CN105936807A - Stain-resistant breathable elastic metal flash paint for photo frames - Google Patents
Stain-resistant breathable elastic metal flash paint for photo frames Download PDFInfo
- Publication number
- CN105936807A CN105936807A CN201610417177.0A CN201610417177A CN105936807A CN 105936807 A CN105936807 A CN 105936807A CN 201610417177 A CN201610417177 A CN 201610417177A CN 105936807 A CN105936807 A CN 105936807A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- weight
- defoamer
- resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a stain-resistant breathable elastic metal flash paint for photo frames. The paint comprises the following raw materials by weight: 25-45 parts of alkyd resin, 6-12 parts of amino resin, 35-45 parts of an elastic emulsion AP-5085, 1-5 parts of modified fatty acid polyamide wax, 2-6 parts of EVA wax, 1-4 parts of water-based acetic acid-butyryl cellulose, 2-5 parts of a coupling agent, 4-8 parts of water-based aluminum powder, 1-6 parts of organic bentonite, 2-6 parts of silvery white pearl powder, 4-8 parts of nano silica slurry, 3-6 parts of a dispersant 731A, 2-6 parts of a preservative, 4-8 parts of a thickening agent RM-8W, 2-6 parts of a leveling agent RM-2020, 1-6 parts of a defoaming agent, and 4-8 parts of a mixed diluent. The metal flash paint provided by the invention has excellent stain resistance and breathability, and has good elastic performance.
Description
Technical field
The present invention relates to flash coating material field, particularly relate to a kind of photo frame resistant poromeric elastic flash metal luster and be coated with
Material.
Background technology
At present, present in metal flash paint, flakey aluminium powder forms the arranged in parallel of multilamellar, energy in film
Enough ultraviolet, infrared ray and visible ray are effectively reflected, delay its aging damage to film, also can
Enough infiltrations effectively stoping water, gas and ion, because of decoration and the antiseptic effect of its this uniqueness, at photo frame table
In topcoating film, application is more and more.
The resistant of metallized coating the most of the prior art, ventilative and elastic performance cannot meet actual making
The demand of used time, therefore needs badly and designs a kind of excellent resistant, breathes freely and the metallized coating of elastic performance comes
Demand when meeting actually used.
Summary of the invention
For solving technical problem present in background technology, the present invention proposes a kind of photo frame resistant poromeric elastic
Metallized coating, has the resistant of excellence, ventilative and elastic performance.
A kind of photo frame resistant poromeric elastic metallized coating that the present invention proposes, its raw material wraps by weight
Include: alkyd resin 25-45 part, amino resins 6-12 part, elastic emulsion AP-5085 35-45 part, modification
Fatty acid polyamide wax 1-5 part, EVA wax 2-6 part, aqueous acetic acid-bytyry cellulose 1-4 part, coupling
Agent 2-5 part, aqueous aluminum powder 4-8 part, organobentonite 1-6 part, silvery white pearl essence 2-6 part, nanometer two
Silicon oxide slurry 4-8 part, dispersant 731A 3-6 part, preservative 2-6 part, thickening agent RM-8W 4-8 part,
Levelling agent RM-2020 2-6 part, defoamer 1-6 part, mixed diluent 4-8 part.
Preferably, described coupling agent is by coupling agent KH-560 and coupling agent NDZ-401 1-3:2-5 by weight
Mix.
Preferably, described preservative is mixed by weight 2-5:3-9 by dry film preservative BAF and antifungus agent LXE
Conjunction forms.
Preferably, described defoamer is mixed by weight 1-3:2-5 by defoamer A36 and defoamer AMP-95
Conjunction forms.
