CN105925017A - 一种环保内饰涂层材料 - Google Patents
一种环保内饰涂层材料 Download PDFInfo
- Publication number
- CN105925017A CN105925017A CN201610303064.8A CN201610303064A CN105925017A CN 105925017 A CN105925017 A CN 105925017A CN 201610303064 A CN201610303064 A CN 201610303064A CN 105925017 A CN105925017 A CN 105925017A
- Authority
- CN
- China
- Prior art keywords
- coating material
- interior trim
- formaldehyde
- environmentally
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种环保内饰涂层材料,其特征在于,按照如下质量分数进行配比:重钙40%‑60%,灰钙15%‑25%,纤维素3%‑5%,硅藻泥25%‑35%,辅料1%‑5%,其中辅料的主要组分为:纳米级贵金属催化剂,改性二氧化钛,硅酸盐水泥,滑石粉,纳米活性炭,可再分散乳胶粉,隔热反射材料,防霉剂,高岭土,色料,抗碱剂,凹凸棒粘土粉,木质纤维。本发明制备的环保内饰涂层材料具有很强的吸附性和离子交换性能,相比传统涂层材料,可大大提升吸附空气中的甲醛的能力,同时在催化剂作用下将部分甲醛等有害气体,解决传统产品在干燥后重新释放甲醛等,无法彻底清除甲醛的问题,兼具净化空气、杀菌除臭等效果。
Description
技术领域
本发明涉及一种墙体涂料,具体涉及一种环保墙体内饰涂层材料。
背景技术
涂料作为目前家居装饰最为普遍的材料,已经被千家万户作为装修的必备材料,随着生活水平的提高,人们对环保、隔音、防辐射等要求越来越高。
近年来,许多环保新型室内外涂料、装修材料,在国内外越来越受到消费者的青睐,不含有害化学物质,除了具有不燃、隔音、防水、重量轻以及隔热等特点外,还有除湿、除臭、净化室内空气等作用,是优良的环保型室内外装修材料。
硅藻泥作为一种新型的天然材料,具有消除甲醛、净化空气、调节湿度、释放负氧离子、防火阻燃、墙面自洁、杀菌除臭等功能,越来越多的被用于新型涂层材料,由于硅藻泥健康环保,不仅有很好装饰性,还具有功能性,是替代壁纸和乳胶漆的新一代室内装饰材料,但是传统的硅藻泥产品在隔热反射、水分吸收、细度调节、氨、甲醛、苯等净化方面效果有待提升。
发明内容
为了解决传统的硅藻泥产品在隔热反射、水分吸收、细度调节、氨、甲醛、苯等净化方面的不足,本发明提供了一种简单易操作的环保内饰涂层材料配比和制备方法,具体如下:
本发明涉及一种环保内饰涂层材料,其特征在于,按照如下质量分数进行配比:重钙40%-60%,灰钙15%-25%,纤维素3%~5%,硅藻泥25%-35%,辅料1%-5%;
辅料的主要组分为:纳米级贵金属催化剂3-5份,改性二氧化钛10-15份,硅酸盐水泥10-20份,滑石粉10-30份,纳米活性炭5-10份,可再分散乳胶粉1-3份,隔热反射材料3-8份,防霉剂0.1-1份,高岭土5-15份,色料0.1-0.5份,抗碱剂3-8份,凹凸棒粘土粉3-8份,木质纤维1-2份。
进一步的,所述重钙为325目,白度恳求:95%,碳酸钙含量:98%。
进一步的,所述改性二氧化钛,其含量大于98%。
进一步的,所述硅藻泥为天然硅藻土,其中主要成分是二氧化硅,白色,其中二氧化硅含量不小于90%。
进一步的,所述环保内饰涂层材料制备方法如下:
