaping
Speed is 350m/s;
Roving Frames: spinning tension, the uniform tension in order of large, medium and small yarn and front and rear row yarn are adjusted;
Spinning process: spinning process is carried out in SEILE textile equipment, double-colored by A, B two completed the process by Roving Frames
Yarn passes through the double horn mouth in SEILE textile equipment respectively, while feeding draft area;
Winding procedure.