Preferably, its raw material includes by weight: alkyd resin 28-42 part, amino resins 7-11 part, bullet
Property latex A P-5085 38-42 part, modified fat acid polyamide wax 2-4 part, EVA wax 3-5 part, aqueous vinegar
Acid-bytyry cellulose 2-3 part, coupling agent 3-4 part, aqueous aluminum powder 5-7 part, organobentonite 2-5 part,
Silvery white pearl essence 3-5 part, nano silicon slurry 5-7 part, dispersant 731A 4-5 part, preservative 3-5
Part, thickening agent RM-8W 5-7 part, levelling agent RM-2020 3-5 part, defoamer 2-5 part, mixed diluting
Agent 5-7 part.
Preferably, its raw material includes by weight: alkyd resin 35 parts, 9 parts of amino resins, elastic emulsion
AP-5085 40 parts, modified fat acid polyamide wax 3 parts, 4 parts of EVA wax, aqueous acetic acid-bytyry fiber
Element 2.5 parts, coupling agent 3.5 parts, aqueous aluminum powder 6 parts, organobentonite 3.5 parts, silvery white pearl essence 4
Part, 6 parts of nano silicon slurry, dispersant 731A 4.5 parts, preservative 4 parts, thickening agent RM-8W 6
Part, levelling agent RM-2020 4 parts, defoamer 3.5 parts, mixed diluent 6 parts.
Preferably, described mixed diluent is by dimethylbenzene, butyl acetate, ethylene glycol ether acetate and butanol
Mix by weight 4-5:1-3:2-4:0.5-1.5.
A kind of photo frame resistant poromeric elastic metallized coating of the present invention, its raw material include alkyd resin,
Amino resins, elastic emulsion AP-5085, modified fat acid polyamide wax, EVA wax, aqueous acetic acid-butyryl
Base cellulose, coupling agent, aqueous aluminum powder, organobentonite, silvery white pearl essence, nano silicon slurry,
Dispersant 731A, preservative, thickening agent RM-8W, levelling agent RM-2020, defoamer and mixed diluent,
Wherein, with alkyd resin, amino resins and elastic emulsion AP-5085 as base material, give coating of the present invention excellent
Different hardness, wearability, toughness and elasticity；With modified fat acid polyamide wax, EVA wax and aqueous acetic acid-
Bytyry cellulose acts on aqueous aluminum powder, strengthens solvent release, promotes solvent quickly to volatilize, so that
Film rapid desufflation, by means of this quick and powerful contractility, evens up aluminum paste, it is achieved orientation row
Row, by conservative control proportioning, are effectively increased the directionality of aluminium powder, are difficult to grow dim, and construction easily, has
There are good gloss and flash effect；Add organobentonite, silvery white pearl essence and nano silicon slurry,
Under the effect of coupling agent, it is achieved that to alkyd resin, amino resins and the surface of elastic emulsion AP-5085
Modification, is effectively increased weatherability and the wearability of base material；And at dispersant 731A, preservative, thickening agent
Under RM-8W, levelling agent RM-2020, defoamer and mixed diluent coordinate, promote the flash metal luster of the present invention
Coating has the resistant of excellence, ventilative and elastic performance.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described in detail, it should be appreciated that embodiment is served only for
The bright present invention rather than be used for limiting the invention, any made on the basis of the present invention amendment,
Equivalents etc. are the most within the scope of the present invention.