(1)、首先按照比例称量一定量的主料和辅料,分别放置在无尘的密闭容器;
(2)、将主按照比例混合加入洁净的搅拌机进行充分搅拌,搅拌时间为50分钟,然后按照质量比例依次加入硅酸盐水泥,滑石粉,纳米活性炭,可再分散乳胶粉,隔热反射材料,防霉剂,高岭土,色料,抗碱剂,凹凸棒粘土粉,木质纤维,纳米级贵金属催化剂,改性二氧化钛,根据搅拌的均匀度判断, 1.5-2小时后即可关闭搅拌机;
(3)、将上述搅拌均匀后的材料容器盛放后置入干燥箱进行干燥,50-60℃干燥24-48小时,采用聚乙烯包装袋进行分装,密封包装即可。
与现有技术相比,本发明的益处是:
本发明中加入硅藻土为天然硅藻土,除了不会散发出对人体有害的化学物质外,还有改善居住环境的作用。
主要表现在在室内的湿度上升时,硅藻土壁材上的超微细孔能够自动吸收空气中的水份,将其储存起来。如果室内空气中的水份减少、湿度下降,硅藻土壁材就能够将储存在超微细孔中的水份释放出来,其次,加入改性二氧化钛能够长时间消除异味和吸收、分解有害化学物质,并能够长期保持室内墙面清洁,同时纳米级贵金属催化剂能有效的帮助分解如苯、氨等有害化学物质,可大大提升吸附空气中的甲醛的能力。
具体实施方式
实施例1
一种环保内饰涂层材料,按照如下质量分数进行配比:重钙45%,灰钙15%,纤维素3%,硅藻泥32%,辅料5%,其中辅料的主要组分为:纳米级贵金属催化剂3份,改性二氧化钛10份,硅酸盐水泥10份,滑石粉10份,纳米活性炭5份,可再分散乳胶粉1份,隔热反射材料3份,防霉剂0.1份,高岭土5份,色料0.1份,抗碱剂3份,凹凸棒粘土粉3份,木质纤维1份。
实施例2
一种环保内饰涂层材料,按照如下质量分数进行配比:重钙60%,灰钙10%,纤维素4%,硅藻泥25%%,辅料1%,其中辅料的主要组分为:纳米级贵金属催化剂5份,改性二氧化钛15份,硅酸盐水泥20份,滑石粉30份,纳米活性炭10份,可再分散乳胶粉3份,隔热反射材料8份,防霉剂1份,高岭土15份,色料0.5份,抗碱剂8份,凹凸棒粘土粉8份,木质纤维2份。
实施例3
一种环保内饰涂层材料,按照如下质量分数进行配比:重钙50%,灰钙15%,纤维素3%,硅藻泥31%,辅料1%,其中辅料的主要组分为:纳米级贵金属催化剂5份,改性二氧化钛12份,硅酸盐水泥15份,滑石粉20份,纳米活性炭8份,可再分散乳胶粉2份,隔热反射材料3份,防霉剂1份,高岭土10份,色料0.3份,抗碱剂5份,凹凸棒粘土粉6份,木质纤维1.8份。
Claims (2)
1.一种环保内饰涂层材料,其特征在于包括主料和辅料,主料按照以下百分比组成:重钙40%-60%,灰钙15%-25%,纤维素3%~5%,硅藻泥25%-35%,辅料按照以下质量比组成:纳米级贵金属催化剂3-5份,改性二氧化钛10-15份,硅酸盐水泥10-20份,滑石粉10-30份,纳米活性炭5-10份,可再分散乳胶粉1-3份,隔热反射材料3-8份,防霉剂0.1-1份,高岭土5-15份,色料0.1-0.5份,抗碱剂3-8份,凹凸棒粘土粉3-8份,木质纤维1-2份。
2.根据权利要求1所述,一种环保内饰涂层材料,其制备方法如下:
(1)、首先按照比例称量一定量的主料和辅料,分别放置在无尘的密闭容器;
(2)、将主按照比例混合加入洁净的搅拌机进行充分搅拌,搅拌时间为50分钟,然后按照质量比例依次加入硅酸盐水泥,滑石粉,纳米活性炭,可再分散乳胶粉,隔热反射材料,防霉剂,高岭土,色料,抗碱剂,凹凸棒粘土粉,木质纤维,纳米级贵金属催化剂,改性二氧化钛,根据搅拌的均匀度判断, 1.5-2小时后即可关闭搅拌机;
(3)、将上述搅拌均匀后的材料容器盛放后置入干燥箱进行干燥,50-60℃干燥24-48小时,采用聚乙烯包装袋进行分装,密封包装即可。