In detailed description of the invention, the weight portion of alkyd resin can be 25 parts, 26 parts, 27 parts, 28 parts,
29 parts, 30 parts, 31 parts, 32 parts, 33 parts, 34 parts, 35 parts, 36 parts, 37 parts, 38 parts, 39 parts,
40 parts, 41 parts, 42 parts, 43 parts, 44 parts, 45 parts；The weight portion of amino resins can be 6 parts, 7
Part, 8 parts, 9 parts, 10 parts, 11 parts, 12 parts；The weight portion of elastic emulsion AP-5085 can be 35 parts,
36 parts, 37 parts, 38 parts, 39 parts, 40 parts, 41 parts, 42 parts, 43 parts, 44 parts, 45 parts；Modified
The weight portion of fatty acid polyamide wax can be 1 part, 2 parts, 3 parts, 4 parts, 5 parts；The weight portion of EVA wax
It can be 2 parts, 3 parts, 4 parts, 5 parts, 6 parts；The weight portion of aqueous acetic acid-bytyry cellulose can be
1 part, 1.5 parts, 2 parts, 2.5 parts, 3 parts, 3.5 parts, 4 parts；The weight portion of coupling agent can be 2 parts,
2.5 parts, 3 parts, 3.5 parts, 4 parts, 4.5 parts, 5 parts；The weight portion of aqueous aluminum powder can be 4 parts, 5
Part, 6 parts, 7 parts, 8 parts；Bentonite weight portion can be 1 part, 1.5 parts, 2 parts, 2.5 parts,
3 parts, 3.5 parts, 4 parts, 4.5 parts, 5 parts, 5.5 parts, 6 parts；The weight portion of silvery white pearl essence can be
2 parts, 3 parts, 4 parts, 5 parts, 6 parts；The weight portion of nano silicon slurry can be 4 parts, 5 parts,
6 parts, 7 parts, 8 parts；The weight portion of dispersant 731A can be 3 parts, 3.5 parts, 4 parts, 4.5 parts, 5
Part, 5.5 parts, 6 parts；The weight portion of preservative can be 2 parts, 3 parts, 4 parts, 5 parts, 6 parts；Thickening
The weight portion of agent RM-8W can be 4 parts, 5 parts, 6 parts, 7 parts, 8 parts；The weight of levelling agent RM-2020
Amount part can be 2 parts, 3 parts, 4 parts, 5 parts, 6 parts；The weight portion of defoamer can be 1 part, 1.5 parts,
2 parts, 2.5 parts, 3 parts, 3.5 parts, 4 parts, 4.5 parts, 5 parts, 5.5 parts, 6 parts；Mixed diluent
Weight portion can be 4 parts, 5 parts, 6 parts, 7 parts, 8 parts.
Embodiment 1
A kind of photo frame resistant poromeric elastic metallized coating that the present invention proposes, its raw material wraps by weight
Include: alkyd resin 35 parts, 9 parts of amino resins, elastic emulsion AP-5085 40 parts, modified fat acid gather
Amide waxe 3 parts, 4 parts of EVA wax, aqueous acetic acid-bytyry cellulose 2.5 parts, coupling agent 3.5 parts, water
Property aluminium powder 6 parts, organobentonite 3.5 parts, silvery white pearl essence 4 parts, 6 parts of nano silicon slurry,
Dispersant 731A 4.5 parts, preservative 4 parts, thickening agent RM-8W 6 parts, levelling agent RM-2020 4 parts,
Defoamer 3.5 parts, mixed diluent 6 parts.
Wherein, described coupling agent is mixed by weight 1.5:3.5 by coupling agent KH-560 and coupling agent NDZ-401
Conjunction forms.Described preservative is mixed by weight 3.5:6 by dry film preservative BAF and antifungus agent LXE.
Described defoamer is mixed by weight 2:3.5 by defoamer A36 and defoamer AMP-95.Described mixed
Close diluent by dimethylbenzene, butyl acetate, ethylene glycol ether acetate and butanol by weight 4.5:2:3:
1 mixes.
Embodiment 2
A kind of photo frame resistant poromeric elastic metallized coating that the present invention proposes, its raw material wraps by weight
Include: alkyd resin 25 parts, 12 parts of amino resins, elastic emulsion AP-5085 35 parts, modified fat acid gather
Amide waxe 5 parts, 2 parts of EVA wax, aqueous acetic acid-bytyry cellulose 4 parts, coupling agent 2 parts, aqueous aluminum
8 parts of powder, organobentonite 1 part, silvery white pearl essence 6 parts, 4 parts of nano silicon slurry, dispersant
731A 6 parts, preservative 2 parts, thickening agent RM-8W 8 parts, levelling agent RM-2020 2 parts, defoamer 6
Part, mixed diluent 4 parts.
Wherein, described coupling agent is by coupling agent KH-560 and the coupling agent NDZ-401 mixing of 1:5 by weight
Become.Described preservative is mixed by weight 2:9 by dry film preservative BAF and antifungus agent LXE.Described
Defoamer is mixed by weight 1:5 by defoamer A36 and defoamer AMP-95.Described mixed diluting
Agent is mixed by weight 4:3:2:1.5 by dimethylbenzene, butyl acetate, ethylene glycol ether acetate and butanol
Form.
Embodiment 3
A kind of photo frame resistant poromeric elastic metallized coating that the present invention proposes, its raw material wraps by weight
Include: alkyd resin 45 parts, 6 parts of amino resins, elastic emulsion AP-5085 45 parts, modified fat acid gather
Amide waxe 1 part, 6 parts of EVA wax, aqueous acetic acid-bytyry cellulose 1 part, coupling agent 5 parts, aqueous aluminum
4 parts of powder, organobentonite 6 parts, silvery white pearl essence 2 parts, 8 parts of nano silicon slurry, dispersant
731A 3 parts, preservative 6 parts, thickening agent RM-8W 4 parts, levelling agent RM-2020 6 parts, defoamer 1
Part, mixed diluent 8 parts.
Wherein, described coupling agent is by coupling agent KH-560 and the coupling agent NDZ-401 mixing of 3:2 by weight
Become.Described preservative is mixed by weight 5:3 by dry film preservative BAF and antifungus agent LXE.Described
Defoamer is mixed by weight 3:2 by defoamer A36 and defoamer AMP-95.Described mixed diluting
Agent is mixed by weight 5:1:4:0.5 by dimethylbenzene, butyl acetate, ethylene glycol ether acetate and butanol
Form.
Embodiment 4
A kind of photo frame resistant poromeric elastic metallized coating that the present invention proposes, its raw material wraps by weight
Include: alkyd resin 28 parts, 11 parts of amino resins, elastic emulsion AP-5085 38 parts, modified fat acid gather
Amide waxe 4 parts, 3 parts of EVA wax, aqueous acetic acid-bytyry cellulose 3 parts, coupling agent 3 parts, aqueous aluminum
7 parts of powder, organobentonite 2 parts, silvery white pearl essence 5 parts, 5 parts of nano silicon slurry, dispersant
731A 5 parts, preservative 3 parts, thickening agent RM-8W 7 parts, levelling agent RM-2020 3 parts, defoamer 5
Part, mixed diluent 5 parts.
Wherein, described coupling agent is mixed by weight 1.5:4 by coupling agent KH-560 and coupling agent NDZ-401
Form.Described preservative is mixed by weight 3:8 by dry film preservative BAF and antifungus agent LXE.Institute
State defoamer to be mixed by weight 1.5:4 by defoamer A36 and defoamer AMP-95.Described mixing
Diluent is by dimethylbenzene, butyl acetate, ethylene glycol ether acetate and butanol 4.2:2.5:2.5 by weight:
1.2 mix.
Embodiment 5
A kind of photo frame resistant poromeric elastic metallized coating that the present invention proposes, its raw material wraps by weight
Include: alkyd resin 42 parts, 7 parts of amino resins, elastic emulsion AP-5085 42 parts, modified fat acid gather
Amide waxe 2 parts, 5 parts of EVA wax, aqueous acetic acid-bytyry cellulose 2 parts, coupling agent 4 parts, aqueous aluminum
5 parts of powder, organobentonite 5 parts, silvery white pearl essence 3 parts, 7 parts of nano silicon slurry, dispersant
731A 4 parts, preservative 5 parts, thickening agent RM-8W 5 parts, levelling agent RM-2020 5 parts, defoamer 2
Part, mixed diluent 7 parts.
Wherein, described coupling agent is mixed by weight 2.5:3 by coupling agent KH-560 and coupling agent NDZ-401
Form.Described preservative is mixed by weight 4:4 by dry film preservative BAF and antifungus agent LXE.Institute
State defoamer to be mixed by weight 2.5:3 by defoamer A36 and defoamer AMP-95.Described mixing
Diluent is by dimethylbenzene, butyl acetate, ethylene glycol ether acetate and butanol 4.8:1.5:3.5 by weight:
0.8 mixes.
The above, the only present invention preferably detailed description of the invention, but protection scope of the present invention not office
Being limited to this, any those familiar with the art is in the technical scope that the invention discloses, according to this
The technical scheme of invention and inventive concept thereof in addition equivalent or change, all should contain the protection in the present invention
Within the scope of.
Claims (7)
1. a photo frame resistant poromeric elastic metallized coating, it is characterised in that its raw material is by weight
Including: alkyd resin 25-45 part, amino resins 6-12 part, elastic emulsion AP-5085 35-45 part, change
Property fatty acid polyamide wax 1-5 part, EVA wax 2-6 part, aqueous acetic acid-bytyry cellulose 1-4 part, idol
Connection agent 2-5 part, aqueous aluminum powder 4-8 part, organobentonite 1-6 part, silvery white pearl essence 2-6 part, nanometer
Silica slurry 4-8 part, dispersant 731A 3-6 part, preservative 2-6 part, thickening agent RM-8W 4-8
Part, levelling agent RM-2020 2-6 part, defoamer 1-6 part, mixed diluent 4-8 part.
Photo frame resistant poromeric elastic metallized coating the most according to claim 1, it is characterised in that
Described coupling agent is mixed by weight 1-3:2-5 by coupling agent KH-560 and coupling agent NDZ-401.
Photo frame resistant poromeric elastic metallized coating the most according to claim 1 and 2, its feature
Being, described preservative is mixed by weight 2-5:3-9 by dry film preservative BAF and antifungus agent LXE.
4. according to the resistant poromeric elastic metallized coating of the photo frame described in any one of claim 1-3, its
Being characterised by, described defoamer is mixed by weight 1-3:2-5 by defoamer A36 and defoamer AMP-95
Form.
5. according to the resistant poromeric elastic metallized coating of the photo frame described in any one of claim 1-4, its
Being characterised by, its raw material includes by weight: alkyd resin 28-42 part, amino resins 7-11 part, elasticity
Latex A P-5085 38-42 part, modified fat acid polyamide wax 2-4 part, EVA wax 3-5 part, aqueous vinegar
Acid-bytyry cellulose 2-3 part, coupling agent 3-4 part, aqueous aluminum powder 5-7 part, organobentonite 2-5 part,
Silvery white pearl essence 3-5 part, nano silicon slurry 5-7 part, dispersant 731A 4-5 part, preservative
3-5 part, thickening agent RM-8W 5-7 part, levelling agent RM-2020 3-5 part, defoamer 2-5 part, mixing
Diluent 5-7 part.
6. according to the resistant poromeric elastic metallized coating of the photo frame described in any one of claim 1-5, its
Being characterised by, its raw material includes by weight: alkyd resin 35 parts, 9 parts of amino resins, elastic emulsion
AP-5085 40 parts, modified fat acid polyamide wax 3 parts, 4 parts of EVA wax, aqueous acetic acid-bytyry fiber
Element 2.5 parts, coupling agent 3.5 parts, aqueous aluminum powder 6 parts, organobentonite 3.5 parts, silvery white pearl essence 4
Part, 6 parts of nano silicon slurry, dispersant 731A 4.5 parts, preservative 4 parts, thickening agent RM-8W
6 parts, levelling agent RM-2020 4 parts, defoamer 3.5 parts, mixed diluent 6 parts.
7. according to the resistant poromeric elastic metallized coating of the photo frame described in any one of claim 1-6, its
Being characterised by, described mixed diluent is pressed by dimethylbenzene, butyl acetate, ethylene glycol ether acetate and butanol
Weight ratio 4-5:1-3:2-4:0.5-1.5 mixes.